Degradation and damage analysis of composite pressure vessels via experimental modal analysis
(2023)
For mobile gas storage systems, the application of type IV pressure vessels is state of the art. Type IV tanks consist of an inner polymer liner fully wrapped with fibre-reinforced plastic (FRP). Because of the complex fabric of the FRP as well as a difficulty estimable interaction behaviour between the single components under load, there are still no satisfying non-destructive testing methods to assess the current state of failure nor to estimate the level of degradation accurately and economically. At BAM division 3.5, analysing the ageing process of mobile composite pressure vessels is a major task to ensure safe usage over the whole lifetime. In this context, key aspects of our ongoing research activities are the invention of new test procedures and the development of accurate lifetime prediction models. In order to determine the level of degradation or damage, one meaningful non-destructive approach is to analyse the structural dynamic behaviour via an experimental modal analysis (EMA). Over the last few years, different types and sizes of composite pressure vessels have been tested in several research projects. The presented paper gives an insight into how to extract and interpret modal parameters and how to fit them to the results of residual strength tests.
Kurzfassung. Die meisten Faserverbundbehälter, die in Europa für den Transport gefährlicher Stoffe oder als Speicherbehälter für Wasserstoff oder Erdgas in Fahrzeugen Verwendung finden, werden für eine nicht begrenzte Lebensdauer ausgelegt. In regelmäßigen Abständen sind für diese Druckbehälter wiederkehrende Prüfungen vorgeschrieben, die in der Regel aus visuellen Inspektionen und hydraulischen Innendruckprüfungen bestehen. Die wiederkehrenden Prüfungen sind jedoch weder geeignet, die sichere Betriebsdauer festzulegen noch den Alterungszustand der Druckbehälter zu beurteilen. Aufgrund des weiter steigenden Drucks zur Kosten- und Gewichtsreduktion von Faserverbundbehältern und der damit einhergehenden Ausnutzung der existierenden Sicherheitsmargen gewinnen Methoden zur Beurteilung des Alterungsverhaltens dieser Druckbehälter immer mehr an Bedeutung.
Vor diesem Hintergrund wurde in der BAM das Vorhaben „Alterungsverhalten von Composite-Druckgefäßen mit Carbonfaser-Compositen unter gekoppelten Beanspruchungen (COD-AGE)“ gestartet, um die Alterung von Faserverbundbehältern mittels verschiedener zerstörungsfreier Prüfverfahren zu untersuchen. Die hier vorgestellten Ergebnisse wurden an einem Typ 4 Hybridbehälter mit Kunststoffliner gewonnen, in den im Rahmen des Herstellungsprozesses optische Glasfasern in verschiedenen Schichten integriert wurden. Der Behälter wurde mittels hydraulischem Innendruck und erhöhter Umgebungstemperatur zyklisch bis zum Lebensende belastet. Zwischen den einzelnen Lastsequenzen erfolgte eine an die wiederkehrende Prüfung im Betrieb angelehnte hydraulische Druckbelastung.
Sowohl die hydraulische Alterung als auch die Druckrampen wurden mittels Schallemissionsprüfung (SEP) und verteilter faseroptischer Sensorik mit dem Ziel einer frühzeitigen Versagensvorhersage überwacht. Durch die Schallemissionsanalyse sollte untersucht werden, ob zum Lebensende hin ein signifikanter Anstieg der Schallemissionsaktivität und -intensität, unterteilt in verschiedene Lastbereiche, beobachtet werden kann. Zusätzlich zum kontinuierlichen Monitoring der Zyklierung sollten die Druckrampen separat untersucht werden, um hier Potenziale für die wiederkehrende Prüfung zu erkennen.
Due to high specific stiffness, fibre reinforced plastics are the dominant material group for the design of mobile pressure vessels. At the Federal Institute of Materials Research and Testing (BAM) aging process of composite pressure vessels is studied to be able to give more accurate lifetime predictions in future. Investigations are based on type III breathing air cylinders consisting of an aluminium tank which is fully wrapped with carbon fibre reinforced plastics. Goal is to detect changes of residual stresses over life time which directly affect fatigue strength. Within this paper an approach is presented to monitor residual stresses via an experimental modal analysis (EMA). First, the influence of changed stress conditions on modal parameters is analysed via a numerical study. Secondly, a test bench for an EMA is set up. To be able to analyse cylinders of different prestress condition, several specimens are prestress modified via high-temperature and high-pressure treatment. During modification processes, specimens are monitored via optical fibres to control prestress modifications. Through experimental measurements of the modified specimens via EMA changes in prestressing can be detected. Finally, validity and accuracy of the EMA is evaluated critically by comparing all numerically and experimentally obtained data.
Fibre-reinforced plastics (FRP) especially carbon-fibre-reinforced polymer (CFRP) and glass-fibre-reinforced polymer (GFRP) are commonly used materials in high pressure vessels and storage units for automotive and aerospace purposes. Optical fibres are suitable to be integrated or directly applied to the surface of FRP components. Using optical fibres it is possible to monitor the distributed strain profiles and changes within the fatigue life of a pressure vessel to ensure the operational safety. Within artificial ageing experiments we used swept wavelength interferometry (SWI) based distributed strain sensing for the monitoring of commercial high-pressure composite cylinder. This artificial ageing was performed using test conditions of 503bar pressure load (service pressure 300 bar) and 89 °C for 100 h. The polyimide coated optical fibres were glued to the surface externally in circumferential and axial direction. Using distributed strain sensing (DSS) material expansion of over 0.5% were monitored with sub-centimetre spatial resolution. Within the circumferential direction we observed up to 10 % local fluctuation compared to the median strain caused by inhomogeneous material expansion, which could cause local material fatigue. In addition, we determined material degradation manifested itself as localized remaining material expansion and/or contraction. Results have been validated by other non-destructive methods like digital strip projection.
Within a current research project at the Federal Institute for Materials Testing and Research (BAM), the degradation process of composite pressure vessels is studied to be able to give more accurate lifetime predictions in future. The presented research is based on type III pressure vessels consisting of an aluminium tank which is fully wrapped with carbon fibre reinforced plastics. Focus is set on the analysis of residual stresses which are induced into the pressure vessel during manufacturing process in order to increase high cycle fatigue. However, with increasing lifetime residual stress conditions do change. To be able to measure and monitor stress conditions, the application of a non-destructive measurement method is aspired.
In this paper, potential of an experimental modal analysis is worked out to capture and monitor aging and degradation effects in pressure vessels. With the presented method, information about changes in residual stress can be obtained via an analysis of the modal parameters. To realize an application, first, a finite element simulation is used to prove and evaluate potential capability and validity. In the following, a test bench is set up and successively optimized in its accuracy and efficiency. Sensitivity of the applied measurement technique is experimentally ascertained trough the measurement of several prestress modified pressure vessels. Finally, experimental results are interpreted and evaluated with the help of numerically gained findings.
Due to high specific stiffness a nd strength properties, fibre reinforced plastics are used more and more often for the construction of pressure vessels. Within a recent research project run by the Federal Institute for Materials Research and Testing (BAM), aging process of composite pressure vessels is investigated in order to be able to give more accurate lifetime predictions in the future. Focus is set on type III pressure vessels consisting of an aluminium tank which is fully wrapped with carbon fibre reinforced plastics. In order to increase high-cycle fatigue, residual stresses are induced into the pressure vessel during manufacturing process. In particular, residual compressive stresses within the inner aluminium layer have been defined as a main parameter affecting fatigue strength. The aim is to identify and evaluate residual stresses of the pressure vessel by analysing its modal parameters. Through the set-up of a finite-element model potential capability and validity for the use of modal analysis is proven and evaluated, considering influences resulting from manufacturing deviations, too. In the following, a number of stress sensitive modes are defined. Based on these preliminary numerical investigations, a test bench is set up in order to measure pressure vessels via an experimental modal analysis. A final critical evaluation regarding the accuracy of the modal analysis is made by comparing experimental results with data obtained through simulations.
Emergency response units increasingly use pressure cylinders made from fibre composites for breathing air as elements of personal protective equipment (PPE). Such applications expose the composite cylinders to harsh temperature and handling conditions. At least in Europe, standards have been used for certifying PPE, which are designed and mandatory for the approval of pressure receptacles for the transport of dangerous goods. Therefore, service conditions specific to PPEs are not accounted for in these standards. In this paper, BAM (Federal Institute for Materials Research and Testing) investigates the residual safety of a composite cylinder design at the end of their designated service life of 15 years. The cylinders (test pressure PH 450 bars; 6.8 Litres) are of one design type with aluminium liner and fully wrapped with carbon fibres, which is commonly considered a “Type III” cylinder. All cylinders were used as PPE by the Berlin fire department and randomly picked in three samples of 25 cylinders each before tested.
At BAM, the cylinder samples underwent hydraulic load cycle tests (LCT), conventional burst tests (BT) and so called slow burst tests (SBT). A concept for quantification of strength degradation already introduced by BAM was applied. This concept is based on a probabilistic assessment of the average strength and scatter of each sample of cylinders. The strength distributions of the used PPEcylinders is shown and analysed. Some unexpected effects are shown and a refinement of the statistical assessment is introduced.