Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Dokumenttyp
- Zeitschriftenartikel (2)
- Vortrag (1)
Sprache
- Englisch (3) (entfernen)
Schlagworte
- Cold cracking (1)
- Component test (1)
- Component-like test (1)
- Creep-resistant steel (1)
- High-strength steels (1)
- Hydrogen (1)
- Minimum Waiting Time (1)
- Offshore steel grade (1)
- Post weld heat treatment (1)
- Repair-welding (1)
Organisationseinheit der BAM
Paper des Monats
- ja (1)
Eingeladener Vortrag
- nein (1)
Offshore wind turbines continuously increase in size and weight and demand adequate offshore foundations concepts like monopiles, tripods, or jackets. These components are typically constructed using submerged arc welding (SAW) with high-strength thick steel plates like the S420ML. During welding, the occurrence of delayed hydrogen-assisted cracking (HAC) must be anticipated. HAC is a critical combination of the local hydrogen concentration within a susceptible microstructure under certain mechanical load, i.e., the occurring (welding) residual stresses. The welding sequence of the thick-walled plates complicates the residual stress distribution due to the necessary repeated thermal cycling, i.e., welding seam/layer deposition to fill the joint. For that purpose, SAW with two-wire-technique was used to weld a specially designed and prototype-like mock-up of a real component with a thickness of 50 mm, filled with over 20 passes and a seam length of 1000 mm. Additional welded stiffeners simulated the effect of a high restraint, to achieve critical HAC conditions. The necessity of a minimum waiting time (MWT) before the NDT can be conducted (to exclude HAC) was critically verified by the application of ultrasonic testing of the welded joint at different time-steps of the NDT of up to 48 h after the completion welding. The residual stresses were determined by a robot XRD goniometer. Tensile residual stresses up to the yield limit are found both in the weld metal and in the heat-affected zone. Numerical modeling allowed the qualitative estimation of the hydrogen diffusion in the weld. No noticeable HAC occurrence was identified and confirms the high cracking resistance of the investigated material. Finally, the applicability of the MWT concept should be critically discussed.
Creep-resistant steels such as the 13CrMoV9-10, used in the construction of thick-walled pressure vessels, are most commonly submerged arc welded (SAW). These steels can develop stress relief cracks (SRC) if the mandatory post weld heat treatment (PWHT) is performed improperly. Current PWHT parameters, such as heating rate and holding time at a specific holding temperature, are based on both empirical experience and conventional free shrinking welding experiments to characterize the SRC-susceptibility of the weld. These cannot adequately depict the higher residual stresses caused by the structurally induced stiffness of the surrounding construction. This study discusses the development of a repeatable, precise, and time-efficient methodology to study the effects of different stress levels and heating rates on the SRC susceptibility of the coarse grain heat-affected zone (CGHAZ). For that purpose, samples were thermically treated to simulate a coarse grain heat-affected zone (CGHAZ) and subsequently exposed to representative levels of stress during the heating phase of a PWHT. The recorded stress and heating rate–dependent strains were mathematically analyzed via curve tracing/calculus to identify interdependent effects. This procedure facilitates the measurement of material characteristics such as carbide growth on grain boundaries at the µm-scale via an integrated value over the entire sample volume. The first and second derivatives show a slight, precipitate-dependent, increase in hardness of the sample, depending on the heating rate and applied stress. This new methodology generates an improved assessment of the SRC susceptibility of SAW microstructures of creep-resistant CrMoV steels.
Creep-resistant steels such as the 13CrMoV9-10 used in pressure vessel construction, with wall thicknesses of 250 mm and above, are most commonly submerged arc welded (SAW). The characteristic high heat input during the SAW-process introduces very high, localized residual stresses, which can lead to stress relief cracking (SRC) if the mandatory post weld heat treatment (PWHT) of the welding joint is performed improperly. Current PWHT parameters, such as heating rate and holding time at a specific holding temperature are mostly based on both empirically experience and conventional free shrinking welding experiments to characterize the SRC-susceptibility of the weld. These cannot adequately depict the higher residual stresses caused by the structurally induced stiffness of the surrounding construction and its constraint on the thermal shrinkage of the weld. Nor do they consider the resulting metallurgic effects such as the growth of precipitates during the PWHT and the resulting differences in hardness of the grain boundaries or the premature aging via a dissimilar precipitation behavior. The effect of the heating rate of the PWHT on the SRC susceptibility has to date not been adequately studied either.
This study discusses the development of a repeatable, precise and time efficient methodology to study the effects of different stress levels and heating rates on the SRC susceptibility of the coarse grain heat affected zone (CGHAZ). For that purpose, samples were thermically treated to simulate a CGHAZ and subsequently exposed to representative levels of stress during PWHTs with defined parameters. The recorded stress and heating rate dependent strains were mathematically analyzed via curve tracing/ calculus to identify interdependent effects. This procedure facilitates the measurement of material characteristics such as carbide growth on grain boundaries at the µm-scale via an integrated value over the entire sample volume. The first and second derivate show a slight, precipitate dependent, increase in hardness of the sample, depending on the heating rate and applied stress. Additionally, the formation and growth of special carbides is well known to have a volumetric effect, which together with the material characterization and this new methodology is believed to generate an improved assessment of the SRC susceptibility of SAW microstructures of creep-resistant CrMoV steels. The main advantage of the suggested methodology is the material independence. It thus provides, a comparative value between welds under ideal conditions in the lab and real-world scenarios by including an idealized, simulated component rigidity.