The article covers data on the Brinell hardness of the forged precipitation-hardened aluminum alloy EN AW-2618A in the initial T61 condition (i. e. slightly underaged) and after isothermal aging for up to 25,0 0 0 h at aging temperatures between 160 °C and 350 °C. In addition, the hardness was determined on specimens after creep testing at 190 °C and various stresses. The hardness decreases with increasing ag- ing time due to the microstructural evolution of the harden- ing precipitates. The drop occurs faster the higher the aging temperature. Aging under creep load additionally accelerates the hardness decrease.
Materials subjected to high-temperature service conditions will change their microstructure with time. Associated with this aging process is a change of mechanical properties as well as a change of damage mechanisms. Within the scope of the FVV project Aging and Lifetime, Fraunhofer IWM in Freiburg and BAM in Berlin (both Germany) experimentally characterized the widespread high-temperature aluminum alloy EN AW-2618A in different overaging states. Based on the experimental findings, models for numerical lifetime assessment with the finite-element method were implemented.
Texture formation in amorphous Al86Ni6Y4.5La1.5Co2 splats by thermal and mechanical treatment
(2016)
The crystallization behavior of amorphous Al86Ni6Y4.5La1.5Co2 splats was analyzed by differential scanning calorimetry (DSC) and X-ray diffraction (XRD). Rietveld refinement was used to analyze the preferred orientation of fcc aluminum nanocrystals in the residual amorphous matrix after annealing. Fiber textures in [200] and [220] directions were found after heating to 360 C. The influence of cold rolling on the preferred crystal orientation was studied as a function of the thickness reduction of the specimen. It was found that cold rolling significantly increases the (220) texture, while the (200) texture remains unchanged. Based on the experimental results the formation of (220) and (200) texture during the crystallization of the amorphous splats was ascribed to two different processes, internal stresses induced during splat formation or cold-rolling.