Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Dokumenttyp
Sprache
- Englisch (7)
Referierte Publikation
- ja (7)
Schlagworte
- Mechanochemistry (3)
- Amorphous Zinc phosphate (1)
- Amorphous materials (1)
- Calcium-carbonate (1)
- Ceria (1)
- Cobalt (1)
- Crystal-growth (1)
- Crystallization (1)
- Fluorapatite-gelatin nanocomposites (1)
- Fluorination (1)
Organisationseinheit der BAM
Designing the shape and size of catalyst particles, and their interfacial charge, at the nanometer scale can radically change their performance. We demonstrate this with ceria nanoparticles. In aqueous media, nanoceria is a functional mimic of haloperoxidases, a group of enzymes that oxidize organic substrates, or of peroxidases that can degrade reactive oxygen species (ROS) such as H2O2 by oxidizing an organic substrate. We show that the chemical activity of CeO2−x nanoparticles in haloperoxidase- and peroxidaselike reactions scales with their active surface area, their surface charge, given by the ζ-potential, and their surface defects (via the Ce3+/Ce4+ ratio). Haloperoxidase-like reactions are controlled through the ζ-potential as they involve the adsorption of charged halide anions to the CeO2 surface, whereas peroxidase-like reactions without charged substrates are controlled through the specific surface area SBET. Mesoporous CeO2−x particles, with large surface areas, were prepared via template-free hydrothermal reactions and characterized by small-angle X-ray scattering. Surface area, ζ-potential and the Ce3+/Ce4+ ratio are controlled in a simple and predictable manner by the synthesis time of the hydrothermal reaction as demonstrated by X-ray photoelectron spectroscopy, sorption and ζ-potential measurements. The surface area increased with synthesis time, whilst the Ce3+/Ce4+ ratio scales inversely with decreasing ζ-potential. In this way the catalytic activity of mesoporous CeO2−x particles could be tailored selectively for haloperoxidase- and peroxidase-like reactions. The ease of tuning the surface properties of mesoporous CeO2x particles by varying the synthesis time makes the synthesis a powerful general tool for the preparation of nanocatalysts according to individual needs.
Solid state reactions are slow because the diffusion of atoms or ions through the reactant, intermediate and crystalline product phases is the rate-limiting step. This requires days or even weeks of high temperature treatment, and consumption of large amounts of energy. We employed spark-plasma sintering, an engineering technique that is used for high-speed consolidation of powders with a pulsed Electric current passing through the sample to carry out the fluorination of niobium oxide in minute intervals. The approach saves time and large amounts of waste energy. Moreover, it allows the preparation of fluorinated niobium oxides on a gram scale using poly (tetrafluoroethylene) (®Teflon) scrap and without toxic chemicals.
The synthesis can be upscaled easily to the kg range with appropriate sintering equipment. Finally, NbO2F and Nb3O7F prepared by spark plasma sintering show significant photoelectrocatalytic (PEC) oxygen evolution from water in terms of photocurrent density and incident photon-to-current Efficiency (% IPCE), whereas NbO2F and Nb3O7F prepared by conventional high temperature chemistry show little to no PEC response. Our study is a proof of concept for the quick, clean and energy saving production of valuable photocatalysts from plastic waste.
Zinc phosphate, an important pigment in phosphate conversion coatings, forms protective films on rubbing surfaces.
We have simulated the underlying reactions under shear by ball-milling zinc phosphate and monitored the reaction of hopeite (Zn3(PO4)2·4H2O) and the retarded recrystallization of the amorphous reaction product by powder X-ray diffraction (PXRD) and quantitative infrared (IR) spectroscopy. Abrasion of stainless steel was simulated by addition of pure 57Fe. The results provide insight into the chemistry of phosphate conversion coatings or during battery cycling of metal phosphates and give theoretical guidance for the preparation of amorphous phosphates. Thermal analysis revealed that the release of structural water is a key step during the reaction of hopeite under shear to ball-milled amorphous zinc phosphate. The back-reaction and associated recrystallization kinetics of amorphous zinc phosphate show a classical Langmuir behavior. Fe impurities inhibit the recrystallization of ball-milled amorphous zinc phosphate strongly. 57Fe Mössbauer spectroscopy and PXRD revealed that Fe is oxidized to Fe2+ and Fe3+ during ball-milling and incorporated locally at the tetrahedral and octahedral sites of the structure. Ball-milled amorphous zinc phosphate is metastable as γ-Zn3−xFex(PO4)2. EPR studies showed the incorporation of Fe3+ to be coupled with the formation of Zn2+ vacancies. The Fe3+ defect sites bind water because of their higher Pearson hardness (compared to Fe2+ and Zn2+), thereby reducing water mobility and inhibiting further reactions like the recrystallization to hopeite. Our findings reveal the amorphization mechanism of Zn3(PO4)2·4H2O in stainless steel ball mills at the atomic scale and highlight how the reactivity of amorphous products is affected by impurities associated with the processing method.
Amorphous calcium carbonate (ACC) is an important precursor in the biomineralization of crystalline CaCO3. In nature, it serves as a storage material or as a permanent structural element, whose lifetime is regulated by an organic matrix. The relevance of ACC in materials science is primarily related to our understanding of CaCO3 crystallization pathways and CaCO3/(bio)polymer nanocomposites. ACC can be synthesized by liquid–liquid phase separation, and it is typically stabilized with macromolecules. We have prepared ACC by milling calcite in a planetary ball mill. Phosphate “impurities” were added in the form of monetite (CaHPO4) to substitute the carbonate anions, thereby stabilizing ACC by substitutional disorder. The phosphate anions do not simply replace the carbonate anions. They undergo shear-driven acid/base and condensation reactions, where stoichiometric (10%) phosphate contents are required for the amorphization to be complete. The phosphate anions generate a strained network that hinders ACC recrystallization kinetically. The amorphization reaction and the structure of BM-ACC were studied by quantitative Fourier transform infrared spectroscopy and solid state 31P, 13C, and 1H magic angle spinning nuclear magnetic resonance spectroscopy, which are highly sensitive to symmetry changes of the local environment. In the first—and fast—reaction step, the CO32– anions are protonated by the HPO42– groups. The formation of unprecedented hydrogen carbonate (HCO3–) and orthophosphate anions appears to be the driving force of the reaction, because the phosphate group has a higher Coulomb energy and the tetrahedral PO43– unit can fill space more efficiently. In a competing second—and slow—reaction step, pyrophosphate anions are formed in a condensation reaction. No pyrophosphates are formed at higher carbonate contents. High strain leads to such a large energy barrier that any reaction is suppressed. Our findings aid in the understanding of the mechanochemical amorphization of calcium carbonate and emphasize the effect of impurities for the stabilization of the amorphous phases in general. Our approach allowed the synthesis of new amorphous alkaline earth defect variants containing the unique HCO3– anion. Our approach outlines a general strategy to obtain new amorphous solids for a variety of carbonate/phosphate systems that offer promise as biomaterials for bone regeneration.
Divalent metal phosphonates are promising hybrid materials with a broad field of application. The rich coordination chemistry of the phosphonate linkers enables the formation of structures with different dimensionalities ranging from isolated complexes and layered structures to porous frameworks incorporating various functionalities through the choice of the building blocks.
In brief, metal phosphonates offer an interesting opportunity for the design of multifunctional materials. Here, we provide a short review on the class of divalent metal phosphonates discussing their syntheses, structures, and applications. We present the advantages of the recently introduced mechanochemical pathway for the Synthesis of divalent phosphonates as a possibility to generate new, in certain cases metastable compounds. The benefits of in situ investigation of synthesis mechanisms as well as the implementation of sophisticated methods for the structure analysis of the resulting compounds are discussed.
The transformation of amorphous precursors into crystalline solids and the associated mechanisms are still poorly understood. We illuminate the formation and reactivity of an amorphous cobalt phosphate hydrate precursor and the role of water for its crystallization process. Amorphous cobalt phosphate hydrate nanoparticles (ACP) with diameters of ∼20 nm were prepared in the absence of additives from aqueous solutions at low concentrations and with short reaction times. To avoid the kinetically controlled transformation of metastable ACP into crystalline Co₃(PO₄)₂ × 8H₂O (CPO) its separation must be fast. The crystallinity of ACP could be controlled through the temperature during precipitation. A second amorphous phase (HT-ACP) containing less water and anhydrous Co₃(PO₄)₂ was formed at higher temperature by the release of coordinating water. ACP contains approximately five molecules of structural water per formula unit as determined by thermal analysis (TGA) and quantitative IR spectroscopy. The Co²+ coordination in ACP is tetrahedral, as shown by XANES/EXAFS spectroscopy, but octahedral in crystalline CPO. ACP is stable in the absence of water even at 500 °C. In the wet state, the transformation of ACP to CPO is triggered by the diffusion and incorporation of water into the structure. Quantitative in situ IR analysis allowed monitoring the crystallization kinetics of ACP in the presence of water.
The nature of the bound water in solids with hydrogen-bonded networks depends not only on temperature and pressure but also on the nature of the constituents. The collapse and reorientation of these network structures determines the stability of hydrated solids and transitions to other crystalline or amorphous phases. Here, we study the mechanochemically induced loss of bound water in Co₃(PO₄)₂·8H₂O and compare this process to the behavior under hydrostatic pressure.
The associated phase transition and its kinetics were monitored by X-ray powder diffraction with Synchrotron radiation and quantitative IR spectroscopy. High shearing forces are responsible for the degradation of the hydrogen-bonded network and the concomitant crystalline–amorphous transformation. UV/Vis spectroscopy, extended X-ray absorption spectroscopy (EXAFS), and X-ray absorption near-edge spectroscopy (XANES) provided information about the short-range order in the amorphous solid, and thermal analysis revealed its composition and showed that the moderate charge densities of the Co²⁺ and PO₄³⁻ ions, which make the hydration enthalpy comparable to the binding energy of the counteranions, and the Formation of hydrogen-bonded networks favor multistage crystallization processes associated with the release and uptake of coordinated water. The changes of the Co²⁺ coordination induce a color change from pink to blue; therefore, Co₃(PO₄)₂·8H₂O can be used as an overheat temperature indicator.