Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Dokumenttyp
- Zeitschriftenartikel (15)
Sprache
- Englisch (15)
Referierte Publikation
- ja (15) (entfernen)
Schlagworte
Organisationseinheit der BAM
- 5 Werkstofftechnik (11)
- 5.3 Polymere Verbundwerkstoffe (11)
- 7 Bauwerkssicherheit (10)
- 7.5 Technische Eigenschaften von Polymerwerkstoffen (10)
- 8 Zerstörungsfreie Prüfung (3)
- 8.5 Röntgenbildgebung (3)
- 5.5 Materialmodellierung (2)
- 4 Material und Umwelt (1)
- 4.1 Biologische Materialschädigung und Referenzorganismen (1)
- 5.2 Metallische Hochtemperaturwerkstoffe (1)
- 6 Materialchemie (1)
- 6.2 Material- und Oberflächentechnologien (1)
The aim of this research is to study the influence of moisture absorption at low moisture contents on the creep behaviour of an epoxy adhesive in steel bonded joints. Single lap joints were manufactured using high strength steel adherends and a two-component epoxy adhesive. The single lap joints were tested at load Levels corresponding to average lap shear stresses of±5%, 15%, 30% and 45% of the dry lap shear strength in both 40 °C air and 40 °C distilled water. Specimens were not pre-aged to be able to analyse the coupled effect of moisture and loading. The test results show that an increase in the load level resulted in an increase in the instantaneous strain and in the creep strain rate. The creep strain of single lap joints loaded in water was generally larger than for the ones loaded in air. For joints loaded in water the creep behaviour was found to be dependent on the moisture concentration in the adhesive. At low moisture percentages creep was suppressed, resulting in a lower instantaneous strain. At higher moisture percentages creep was promoted, resulting in a larger strain rate. The suppression of creep at low moisture percentages is attributed to water molecules bonding to the epoxy macromolecules, resulting in a reduction in molecular mobility and a smaller creep strain. At higher moisture percentages the plasticizing effect of the water dominates, resulting in a larger creep strain. The Maxwell threeelement solid model and Kelvin-Voigt three-element solid model were used to simulate the creep behaviour of the single lap joints loaded in air and water. The models gave good representations of the creep Response across the different load levels in both water and air, they were however unable to give a correct representation of the instantaneous strain of the single lap joints loaded in water. This is attributed to the models being unable to account for the present short-term relaxation process that is dependent on the moisture concentration.
The physical and chemical effects of diesel and biodiesel fuels on two high-density polyethylene (PE-HD) types were investigated. Both semi-crystalline PE-HD are common thermoplastic materials for container and storage tank applications. Biodiesel, a composition of unsaturated fatty acid esters from renewable resources, was chosen as it is regarded a possible green alternative to fossil fuels. The study aims at identifying significant differences between biodiesel and conventional diesel fuels based on the differences in the chemical nature of the two. The physical effects of the fuels on the polymer at first comprises the sorption behavior, i.e. kinetics and final equilibrium concentration. Not only are both fuels absorbed by the amorphous phase of the semi-crystalline PE-HD, they also induce a plasticization effect that modifies the molecular mobility and therefore also the characteristic yielding properties, manifest in the obtained stress-strain curves. The chemical effects related to degradation phenomena is investigated by a long-term storage scenario using partially immersed tensile test specimens in diesel and biodiesel. We were able to confirm the proposed co-oxidation mechanism by Richaud et al. for polyethylene-unsaturated penetrant systems on a larger scale based on practical tensile tests. One of the investigated polyethylene grades subjected to tensile drawing showed a significant loss of plastic deformation and the onset of premature failure after 150 days of storage in biodiesel. Further biodiesel storage showed a systematically reduced elongation at break before necking. None of these effects were observed in diesel. Oxidation of fuels and polymer after progressing storage times were analyzed by the evolution of carbonyl species in FT-IR/ATR spectroscopy.
In the present study, a simple approach was used to investigate the effect of UV-exposure on two high density Polyethylene materials (PE-HD), commonly used for storage tanks, on fuel sorption behavior and colonization by microorganisms. The aim was to investigate whether the sorption behavior of the fuels (diesel/biodiesel) and the colonization by microorganisms, frequently occurring in the fuel, is affected and may lead to undesirable or safety-relevant material changes. We showed that the UV-irradiation leads to significant changes of the sorption behavior due to chemi-crystallization and crosslinking. The fuel Sorption is affected by the UV-induced formation of polar carbonyl and hydroxyl groups predominantly occurring at the surface. With respect to microbial colonization behavior for Bacillus subtilis and Pseudomonas aeruginosa, isolated from a contaminated diesel sample, differences of the initial adhesion could be shown depending on the initial type of polyethylene as well as on the degree of UV-induced degradation.
High-density polyethylene becomes optically transparent during tensile drawing when previously saturated with diesel fuel. This unusual phenomenon is investigated as it might allow conclusions with respect to the material behavior. Microscopy, differential scanning calorimetry, density measurements are applied together with two scanning X-ray scattering techniques: wide angle X-ray scattering (WAXS) and X-ray refraction, able to extract the spatially resolved crystal orientation and internal surface, respectively. The sorbed diesel softens the material and significantly alters the yielding characteristics. Although the crystallinity among stretched regions is similar, a virgin reference sample exhibits strain whitening during stretching, while the diesel-saturated sample becomes transparent. The WAXS results reveal a pronounced fiber texture in the tensile direction in the stretched region and an isotropic orientation in the unstretched region. This texture implies the formation of fibrils in the stretched region, while spherulites remain intact in the unstretched parts of the specimens. X-ray refraction reveals a preferred orientation of internal surfaces along the tensile direction in the stretched region of virgin samples, while the sample stretched in the diesel-saturated state shows no internal surfaces at all. Besides from stretching saturated samples, optical transparency is also obtained from sorbing samples in diesel after stretching.
The impact fracture behavior of two common high-density polyethylene grades for container applications were intensively studied by the instrumented Charpy impact test after well-defined exposure to UV-irradiation. Individual stages of the impact event, such as crack initiation and crack propagation energy as well as maximum impact load, were investigated from the recorded load–deflection curves. UV-induced material property changes were further investigated by infrared spectroscopy, differential scanning calorimetry, and dynamic-mechanical analysis as well as density measurements. Based on the results of the Charpy impact test, three indicators were identified to describe the extend of photooxidation on high-density polyethylene: (a) a reduced Charpy impact strength—at least to half of its initial value for a distinctly brittle impact fracture, (b) a marked decrease in the crack propagation contribution to the impact strength, and (c) an increase of the brittle features of the fracture surface.
Effect of different sulphur-based crosslink networks on the nitrile rubber resistance to biodiesel
(2017)
Biodiesel possesses some comparable physical properties to petroleum diesel in addition to its improved environmental benefits. Nonetheless, both fuels differ greatly with respect to their chemical compositions.
Therefore, the compatibility of the materials, which are commonly employed in contact with diesel, must also be assured for biodiesel. This paper assessed the influence of sulphur-based curing systems on the resistance of nitrile rubber to soybean biodiesel. Formulations were prepared using highacrylonitrile-content nitrile rubber by employing a two-level experimental design. The amounts of two different accelerators and sulphur were varied to achieve different types of vulcanisation systems.
Thermal analyses, mechanical tests and microscopy analyses were conducted to evaluate the behaviour of the material after contact with biodiesel. The results showed that the choice of the accelerator played an important role on the resistance of the rubber to the biofuel, and crosslink density was not a key factor with respect to the resistance.
The fracture surface of slow and continuous crack propagation during environmental stress cracking of a semicrystalline polyethylene exhibits isotropic roughness exponents at the local scale but resolved across the macroscopic fracture surface a clear position dependence is found. The spatially resolved roughness exponent admits values in the range between 0.1 and 0.4, demonstrating nontrivial exponents in the small length-scale regime. Instead, they vary across the fracture surface according to the stress-state distribution, which suggests that the exponents are intimately linked to the locally dominating dissipation processes during craze cracking.
In previous papers, we investigated the influence of biodiesel or diesel on mechanical properties of a high-density polyethylene (PE-HD) for tank applications using Charpy impact tests and dynamicmechanical analysis (DMA). In this work, covering two more PE-HD materials, we extend our study to addressing the tensile properties, especially changes of Young's modulus, after immersion in biodiesel or diesel at 60 °C. As we cover sorption and desorption behavior, during desorption, i.e. storage at 60 °C in a circulating air oven, ageing or degradation phenomena were also observed and characterized in some detail using spectral reflectance measurements and FT-IR spectroscopy. The results obtained here support the concept of co-oxidation, i.e. the faster oxidation of the PE-HD matrix if the samples were previously saturated with biodiesel, itself easily oxidizable.
The full-notch creep test (FNCT) is widely used to characterize the slow crack growth (SCG) behavior of polyolefin materials in “inert” media as well as effects of environmental stress cracking (ESC) in which the medium has decisive influence on damage mechanism and time to failure. The test is of greatest importance for pipe and blow molding types of polyethylene, high density (PE-HD). Usually the full-notch creep test is applied as a standardized testing method (ISO 16770) using a few universal liquid media, such as solutions of Arkopal N 100. In our study, selected relevant polyethylene, high density materials are investigated also in real media – practical formulations as well as representative pure chemicals – and influences of temperature and geometry of specimen and notch are explicitly addressed. Furthermore, the investigations comprise also the environmental stress cracking behavior of polyethylene, high density in media that are sorbed to a significant extent – examples are diesel and biodiesel – based on comparison with samples previously saturated with those media. Thus, also the underlying diffusion controlled sorption process has to be assessed before. The investigations were performed using a full-notch creep testing device with 12 individual sub-stations, each equipped with individual electronic stress and temperature control and continuous online monitoring of the specimen elongation.
Different imaging techniques were employed to monitor Full Notch Creep Test (FNCT) experiments addressing environmental stress cracking in more detail. The FNCT is a well-established test method to assess slow crack growth and environmental stress cracking of polymer materials, especially polyethylene. The standard test procedure, as specified in ISO 16770, provides a simple comparative measure of the resistance to crack growth of a certain material based on the overall time to failure when loaded with a well-defined mechanical stress and immersed in a liquid medium promoting crack propagation.
Destructive techniques which require a direct view on the free fracture surface, such as light microscopy and laser scanning microscopy, are compared to non-destructive techniques, i.e. scanning acoustic microscopy and xray micro computed tomography. All methods allow the determination of an effective crack length. Based on a series of FNCT specimens progressively damaged for varied Durations under standard test conditions, the estimation of crack propagation rates is also enabled. Despite systematic deviations related to the respective Imaging techniques, this nevertheless provides a valuable tool for the detailed evaluation of the FNCT and its further development.