Schlagworte
- Glass transition (1)
- Nanocalorimetry (1)
- Nanoparticles (1)
- Plasma deposited polymers (1)
- Thin polymer films (1)
Organisationseinheit der BAM
Polymer nanoparticles (NPs) can be highly attractive in numerous applications including biomedicine where the use of inorganic matter may be detrimental for living tissues. In conventional wet chemistry, polymerization and functionalization of NPs with specific chemical groups involves complex and often numerous reactions. Here, we report on a solvent-free, single-step, low temperature plasma-based synthesis of carboxylated NPs produced by polymerization of acrylic acid under the conditions of a glow discharge. In a monomer-deficient regime, strong fragmentation of the monomer molecules by electron impact results in the formation of 15 nm-sized NPs with <1% retention of the carboxyl groups. In an energy-deficient regime, larger 90 nm-sized NPs are formed with better retention of the carboxyls that reaches 16 %. All types of the NPs exhibit the glass transition above the room temperature which makes them highly stable under aqueous environment with no dissolution or swelling. They are also found to degrade thermally when heated above 150 °C with a decrease of the mean NP size, yet with the retention of the chemical composition. Thus, plasma polymerization proves to be a versatile approach for the production of polymer NPs with tuneable size distribution, chemical composition and physical properties.
In the recent years, highly crosslinked plasma polymers have started to unveil their potential in numerous biomedical applications in thin-films form. However, conventional diagnostic methods often fail due to their diverse molecular dynamics conformations. Here, glassy dynamics and the melting transition of thin PEO-like plasma assisted deposited (ppPEO) films (thickness 100 nm) were In situ studied by a combination of specific heat spectroscopy, utilizing pJ/K sensitive AC-calorimeter chip, and composition analytical techniques. Different crosslinking densities were obtained by different plasma powers during the deposition of the films. Glassy dynamics was observed for all values of the plasma power. It was found that the glassy dynamics slows down with increasing the plasma power. Moreover, the underlying relaxation time spectra broaden indicating that the molecular motions become more heterogeneous with increasing plasma power. In a second set of experiment, the melting behavior of the ppPEO films was studied. The melting temperature of ppPEO was found to be decreasing with increasing plasma power. This was explained by a decrease of the order in the crystals due to formation of chemical defects during the plasma process.