Unlike conventional alloys, high entropy alloys are characterized by one or more solid solution phase(s) without a clearly defined solvent, all element contribute to the matrix in a way that is still not entirely understood. In addition, it is not known to what extent classic thermodynamic rules can be applied to these multi-element alloys, especially concerning the question about what factor incites the matrix to undergo a phase transformation.
This work tackles directly some of these aspects on a chosen alloy, Al8Cr17Co17Cu8Fe17Ni33 (at.%), which presents a high temperature single-phase γ state and a two-phase state with γ′ precipitates, above and below 900 ◦C, respectively. A combined investigation via microstructural observations, hardness testing, X-ray absorption and photoelectron spectroscopy was carried out above the γ′ formation temperature. Hardness values are independent of the annealing temperatures, microstructural analysis shows no phase formation and X-ray absorption spectroscopy does not reveal observable changes in neither local atomic nor electronic structure, indicating that approaching γ′ formation temperature is not influenced by atomic or electronic rearrangements.
Interestingly, short-range chemical order remains quantitatively compatible at any annealing temperature in the single-phase γ state, and the observed preferred pairs Al–Cu and Al–Ni in the γ state match with the γ’ precipitates composition below 900 ◦C.
This work presents an X-ray absorption spectroscopy study on a single-phase state of the Al8Cr17Co17Cu8Fe17Ni33 compositionally complex alloy, focused on the local crystal structure around each alloying element. The comparison of 1st shell bond lengths, obtained by the analysis of extended X-ray absorption fine structure (EXAFS) measured at the K-edges of each alloying element, indicates that Al8Cr17Co17Cu8Fe17Ni33 crystallizes in a distorted arrangement of an fcc lattice. A modest bond length dependence of the alloying elements with increasing atomic number is observed, with minima and maxima at Cr/Co, and Al/Cu, respectively. 1st shell bond lengths spread over ~0.03 Å; consequently, such variations cannot result in lattice distortions greater than ~0.04 Å. EXAFS results clearly indicate short-range order in the alloy: pairing of Al with Ni and Cu is favored, correlating well with a g’ precipitate composition (Al-Ni-Cu rich) reported in previous work, while Al-Cr bonding is unfavored and no Al-Al pairs are observed. Electronic structure information was obtained through comparison between near-edge regions of alloying Elements and corresponding pure metals. Intensity comparison of K-edge features agree with a charge variation of p states in Al8Cr17Co17Cu8Fe17Ni33, where Ni and Cu act as p states electron acceptors, suggesting an orbital hybridization with Al, responsible for a shrinkage in Al metallic radius in the alloy by 0.17 Å.
This article reports a comprehensive investigation of the average and local structure of La5.6WO12-δ, which has excellent mixed proton, electron and oxide ion conduction suitable for device applications. Synchrotron X-ray and neutron powder diffraction show that a cubic fluorite supercell describes the average structure, with highly disordered lanthanum and oxide positions. On average, the tungsten sites are sixfold coordinated and a trace [3.7 (1.3)%] of anti-site disorder is detected. In addition to sharp Bragg reflections, strong diffuse neutron scattering is observed, which hints at short-range order. Plausible local configurations are considered and it is shown that the defect chemistry implies a simple 'chemical exchange' interaction that favours ordered WO6 octahedra. The local model is confirmed by synchrotron X-ray pair distribution function analysis and EXAFS experiments performed at the La K and W L-3 edges. It is shown that ordered domains of similar to 3.5 nm are found, implying that mixed conduction in La5.6WO12-δ is associated with a defective glassy-like anion sublattice. The origins of this ground state are proposed to lie in the nonbipartite nature of the face-centred cubic lattice and the pairwise interactions which link the orientation of neighbouring octahedral WO6 sites. This 'function through frustration' could provide a means of designing new mixed conductors.