The durability of concrete structures due to alkali-silica-reaction (ASR) is usually been assessed by ASR concrete prism tests (CPT). Therefore, the expansion of concrete specimens indicates an alkalisensitivity.
In Germany these tests are performed at 40°C or accelerated 60°C. Nevertheless, ASR prism tests are expensive, power and time-consuming. For these reasons, an alternative chemical test (“mod. BTU-test”) was developed in the past. The “mod. BTU-test” was correlated with German standard CPT.
In this test, the solubility of silica and alumina in the liquid phase is measured by ICP-OES.
For special requirements in concrete road construction, stricter test procedures are necessary. The specimens are repeatedly subjected to cyclic alternating storage in NaCl. On the one hand, the presence of NaCl increases the ASR expansion, on the other hand NaCl also changes the dissolution behaviour of silica and alumina.
For now is not possible to correlate the solubilities of “mod. BTU-test” and ASR expansions influenced by NaCl. Therefore, four aggregates with different ASR sensitivities were chosen and ASR concrete prism tests (in addition with NaCl) have been performed. According to the “mod. BTU-test” the solubilities of silica and alumina in presence of different NaCl concentrations were measured.
This paper is about the regression analysis of silica and alumina dissolution and ASR expansion tests in presence of NaCl. The regression analysis shows the influence of a quasi-continuous and an interrupted cyclic alternating storage. Additionally the effects of temperature and NaCl concentration are investigated. In the end, a suitable NaCl concentration of the “mod. BTU-test” for dissolution experiments is recommended. The “mod. BTU-Test” with NaCl might be a serious and reliable test method for ASR classification for concrete road construction.
The use of supplementary cementing materials (SCMs) added to concrete mixtures can avoid the alkali-silica reaction. Such materials have a wide range of composition and therefore the inhibition mechanisms can be very differently.
The effectiveness of SCMs which provide silica and alumina into the alkaline solution cannot only be explained by reducing the OH--concentration of the pore solution. From dissolution experiments in potassium hydroxide solutions, an interaction was noted between the aggregate and five SCMs via the alkaline solution. Under specific conditions, no silica is released from the aggregate grains.
Mineralogical investigations (XRD, SEM+EDX) of the grain surfaces confirm that quartz is the main source of silica. In the presence of alumina providing SCMs, the quartz dissolution is strongly reduced or even sometimes stopped. On surfaces of grains a very thin layer can be observed which is probably responsible for reduction or stopping of the silica dissolution and therefore for the inhibition of ASR.
The knowledge of dissolution processes of aggregates and supplementary cementing materials (SCMs) in alkaline solutions can help to describe the expansion of concretes caused by alkali-silica reaction (ASR) and the effects to avoid ASR by using SCMs in more details. Therefore, dissolution experiments in alkaline solutions under different pH values and different temperatures were performed using aggregates in the original grain size and SCMs in different ratios. The concentrations of soluble silica and additionally alumina were determined by ICP-OES. The investigations showed that up to now the “best” conditions to explain the damage behavior of concrete structures are a pH value of 13 (e.g. 0.1 M KOH solution) and a temperature of 80 °C. The evaluation bases on the parameter “excess silica” which is calculated from the dissolved silica and alumina of the aggregates and the SCMs. It was demonstrated that SCMs reduce and sometimes stop the dissolution of aggregates. The efficiency of the SCMs depends on their amount and chemical composition.