Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Dokumenttyp
- Zeitschriftenartikel (5)
- Beitrag zu einem Tagungsband (3)
- Vortrag (1)
Sprache
- Englisch (9) (entfernen)
Schlagworte
- CFRP (4)
- GFRP (4)
- Active thermography (3)
- Thermography (3)
- Mechanochemistry (2)
- Active and passive thermography (1)
- Artificial and natural defects (1)
- Emissivity (1)
- FFF-3D printer (1)
- Fibre reinforced composites (1)
Organisationseinheit der BAM
Paper des Monats
- ja (1)
Eingeladener Vortrag
- nein (1)
Fused filament fabrication (FFF) is a material extrusion-based technique often used in desktop 3D printers. Polymeric filaments are melted and are extruded through a heated nozzle to form a 3D object in layers. The extruder temperature is therefore a key parameter for a successful print job but also one of the main emission driving factors as harmful pollutants (e.g., ultrafine particles) are formed by thermal polymer degradation. The awareness of potential health risks has increased the number of emission studies in the past years. However, studies usually refer their calculated emission data to the printer set extruder temperature for comparison purposes. In this study, we used a thermocouple and an infrared camera to measure the actual extruder temperature and found significant temperature deviations to the displayed set temperature among printer models. Our result shows that printing the same filament feedstocks with three different printer models and with identical printer set temperature resulted in a variation in particle emission of around two orders of magnitude. A temperature adjustment has reduced the variation to approx. one order of magnitude. Thus, it is necessary to refer the measured emission data to the actual extruder temperature as it poses a more accurate comparison parameter for evaluation of the indoor air quality in user scenarios or for health risk assessments.
Low-velocity impact damages were monitored in-situ using an infrared camera before, during and after Impact load. Thermal images were recorded as a function of time at the front side (impact) as well as at the rear side of the plates using a high frame rate. In CFRP and GFRP specimens with different thicknesses and made of various types of fibers and matrix materials, different kind of damages were observed. The sizes of the heated areas being related to the damages and the amount of energy dissipated into heat was determined quantitatively as a function of impact energy and are a measure of the resistance of the different materials against impact load.
Impact damages and delaminations in fibre-reinforced composites (FRC) might not be visible at the surface, but could have an influence on the resistance and on the long-term behaviour of the component. Therefore, and especially for safety relevant structures, non-destructive methods are required for the assessment of such damages.
Active thermography methods are suitable to characterize damages after loading using different kind of excitation techniques and various configurations of infrared (IR) camera and heating sources. Here, flash lamps, impulse excitation with infrared radiator and lock-in technique with halogen lamps or widened laser beams are suited. In addition, non-optical sources like sonotrodes (requiring direct contact to the structure) or induction generators (only suited for carbon fibre reinforced polymer (CFRP) structures) could be applied as well. For the investigation of the evolution of the damage during the impact, passive thermography can be applied in-situ. Elastic and plastic deformations alter the temperature of the structure and thus the temperature on the surface.
In this contribution, at first the general principles of quantitative defect characterisation in FRC using active thermography with flash, impulse and lock-in excitation are described. Optical and thermal properties of the FRC material and its anisotropy are considered. Results of phase differences obtained at flat bottom holes with flash and lock-in thermography are compared for qualifying both methods for quantitative defect characterization. Secondly, the damage evolution of CFRP and GFRP structures under impact load and static tensile loading is described. The spatial and temporal evolution of the surface temperature enables us to distinguish matrix cracks or fibre-matrix separation from delaminations between the layers. Afterwards, all results for loading defects, obtained by passive and active thermography, are compared with each other. Fig. 1 and 2 show the difference of passive and flash thermography obtained at impact and tensile loaded CFRP plates, respectively. As one purpose of these investigations is the development of standards within national (DIN) and European (CEN) standardisation bodies, new draft and final standards are presented and further needs are discussed at the end of the presentation.
Quantification of impact damages in CFRP and GFRP structures with thermography and ultrasonics
(2018)
The extent of damage caused by impacts in fibre reinforced composites depends on the energy of the impacts, on the velocity and the shape of the impacting body, on the material and structure of the composite and on the geometry of the structure. Here, mainly the thickness of the component is essential. The non-destructive evaluation of these damages can be carried out using both ultrasound and active thermography methods. A comparison of the detection sensitivity of these methods for the different damages is carried out in this paper depending on the fibre composite material used (CFRP and GFRP), the thickness of the material and the impact energy. The NDT methods used after the damage are supplemented by thermographic measurements with high temporal resolution, which were already recorded during the impact.
We present an in situ triple coupling of synchrotron X-ray diffraction with Raman spectroscopy, and thermography to study milling reactions in real time. This combination of methods allows a correlation of the structural evolution with temperature information. The temperature information is crucial for understanding both the thermodynamics and reaction kinetics. The reaction mechanisms of three prototypical mechanochemical syntheses, a cocrystal formation, a C@C bond formation (Knoevenagel condensation), and the formation
of a manganese-phosphonate, were elucidated. Trends in the temperature development during milling are identified. The heat of reaction and latent heat of crystallization of the product contribute to the overall temperature increase. A decrease in temperature occurs via release of, for example, water as a byproduct.
Solid and liquid intermediates are detected. The influence of the mechanical impact could be separated from temperature effects caused by the reaction.
The increased use of fibre reinforced plastic (FRP) composites for improved efficiency and reliability in energy related applications, e.g. wind and marine turbine blades, nacelles, oil and gas flexible risers, also increases the demand for innovative non-destructive testing technologies. In this contribution, results concerning the characterisation of CFRP and GFRP during and after quasi-static tensile loading are presented. It includes the measurement of optical properties in the infrared spectral range, tensile loading tests with the observation of the temperature distribution at one or both sides of the specimens using an infrared camera for the preparation and monitoring of intended natural defects, and active thermography inspections after tensile loading. It is shown that the defect preparation was successful. Thermographic monitoring during and active thermography testing after tensile loading enable the detection of the lateral extend of the generated defects. Differences between CFRP and GFRP materials are discussed.
We present a first direct measurement of the temperature during milling combined with in situ Raman spectroscopy monitoring. The data reveal a low temperature increase due to the mechanical impact and clear temperature increases as a consequence of the reaction heat. Based on the data, temperature rises as postulated in the magma plasma and hot spot theory can be excluded for soft matter milling syntheses.
The increased use of fibre-reinforced plastic (FRP) composites for improved efficiency and reliability in energy related applications e.g. wind and marine turbine blades, nacelles, oil and gas flexible risers, also increases the demand for innovative non-destructive testing technologies. Thus, in order to achieve increased acceptance of suited and optimized non-destructive testing (NDT) methods in industry, the European Metrology Research Programme (EMRP) project ENG57 Validated Inspection Techniques for Composites in Energy Applications (VITCEA) deals with the development and validation of innovative NDT technologies. In this contribution, results concerning thermographic investigations at test specimens during tensile loading and active thermography testing after tensile loading are presented. Additionally, the determination of the optical properties (relative transmittance and directional spectral emissivity) of CFRP and GFRP test specimens is described.
Amongst various other NDT methods, within the EMRP-project
‘VITCEA’ active thermography is validated for testing of CFRP and
GFRP structures constructed for energy application. In this
contribution, the optical and thermal properties of CFRP and GFRP
reference defect artefact (RDA) and natural defects artefact (NDA)
test specimens are characterized. Different excitation techniques
and techniques for data analysis are compared for optimizing the
number of detected defects.