We report on the in situ investigation of mechanochemical syntheses of metal phosphonates. The metal phosphonates are formed in milling reactions starting from a metal acetate and a phosphonic acid. The conversions are observed by synchrotron PXRD and Raman spectroscopy to shed light on the reaction mechanisms including possible intermediates.
Self-mated magnesia stabilized zirconia (Mg-PSZ) ceramic sliding couples have been investigated at 100 N load (P0max= 1324 MPa) in oscillating sliding conditions in different humidity conditions in air and in hot steam. Temperatures have been varied up to 400 °C and pressures up to 6 bars. The results show that the wear behavior of MgO-ZrO2 under high Hertzian contact pressures is strongly dependent on temperature and is similar for both dry oscillating and oscillating in hot steam. However, although the evolution in wear rates on temperature is similar and the wear rates of MgO-ZrO2 plunged above 300 °C in hot steam and air by nearly three orders of magnitude, SEM micrographs revealed in hot steam at 400 °C smooth wear tracks. In contrast, hot steam enhanced the tribochemistry of self-mated alumina couples and reduced wear rates. Hot steam decreased the coefficients of friction of MgO-ZrO2 with increasing temperature, but not the wear rates.
Typology of Inks
Archives and museums around the world contain a vast number of manuscripts that were written in different inks: carbon inks, plant inks, iron-gall inks and mixed inks. Yet most archaeometric studies of manuscripts focus on the palette of pigments found in illuminated manuscripts whereas identification of the inks is still largely based on cultural-historical studies and visual inspections. One of the reasons of this disproportion in the studies can be explained by the properties of Raman spectroscopy, the technique of choice for identification of pigments. In contrast, this technique is only partially viable when dealing with organic colourants. Brown and Clark discuss these difficulties and the uncertainties of identification of iron-gall inks by Raman spectroscopy in their pioneering work on early medieval Anglo-Saxon manuscripts (K. Brown and R. Clark 2004). To facilitate instrumental analysis of inks, we have developed a protocol that starts with the identification of the inks type (Rabin et al. 2012) which doesn’t require complicated instrumentation and can be carried out by paleographers and codicologists.
Three typological ink classes
The black writing materials used in manuscript production in Antiquity und Middle Ages can be sorted in three typologically different ink classes: soot, plant and iron-gall. Soot ink is a fine dispersion of carbon pigments in a water soluble binding agent; plant-based ink consists of a solution of the tannins extracted from gallnuts or tree bark; iron-gall ink, is produced by mixing a soluble compound of iron (II) with gallic or tannic acid extracted from gallnuts or tree bark. Therefore, iron-gall ink presents a boundary case between solution and dispersion ink, in which a water-soluble preliminary stage oxidizes and evolves into a black, insoluble precipitate similar to the carbon pigments when the writing is exposed to air (Krekel 1999). The additional category of mixed inks, i.e. inks produced by addition of various metals to the soot inks or intentional mixing of iron-gall and soot - based inks started attracting scholarly attention only recently because their significance was established only a short while ago (Brun et al. 2016, Colini 2018, Nehring et al. 2021). We suggest that plant and mixed inks build a bridge from the carbon ink of Antiquity to the properly formulated iron-gall ink that became a standard black ink from the late Middle Ages to the 19th century when it gave way to modern inks.
Low melting Li2O-PbO-B2O3, Me2O-ZnO-B2O3, Me = Li, Na, K, Rb and CaO-ZnO-B2O3 glasses were studied with Raman and infrared spectroscopies to advance the structural understanding of zinc borate glasses as potential candidates for substitution of lead containing glasses. Although the effect of type of alkali ions on the number (N4) of fourfold coordinated boron (B4) in the glasses is small, the alkali ions direct the type of borate groups, i.e., pentaborate in lithium, sodium, and calcium zinc borate glasses, as well as diborate in potassium and rubidium containing ones. Both groups were simultaneously found in Li2O-PbO-B2O3. Alkali ions are mainly responsible for the formation of B4-units and metaborate. Zinc ions favorably compensate non-bridging oxygen and partially form ZnO4. With decreasing N4 and field strength of the alkali ions the atomic packing density, glass transition temper ature and Young’s Modulus also decrease. The coefficient of thermal expansion increases with decreasing N4.