Nowadays, sensors based on polymers/nanostructured metal oxide composites have been investigated exten-sively because of their sensitivity to NO2 gas at ambient temperature. In this work, nanocomposite membranes of xanthan gum (XG) with different contents of MnO2 nanoparticles were prepared as a potential NO2 gas sensor operating at room temperature by a simple one-step oxidation-reduction reaction. The structural, morphological, thermal, and electrical properties of the composite membrane were investigated. The FT-IR results confirm the successful preparation of MnO2 through the oxidation of XG by KMnO4 and reveal further the structural changes of the XG/MnO2 nanocomposite upon its exposure to NO2 gas. The capping of the synthesized MnO2 nano-particles by XG, the surface composition of the XG/MnO2 nanocomposite membranes, and the effect of NO2 gas on the surface composition was investigated using the XPS technique. The DC conductivity and dielectric loss of nanocomposites were higher than for neat XG. The conductivities of the nanocomposites XG/MO-4, XG/MO-4/ low NO2, and XG/MO-4/high NO2 composites are half, one, and three orders of magnitude higher than that for pure XG revealing a transition from insulating to conductive properties. The results demonstrated that XG/MnO2 nanocomposite membranes are promising for potential applications in NO2 gas sensing.
The work explores the synthesis and the properties of a novel composite membrane System based on modified polystyrene (PS) grafted onto a polyvinyl chloride (PVC) membrane.
PVC membranes were prepared by solution-casting followed by exposure to an atmospheric pressure dielectric barrier discharge (DBD) with O2 to obtain an activated Surface for grafting PS to it. Moreover, the thus prepared membranes were chemically modified furthermore by amination with polyethyleneimine or sulfonation with 4 M sulfuric acid.
The membrane surface characteristics such as wettability, structure and morphology were investigated using water contact angle measurements, attenuated total reflection Fourier transform infrared spectroscopy and scanning electron microscopy experiments. The thermogravimetric stability and electrolytic responses of the membranes were studied utilizing TGA, ion exchange capacity (IEC), and solvent uptake. A significant result of plasma and chemical modification was to produce a membrane material with low permeability. Thus, the methanol permeability of the sulfonated membranes measured for 12 h was measured to 2.34$108 cm2 s1 compared to 177.00$108 cm2 s1 of Nafion 117®which is considered as a benchmark. This result indicates that the prepared sulfonated samples are an innovative and effective material for decreasing the methanol crossover in fuel cells to a great extent. This makes the PVC-g-St membranes are promising and attractive as new materials for polyelectrolyte membrane for fuel cells.