The objective of the present work was the investigation and demonstration of the potential of sol-gel alumina layers as corrosion protection of commercial power plant steels under oxyfuel conditions. The starting points of this work were modified Yoldas-sols which were developed in the BAM-department 5.6. These sols were suitable for the spin-coating method only. The application of coatings on tubes by spin-coating is impossible. Therefore, the chemical composition of the modified Yoldas-sol had to be adapted to the dip- and spray-coating techniques.
Exclusively the sol with the composition s-0.52-6-1.5 with a nitrate/aluminium ratio of 0.52; a solid content of 6 wt.% and a PVP (binder) content of 1.5 wt.% could fulfill the necessary criteria: long-term stability; formation of a dense, crack-free and well adhered layer on polished metal surfaces; as well as high protective abilities against corrosion in H2O-CO2-O2-SO2.
The commercial power plant steel X20CrMoV12-1 (X20) and the steel X12Cr13 were successfully coated with the sol s-0.52-6-1.5 by means of the dip-coating method. An at least 400 nm thick alumina layer (δ-Al2O3) is necessary to ensure the corrosion protection of these steels. The corrosion of the coated samples compared to that of the uncoated ones was significantly reduced, even after 1000 h of exposure in a H2O-CO2-O2-SO2 atmosphere at 600°C. Sulfur and carbon were not detected at the substrate surface or beneath the coating. Hence the transport of the flue gas components SO2 and CO2 into as well as through the alumina layer could be hindered. The diffusion of the alloying elements (Cr, Mn, Si) into the alumina layer resulted in the formation of mixed oxides like δ-(Al,Cr)2O3. Formation of such phases considerably contributed to the corrosion protection.
The long-term stability of the sol s-0.52-6-1.5 and the high protective abilities of the alumina layer on commercial power plant steels provide a good basis for an industrial application.
Geothermal brine is considered to be an aggressive environment as it contains various dissolved salts. Even though carbon steel is commonly used as a construction material due to its machinability and economical reason, it is susceptible to uniform and localized corrosion in a high temperature and high pressure system. Therefore, a coating system is introduced to protect the carbon steel against corrosion in such environment.
-It is necessary to find the optimum composition of SiO2 addition in the organic coatings to enhance the material performance, i.e. coatings adhesion, thickness optimization, thermal resistance.
Current project aims at the addition of Polyaniline (PANi) as the active agent to improve the corrosion resistance of materials against a high saline medium at elevated temperatures.
Geothermal brine is considered to be an aggressive
environment as it contains various dissolved salts.
Even though carbon steel is commonly used as a
construction material due to its machinability and
economical reason, it is susceptible to uniform and
localized corrosion in a high temperature and high
pressure system. Therefore, a coating system is
introduced to protect the carbon steel against
corrosion in such environment.
1. Carbon steel is susceptible to uniform corrosion in presence of oxygen, with corrosion rate of immersion at 150 °C of 0.39 mm/a.
2. Exposure test of carbon steel at 150°C and 10 bar (pressurized by Ar) results in pitting corrosion with depth of 19 µm and width 4 µm on average.
3. OCP measurement shows that the stability of measurement is reached after 40 hours of immersion in the solution.
4. EIS measurement is useful to observe the effect of temperature, immersion time, and coating composition on the corrosion processes of coated metals for use in geothermal application.
Finally it can be summarized that this book fulfills its intention of providing theoretical background and examples for practical applications of coatings used for corrosion protection.
It can be recommended to those being interested in coatings, serving as an overview on aspects which needs to be considered when working with such systems.
1. Introduction
Alumina coatings are one possibility to increase the corrosion resistance, lifetime and application range of thermally loaded steel components, e.g. in modern power plants where the use of the Oxy-fuel technology corrosive fuel gas (H2O-CO2-O2-SO2 at 650 °C) affects the steel parts. In previous investigations the efficacy of protective alumina coatings on steel P 92 under those conditions was demonstrated. A shutdown and re-start of power plants or parts of them causes thermal stresses of the components which can cause detrimental effects like microstructural changes in the steel itself, changes in its oxidation behavior, delamination or microstructural changes in the coating. All those effects can lead to failure of the components, resulting in lifetime reduction.
2. Objectives
As a first step, we concentrate on the influence of thermal cycling tests and observe the impact on the microstructure of the coating and the interface in laboratory air. These investigations will help understanding the processes which occur, show directions of potentially necessary changes of the coating due to improved thermal stress behaviour.
3. Materials & methods
P 92 is a ferritic-martensitic steel, containing 9% Cr which forms protective Cr-oxide-rich scales in dry environments and non-protective ones in water-containing environments. Coupons of P 92, having ground surfaces, were dip-coated via a sol-gel process and subjected to thermal cycling for 500 h (1000 cycles) in laboratory air in a temperature range between room temperature and 660° C. The resulting mass loss was determined by weighing.
Samples for TEM investigations were produced as cross sections normal to the sample surface by FIB preparation (Quanta 3D, (FEI)). The TEM/STEM investigations were performed using a JEM2200FS (JEOL) operated at 200 kV. The microstructure of the coating and the interface after cycling tests was characterized via TEM, HREM, and STEM images, electron diffraction as well as EDX and EFTEM methods.
4. Results
At steep edges in the surface profile the coating was imperfect and cracks have formed during the thermal cycling. Flat surface regions are well-covered. The whole interface region between the steel and the coating shows a dense Cr-oxide-rich zone, which can form protective regions in case of local failure. The Cr-oxide zone is followed by a region of mixed oxides, containing Cr, Mn, Fe, and Al in variable composition, to which a porous δ-Al2O3 zone is joined.
5. Conclusions
• Alumina coatings promote the formation of dense, Cr-rich zones at the interface, which makes the system self-healing.
• These zones are stable during thermal stresses, even in regions with cracked coatings.
• They cause reduction of outward diffusion and mass loss during thermal cycling.
Geothermal brine is a complex system containing a wide variety of dissolved salts resulting from the condition s in a geothermal well. These fluids lead to corrosion in pipes and other parts of geothermal system construction and necessitate intense research efforts in finding new suitable materials. Carbon steel is susceptible to corrosion in geothermal brine especially when it is exposed to a high temperature and high-pressure medium, which is considered to be an aggressive environment. An artificial geothermal water, bas ed on a brine composition found in Indonesia, was used to investigate the performance of high alloyed materials. The electrolyte has pH 4 and contains 1,500 mg/l Cl-, 20 mg/l SO4 2-, 15 mg/l HCO3 -, 200 mg/l Ca 2+, 250 mg/l K+, and 600 mg/l Na+. In order to protect the bare material in geothermal application, it is necessary to either use high alloyed material s or coatings. In this research, a coating system consisting of polyaniline and silicon dioxide was investigated regarding its behavior to protect carbon steel. In detail, the effect of SiO2 and polyaniline (PANi) addition was evaluated by exposure and electrochemical tests for 7 days, i.e. electrochemical impedance spectroscopy (EIS) and open circuit potential (OCP ) at room temperature and 150 °C with 1 MPa pressure .
Electrochemical study of polyaniline/silicon dioxide containing coatings in geothermal solution
(2018)
Polyaniline/Silicon Dioxide containing coatings were electrochemically investigated in a saline geothermal solution.
With the increase of exposure time, impedance values of coated specimens decreased at low frequency, which could be caused by the decrease of pore resistance due to electrolyte or water uptake.
Coating system needs further optimization work.
Geothermal brine is a complex system containing a wide variety of dissolved salts resulting from the condition s in a geothermal well. These fluids lead to corrosion in pipes and other parts of geothermal system construction and necessitate intense research efforts in finding new suitable materials. Carbon steel is susceptible to corrosion in geothermal brine especially when it is exposed to a high temperature and high-pressure medium, which is considered to be an aggressive environment. An artificial geothermal water, bas ed on a brine composition found in Indonesia, was used to investigate the performance of high alloyed materials. The electrolyte has pH 4 and contains 1,500 mg/l Cl-, 20 mg/l SO4 2-, 15 mg/l HCO3 -, 200 mg/l Ca 2+, 250 mg/l K+, and 600 mg/l Na+. In order to protect the bare material in geothermal application, it is necessary to either use high alloyed material s or coatings. In this research, a coating system consisting of polyaniline and silicon dioxide was investigated regarding its behavior to protect carbon steel. In detail, the effect of SiO2 and polyaniline (PANi) addition was evaluated by exposure and electrochemical tests for 7 days, i.e. electrochemical impedance spectroscopy (EIS) and open circuit potential (OCP) at room temperature and 150 °C with 1 MPa pressure.
All in all, practicing professionals as well as researchers can read this book with pleasure and great benefit. It presents a comprehensive collection of data and practical examples manifested in about 100 graphs, 80 schemes of processes and devices, a manifold of images showing the microstructure of alloys or details of components and several phase diagrams. Tables containing data on commercially available coatings, alloys, compositions of corrosive salts, function of constituents of coatings add further important pieces of information. Thus, this book is a valuable source of information for anyone engaged in work with or research on high temperature coatings.