Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Dokumenttyp
- Zeitschriftenartikel (7)
- Vortrag (7)
- Posterpräsentation (5)
- Beitrag zu einem Tagungsband (3)
Schlagworte
- Additive manufacturing (11)
- Neutron diffraction (7)
- Residual stress (7)
- IN718 (5)
- SLM (5)
- Additive Fertigung (4)
- Selective laser melting (4)
- Additive Manufacturing (3)
- Computed tomography (3)
- Selective Laser Melting (3)
- AM (2)
- Computed Tomography (2)
- Computertomographie (2)
- Eigenspannungen (2)
- IN 625 (2)
- Laser beam melting (2)
- Microstructure (2)
- Neutronenstreuung (2)
- Porosity (2)
- Ressidual stress (2)
- Selektives Laserschmelzen (2)
- Build Angle (1)
- Computer Tomographie (1)
- Coordinate measurement machine (1)
- Damage analysis (1)
- Distortion (1)
- Drucktest (1)
- Electron back-scattered diffraction (1)
- Flow Chemistry (1)
- Gitterstrukturen (1)
- Hatch length (1)
- Hybrid manufacturing (1)
- IN 718 (1)
- Imaging (1)
- In-Situ (1)
- In-situ compression CT (1)
- In718 (1)
- Inline NMR Spectroscopy (1)
- Integrated Processes (1)
- Laboratory X-ray diffraction (1)
- Laser Beam Melting (1)
- Lattice Structures (1)
- Lattice structure (1)
- Lattice structures (1)
- Microstructure and texture (1)
- Modular Production (1)
- Nickel-based superalloy (1)
- Normung (1)
- Powder analysis (1)
- Process Analytical Technology (1)
- Pulver (1)
- Reaction Monitoring (1)
- Residual Stresses (1)
- Residual stresses (1)
- Roughness (1)
- Röntgen-Refraktion (1)
- Schadensanalyse (1)
- Static Mixing (1)
- Synchrotron X-ray diffraction (1)
- Synchrotron computed tomography (1)
- Ti-6Al-4V (1)
- WAAM (1)
- X-Ray refraction (1)
- standardization (1)
Organisationseinheit der BAM
- 8 Zerstörungsfreie Prüfung (15)
- 8.5 Röntgenbildgebung (15)
- 5 Werkstofftechnik (7)
- 5.0 Abteilungsleitung und andere (7)
- 9 Komponentensicherheit (7)
- 9.4 Integrität von Schweißverbindungen (7)
- 9.2 Versuchsanlagen und Prüftechnik (3)
- 1 Analytische Chemie; Referenzmaterialien (1)
- 1.4 Prozessanalytik (1)
- 8.0 Abteilungsleitung und andere (1)
Eingeladener Vortrag
- nein (7)
The quality of components made by laser beam melting (LBM) additive manufacturing is naturally influenced by the quality of the powder bed. A packing density <1 and porosity inside the powder particles lead to intrinsic voids in the powder bed. Since the packing density is determined by the particle size and shape distribution, the determination of these properties is of significant interest to assess the printing process. In this work, the size and shape distribution, the amount of the particle’s intrinsic porosity, as well as the packing density of micrometric powder used for LBM, have been investigated by means of synchrotron X-ray computed tomography (CT). Two different powder batches were investigated: Ti–6Al–4V produced by plasma atomization and stainless steel 316L produced by gas atomization. Plasma atomization particles were observed to be more spherical in terms of the mean anisotropy compared to particles produced by gas atomization. The two kinds of particles were comparable in size according to the equivalent diameter. The packing density was lower (i.e., the powder bed contained more voids in between particles) for the Ti–6Al–4V particles. The comparison of the tomographic results with laser diffraction, as another particle size measurement technique, proved to be in agreement.
Additive Manufacturing (AM) of metals has become industrially viable for a large variety of applications, including aerospace, automotive and medicine. Powder bed techniques such as Selective Laser Melting (SLM) based on layer-by-layer deposition and laser melt enable numerous degrees of freedom for the geometrical design. Developing during the manufacturing process, residual stresses may limit the application of SLM parts by reducing the load bearing capacity as well as induce unwanted distortion depending on the boundary conditions specified in manufacturing.
The residual stress distribution in the bulk of IN718 elongated prisms produced by SLM was studied non-destructively by means of neutron diffraction. The samples with different scanning strategies, i.e. hatching length, were measured in as-build condition (on a build plate) and after removal from the build plate.
The absolute values of all stress components decreased after removal from the build plate. Together with surface scan utilizing a coordinate-measuring machine (CMM), it is possible to link the stress release to the sample distortion. Obtained results indicated different residual stress states for each of the transversal, longitudinal and normal component depending on the thermal gradient in the respective direction.
Having been introduced almost two decades ago, Additive Manufacturing (AM) of metals has become industrially viable for a large variety of applications, including aerospace, automotive and medicine. Powder bed techniques such as Selective Laser Melting (SLM) based on layer-by-layer deposition and laser melt enable numerous degrees of freedom for the geometrical design. Developing during the manufacturing process, residual stresses may limit the application of SLM parts by reducing the load bearing capacity as well as induce unwanted distortion depending on the boundary conditions specified in manufacturing.
The residual stress distribution in IN718 elongated prisms produced by SLM was studied non-destructively by means of neutron (bulk) and laboratory X-ray (surface) diffraction. The samples with different scanning strategies, i.e. hatching length, were measured in as-build condition (on a build plate) and after removal from the build plate.
The absolute values of all stress components decreased after removal from the build plate. Together with surface scan utilizing a coordinate-measuring machine (CMM), it is possible to link the stress release to the sample distortion. Obtained results indicated different residual stress states for each of the transversal, longitudinal and normal component depending on the thermal gradient in the respective direction.
Having been introduced almost two decades ago, Additive Manufacturing (AM) of metals has become industrially viable for a large variety of applications, including aerospace, automotive and medicine. Powder bed techniques such as Selective Laser Melting (SLM) based on layer-by-layer deposition and laser melt enable numerous degrees of freedom for the geometrical design. Developing during the manufacturing process, residual stresses may limit the application of SLM parts by reducing the load bearing capacity as well as induce unwanted distortion depending on the boundary conditions specified in manufacturing.
The residual stress distribution in IN718 elongated prisms produced by SLM was studied non-destructively by means of neutron (bulk) and laboratory X-ray (surface) diffraction. The samples with different scanning strategies, i.e. hatching length, were measured in as-build condition (on a build plate) and after removal from the build plate.
The absolute values of all stress components decreased after removal from the build plate. Together with surface scan utilizing a coordinate-measuring machine (CMM), it is possible to link the stress release to the sample distortion. Obtained results indicated different residual stress states for each of the transversal, longitudinal and normal component depending on the thermal gradient in the respective direction.
The layer-by-layer Additive Manufacturing (AM) by means of Selective Laser Melting (SLM) offers many prospects regarding the design of a part used in aeroplane components and gas turbines. However, structural deviations from the nominal morphology are unavoidable. The cooling of the finished part leads to shrinkage and a high surface roughness is induced by attached powder particles affecting the part volume too.
The integrity and load-bearing capacity of a SLM produced lattice structure has been investigated by means of in-situ X-ray computed tomography during compression. The lattice structure was compressed by 10 % in height with an applied maximum force of 5 kN. Additionally, a single strut has been investigated ex-situ as a component of the lattice structure. With the higher resolution achieved on the single strut, the pore distribution (size and location) as well as the surface roughness were assessed. The particle and pore size distribution of the raw powder have been investigated, too. One of the main results coming from the in-situ analysis was that the nodes were identified as the weakest points in the lattice structure.
Im Fokus dieser Arbeit steht die computertomographische (CT) Untersuchung (Synchrotron- und Labor-CT) von IN625-Pulver und den daraus gefertigten Streben, welche wiederum zu Gitterstrukturen zusammengesetzt werden. Aufgrund der Filigranität wurde zur Fertigung dieser Proben das pulverbettbasierte selektive Laserschmelzen verwendet.
Porositätsanalysen und Größenverteilungen wurden für das Pulver bei einer rekonstruierten Voxelgröße von 0,5µm ermittelt. 6,0mm lange Streben variierten im Aufbauwinkel von 30° bis 90° zur Bauplattform und zeigten so den Unterschied zwischen Up- und Down-Skin hinsichtlich der Rauigkeit und Porenverteilung. Die Gitterstrukturen konnten in-situ mit bis zu 5,0kN belastet werden, um deren Verformung computertomographisch zu erfassen.
Die Schicht-für-Schicht additive Fertigung (AM) in Form des selektiven Laser- bzw. Elektronenstrahlschmelzens (SLM und EBM) bietet einerseits Vorteile bezüglich des Probendesigns, andererseits sind strukturelle Abweichungen von der nominellen Morphologie unvermeidbar. Beispielsweise führt das Abkühlen des fertigen Bauteils zu verringerten Abmessungen und angeschmolzene Pulverpartikel sorgen für unregelmäßige Oberflächen mit nicht vernachlässigbaren Rauigkeiten.
Im Fokus dieser Arbeit steht die computertomographische (CT) Untersuchung von IN625 Pulver und den daraus SLM-gefertigten Streben, Einheitszellen und Gitterstrukturen.
Mit Hilfe von Synchrotron – CT konnte das IN625 Pulver mit einer Voxelgröße von 0,5µm untersucht werden. Für die Untersuchung der daraus gefertigten verschiedenen Probengemetrien wurde Labor CT genutzt.
6 mm lange Streben variierten im Aufbauwinkel von 40° bis 90°. Der Unterschied zwischen Unter- und Oberseite während der Fertigung wird sowohl bei Porenverteilung als auch bei der Oberflächenrauigkeit deutlich. Ein Vergleich der Strebenabmessungen für die nominalen Durchmesser von 0,5 mm bis 3 mm zwischen CT and GOM zeigte keine signifikanten Differenzen.
Vier dieser Streben wurden zu einer bbc Einheitszelle zusammengefügt, welche sich wiederum zu den Gitterstrukturen ergänzen.
An einem Gitterwürfel (3x3x3 Einheitszellen) wurden In-Situ (Druck) CT bis 5kN durchgeführt. Mit einer Kraft von etwa 3kN erreichen wir den plastischen Bereich und beobachten zudem Strebenverzug.
Außerdem wurde ein Vergleich zu den CAD-Files wurde genutzt um einen möglichen Verzug während der Fertigung beurteilen zu können. Dafür wurden 4x4x4 cm³ Gitterstrukturen gebaut und evaluiert.
Mit diesen CT Messungen bestätigen wir eine signifikante Schrumpfung, die Bereits während der Fertigung berücksichtigt werden muss.
Die Schicht-für-Schicht additive Fertigung (AM) in Form des selektiven Laser- bzw. Elektronenstrahlschmelzens (SLM und EBM) bietet einerseits Vorteile bezüglich des Probendesigns, andererseits sind strukturelle Abweichungen von der nominellen Morphologie unvermeidbar. Beispielsweise führt das Abkühlen des fertigen Bauteils zu verringerten Abmessungen und angeschmolzene Pulverpartikel sorgen für unregelmäßige Oberflächen mit nicht vernachlässigbaren Rauigkeiten.
Im Fokus dieser Arbeit steht die computertomographische (CT) Untersuchung von IN625 Pulver und den daraus SLM-gefertigten Streben, Einheitszellen und Gitterstrukturen.
Mit Hilfe von Synchrotron – CT konnte das IN625 Pulver mit einer Voxelgröße von 0,5µm untersucht werden. Für die Untersuchung der daraus gefertigten verschiedenen Probengemetrien wurde Labor CT genutzt.
6 mm lange Streben variierten im Aufbauwinkel von 40° bis 90°. Der Unterschied zwischen Unter- und Oberseite während der Fertigung wird sowohl bei Porenverteilung als auch bei der Oberflächenrauigkeit deutlich. Ein Vergleich der Strebenabmessungen für die nominalen Durchmesser von 0,5 mm bis 3 mm zwischen CT and GOM zeigte keine signifikanten Differenzen.
Vier dieser Streben wurden zu einer bbc Einheitszelle zusammengefügt, welche sich wiederum zu den Gitterstrukturen ergänzen.
An einem Gitterwürfel (3x3x3 Einheitszellen) wurden In-Situ (Druck) CT bis 5kN durchgeführt. Mit einer Kraft von etwa 3kN erreichen wir den plastischen Bereich und beobachten zudem Strebenverzug.
Außerdem wurde ein Vergleich zu den CAD-Files wurde genutzt um einen möglichen Verzug während der Fertigung beurteilen zu können. Dafür wurden 4x4x4 cm³ Gitterstrukturen gebaut und evaluiert.
Mit diesen CT Messungen bestätigen wir eine signifikante Schrumpfung, die Bereits während der Fertigung berücksichtigt werden muss.
Die Schicht-für-Schicht additive Fertigung (AM) in Form des selektiven Laserschmelzens (SLM) bietet einerseits Vorteile bezüglich des Probendesigns, andererseits sind thermische Eigenspannungen (ES) aufgrund des hohen Temperaturgradienten unvermeidbar. Diese Eigenspannungen wurden in zwei SLM-gefertigten Proben aus IN718 zerstörungsfrei mit Neutronenstreuung hinsichtlich der folgenden zwei Einflüsse analysiert: der Einfluss der Hatch-Länge und das Abtrennen des Werkstücks von der Bauplatte. Begleitet wurden die Messungen der Eigenspannungen durch optische Mikroskopie und die taktile Vermessung der Oberfläche. Eine Korrelation zwischen den Eigenspannungen und der Hatch-Länge konnte beobachtet und erklärt werden.
Der Einfluss der Probenabtrennung von der Bauplatte auf den Eigenspannungszustand in SLM IN718
(2017)
Die Schicht-für-Schicht additive Fertigung (AM) in Form des selektiven Laserschmelzens (SLM) bietet einerseits Vorteile bezüglich des Probendesigns, andererseits sind thermische Eigenspannungen (ES) aufgrund des hohen Temperaturgradienten unvermeidbar. Diese Eigenspannungen wurden in zwei SLM-gefertigten Proben aus IN718 zerstörungsfrei mit Neutronenstreuung hinsichtlich der folgenden zwei Einflüsse analysiert: der Einfluss der Hatch-Länge und das Abtrennen des Werkstücks von der Bauplatte. Begleitet wurden die Messungen der Eigenspannungen durch optische Mikroskopie und die taktile Vermessung der Oberfläche. Eine Korrelation zwischen den Eigenspannungen und der Hatch-Länge konnte beobachtet und erklärt werden.