Full penetration high power bead-on-plate laser beam welding tests of up to 20 mm thick 2205 duplex steel plates were performed in PA position. A contactless inductive electromagnetic (EM) weld pool support system was used to prevent gravity drop-out of the melt. Welding experiments with 15 mm thick plates were carried out using IPG fiber laser YLR 20000 and Yb:YAG thin disk laser TruDisk 16002. The laser power needed to achieve a full penetration was found to be 10.9 and 8.56kW for welding velocity of 1.0 and 0.5 m min(-1), respectively. Reference welds without weld pool support demonstrate excessive root sag. The optimal value of the alternating current (AC) power needed to completely compensate the sagging on the root side was found to be approximate to 1.6 kW for both values of the welding velocity. The same EM weld pool support system was used in welding tests with 20 mm thick plates. The laser beam power (TRUMPF Yb:YAG thin disk laser TruDisk 16002) needed to reach a full penetration for 0.5 m min(-1) was found to be 13.9 kW. Full penetration welding without EM weld pool support is not possible-the surface tension cannot stop the gravity drop-out of the melt. The AC power needed to completely compensate the gravity was found to be 2 kW. (C) 2016 Laser Institute of America
An electromagnetic weld pool support system for 20 mm thick duplex stainless steel AISI 2205 was investigated numerically and compared to experiments. In our former publications, it was shown how an AC magnetic field below the process zone directed perpendicular to the welding direction can induce vertically directed Lorentz forces. These can counteract the gravitational forces and allow for a suppression of material drop-out for austenitic stainless steels and aluminum alloys. In this investigation, we additionally adopted a steady-state complex magnetic permeability model for the consideration of the magnetic hysteresis behavior due to the ferritic characteristics of the material. The model was calibrated against the Jiles-Atherton model. The material model was also successfully tested against an experimental configuration before welding with a 30 mm diameter cylinder of austenitic stainless steel surrounded by duplex stainless steel. Thereby, the effects of the Curie temperature on the magnetic characteristics in the vicinity of the later welding zone were simulated. The welding process was modelled with a 3D turbulent steady-state model including heat transfer and fluid dynamics as well as the electromagnetic field equations. Main physical effects, the thermo-capillary (Marangoni) convection at the weld pool boundaries, the natural convection due to gravity as well as latent heat of solid–liquid phase transitions at the phase boundaries were accounted for in the model. The feedback of the electromagnetic forces on the weld pool was described in terms of the electromagneticinduced pressure. The FE software COMSOL Multiphysics 4.2 was used in this investigation. It is shown that the gravity drop-out associated with the welding of 20 mm thick duplex stainless steel plates due to the hydrostatic pressure can be prevented by the application of AC magnetic fields between around 70 mT and 90 mT. The corresponding oscillation frequencies were between 1 kHz and 10 kHz and the electromagnetic AC powers were between 1 kW and 2.3 kW. In the experiments, values of the electromagnetic AC power between 1.6 kW and 2.4 kW at oscillation frequencies between 1.2 kHz and 2.5 kHz were found to be optimal to avoid melt sagging or drop-out of melt in single pass fullpenetration laser beam welding of 15 mm and 20 mm thick AISI 2205.
Hydrogen in metals can cause a degradation of the mechanical properties, the so-called hydrogen embrittlement. In combination with internal stresses, hydrogen assisted cracking (HAC) can occur. This phenomenon is not completely understood yet. To better characterise the cracking behaviour, it is important to gain information about the evolution of the 3D crack network. For this purpose samples of lean duplex stainless steel were loaded with hydrogen by means of electrochemical charging and investigated by means of synchrotron refraction CT and SEM fractography after uniaxial tensile loading. Synchrotron refraction CT is an analyser-based imaging (ABI) technique. It uses a Si (111) single crystal as analyser, which is placed into the beam path between sample and detector. According to Bragg’s law only incident x-rays within a narrow range around the Bragg-angle are diffracted from the analyser into the detector. Hence, the analyser acts as an angular filter for the transmitted beam. This filtering allows to turn the refraction and scattering of x-rays into image contrast. Refraction occurs at all interfaces, where the density of the material changes and is more sensitive to density changes than the attenuation. Therefore, it is possible to detect smaller cracks than with classical x-ray imaging techniques, like CT, with comparable spacial resolution. It also visualises the 3D structure of the cracks and gains quantitative information about their morphology and distribution. Since cracks introduced by HAC are usually very small and have a small opening displacement, synchrotron refraction CT is expected to be well suited for imaging this cracking mechanism and can be a valuable tool to characterise the formation and the evolution of a 3D crack network.
3D Crack analysis in hydrogen charged lean duplex stainless steel with synchrotron refraction CT
(2016)
Hydrogen in metals can cause a degradation of the mechanical properties, the so-called hydrogen embrittlement. In combination with internal stresses, hydrogen assisted cracking (HAC) can occur. This phenomenon is not completely understood yet. To better characterise the cracking behaviour, it is important to gain information about the evolution of the 3D crack network. For this purpose samples of lean duplex stainless steel were loaded with hydrogen by means of electrochemical charging and investigated by means of synchrotron refraction CT and SEM fractography after uniaxial tensile loading. Synchrotron refraction CT is an analyser-based imaging (ABI) technique. It uses a Si (111) single crystal as analyser, which is placed into the beam path between sample and detector. According to Bragg’s law only incident x-rays within a narrow range around the Bragg-angle are diffracted from the analyser into the detector. Hence, the analyser acts as an angular filter for the transmitted beam. This filtering allows to turn the refraction and scattering of x-rays into image contrast. Refraction occurs at all interfaces, where the density of the material changes and is more sensitive to density changes than the attenuation. Therefore, it is possible to detect smaller cracks than with classical x-ray imaging techniques, like CT, with comparable spacial resolution. It also visualises the 3D structure of the cracks and gains quantitative information about their morphology and distribution. Since cracks introduced by HAC are usually very small and have a small opening displacement, synchrotron refraction CT is expected to be well suited for imaging this cracking mechanism and can be a valuable tool to characterise the formation and the evolution of a 3D crack network.
Duplex stainless steels (DSS) are frequently used, especially in applications requiring high strength combined with high corrosion resistance in aggressive media. Examples include power plant components and maritime structures. During welding of these steels, local variations in chemical composition can occur. This results in ferritization of the material and negatively affects the mechanical properties of the components. In this work, tungsten inert gas (TIG) welding experiments were performed with DSS. Chemical composition analysis was realized in situ by using Laser Induced Breakdown Spectroscopy (LIBS). The aim of the work is to quantitatively measure the chemical composition in the weld seam of various DSS and to identify possible influences of welding parameters on the microstructure of the material. The chemical concentrations of the main alloying elements Cr, Ni, Mn on the surface of the sample during the welding process and the cooling process were measured. Mn and Ni are austenite stabilizers and their content increases during welding by using certain high alloyed filler material. Spectra were recorded every 1.3 s at a spacing of approximately 2 mm. During the cooling process the location of the measurement was not changed. The LIBS method is proofed to be suitable for the quantitative representation of the chemical compositions during the welding process.
Nichtrostende Duplexstähle (DSS) werden häufig verwendet, insbesondere bei Anwendungen, die eine hohe Festigkeit in Verbindung mit einer hohen Korrosionsbeständigkeit in aggressiven Medien erfordern. Beispiele hierfür sind Kraftwerkskomponenten und maritime Anwendungen. Beim Schweißen dieser Stähle kann es zu lokalen Schwankungen in der chemischen Zusammensetzung kommen. Dies führt zu einer Ferritisierung des Werkstoffs und beeinträchtigt die mechanischen Eigenschaften der Bauteile. In dieser Arbeit wurden Versuche zum Wolfram-Inertgas-Schweißen (WIG) mit DSS durchgeführt. Die Analyse der chemischen Zusammensetzung wurde in situ mit Hilfe der laserinduzierten Plasmaspektroskopie (LIBS) durchgeführt. Ziel der Arbeit ist es, die chemische Zusammensetzung in der Schweißnaht verschiedener DSS quantitativ zu messen und mögliche Einflüsse der Schweißparameter auf die Mikrostruktur des Werkstoffs zu ermitteln. Gemessen wurden die chemischen Konzentrationen der Hauptlegierungselemente Cr, Ni, Mn auf der Oberfläche der Probe während des Schweißprozesses und des Abkühlungsprozesses. Mn und Ni sind Austenitstabilisatoren, deren Gehalt beim Schweißen durch die Verwendung bestimmter hochlegierter Schweißzusatzwerkstoffe zunimmt. Die Spektren wurden alle 1,3 s in einem Abstand von etwa 2 mm aufgezeichnet. Während des Abkühlungsprozesses wurde der Ort der Messung nicht verändert. Die LIBS-Methode eignet sich nachweislich zur quantitativen Darstellung der chemischen Zusammensetzungen während des Schweißvorgangs.
Duplex stainless steels (DSS) are frequently used, especially in applications requiring high strength combined with high corrosion resistance in aggressive media. Examples include power plant components and maritime structures. During welding of these steels, local variations in chemical composition can occur. This results in ferritization of the material and negatively affects the mechanical properties of the components. In this work, tungsten inert gas (TIG) welding experiments were performed with DSS. Chemical composition analysis was realized in situ by using Laser Induced Breakdown Spectroscopy (LIBS). We could quantitatively measure the chemical composition in the weld seam of various DSS and identify possible influences of welding parameters on the microstructure of the material. The chemical concentrations of the main alloying elements Cr, Ni, Mn on the surface of the sample during the welding process and the cooling process were measured. Mn and Ni are austenite stabilizers and their content increases during welding by using certain high alloyed filler material.
Erstellung von Tiefenprofilen auf Schweißnähten mittels Laserinduzierter plasmaspektroskopie (LIPS)
(2021)
Duplexstähle sind hochlegierte, nichtrostende Stähle. Sie bieten aufgrund des ausgewogenen Phasenverhältnisses von Austenit und Ferrit einige physikalische Vorteile gegenüber anderen nichtrostenden Stählen. Beim Schweißen können sich durch die Kondensation von Schweißrauch und verdampftem Material verschiedene chemische Elemente auf der Oberfläche der erstarrten Schweißnaht anreichern. Dann ist die Bildung einer schützenden Chromoxidschicht nicht mehr gewährleistet und es kann an diesen Stellen zu Lochfraß kommen. Frühere Arbeiten haben gezeigt, dass die Anreicherung von Mangan und Chrom an der Oberfläche der Wärmeeinflusszone des geschweißten Edelstahls 304L mit LIBS gemessen werden kann. Wir stellen die Ergebnisse der Optimierung der LIBS-Parameter für präzise Dickenmessungen solcher dünnen Schichten und für Tiefenprofilmessungen vor. Dazu haben wir galvanisch beschichtete Kupferproben mit bekannten Schichtdicken verwendet. Die Mangankonzentration im Schweißgut ist reduziert. Dies hat einen großen Einfluss auf die metallografische Struktur des Materials.
Duplex steels are high-alloyed, stainless steels. They offer some physical advantages over other stainless steels due to the balanced phase ratio of austenite and ferrite. During welding processes, when welding fumes and vaporized material condensates, different chemical elements can accumulate on the surface of the solidified weld. Then, the formation of a protective chromium oxide layer is no longer guaranteed and pitting corrosion can occur at these places. Previous work has shown that the accumulation of manganese and chromium on the surface of the heat-affected zone of the welded high-grade steel 304L can be measured by LIBS.
We present the results of the optimization of LIBS parameters for precise thickness measurements of such thin films and for depth profile measurements Therefore, we used galvanically coated copper samples with known film thicknesses. The Concentration of manganese is reduced in the weld metal. This has a high impact on the metallografic structure of the material.
Schweißprozesse von nichtrostenden Duplexstählen verursachen aufgrund hoher Abkühlungsraten und Änderungen der chemischen Zusammensetzung ein unausgewogenes Austenit (γ)/Ferrit (δ)-Verhältnis. Das verursacht eine Degradation der mechanischen Eigenschaften und der Korrosionsbeständigkeit. Die In-situ-Überwachung des Schweißbades soll mit Hilfe der laserinduzierten Plasmaspektroskopie (LIPS) realisiert werden. Ein großer Vorteil dieser Technik ist die hochgenaue zeit- und ortsaufgelöste Messung der chemischen Zusammensetzung während des Schweißens. Bisherige Untersuchungen haben ergeben, dass die LIBS-Methode geeignet ist, chemische Elemente während des Schweißens zu detektieren und eine Verteilung ausgewählter Elemente aufzuzeigen. Chemische Zusammensetzungen können mit vorab erstellten Kalibrierkurven dargestellt weerden.