As opposed to reviewing results on experimental determination of residual stress by diffraction, this paper discusses the open issues when dealing with residual stress determination in additive manufactured parts, in particular those manufactured with laser powder bed fusion techniques. Three points are addressed in detail: (a) the proper determination of the strain-free reference d0, (b) the problem of the determination of the principal axes, and (c) the use of the correct diffraction elastic constants. It is shown that all methods to determine the strain-free reference d0 suffer from caveats, and care must be taken in evaluating the most suitable for the problem being tackled. In addition, it is shown that, in some systems, the principal axes do correspond to the geometrical axes of the specimen, but this needs to be systematically checked, especially in the case of uni- or bidirectional hatching strategies. Finally, the need to experimentally determine the proper diffraction elastic constants is underlined, especially in the case of strongly textured specimens, which again depends on the deposition strategy.
Laser based Powder Bed Fusion (L-PBF) is an additive manufacturing technique that has been continuously developed in the past years. It offers unparalleled design freedom and the resulting mechanical properties match, in some cases even exceed, those of materials processed by conventional manufacturing techniques. Nonetheless the process is prone to create Residual Stresses (RS) resulting from the sequential melting and solidification of the material. RS can reduce load bearing capacity and generate unwanted distortions thus diminishing the potential of L-PBF. This research activity aimed at characterizing the RS state in Inconel 718 L-PBF specimens using multiple diffraction methods. The microstructure as well as the surface and bulk residual stresses were investigated. The RS analysis was performed using X-ray, synchrotron and neutron diffraction methods to provide information at different depths within the specimen. The measurements were performed at the Bundesanstalt für Materialforschung und –prüfung (BAM), the EDDI beamline at BESSY II synchrotron and E3 line at BER II neutron reactor of the Helmholtz-Zentrum für Materialien und Energie (HZB) Berlin. The results revealed a depth depending RS state. The longitudinal and transverse stress components measured by X-ray and synchrotron at the surface agree well, exhibiting stress values around the yield strength of the material. In addition, synchrotron mapping showed gradients along the width and length of the sample for the longitudinal and transverse stress components. Lower RS values compared to surface RS were measured in the bulk of the material using neutron diffraction. The longitudinal stress component in the bulk was tensile and gradually decreased towards the edge of the specimen. The normal component however did not change significantly along the specimen dimensions and was of compressive nature. The transversal component was almost negligible. The results indicate that a stress re-distribution takes place during the deposition of the consecutive layers, which has to be further investigated.