A major source of capacity fade of the common vanadium redox flow battery (VRFB) is the vanadium ion transport through the separator. However, different transport models disagree significantly in the diffusion coefficient for the different V species and the influence of different transport mechanisms. The underlying hypothesis of this work is that reactions inside the membrane are partly responsible for these discrepancies. Accordingly, it was investigated if redox reactions inside the nanoscopic water body of Nafion 117 can occur. X-ray absorption near edge structure spectroscopy (XANES) was used to distinguish between the different V species inside hydrated Nafion 117 and novel PVDF-based membranes. It was validated that the speciation of vanadium can be performed using the pre-edge peak energy and intensity. The experiments were performed as follows: strips of the membrane were exposed from one site to a V3+ solution (green) and from the other site to a VO2+ solution (yellow). The ions could diffuse into the membrane from both sides. A change of color of the membrane strip was observed. The blue color in the middle of the strip indicated that VO2+ was formed where V3+ and VO2+ got in contact. Using XANES this reaction inside Nafion was proven.
Polymeric core-shell particles were synthesized in a semi-batch emulsion polymerization process. The shell of the particles consist of PVDF with a high amount of beta-phase. Small-angle X-ray scattering (SAXS) was used to quantify the size of the cores of the particles and the thickness of the shell.
A facile and convenient approach for the synthesis of core–shell particles via emulsion polymerization is presented. The shell consists of poly(vinylidene fluoride) (PVDF) and the core of poly(methyl methacrylate) (PMMA), poly(glycidyl methacrylate) (PGMA) or poly(methyl acrylate) (PMA). In a first step, a non-fluorinated (meth)acrylate monomer is polymerized in the emulsion to produce poly(meth)acrylate core particles. Secondly, vinylidene fluoride (VDF) is directly added to the reactor and polymerized for shell formation. Small-angle X-ray scattering (SAXS) was employed to characterize the structure of the core–shell particles. Interestingly, the particles’ core contains fluorinated and non-fluorinated polymers, whereas the shell of the particles consists only of PVDF. The resulting particles with a diameter of around 40 nm show a significantly higher PVDF β phase content than the PVDF homopolymer obtained by emulsion polymerization