Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Dokumenttyp
- Beitrag zu einem Tagungsband (8) (entfernen)
Schlagworte
- Ultrasound (3)
- Carbon fiber reinforced polymers (2)
- Laminography (2)
- Non-destructive testing (2)
- Photon counting detectors (2)
- Serial sectioning (2)
- Thermography (2)
- X-ray imaging (2)
- Brennfleckmessung (1)
- CFRP (1)
Organisationseinheit der BAM
Im Europäischen EMPIR-Projekt „NanoXSpot“ (Measurement of the focal spot size of Xray tubes with spot sizes down to 100 nm) werden neue Messmethoden für Brennflecke von Röntgenröhren entwickelt. Teil des Projektes ist die Entwicklung eines zur Lochkameramethode äquivalenten Messverfahrens für kleine Brennflecke. ASTM E 1165-20, Annex A, beschreibt die Bestimmung von Brennfleckgrößen aus Kantenprofilen von Lochaufnahmen für Röntgenröhren mit Brennflecken > 50 μm. Es wurde bereits vorgeschlagen über die Analyse der richtungsabhängigen Kantenunschärfe einer Lochblende und anschließender CT-Rekonstruktion die Intensitätsverteilung des Brennflecks äquivalent zur Lochkameraaufnahme zu berechnen. Die Lochkameramethode, wie in EN 12543-2 und ASTM E 1165-20 beschrieben, ist im unteren Größenbereich für Mikrofokusröhren nicht geeignet, da Pinholes < 10 μm schwer zu fertigen sind und lange Belichtungszeiten erwartet werden. Mit Hilfe exakt gefertigter Lochblenden sowie strukturierter Targets mit
konvergierenden Strukturen wird der Bereich mit der Single-Shot-CT-Methode auf die Messung von Mikrofokusröhren, alternativ zur Vermessung von Kanten oder Strichgruppenkörpern, erweitert. Die rekonstruierten Brennfleckformen werden mit Kantenund Lochkameraaufnahmen quantitativ verglichen, um die Messgenauigkeit zu bewerten.
Außerdem werden CNR und Messzeit bestimmt, um die Wirtschaftlichkeit der Verfahren zu bewerten.
Modern wind turbine rotor blades consist of sandwich shell segments made from glass fiber reinforced polymers. During manufacturing, defects can arise which could lead to failure of the whole component under dynamic mechanical and thermal loads. Hence during operation defects can arise which, if detected, can be repaired locally and in-situ by applying repair patches instead of taking the whole rotor blade down and repair it remotely. This method is much more time and cost effective, since the shut-down time of the energy converter is limited to a minimum. These repair patches can, however, also lead to new defects if not applied optimally. Therefore, it is necessary to control the quality of the repair patches to ensure the best possible restoration of structural integrity of the component. As a rotor blade is an object with a large aspect ratio, X-ray laminography is predestined to provide 3D information of the objective volume. To enhance the amount of information gained from laminographic reconstruction, we use in this study a photon counting and energy discriminating X-ray detector and apply a material decomposition algorithm to the data. By inherently separating the incident spectra within the detection process into two distinct energy bins, the basis material decomposition can provide material resolved images. Choosing glass and epoxy resin as basis materials and numerically solving the inverse dual-energy equation system, the reconstructed laminographic datasets contain highly valuable information about the distribution of the basis materials within the structure. Furthermore, cross- artifacts arising from the limited angle of the projection data can be reduced by this method which allows to investigate structures that were hidden underneath the artefacts.
A composite material is a combination of two or more materials with very different mechanical, thermal and electrical properties. The various forms of composite materials, due to their high material properties, are widely used as structural materials in the aviation, space, marine, automobile, and sports industries. However, some defects like voids, delamination, or inhomogeneous fiber distribution that form during the fabricating processes of composites can seriously affect the mechanical properties of the composite material. In this study, several imaging NDE techniques such as: thermography, high frequency eddy current, ultrasonic, x-ray radiography, x-ray laminography, and high resolution x-ray CT were conducted to characterize the microstructure of carbon fiber composites. Then, a 3D analysis was implemented by the destructive technique of serial sectioning for the same sample tested by the NDE methods. To better analyze the results of this work and extract a clear volume image for all features and defects contained in the composite material, an intensive comparison was conducted among hundreds of 3D-NDE and multi serial sections’ scan images showing the microstructure variation.
Defect recognition in CFRP components using various NDT methods within a smart manufacturing process
(2018)
The manufacturing process of carbon fiber reinforced polymer (CFRP) components is gaining a more and more significant role when looking at the increasing amount of CFRPs used in industries today. The monitoring of the manufacturing process and hence the reliability of the manufactured products, is one of the major challenges we need to face in the near future. Common defects which arise during manufacturing process are e.g. porosity and voids which may lead to delaminations during operation and under load. To find irregularities and classify them as possible defects in an early stage of the manufacturing process is of high importance for the safety and reliability of the finished products, as well as of significant impact from an economical point of view. In this study we compare various NDT methods which were applied to similar CFRP laminate samples in order to detect and characterize regions of defective volume. Besides ultrasound, thermography and eddy current, different X-ray methods like radiography, laminography and computed tomography are used to investigate the samples. These methods are compared with the intention to evaluate their capability to reliably detect and characterize defective volume. Beyond the detection and evaluation of defects, we also investigate possibilities to combine various NDT methods within a smart manufacturing process in which the decision which method shall be applied is inherent within the process. Is it possible to design an in-line or at-line testing process which can recognize defects reliably and reduce testing time and costs? This study aims to show up opportunities of designing a smart NDT process synchronized to the production based on the concepts of smart production (Industry 4.0). A set of defective CFRP laminate samples and different NDT methods were used to demonstrate how effective defects are recognized and how communication between interconnected NDT sensors and the manufacturing process could be organized.
Classical film radiography is a well-established NDT technique and it is most commonly used for testing weld seams and corroded pipes e.g. in oil and gas industry or in nuclear power plants. In the course of digitization, digital detector arrays (DDA) are finding their way into industrial applications and are replacing film radiography step by step. This study deals with the latest generation of DDAs, the photon counting and energy resolving detectors (PCD), and their characteristics compared to charge integrating detectors (CID). No matter which technology to use, radiography still lacks a general issue: A three-dimensional object is projected onto a two dimensional image. Of course, advanced computed tomography (CT) algorithms exist since many years, but if the object to investigate is too large to fit into the manipulation system or its shape is not appropriate, CT is not feasible or sensible to be applied. To overcome this limitation, numerous laminographic algorithms have been developed in the past. In this study, photon counting detectors are used in combination with co-planar translational laminography to gain reconstructed three-dimensional volumes. Both laminographic testing and PCDs require a serious knowledge of many parameters that can influence the image quality in the resulting datasets. These are e.g. the detector efficiency and calibration procedure, setting of energy thresholds, exposure data, number of projections, beam length correction and spatial resolution. The use of PCDs yields more variables to be considered compared to CIDs. The most important parameters in laminographic testing and in the use of PCDs are described in this study and limits are discussed.
Carbon fiber composites have been increasingly used in aerospace, military, sports, automotive and other fields due to their excellent properties, including high specific strength, high specific modulus, corrosion resistance, fatigue resistance, and low thermal expansion coefficient. Interlaminar fracture is a serious failure mode leading to a loss in composite stiffness and strength. Iscontinuities formed during manufacturing process degrade the fatigue life and interlaminar fracture resistance of the composite. In his study, three approaches were implemented and their results were correlated to quantify discontinuities effecting static and fatigue interlaminar fracture behavior of carbon fiber composites.
Samples were fabricated by hand layup vacuum bagging manufacturing process under three different vacuum levels, indicated High (-686 mmHg), Moderate (-330 mmHg) and Poor (0 mmHg). Discontinuity content was quantified throughthickness by destructive and nondestructive techniques. Eight different NDE methods were conducted including imaging NDE methods: X-Ray laminography, ultrasonic, high frequency eddy current, pulse thermography, pulse phase thermography and lock-in-thermography, and averaging NDE techniques: X-Ray refraction and thermal conductivity measurements. Samples were subsequently destructively serial sectioned through-thickness into several layers. Both static and fatigue interlaminar fracture behavior under Mode I were conducted. The results of several imaging NDE methods revealed the trend in percentages of discontinuity. However, the results of averaging NDE methods showed a clear correlation since they gave specific values of discontinuity through-thickness. Serial sectioning exposed the composite’s internal structure and provided a very clear idea about the type, shape, size, distribution and location of most discontinuities included. The results of mechanical testing showed that discontinuities lead to a decrease in Mode I static interlaminar fracture toughness and a decrease in Mode I cyclic strain energy release rates fatigue life. Finally, all approaches were correlated: the resulted NDE percentages and parameters were correlated with the features revealed by the destructive test of serial sectioning and static and fatigue values in order to quantify discontinuities such as delamination and voids.
The new standard ‘ISO 17636-2:2013: Non-destructive testing of welds — Radiographic testing — Part 2: X- and gamma-ray techniques with digital detectors’, defines the practice for radiographic inspection of welded pipes for manufacturing and in-service inspection. It is applied in Europe for inspections of pipe welds in nuclear power plants as well as in chemical plants and allows a faster inspection with digital detector arrays (DDA) than with film. Nevertheless, it does not allow the evaluation of the depth and shape of volumetric and planar indications. In 2001 a planar tomography scanner, TomoCAR, was introduced for mechanized radiographic testing (RT) inspection and non-destructive measurement of cross sections. The project TomoWELD is based on a new concept of the scan geometry, an enhanced GPU based reconstruction, and the application of a new generation of photon counting DDAs based on CdTe crystal CMOS hybrids. The new detector permits the selection of energy thresholds to obtain an optimum energy range and reduction of the influence of scattered radiation. The concept and first measurements are presented. Flaw depth and shape of volumetric and planar irregularities can be determined.
Since a few years the direct detection of X-ray photons into electrical signals is possible by usage of highly absorbing photo conducting materials (e.g. CdTe) as detection layer of an underlying CMOS semiconductor X-ray detector. Even NDT energies up to 400 keV are possible today, as well. The image sharpness and absorption efficiency is improved by the replacement of the unsharp scintillation layer (as used at indirect detecting detectors) by a photo conducting layer of much higher thickness. If the read-out speed is high enough (ca. 50 – 100 ns dead time) single X-ray photons can be counted and their energy measured. Read-out noise and dark image correction can be avoided. By setting energy thresholds selected energy ranges of the X-ray spectrum can be detected or suppressed. This allows material discrimination by dual-energy techniques or the reduction of image contributions of scattered radiation, which results in an enhanced contrast sensitivity. To use these advantages in an effective way, a special calibration procedure has to be developed, which considers also time dependent processes in the detection layer. This contribution presents some of these new properties of direct detecting digital detector arrays (DDAs) and shows first results on testing fiber reinforced composites as well as first approaches to dual energy imaging.