Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Erscheinungsjahr
- 2023 (15) (entfernen)
Dokumenttyp
- Vortrag (12)
- Beitrag zu einem Tagungsband (2)
- Posterpräsentation (1)
Referierte Publikation
- nein (15)
Schlagworte
- Corrosion (5)
- Korrosion (5)
- Nichtrostender Stahl (4)
- Atmosphärische Korrosion (2)
- Copper (2)
- Deckschichtbildung (2)
- Electrochemistry (2)
- Geothermal (2)
- Grabenkorrosion (2)
- Korrosionsverhalten (2)
Organisationseinheit der BAM
- 7.6 Korrosion und Korrosionsschutz (15) (entfernen)
Eingeladener Vortrag
- nein (12)
In the late 1980s, a new type of corrosion appeared in drinking water installations where galvanized steel pipes failed forming a deep groove with no corrosion at the other surfaces. The reason was discussed quite fiercely between failure analysts and material suppliers. In the end the discussion lead to the solution: inductive welded pipes of a certain sulphur content were prone to selective corrosion. The history of the arguments is discussed using old communications between Wilhelm Schwenk and Wolfgang Stichel, who later published the results in a paper unfortunately only I german.
Thus the knowledge got lost and new cases based on the same material problems are observed in application of so-called C-Steel piping systems. Failure cases are shown.
In maritimer Exposition können Zinkbauteile Nutzungsdauern von 50 Jahren erreichen. Dabei werden Expositionen mit Spritzwasserbelastung durch Meerwasser nicht betrachtet. Normative Betrachtungen und Korrosionsprognosen basierend auf Einjahreswerten liefern hier grundlegend falsche Ergebnisse, da sie eine signifikant höhere Belastung der Atmosphäre mit SO2 voraussetzen.
Anhand der Wirksumme ist eine Abschätzung des legierungsabhängigen Einflusses auf den Korrosionswiderstand gegen chloridhaltige Medien möglich. Die berechneten Werte sind nur bei optimaler Wärmebehandlung und Verarbeitung zutreffend.
Die Anwendung einer einfachen Formel unter Berücksichtigung von Chrom, Molybdän und Stickstoff ist in der Regel völlig ausreichend. Das daraus abgeleitete Ranking von Werkstoffen ist für diverse technische Regelwerke und zur Unterstützung der Werkstoffauswahl geeignet.
Für die Warenein-/Ausgangskontrolle ist die alleinige Feststellung der Wirksumme unzureichend. Ergänzende Korrosionsuntersuchungen/-prüfungen zur Beschreibung des Korrosionswiderstandes sind dafür notwendig. Gleiches gilt für die Beurteilung von Schadensfällen. Hier sind Verarbeitung, Einsatzbedingungen und die Konstruktion von ausschlaggebender Bedeutung.
Der Vortrag stellt die Projektskizze zum Thema Gefügeveränderung bei trockener Schleifbearbeitung vor. Das Projekt hat das Ziel, das sich aus dem Trockenschleifverfahren ergebende chemische, mechanische und thermische Belastungskollektiv in der Kontaktzone zwischen Schleifmittel und Stahloberfläche in Abhängigkeit der verwendeten Schleifparameter genau zu beschreiben und die daraus resultierenden Oberflächen- und Gefügeveränderungen zu identifizieren und zu klassifizieren.
Neubewertung von metallenen Dach- und Fassadenmaterialien unter Dauerhaftigkeits- und Umweltaspekten
(2023)
Metallene Dach- und Fassadenmaterialien unterliegen nach ihrer Installation infolge von Korrosions- und Abschwemmprozessen einem Abtrag von Metallionen. Durch Regenereignisse gelangen diese in umliegende Gewässer und Böden. Die verwendeten metallenen Werkstoffe, wie z.B. Kupfer und Zink bilden zeitabhängig schützende Deckschichten aus, die die Dauerhaftigkeit der Werkstoffe gewährleisten und damit den Austrag von Metallionen signifikant begrenzen. Die Geschwindigkeit der Deckschichtbildung sowie die erreichte Schutzwirkung sind von verschiedenen Umwelteinflüssen und klimatischen Bedingungen abhängig. Diese haben sich in den letzten Jahrzehnten in Europa stark verändert, so dass es einer aktuellen Datenbasis für die Bewertung der Dauerhaftigkeit und der Umweltauswirkungen bedarf. Im Rahmen eines Forschungsvorhabens werden aktuell Feldstudien zur Ermittlung des Runoffs und der Schutzwirkung der gebildeten Deckschichten durchgeführt. Ergänzt werden diese durch Laborversuche mit künstlicher Beregnung.
Die Bedingungen für den schadensfreien Einsatz nichtrostender Stähle, nicht nur bei Schweißverbindungen, sind:
1) Die Passivschicht muss sich vollständig ausbilden können.
Voraussetzung dafür sind glatte, blanke, saubere Oberfläche, eine gleichmäßige Elementverteilung, wenig Ausscheidungen und Verunreinigungen. Eine mögliche Beeinflussung der Gefügeausbildung durch Warmumformung und durch die
schweißtechnische Verarbeitung sind zu beachten. Anlauffarben
müssen durch geeignete geeignete chemische bzw. mechanische Nachbehandlung entfernt werden.
2) Die Repassivierung von Defektstellen unter Einsatzbedingungen muss möglich sein, was durch geeignete Werkstoffauswahl und die Legierungszusammensetzung sicherzustellen ist. Unplanmäßige Betriebszustände oder Störungen können kritische Systemzustände hervorrufen, die die Repassivierung beeinträchtigen oder verhindern.
Eine geeignete Unterhaltsreinigung ist sicherzustellen.
Since geothermal wells are a feasible energy source to replace fossil fuel supply, many technologies have been developed to take advantage of geothermal energy. Nevertheless, service conditions in geothermal facilities are in many cases extreme in terms of corrosion due to the chemical composition of hydrothermal fluids and temperatures. Therefore, materials selection based on preliminary material qualification is essential to guarantee a secure and reliable operation of the facilities. During operation of a geothermal research facility in Groß Schönebeck copper and lead effects have been found downhole. Occurring mechanisms and measures to prevent precipitation or scaling needed to be investigated as well as potential influences of such precipitates on corrosion resistance of metallic materials used for equipment.
This contribution deals with the evaluation of the corrosion behavior of carbon steel and corrosion resistant alloys in copper and/or lead containing artificial geothermal water, simulating the conditions in the Northern German Basin.
The behavior of these materials in an artificial geothermal water obtained by electrochemical measurements and exposure tests are presented. While carbon steel exhibits precipitation and deposition, higher alloyed material shows different response to such species and a higher resistance in saline geothermal water.
Basing on these results the suitability of the investigated corrosion resistant alloy is given for use in such conditions, whereas carbon steel creates difficulties due to its susceptibility to Cu- and Pb-precipitation.
Significant Cu-deposition and precipitation only occurred in combination with carbon steel. High-alloyed materials prevent the disturbing Cu-agglomeration. Pb-deposition and precipitation only occurred in combination with carbon steel. No negative Pb-effect could be observed in combination with high-alloyed steels. High alloyed corrosion resistant alloys are suitable and shall be chosen for future design of the piping system, either in massive or in cladded form, to prevent unwanted interactions with brine components.
It is well known that cement manufacture, including CaCO3 calcination and clinker formation, is associated with substantial energy consumption and significant greenhouse gas emissions. Alkali-activated binders (AAB) and concretes made from them can significantly contribute to reducing CO2 emissions caused by the construction industry. However, to what extent and for how long concretes made from AAB can protect the steel in reinforced concrete components from corrosion is still unclear. Unlike PC-based binders, AABs are made by reacting alkaline solutions with solid precursors such as fly ash and ground granulated blast furnace slag (GGBFS). Therefore, steel reinforcement corrosion mechanisms in AAMs differ from PC-based binders. The present study aims to evaluate the corrosion behavior of steel rebar in alkali-activated materials (AAMs) synthetic pore solution with different chemical concentrations representing different GGBFS and Flay Ash based binders by performing electrochemical tests to measure the corrosion rate and corrosion potential of steel rebar. This information can be used to improve the design of AAMs in order to ensure a longer service life for these materials.
Im Vortrag werden die wesentlichen Grundlagen zum Verständnis der Korrosion metallener Werkstoffe in komprimierter Form vorgestellt. Der Schwerpunkt liegt auf der Betrachtung der atmosphärischen Korrosion und den sich daraus ergebenden Anforderungen an den Korrosionsschutz insbesondere für den Bereich Verpackungen.
Bedingung für den schadensfreien Einsatz nichtrostender Stähle ist die vollständige Ausbildung der Passivschicht. Voraussetzung dafür sind glatte, blanke, saubere Oberfläche, eine gleichmäßige Elementverteilung, wenig Ausscheidungen und Verunreinigungen. Eine mögliche Beeinflussung der Gefügeausbildung durch Warmumformung und durch die schweißtechnische Verarbeitung sind zu beachten. Anlauffarben müssen durch geeignete geeignete chemische bzw. mechanische Nachbehandlung entfernt werden. Eine ausreichende Nachbehandlung kann durch elektrochemische Prüfverfahren ebenso sichergestellt werden wie mittels der KorroPad-Prüfmethode. Letzte ist einfach und schnell in der Anwendung und ermöglicht es dem Verarbeiter, die Geeignetheit einer Nachbehandlung zu überprüfen.
In the maritime context of offshore operation, corrosion, in combination with the materials used, poses a particular challenge to ensure safe operation over long indefinite periods and to minimise susceptibility to failure. Until today, only a few corrosion protection systems have proven themselves for the interaction of efficiency, installation, and maintenance in the offshore sector. In addition, available corrosion test methods sometimes have major deficits about conclusions of the durability. Therefore, there is more research and development needed.
The flagship project H2Mare of the Federal Ministry of Education and Research aims to enable the production of green hydrogen and PtX products at high seas. Research is being driven forward by the partners in four individual projects, where BAM is involved in two.
In PtX-Wind, major kinds of corrosion attacks at offshore constructions are characterized and investigated, and suitable corrosion protection measures determined. In TransferWind, attention focusses on transferring scientific results into standardization.
This poster at the H2Mare Conference 2023 presents an overview of the investigation methods and contribution of the department “Corrosion and Corrosion Protection”.
Anhand der Wirksumme ist eine Abschätzung des legierungsabhängigen Einflusses auf den Korrosionswiderstand gegen chloridhaltige Medien möglich. Die berechneten Werte sind nur bei optimaler Wärmebehandlung und Verarbeitung zutreffend.
Die Anwendung einer einfachen Formel unter Berücksichtigung von Chrom, Molybdän und Stickstoff ist in der Regel völlig ausreichend. Das daraus abgeleitete Ranking von Werkstoffen ist für diverse technische Regelwerke und zur Unterstützung der Werkstoffauswahl geeignet.
Für die Warenein-/Ausgangskontrolle ist die alleinige Feststellung der Wirksumme unzureichend. Ergänzende Korrosionsuntersuchungen/-prüfungen zur Beschreibung des Korrosionswiderstandes sind dafür notwendig. Gleiches gilt für die Beurteilung von Schadensfällen. Hier sind Verarbeitung, Einsatzbedingungen und die Konstruktion von ausschlaggebender Bedeutung.
In the late 1980s, a new type of corrosion appeared in drinking water installations where galvanized steel pipes failed forming a deep groove with no corrosion at the other surfaces. The reason was discussed quite fiercely between failure analysts and material suppliers. In the end the discussion lead to the solution: inductive welded pipes of a certain sulphur content were prone to selective corrosion. The history of the arguments is discussed using old communications between Wilhelm Schwenk and Wolfgang Stichel, who later published the results in a paper unfortunately only I german.
Thus the knowledge got lost and new cases based on the same material problems are observed in application of so-called C-Steel piping systems. Failure cases are shown.