Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Erscheinungsjahr
- 2019 (32) (entfernen)
Dokumenttyp
- Zeitschriftenartikel (32) (entfernen)
Schlagworte
- Corrosion (6)
- Carbon steel (3)
- Additive manufacturing (2)
- Artificial weathering (2)
- Condensate (2)
- Corrosion rate (2)
- Degradation (2)
- Flame retardant (2)
- Impurities (2)
- KorroPad (2)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (32) (entfernen)
A thorough characterization of starting materials is the precondition for further research, especially for cement, which contains various phases and presents quite a complex material for fundamental scientific investigation. In the paper at hand, the characterization data of the reference cement CEM I 42.5 R used within the priority program 2005 of the German Research Foundation (DFG SPP 2005) are presented from the aspects of chemical and mineralogical compositions as well as physical and chemical properties. The data were collected based on tests conducted by nine research groups involved in this cooperative program. For all data received, the mean values and the corresponding errors were calculated. The results shall be used for the ongoing research within the priority program.
Der 60 °C-Betonversuch ist eine in Deutschland und international verbreitete Methode um die Empfindlichkeit von Gesteinskörnungen und Betonen hinsichtlich einer Alkali-Kieselsäure Reaktion (AKR) zu prüfen. Dieser Beitrag stellt eine neuentwickelte automatisierte Variante der Prüfmethode in einem Minireaktor vor. Dabei werden die Dehnungen von Betonprismen nicht, wie beim konventionellen Test manuell, sondern automatisch in entsprechend ausgerüsteten Prüfbehältern gemessen. Neben einer Reduzierung des Messaufwands bringt die automatisierte Prüfung im Minireaktor weitere Vorteile. Die Dehnungssignale werden, anders als bei der konventionellen Messung, quasi-kontinuierlich aufgezeichnet und bilden das Expansionsverhalten der Prismen detailliert ab. Außerdem bleiben Unterbrechungen der AKR-provozierenden Lagerung aus, die bei der konventionellen Prüfung notwendig sind. Im Beitrag werden die automatisierte und konventionelle Prüfung anhand der Dehnungen von Prismen zweier Gesteinskörnungen verglichen. In Übereinstimmung mit vorhergehenden Untersuchungen sind im Minireaktor gemessene Dehnungen systematisch kleiner als manuell gemessene. Als mögliche Ursache werden Unterschiede im Auslaugverhalten experimentell untersucht. Zur Überprüfung der Einstufung der zwei Gesteinskörnungen erfolgen außerdem Referenzprüfungen in der Nebelkammerlagerung bei 40 °C.
Additively manufactured test specimens made of polyamide 12 (PA 12) by Laser Sintering as well as of acrylonitrile butadiene styrene (ABS) by Fused Layer Modelling, were characterised with active thermography directly after manufacturing and after artificial weathering. For this, two different excitation methods (flash and pulse heating) were used and compared, regarding their suitability for the detection of constructed and imprinted defects inside the test specimens. To increase the quality of the thermograms, data processing methods like thermal signal reconstruction (TSR) and Fourier Transformation after TSR were applied. To further investigate the long-term stability of the additively manufactured test specimens towards environmental stress, like UV radiation, heat, humidity, water contact and frost with active thermography, an artificial weathering test over 2000 hours (~3 months) was applied to the specimens. The monitoring of the changes in the optical properties of the weathered plastics was supplemented by spectral reflectance and UV/VIS spectroscopy.
Since materials play an important role when designing and servicing industrial facilities. Also, for energy systems there is no way around. Selection of appropriate materials is an essential aspect for successful application and reliable service life. Future engineers must be made aware on the importance of this fact. So, they may prevail in techno‐economic discussions.
The book fulfills its intension of providing to students in science and engineering a comprehensive understanding of different energy processes and what role materials play in this conjunction. Also, it gives interested engineers and scientists an insight in this matter. After being introduced the user should dig deeper in the existing detailed knowledge available for materials selection within these special conditions to assure a reliable operation of the energy production facility.
First phosphorus AB2 monomer for flame-retardant hyperbranched polyphosphoesters: AB2vs. A2 + B3
(2019)
Branched polymers are an important class of polymers with a high number of terminal groups, lower viscosity compared to their linear analogs and higher miscibility, which makes them especially interesting for flame retardant applications, where the flame retardants (FR) are blended with another polymer matrix. Hyperbranched polyphosphoesters (hbPPEs) are gaining more and more interest in the field of flame retardancy, as low molar mass FRs often have the disadvantage of blooming out or leaching, which is not desired in consumer products. Here, we present the first phosphorus-based AB2 monomer for the synthesis of hbPPEs and assess its flame-retardant performance in an epoxy resin compared to a hbPPE synthesized by an A2 + B3 approach. The hbPPE synthesized from an AB2 monomer exhibited a slightly higher performance compared to a similar hbPPE, which was prepared by A2 + B3 polyaddition, probably due to its higher phosphorus content.
Viscosity-modifying agent (VMA) are used in several applications of concrete, such as underwater concrete, Self-Compacting Concrete (SCC) or Self-Levelling Underlayments (SLU) in order to improve the washout resistance and the stability. The study focuses on the modifications of cement pastes properties implied when a VMA (hydroxypropyl guars or HPG) and a superplasticizer are introduced together. For reaching this objective, two chemically different polycarboxylate-based superplasticizers (PCE) and two HPGs exhibiting different molar substitution ratios (MSHP), were studied. A method, combining total organic carbon and size exclusion chromatography, was developed in order to quantify the adsorption of the both admixtures. The adsorption of HPGs appears being significantly lowered by the presence of PCE, while only the adsorption of the less charged PCE is slightly affected by the HPG. As consequence, strong modifications of the rheological properties of cement pastes were noticed when HPG and PCE are combined. The desorption of HPG leads to higher yield stress and residual viscosity than with PCE alone.
Additive manufacturing of alkali-activated materials currently attracts a lot of attention, because of the possibility to produce customized high-performance elements for a range of applications, potentially being more resource-efficient than conventionally produced parts. Here, we describe a new additive manufacturing process for alkali-activated materials that is based on selective laser-heating of lithium aluminate/microsilica slurries. The new process-material combination allows to manufacture elements with complex geometries at high building rates and high accuracy. The process is versatile and transferrable to structures of sizes differing by orders of magnitude. The mechanical strength of the obtained materials was in the range of values reported for conventional metakaolin-based geopolymers, and superior to what has been hitherto reported for alkali-activated materials produced by additive manufacturing. This mechanical performance was obtained despite the fact that the degree of reaction of the lithium aluminate and the microsilica was low, suggesting that significant reactions took place only at the surface of the microsilica particles.
Reliable performance of structural sealant glazing (SSG) systems is necessary to utilise advantages of SSG in glass facades. Conventional durability assessment of structural sealant joints is based on separated weathering tests and empirical fatigue testing. This work presents a new test methodology for performance assessment of SSGjoints at simultaneous weathering and two-dimensional mechanical loading. The climatic and mechanical load function were derived from common loading scenarios according to a worst case approach. A System test specimen, resembling a common SSG-joint, was exposed to 24 h of combined loading in a custom-designed test facility. From the recorded mechanical system response, characteristic parameters were evaluated to assess the performance of the system at varying climatic and mechanical conditions. These experimental results reveal effects of ambient conditions, previous loading and deformation Amplitude peaks on the system response. The proposed test methodology opens up for new performance-related approaches in durability testing.
Electrochemical deposition of polyaniline on carbon steel for corrosion study in geothermal solution
(2019)
Polyaniline has been widely developed for many applications, e.g. sensor, supercapacitor components, electrochromic devices, and anticorrosion pigments. Although the addition of polyaniline pigment in organic coatings has been an alternative for corrosion protection in industrial applications, the protection mechanism is still not fully understood. Herein in this study, as a part of the development of polyaniline/silicon dioxide coating for geothermal application, polyaniline has been deposited electrochemically on carbon steel surface in oxalic acid medium and tested in geothermal solution to understand the contribution of polyaniline to the corrosion protection of a polyaniline-based composite in the geothermal system. To observe the surface/interface reaction between the electrolyte and electrode surface during the electrochemical polymerization, electrochemical impedance spectroscopy (EIS) was applied after each cycle. For corrosion study in the geothermal application, an artificial geothermal solution was used with the composition of 1,500 mg/l Cl⁻, 20 mg/l SO₄²⁻, 15 mg/l HCO₃⁻, 200 mg/l Ca²⁺, 250 mg/l K⁺, and 600 mg/l Na⁺, and pH 4 to simulate a geothermal brine found in Sibayak, Indonesia. An electrochemical measurement was performed by monitoring the open circuit potential over seven days, with the interruption by EIS every 22 hours. The experiments were performed at room temperature and 150 °C (1 MPa) in an oxygen-free environment. Impedance spectra showed a reduction of the total impedance value of approximately 10 times for specimens measured at 150 °C compared to the specimens measured at room temperature, suggesting a less stable layer at high temperature.
Geothermal energy is an interesting alternative to polluting fossil energy sources. Therefore, in Belgium, two wells have been drilled for a deep geothermal power plant. However, the environment to which the installations are exposed is challenging. The geothermal brine has 165 g/l total dissolved solids (of which 90% are sodium and chlorine) and the production temperature can be up to 130 °C. To assess their suitability to be used in a geothermal power plant, the corrosivity of the artificial brine to three common construction materials was investigated with exposure and electrochemical tests. The metals under consideration are a low-alloyed carbon steel (S235JR), an austenitic stainless steel (UNS S31603) and a duplex stainless steel (UNS S31803). The carbon steel, that was found to corrode uniformly, could be considered as a constructional material if a sufficient wall thickness is chosen. The austenitic stainless steel and the duplex stainless steel demonstrate very low uniform
corrosion rates. They are however susceptible to pitting and crevice corrosion. To guarantee safe operation of the geothermal power plant, the susceptibility of the alloys to stress corrosion cracking should be tested and in situ experiments should be performed.