Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Erscheinungsjahr
- 2019 (164) (entfernen)
Dokumenttyp
- Vortrag (79)
- Zeitschriftenartikel (32)
- Beitrag zu einem Tagungsband (26)
- Sonstiges (14)
- Posterpräsentation (6)
- Buchkapitel (4)
- Forschungsbericht (2)
- Tagungsband (Herausgeberschaft für den kompletten Band) (1)
Sprache
- Englisch (92)
- Deutsch (70)
- Mehrsprachig (2)
Schlagworte
- Korrosion (32)
- Corrosion (22)
- Nichtrostender Stahl (10)
- Carbon steel (8)
- Deckschichtbildung (8)
- Gelartige Elektrolyte (7)
- KorroPad (6)
- Korrosionsschutz (6)
- AKR (5)
- Additive Fertigung (5)
Organisationseinheit der BAM
- 7 Bauwerkssicherheit (164) (entfernen)
Eingeladener Vortrag
- nein (79)
The impact of polyaniline in phosphorus flame retardant ethylene-propylene-diene-rubber (EPDM)
(2019)
Usually elastomers are loaded with high amounts of flame retardants to fulfill fire safety requirements. In this study the potential char precursor polyaniline (PANI) and the established fire retardant pentaerythritol (PER) were implemented in ethylene-propylene-diene monomer rubber (EPDM). PANI and PER were used in low loadings (7 phr) and combined with two phosphorous flame retardants, Ammonium polyphosphate (APP) and a piperazine-pyrophosphate/phosphoric acid compound (FP), to boost their performance. A comprehensive study is presented, explaining the impact of PANI on curing and mechanical properties, including compensation for the plasticizer-like effect of APP in EPDM, and improved flame retardancy. In the cone calorimeter test, the combination of EPDM/FP/PANI reduced the effective heat of combustion by 20%. All nine EPDM rubber compounds were investigated with the LOI and UL 94 tests, cone calorimeter, FMVSS 302 and glow wire testing to quantify fire performance. The PANI containing EPDM rubbers, EPDM/APP/PANI and EPDM/FP/PANI outperformed the corresponding PER containing, EPDM/APP/PER and EPDM/FP/PER rubbers in various tests. Moreover, the study investigated the impact of PANI and PER on the mode of action of the phosphorus species and showed that the addition of PANI increased the amount of phosphorus in the condensed phase. To receive a broader understanding of the flame retardant mode of action of PANI in combination with APP and FP, calculations were carried out to estimate the impact of PANI on the protective layer effect.
Alkali-silica reaction (ASR) is a serious Problem concerning the deterioration of concrete. This leads to significant maintenance and reconstruction costs for concrete infrastructures all over the world. The geographical regions, which play a major role in concrete deterioration, are for example coastal Areas or in general, areas with a high air humidity/salinity due to closeness of rivers or lakes.
These exemplary results show, the application of Raman spectroscopy establishes a valuable approach for characterizing the chemical and structural composition of ASR-products. The results prove the potential to trace the kind of reaction products, developing in dependence on the aggregate and to follow up its local alteration from origin of the gel.
Superglassy polymers with a large fractional free volume have emerged as novel materials with a broad range of applications, especially in the field of membrane separations. Highly permeable addition-type substituted polynorbornenes with high thermal resistance and chemical stability are among the most promising materials. The major obstacle for extending the practical membrane application is their strong tendency to physical aging, leading to a partial decline in their superior transport performance over time. In the present study, broadband dielectric spectroscopy with complementary X-ray scattering techniques were employed to reveal changes in microporous structure, molecular mobility, and conductivity by systematic
comparison of two polynorbornenes with different numbers of trimethylsilyl side groups. Their response upon heating (aging) was compared in terms of structure, dynamics, and charge transport behavior. Furthermore, a detailed analysis of the observed
Maxwell−Wagner−Sillars polarization at internal interfaces provides unique information about the microporous structure in the
solid films. The knowledge obtained from the experiments will guide and unlock potential in synthesizing addition-type polynorbornenes with versatile properties.
Polymers of Intrinsic Microporosity (PIMs) of high performance have developed as materials with a wide application range in gas separation and other energy-related fields. Further optimization and long-term behavior of devices with PIMs require an understanding of the structure-property relationships including physical aging. In this context the glass transi-tion plays a central role, but with conventional thermal analysis a glass transition is usually not detectable for PIMs be-fore their thermal decomposition. Fast scanning calorimetry provides evidence of the glass transition for a series of PIMs, as the time scales responsible for thermal degradation and for the glass transition are decoupled by employing ultrafast heating rates of tens of thousands K s-1. The investigated PIMs were chosen considering the chain rigidity. The estimated glass transition temperatures follow the order of the rigidity of the backbone of the PIMs.
Polymeric membranes represent a low-cost, energy efficient solution for gas separation. Recently polymers of intrinsic microporosity (PIMs) have emerged as prestigious membrane materials featuring a large concentration of pores smaller than 1 nm, a BET surface area larger than 700 m2/g and high gas permeability and selectivity. Unusual chain structure combining rigid segments with sites of contortion gives rise to the intrinsic microporosity. However, this novel class of glassy polymers are prone to pronounced physical aging. The initial microporous structures approach a denser state via local small scale fluctuataions, leading to a dramatic reduction in the gas permeabilities. For the first time, dielectric relaxation spectroscopy with state-of-the-art high-resolution analyzers was employed to investigate three representative PIMs with a systematic change in chain rigidity: PIM-EA-TB 〉 PIM-1 〉 PIM-MDPH-TB. The molecular mobility, the charge transport and their response upon heating (aging) in the polymers were measured in a broad temperature range through isothermal frequency scans during different heating / cooling cycles. Multiple dielectric processes following Arrhenius behavior were observed for the investigated polymers. Local fluctuations, Maxwell-Wagner-Sillars (MWS) polarization and structural relaxation phenomena were discussed and attempted to be correlated with the structural features of PIMs. Moreover, all PIMs showed conductivity in the glassy state. The significant increase in the conductivity with increasing temperature far below the glass transition temperature of PIMs is explained in terms of the loosely packed microporous structure and the formation of local intermolecular agglomerates due to interaction of π-electrons in aromatic moieties of the polymer backbone.
High performance polymers of intrinsic microporosity (PIMs) have emerged as novel materials with broad applications from gas separation to electronic devices. Sufficiently rigid, even contorted polymer chains show only limited molecular mobility, therefore undergo inefficient packing and give rise to intrinsic microporosity with pore size generally smaller than 1 nm and BET surface areas larger than 700 m2/g. Further performance optimization and long-term stability of devices incorporating PIMs rely on our understanding of structure-processing-property relationships and physical aging, in which glass transition plays a key role. Up to now no glass transition temperature (Tg) of PIMs could be detected with conventional thermal analysis techniques before degradation. Decoupling the time scales responsible for the glass transition and the thermal decomposition is a reliable strategy to overcome this. This was achieved by employing fast scanning calorimetry (FSC) based on a chip sensor, which is capable to heat and cool a small sample (ng-range) with ultrafast rates of several ten thousand K/s. FSC provides definitive evidence of glass transition of a series of PIMs with a special consideration on the chain rigidity. The determined glass transition temperature of these PIMs follows the order of the rigidity of their backbone structures. FSC provides the first clear-cut experimental evidence of the glass transition of PIM-EA-TB with a Tg of 663 K, PIM-1 of 644 K and PIM-DMDPH-TB of 630 K at a heating rate of 1Χ104 K/s. Local fluctuations are featured in glass transition of highly rigid PIMs. As conformational changes are prevented by the backbone rigidity, the glass transition must rather be assigned to local small scale fluctuations.
Für Bauteile (Komponenten) von Versorgungsanlagen für flüssige Brenn- und Kraftstoffe muss die Beständigkeit der metallenen Werkstoffe und Polymere nachgewiesen werden. Im Anwendungsfall von Heizöl mit 20 % biogenen Anteilen in Form von Rapsölfettsäuremethylester (FAME, Biodiesel) ist es für eine konservative Beurteilung des Korrosionssystems Werkstoff/Medium/Umgebung wichtig, die Alterungseffekte des Mediums einzubeziehen.
Entwicklung eines Prüfverfahrens für die Untersuchung der Beständigkeit von metallenen Werkstoffen und Polymeren in Heizöl und Heizöl-FAME-Blends, das für eine Vorauswahl der Werkstoffe und zum Nachweis der Beständigkeit im Hinblick auf die bauaufsichtlichen Zulassungsverfahren geeignet ist. Ein Schwerpunkt wird bei den metallenen Werkstoffen auf der Erprobung von Messmethoden liegen, mit denen sich in kurzer Versuchszeit ein Korrosionsangriff detektieren lässt.
Metallene Werkstoffe:
Weder örtliche Korrosion noch erhöhte Flächenkorrosion (Korrosionsrate:< 0,1 m/Jahr) sind bei den bisher geprüften Werkstoffen: Aluminium,
C-Stahl 1.0037, austenitischer CrNi-Stahl 1.4301, Kupfer und Messing in Heizöl und B20 (Heizöl mit 20% Biodiesel) aufgetreten. Diese Werkstoffe sind in den Prüfmedien Heizöl und B20 als beständig zu bewerten.
Es wurde keine signifikante Veränderung des pH-Wertes der Prüfmedien gemessen.
Polymere:
Massebestimmung:
Die Prüfkörper der Elastomere ACM, HNBR und PUR sowie in geringerem Maße PE neigten zur Quellung in Heizöl und B20 nach 42 d und 84 d Auslagerung; für PA 6, POM und PVC wurde keine Masseänderung gemessen. Die Masseänderung der Prüfkörper in Heizöl und B20 ist mit Ausnahme von PUR vergleichbar. Bei PE traten Verfärbungen durch die Brennstoffe auf.
Zugeigenschaften:
ACM, HNBR, PE und PVC sind in Heizöl und B20 beständig, da die Änderung der Zugfestigkeit und der Reißdehnung < 15 % beträgt. PA und POM sind bedingt beständig, da die Änderung der Zugfestigkeit und der Reißdehnung < 30% beträgt.
Compatibility of polymeric materials with heating oil/biodiesel blends at different temperatures
(2019)
Materials compatibility is a major concern whenever the fuel composition is changed. The question arises of whether polymeric materials are resistant to heating oil with admixtures of 10 % biodiesel (B10) and 20 % biodiesel (B20).
The polarity of biodiesel increases its solvency and facilitates permeation and extrac-tion. Solvation, swelling and/or extraction lead to changes in the physical properties and chemical changes of polymeric materials.
The objective of this research was to determine the resistance of frequently used sealing materials such as FKM, EPDM, CR, CSM, NBR, IIR, VMQ, FVMQ, PA and PUR in up to four-year aged B10 for 84 days at 20 °C, 40 °C and 70 °C.
The polymeric materials: ACM, FKM, HNBR, PA, PE; POM, PUR and PVC were ex-posed to B20 for 84 days at 40°C and 70°C in another research project.
Mass, tensile strength, breaking elongation and Shore hardness A (D) of the test specimens were determined before and after the exposure for 84 (42) days in the heating oil blends B10 and B20.
There is not determined a threshold for the reduction in tensile properties and Shore hardness in the international standards. Therefore, a threshold of 15 % was deter-mined for the evaluation of the compatibility.
Measurements of the variations in mass, tensile properties and Shore hardness after exposure of the polymers in non-aged and aged heating oil B10 showed clearly that FKM, FVMQ and PA were the most resistant materials in B10. The elastomers CR, CSM, EPDM, IIR, NBR and VMQ were generally not resistant to B10. Damage to the materials increased with higher test temperatures and the age of B10.
FKM, POM and PVC showed high compatibility in B20 at 40°C and 70 °C. ACM, HNBR and PA were evaluated as resistant in B20 at 40 °C but not at 70°C.
Für Bauteile (Komponenten) von Versorgungsanlagen für flüssige Brenn- und Kraftstoffe muss die Beständigkeit der metallenen Werkstoffe und Polymere nachgewiesen werden. Im Anwendungsfall von Heizöl mit 20 % biogenen Anteilen in Form von Rapsölfettsäuremethylester (FAME, Biodiesel) ist es für eine konservative Beurteilung des Korrosionssystems Werkstoff/Medium/Umgebung wichtig, die Alterungseffekte des Mediums einzubeziehen.
Entwicklung eines Prüfverfahrens für die Untersuchung der Beständigkeit von metallenen Werkstoffen und Polymeren in Heizöl und Heizöl-FAME-Blends, das für eine Vorauswahl der Werkstoffe und zum Nachweis der Beständigkeit im Hinblick auf die bauaufsichtlichen Zulassungsverfahren geeignet ist. Ein Schwerpunkt wird bei den metallenen Werkstoffen auf der Erprobung von Messmethoden liegen, mit denen sich in kurzer Versuchszeit ein Korrosionsangriff detektieren lässt.
Die untersuchten Werkstoffe Aluminium, Stahl 1.0037, 1.4301, Kupfer, Messing (CuZn40Pb) und Zink (ZP0410) sind in B0, B20, B100 und in 6 Jahre altem B100 beständig.
Auch in einem Jahr alten B20 und in einem Jahr alten B100 sind die Werkstoffe beständig.
Bei Kupfer blieb die Korrosionsrate in der Flüssigphase sowohl in B20 (0 μ m/ a) als auch in B100 (4 μ m/ a) nach einem Jahr unverändert. Für das 6 Jahre alte B100 stieg die Korrosionsrate des Kupfers an (16 μ m/a). Im Gegensatz dazu sank bei Messing die Korrosionsrate in der Flüssigphase mit dem Alter des Brennstoffs, nach einem Jahr für B20 von 4 μ m/ a auf 1 μ m/a und für B100 von 36 μ m/ a auf 6 μ m/ a, im 6 Jahre alten B100 lag die Korrosionsrate des Messings bei 0 μ m/ a.
In 8 Jahre altem B10 trat bei Zink in der Flüssigphase Flächenkorrosion auf, es ist in dem Medium demnach nicht beständig. Messing zeigte örtliche Korrosion in der Gasphase, es ist folglich unbeständig und für den Einsatz in stark gealterten B10 nicht geeignet.
Aluminium, 1.0037, 1.4301 und Kupfer sind in dem 8 Jahre alten B10 beständig.
Die Änderung der Zugfestigkeit und der Reißdehnung von ACM, HNBR und FKM in Heizöl, B20 und gealterten B10 beträgt < 15 %. Diese Werkstoffe sind in Heizöl, B20 und in gealterten B10 unter Berücksichtigung des von der BAM zur Beurteilung der Beständigkeit festgelegten Grenzwertes von 15 % bei 40 °C als beständig zu bewerten.
PUR ist bei 40 °C nicht beständig in B20 und in gealtertem B10. Bei 70 °C ist HNBR nicht in B20 beständig aufgrund der Verringerung der Zugfestigkeit (40 %) und der Reißdehnung (50 %). FKM ist bei 70 °C in Heizöl und in B20 beständig.
Biodiesel is subject to degradation processes like oil and grease. The oxidative degradation products of vegetable oil esters in biodiesel particularly lead to enhanced sedimentation in blended fuels.
The polarity of biodiesel increases its solvency and facilitates permeation and extraction. Solvation, swelling and/or extraction lead to changes in the physical properties and chemical changes of polymeric materials. It also accelerates the degradation (hydrolysis and oxidation) of these materials with the loss of additives and stabilizers.
The objective of this research was to determine the resistance of frequently used polymeric materials such as ACM, EPDM, FKM, FVMQ, CR, CSM, IIR, HNBR, NBR, PA, PE; POM, PUR, PVC and VMQ in biodiesel and heating oil with 10 %/20 % biodiesel (B10/B20) at 40°C and 70°C.
Mass, tensile strength and breaking elongation of the test specimens were determined before and after the exposure for 84 days in the biodiesel heating oil blends. The visual examination of some elastomer test specimens clearly showed the great volume increase until break or partial dissolution. Shore hardness A and D were determined before and after exposure of the test specimens in the biofuels for 42 days.
The elastomers CR, CSM, EPDM, IIR, NBR and VMQ were generally not resistant to biodiesel and B10 at 40°C and 70°C. FKM, ACM, HNBR, PA, PE, POM, and PVC showed high compatibility in B10/B20 at 40°C. A lower compatibility was determined for ACM in biodiesel. ACM and HNBR were not resistant in B20 at 70°C.
Biodiesel is viewed as a major source of energy. In areas such as the European Union, where 80 % of the oil-based fuel is imported, there is also the desire to reduce dependence on external oil supplies.
Materials compatibility is a major concern whenever the fuel composition is changed. The question arises of whether polymeric materials are resistant to heating oil with 20 % biodiesel (B20) in comparison to pure heating oil.
The polarity of biodiesel increases its solvency and facilitates permeation and extraction. Solvation, swelling and/or extraction lead to changes in the physical properties. Extraction alters the fuel chemistry. These chemical changes could also accelerate the degradation (hydrolysis and oxidation) of the polymeric material with the loss of additives and stabilizers.
The objective of this research was to determine the resistance of frequently used materials for components in middle distillate facilities such as ACM, FKM, HNBR, PA, PE, POM, PUR and PVC in heating oil and heating oil blend B20 for 84 days at 40 °C, and FKM, HNBR, PA, POM, PUR and PVC at 70 °C.
Mass, tensile strength, breaking elongation and Shore hardness A (D) of the test specimens were determined before and after exposure for 84 (42) days in the test fuels under static conditions.
For the investigations under compressed conditions, the mass and the compression set of FKM test specimens were determined before and after exposure for 3, 7, 14, 28, 56 and 90 days in B20 at 40 °C and 70 °C according to ISO 815-1 “Rubber, vul-canized or thermoplastic - determination of compression set – Part 1: At ambient or elevated temperatures”.
There is not determined a threshold for the reduction in tensile properties and Shore hardness in the international standards. Therefore, a threshold of 15 % was determined for the evaluation of the compatibility.
The change of tensile strength and breaking elongation of test specimens made of ACM, FKM, HNBR, PA, PE, POM, PUR and PVC exposed to heating oil and the blend B20 was less than 15 % at 40 °C. A maximum reduction in Shore hardness A of 14 % was determined for ACM at 40 °C and for HNBR of 15 % at 70 °C.
It can be concluded that ACM, FKM, HNBR, PA, PE, POM, PVC and PUR were resistant in B20 at 40°C. FKM, PA, POM and PVC were evaluated as resistant in heat-ing oil and B20 at 70 °C, HNBR and PUR were not resistant in these fuels at 70°C.
Based on the mass increase and compression set values of FKM test specimens it can be stated that FKM is resistant in B20 under compressed conditions at 40 °C and 70 °C.
Verstärkt auftretende Schäden in Betonfahrbahndecken des Bundesfernstraßennetzes, die mit einer Alkali-Kieselsäure-Reaktion (AKR) in Verbindung gebracht werden, haben zu einer massiven Verschärfung der Prüfvorschriften zur Bewertung der Alkaliempfindlichkeit von Ge-steinskörnungen geführt. Die damit verbundene Einschränkung potenziell für den Straßenbau einsetzbarer Gesteinskörnungen ruft eine verstärkte Ressourcenknappheit und ein erhöhtes Transport- und damit einhergehendes Kostenaufkommen hervor. Vor diesem Hintergrund wird nach neuartigen AKR-Vermeidungsstrategien gesucht, die auch eine Verwendung grenzwertig alkaliempfindlich eingestufter Gesteinskörnungen erlaubt. Einen möglichen Lösungsansatz stellt in diesem Kontext die Innenhydrophobierung des Fahrbahndeckenbetons dar. Es soll so durch die Behinderung des Feuchte- und Tausalzeintrags in den Beton der AKR-Schädigungs-prozess signifikant vermindert werden. Für die Bewertung der Leistungsfähigkeit der Innen-hydrophobierung zur Vermeidung einer schädigenden AKR in Betonfahrbahndecken wird zur-zeit im Auftrage der BASt an der BAM ein Forschungsvorhaben bearbeitet. Im Rahmen dieses Beitrags werden erste ausgewählte Ergebnisse dieses Forschungsvorhabens vorgestellt. So wird exemplarisch an einem Oberbeton (0/8) mit einer alkaliempfindlichen Gesteinskörnung der Einfluss eines Hydrophobierungsmittels auf die Frisch- und Festbetoneigenschaften ganz-heitlich aufgezeigt und bewertet. Bei Letzteren stehen zunächst die mechanischen und hygri-schen Parameter sowie der Frost-Tausalzwiderstand im Vordergrund. In einem weiteren Schritt wird der Einfluss der Innenhydrophobierung auf die schädigende AKR mittels verschie-denartiger AKR-Performanceprüfungen beleuchtet.
AKR an Betonfahrbahndecken - ausgewählte Einflussgrößen und neuartige AKR-Vermeidungsstrategie
(2019)
In den letzten Jahren sind im deutschen Bundesautobahnnetz vermehrt Schäden an vor 2005 hergestellten Betonfahrbahndecken aufgetreten, die mit einer Alkali-Kieselsäure-Reaktion(AKR) in Verbindung gebracht werden. Vor diesem Hintergrund werden in diesem Beitrag zunächst die Voraussetzungen und ausgewählte Einflussgrößen für eine schädigende AKR aufgezeigt.
Besondere Aufmerksamkeit wird dabei der Rolle des Tausalzeintrags durch den Winterdienst bei Betonfahrbahndecken geschenkt. So wird mit Löseversuchen in 1 M KOH-Lösung zweier Gesteinskörnungen bei 80 °C gezeigt, dass mit zunehmender NaCI-Zugabe die Löslichkeit von SiÖ2 zunimmt und die von AI2O3 eine Verminderung erfährt. Basierend auf dem so exemplarisch erbrachten Nachweis für die Verstärkung der schädigenden AKR durch das Tausalz wird die Notwendigkeit und Richtigkeit der Durchführung von AKR-Betonversuchen mit Alkalizufuhr im ARS 04/2013 zur zukünftigen Vermeidung von AKR-Schäden an Betonfahrbahndecken im Rahmen von Neubau- und Erneuerungsmaßnahmen im Bundesfernstraßennetz belegt. Zusätzlich durchgeführte WS-Grundprüfungen nach dem ARS 04/2013 mit den beiden Gesteinskörnungen der Löse versuche veranschaulichen, dass die nach der Alkali-Richtlinie des DAfStb als unbedenklich eingestuften Gesteinskörnungen bei den Betonversuchen mit Alkalizufuhr durchaus als alkaliempfindlich bewertet werden können. Dies wiederum führt zu einer Verminderung der für den Betonstraßenbau verfügbaren Gesteinskörnungen.
Vor diesem Hintergrund wird nach neuartigen AKR-Vermeidungsstrategien gesucht, die auch eine Verwendung der als grenzwertig alkaliempfindlich eingestuften Gesteinskörnungen erlaubt.
Einen möglichen Lösungsansatz stellt in diesem Kontext die Innenhydrophobierung des Fahrbahndeckenbetons dar. Es soll so durch die Behinderung des Feuchte- und Tausalzeintrags in den Beton der AKR-Schädigungsprozess signifikant vermindert werden. Für die Bewertung der Leistungsfähigkeit der Innenhydrophobierung zur Vermeidung bzw. Verminderung einer schädigenden AKR in Betonfahrbahndecken wird zurzeit im Aufträge der BASt an der BAM ein Forschungsvorhaben bearbeitet. Im Rahmen dieses Beitrags werden erste Ergebnisse dieses Projekts vorgestellt. So wird exemplarisch an einem Oberbeton (D > 8)/Unterbeton und einem Oberbeton 0/8 mit einer alkaliempfindlichen Gesteinskörnung der Einfluss zweier Hydrophobierungsmittel auf die Frisch- und Festbetoneigenschaften ganzheitlich aufgezeigt und bewertet. Bei Letzteren stehen zunächst die mechanischen und hygrischen Parameter sowie der Frost-Tausalzwiderstand im Vordergrund. In einem weiteren Schritt wird der Einfluss beider Hydrophobierungsmittel auf die schädigende AKR mittels AKR-Betonversuchen mit Alkalizufuhr beleuchtet. Dabei gelangen ergänzend zur Beurteilung des Tausalzeintrags die Laser-Induced Breakdown Spectroscopy (LIBS) und zur Bewertung der Ausprägung der AKR und sekundären Ettringitbildung (SEB) die Dünnschliffmikroskopie zum Einsatz.
AKR an Betonfahrbahndecken - ausgewählte Einflussgrößen und neuartige AKR-Vermeidungsstrategie
(2019)
In den letzten Jahren sind im deutschen Bundesautobahnnetz vermehrt Schäden an vor 2005 hergestellten Betonfahrbahndecken aufgetreten, die mit einer Alkali-Kieselsäure-Reaktion (AKR) in Verbindung gebracht werden. Vor diesem Hintergrund werden in diesem Beitrag zunächst die Voraussetzungen und ausgewählte Einflussgrößen für eine schädigende AKR aufgezeigt.
Besondere Aufmerksamkeit wird dabei der Rolle des Tausalzeintrags durch den Winterdienst bei Betonfahrbahndecken geschenkt. So wird mit Löseversuchen in 1 M KOH-Lösung zweier Gesteinskörnungen bei 80 °C gezeigt, dass mit zunehmender NaCI-Zugabe die Löslichkeit von SiÖ2 zunimmt und die von AI2O3 eine Verminderung erfährt. Basierend auf dem so exemplarisch erbrachten Nachweis für die Verstärkung der schädigenden AKR durch das Tausalz wird die Notwendigkeit und Richtigkeit der Durchführung von AKR-Betonversuchen mit Alkalizufuhr im ARS 04/2013 zur zukünftigen Vermeidung von AKR-Schäden an Betonfahrbahndecken im Rahmen von Neubau- und Erneuerungsmaßnahmen im Bundesfernstraßennetz belegt. Zusätzlich durchgeführte WS-Grundprüfungen nach dem ARS 04/2013 mit den beiden Gesteinskörnungen der Löse versuche veranschaulichen, dass die nach der Alkali-
Richtlinie des DAfStb als unbedenklich eingestuften Gesteinskörnungen bei den Betonversuchen mit Alkalizufuhr durchaus als alkaliempfindlich bewertet werden können. Dies wiederum führt zu einer Verminderung der für den Betonstraßenbau verfügbaren Gesteinskörnungen.
Vor diesem Hintergrund wird nach neuartigen AKR-Vermeidungsstrategien gesucht, die auch eine Verwendung der als grenzwertig alkaliempfindlich eingestuften Gesteinskörnungen erlaubt.
Einen möglichen Lösungsansatz stellt in diesem Kontext die Innenhydrophobierung des Fahrbahndeckenbetons dar. Es soll so durch die Behinderung des Feuchte- und Tausalzeintrags in den Beton der AKR-Schädigungsprozess signifikant vermindert werden. Für die Bewertung der Leistungsfähigkeit der Innenhydrophobierung zur Vermeidung bzw. Verminderung einer schädigenden AKR in Betonfahrbahndecken wird zurzeit im Aufträge der BASt an der BAM ein Forschungsvorhaben bearbeitet. Im Rahmen dieses Beitrags werden erste Ergebnisse dieses Projekts vorgestellt. So wird exemplarisch an einem Oberbeton (D > 8)/Unterbeton und einem Oberbeton 0/8 mit einer alkaliempfindlichen Gesteinskörnung der Einfluss zweier Hydrophobierungsmittel auf die Frisch- und Festbetoneigenschaften ganzheitlich aufgezeigt und bewertet. Bei Letzteren stehen zunächst die mechanischen und hygrischen Parameter sowie der Frost-Tausalzwiderstand im Vordergrund. In einem weiteren Schritt wird der Einfluss beider Hydrophobierungsmittel auf die schädigende AKR mittels AKR-Betonversuchen mit Alkalizufuhr beleuchtet. Dabei gelangen ergänzend zur Beurteilung des Tausalzeintrags die Laser-Induced Breakdown Spectroscopy (LIBS) und zur Bewertung der Ausprägung der AKR und sekundären Ettringitbildung (SEB) die Dünnschliffmikroskopie zum Einsatz.
AKR an Betonfahrbahndecken – ausgewählte Einflussgrößen und neuartige AKR-Vermeidungsstrategie
(2019)
In den letzten Jahren sind im deutschen Bundesautobahnnetz vermehrt Schäden an vor 2005 hergestellten Betonfahrbahndecken aufgetreten, die mit einer Alkali-Kieselsäure-Reaktion (AKR) in Verbindung gebracht werden. Vor diesem Hintergrund werden in diesem Beitrag zunächst die Voraussetzungen und ausgewählte Einflussgrößen für eine schädigende AKR aufgezeigt. Besondere Aufmerksamkeit wird dabei der Rolle des Tausalzeintrags durch den Winterdienst bei Betonfahrbahndecken geschenkt. So wird mit Löseversuchen in 1 M KOH-Lösung zweier Gesteinskörnungen bei 80 °C gezeigt, dass mit zunehmender NaCl-Zugabe die Löslichkeit von SiO2 zunimmt und die von Al2O3 eine Verminderung erfährt. Basierend auf dem so exemplarisch erbrachten Nachweis für die Verstärkung der schädigenden AKR durch das Tausalz wird die Notwendigkeit und Richtigkeit der Durchführung von AKR-Betonversuchen mit Alkalizufuhr im ARS 04/2013 zur zukünftigen Vermeidung von AKR-Schäden an Betonfahrbahndecken im Rahmen von Neubau- und Erneuerungsmaßnahmen im Bundesfernstraßennetz belegt. Zusätzlich durchgeführte WS-Grundprüfungen nach dem ARS 04/2013 mit den beiden Gesteinskörnungen der Löseversuche veranschaulichen, dass die nach der Alkali-Richtlinie des DAfStb als unbedenklich eingestuften Gesteinskörnungen bei den Betonversuchen mit Alkalizufuhr durchaus als alkaliempfindlich bewertet werden können. Dies wiederum führt zu einer Verminderung der für den Betonstraßenbau verfügba-ren Gesteinskörnungen. Vor diesem Hintergrund wird nach neuartigen AKR-Vermeidungsstrategien gesucht, die auch eine Verwendung der als grenzwertig alkaliemp-findlich eingestuften Gesteinskörnungen erlaubt. Einen möglichen Lösungsansatz stellt in diesem Kontext die Innenhydrophobierung des Fahrbahndeckenbetons dar. Es soll so durch die Behinderung des Feuchte- und Tausalzeintrags in den Beton der AKR-Schädigungsprozess signifikant vermindert werden. Für die Bewertung der Leistungsfähigkeit der Innenhydrophobierung zur Vermeidung bzw. Verminderung einer schädigenden AKR in Betonfahrbahndecken wird zurzeit im Auftrage der BASt an der BAM ein Forschungsvorha-ben bearbeitet. Im Rahmen dieses Beitrags werden erste Ergebnisse dieses Projekts vorge-stellt. So wird exemplarisch an einem Oberbeton (D > 8)/Unterbeton und einem Oberbeton 0/8 mit einer alkaliempfindlichen Gesteinskörnung der Einfluss zweier Hydrophobierungsmit-tel auf die Frisch- und Festbetoneigenschaften ganzheitlich aufgezeigt und bewertet. Bei Letz-teren stehen zunächst die mechanischen und hygrischen Parameter sowie der Frost-Tausalzwiderstand im Vordergrund. In einem weiteren Schritt wird der Einfluss beider Hydro-phobierungsmittel auf die schädigende AKR mittels AKR-Betonversuchen mit Alkalizufuhr beleuchtet. Dabei gelangen ergänzend zur Beurteilung des Tausalzeintrags die Laser-Induced Breakdown Spectroscopy (LIBS) und zur Bewertung der Ausprägung der AKR und sekundä-ren Ettringitbildung (SEB) die Dünnschliffmikroskopie zum Einsatz.
Verstärkt auftretende Schäden in Betonfahrbahndecken des Bundesfernstraßennetzes, die mit einer Alkali-Kieselsäure-Reaktion (AKR) in Verbindung gebracht werden, haben zu einer massiven Verschärfung der Prüfvorschriften zur Bewertung der Alkaliempfindlichkeit von Ge-steinskörnungen geführt. Die damit verbundene Einschränkung potenziell für den Straßenbau einsetzbarer Gesteinskörnungen ruft eine verstärkte Ressourcenknappheit und ein erhöhtes Transport- und damit einhergehendes Kostenaufkommen hervor. Vor diesem Hintergrund wird nach neuartigen AKR-Vermeidungsstrategien gesucht, die auch eine Verwendung grenzwertig alkaliempfindlich eingestufter Gesteinskörnungen erlaubt. Einen möglichen Lösungsansatz stellt in diesem Kontext die Innenhydrophobierung des Fahrbahndeckenbetons dar. Es soll so durch die Behinderung des Feuchte- und Tausalzeintrags in den Beton der AKR-Schädigungs-prozess signifikant vermindert werden. Für die Bewertung der Leistungsfähigkeit der Innen-hydrophobierung zur Vermeidung einer schädigenden AKR in Betonfahrbahndecken wird zur-zeit im Auftrage der BASt an der BAM ein Forschungsvorhaben bearbeitet. Im Rahmen dieses Beitrags werden erste ausgewählte Ergebnisse dieses Forschungsvorhabens vorgestellt. So wird exemplarisch an einem Oberbeton (0/8) mit einer alkaliempfindlichen Gesteinskörnung der Einfluss eines Hydrophobierungsmittels auf die Frisch- und Festbetoneigenschaften ganzheitlich aufgezeigt und bewertet. Bei Letzteren stehen zunächst die mechanischen und hygrischen Parameter sowie der Frost-Tausalzwiderstand im Vordergrund. In einem weiteren Schritt wird der Einfluss der Innenhydrophobierung auf die schädigende AKR mittels verschiedenartiger AKR-Performanceprüfungen beleuchtet.
Recent facade fires worldwide have driven change in regulations for façade fire safety in different parts of the world. The Grenfell Tower fire 2017 in London triggered a thorough investigation of many aspects of the fire. One investigation was about the UK building regulations from Dame Judith Hackett. This investigation compares the UK with the situation other parts of the world. Key findings of the review of building regulations by Judith Hackett are:
Reliable performance of structural sealant glazing (SSG) systems is necessary to utilise advantages of SSG in glass facades. Conventional durability assessment of structural sealant joints is based on separated weathering tests and empirical fatigue testing. This work presents a new test methodology for performance assessment of SSGjoints at simultaneous weathering and two-dimensional mechanical loading. The climatic and mechanical load function were derived from common loading scenarios according to a worst case approach. A System test specimen, resembling a common SSG-joint, was exposed to 24 h of combined loading in a custom-designed test facility. From the recorded mechanical system response, characteristic parameters were evaluated to assess the performance of the system at varying climatic and mechanical conditions. These experimental results reveal effects of ambient conditions, previous loading and deformation Amplitude peaks on the system response. The proposed test methodology opens up for new performance-related approaches in durability testing.
Ziel des Projektes ist die Qualifizierung von Duplexstählen in Tunnelbauwerken um die Einsatzmöglichkeiten alternativer nichtrostender Stähle zu den bislang gebräuchlichen rostfreien Edelstählen 1.4404 und 1.4571 zu eruieren. Da Duplexstähle im Vergleich zu austenitischen Stählen über eine doppelt so hohe Festigkeit verfügen, können Bauteile schlanker konstruiert werden, wodurch Material eingespart werden kann. Neben der Wirtschaftlichkeit muss die Dauerhaftigkeit untersucht werden. Dazu wurden speziell konzipierte Wand- und Deckenracks mit unterschiedlichen metallenen Werkstoffen und Oberflächen hergestellt und in den Tunnelbauwerken montiert. Nach bestimmten Auslagerungszeiten von bis zu drei Jahren werden die Proben demontiert und auf ihr Korrosionsverhalten untersucht. Ein weiteres Ziel neben der Qualifizierung der Werkstoffgruppe sind die Reduktion der Instandsetzungs- und Wartungsmaßnahmen der Tunnelbetreiber
Ziel des Projektes ist die Qualifizierung von Duplexstählen in Tunnelbauwerken um die Einsatzmöglichkeiten alternativer nichtrostender Stähle zu den bislang gebräuchlichen rostfreien Edelstählen 1.4404 und 1.4571 zu eruieren. Da Duplexstähle im Vergleich zu austenitischen Stählen über eine doppelt so hohe Festigkeit verfügen, können Bauteile schlanker konstruiert werden, wodurch Material eingespart werden kann. Neben der Wirtschaftlichkeit muss die Dauerhaftigkeit untersucht werden. Dazu wurden speziell konzipierte Wand- und Deckenracks mit unterschiedlichen metallenen Werkstoffen und Oberflächen hergestellt und in den Tunnelbauwerken montiert. Nach bestimmten Auslagerungszeiten von bis zu drei Jahren werden die Proben demontiert und auf ihr Korrosionsverhalten untersucht. Ein weiteres Ziel neben der Qualifizierung der Werkstoffgruppe sind die Reduktion der Instandsetzungs- und Wartungsmaßnahmen der Tunnelbetreiber.
Aufgrund der stark korrosiven Atmosphäre in Tunnelbauwerken kommt es aufgrund von Reinigungs- und Sanierungsmaßnahmen an Ein- und Anbauteilen aus nichtrostendem Stahl häufig zu wartungsbedingten Verkehrsbeeinflussungen und Tunnelsperrungen. Bislang ist nur eine kleine Gruppe rostfreier Edelstähle für die Verwendung in Tunnelbauwerken zugelassen. Im Sinne einer mittel- bis langfristigen Reduktion von Wartungsarbeiten besteht jedoch großes Interesse, die Einsatzmöglichkeiten alternativer nichtrostender Stähle zu erhöhen.
Um dies zu ermöglichen, entwickelten die Bundesanstalt für Materialforschung und -prüfung (BAM), gemeinsam mit dem Landesbetrieb Straßenbau NRW, in Zusammenarbeit mit der Informationsstelle Edelstahl Rostfrei (ISER), mit Unterstützung des Edelstahlherstellers Outokumpu und der Wilhelm Modersohn GmbH & Co. KG ein Forschungsprojekt zur Auslagerung von nichtrostenden Duplexstählen in Straßentunnel. Im Oktober 2019 beteiligte sich der Landesbetrieb Straßen, Brücken und Gewässer in Hamburg und ermöglichte die Auslagerung im Elbtunnel auszuweiten.
The advantages of treating prefabricated components made of Ultra-High-Performance Concrete (UCPC) at 90 °C are largely recognized, while hydrothermal treatment at 185 °C and the corresponding saturation pressure of 1.1 MPa, in contrast, is not applied in building practice so far and was studied only by a few researchers.
In the research presented, the parameters pre-storage-time before treatment and dwell time in the autoclave were systematically varied. The results illustrate in which way compressive strength increases with the duration of treatment. Already samples which were only heated up and immediately cooled down show an increase in strength compared to the 28-day reference of about 10 %. After 20 h the maximum increase of about 25 % is reached. Interestingly the compressive strength of samples treated very long hardly decreases. It can be therefore concluded that for the composition investigated the achievable mechanical strength is not severely sensitive regarding the duration of the treatment.
Also, pre-storage times before autoclaving longer than 0.5 days showed no significant impact on strength development.
The phase composition measured by XRD exhibits significant changes compared to the reference. The amount of ettringite and portlandite have vanished, the cement clinker phases are substantially decreased and hydroxylellestadite and hydrogarnet are formed as new phases. The increase in strength can be assigned to an improved pozzolanic and hydraulic reaction. Contradictory to literature, there was found no tobermorite, a mineral which is known to be susceptible for disintegration at Long autoclaving duration. This explains why no significant strength loss appeared.
The low tensile strength of cement-based materials can be improved by the addition of fibres. In a joint research project, an industrial partner designed special coatings for polymer and carbon fibres by integrating surfactants and hydrophilic compounds. Aim of the developed functionalization was to ensure an even coverage of the fibre surfaces and to anchor them chemically in the cement-based matrix. Task of the BAM was to quantify the effect of the improved bond. In a first step a workable mortar adjusted to the strength of the tested fibres was developed and the fibre distribution assessed by light microscopy and computed tomography. To test the new coating for its efficiency to prevent cracking during hardening and to improve the loadbearing behaviour new test setups were developed or existing methods were adjusted.
The experiments showed that the functionalization leads to a reduction of the crack area measured after the exposure of the wet mortar to strong drying conditions in the wind channel. Regarding the Efficiency to mitigate shrinkage cracks the functionalisation turned out to be more efficient for fibres made from polyacrylonitrile (PAN) than for carbon fibres. An improvement of the tensile strength after cracking of the cementitious matrix could only be documented for the coated carbon fibres. It could be quantified, however, only in the three-point bending tests because the fibres turned out to be too brittle for the applied single fibre pull-through test.
The advantages of treating prefabricated components made of Ultra-High-Performance Concrete (UCPC) at 90 °C are largely recognized, while hydrothermal treatment at 185 °C and the corresponding saturation pressure of 1.1 MPa, in contrast, is not applied in building practice so far and was studied only by a few researchers.
In the research presented, the parameters pre-storage-time before treatment and dwell time in the autoclave were systematically varied. The results illustrate in which way compressive strength increases with the duration of treatment. Already samples which were only heated up and immediately cooled down show an increase in strength compared to the 28-day reference of about 10 %. After 20 h the maximum increase of about 25 % is reached. Interestingly the compressive strength of samples treated very long hardly decreases. It can be therefore concluded that for the composition investigated the achievable mechanical strength is not severely sensitive regarding the duration of the treatment.
Also, pre-storage times before autoclaving longer than 0.5 days showed no significant impact on strength development. The phase composition measured by XRD exhibits significant changes compared to the reference. The amount of ettringite and portlandite have vanished, the cement clinker phases are substantially decreased and hydroxylellestadite and hydrogarnet are formed as new phases. The increase in strength can be assigned to an improved pozzolanic and hydraulic reaction. Contradictory to literature, there was found no obermorite, a mineral which is known to be susceptible for disintegration at Long autoclaving duration. This explains why no significant strength loss appeared.
Ultra high performance concrete (UHPC) is characterised by its high compressive strength of more than 150 MPa and its high durability. Due to thermal treatment at 90°C a strength comparable to the 28-days-strength can be achieved immediately after the treatment and in some cases can be even further increased up to 30 %. The explanations for the increase in strength are the accelerated hydration of the clinker minerals and the intensified pozzolanic reaction contributing to a denser microstructure and hence, a high performance in compressive strength.
Former research shows that thermal treatment can lead to inhomogeneities in form of a visible zonation within the cross-section. The width of the margin increases with shorter pre-storage time before the thermal treatment and with omitting protective measures against desiccation during the treatment. Specimens exhibiting a zonation typically show a lower compressive strength compared to the undisturbed reference whereas changes in chemistry, mineral content and microstructure were not reported in detail.
In this study the zonation of thermally treated UHPC is investigated with respect to its chemistry, mineral composition and microstructure to allow predictions on durability and strength development. Measurements show a change in pore sizes, minerals phase composition and element distribution leading to the visible zonation and weaker bending tensile strength compared to the reference.
Ultra high performance concrete (UHPC) is characterised by its high compressive strength of more than 150 MPa and its high durability. Due to thermal treatment at 90°C a strength comparable to the 28-days-strength can be achieved immediately after the treatment and in some cases can be even further increased up to 30 %. The explanations for the increase in strength are the accelerated hydration of the clinker minerals and the intensified pozzolanic reaction contributing to a denser microstructure and hence, a high performance in compressive strength.
Former research shows that thermal treatment can lead to inhomogeneities in form of a visible zonation within the cross-section. The width of the margin increases with shorter pre-storage time before the thermal treatment and with omitting protective measures against desiccation during the treatment. Specimens exhibiting a zonation typically show a lower compressive strength compared to the undisturbed reference whereas changes in chemistry, mineral content and microstructure were not reported in detail.
In this study the zonation of thermally treated UHPC is investigated with respect to its chemistry, mineral composition and microstructure to allow predictions on durability and strength development. Measurements show a change in pore sizes, minerals phase composition and element distribution leading to the visible zonation and weaker bending tensile strength compared to the reference.
Tuff ist in vielen historischen Objekten in Deutschland verbaut, hat aber wegen seiner Porosität und hygrischen Eigenschaften eine schlechte Verwitterungsresistenz. Ziel des Vorhabens ist die Entwicklung eines gesteinsmehlmodifizierten Schutzsystems auf Kieselsäurebasis (GEMOSK) zur Konservierung verbauter Tuffe. Für die Schutzmittelherstellung wird eine geeignete Mischung aus Kieselsol und feinen Gesteinsmehlen aus Steinbruchrückständen und Tuffabfällen verwendet. Bei erfolgreichem Abschluss des Projektes kann GEMOSK im Denkmalpflegebereich eingesetzt werden. Dadurch werden die Bausubstanz besser erhalten, Tuffsteinressourcen eingespart und Tuffabfälle wiederverwertet.
Explosive spalling is caused by, among others, the thermohydraulic spalling mechanism. During this process, vaporization, dehydration, moisture-transport and condensation processes interact. As a result, a drying and dehydration zone as well as a saturated zone, known as a moisture clog, are observed inside the unilaterally-heated concrete. The presented research is focused on the experimental investigation of the underlying thermohydraulic processes.
To investigate these, a test methodology based on X-ray computed tomography (CT) and nuclear magnetic resonance (NMR) was developed. Thereby, the X-ray CT scans are carried out simultaneously during the application of a defined unilateral-heating regime on a specially-constructed specimen. This miniaturized specimen, equipped with a double-layer casing, reproduces the condition within a planar, unilaterally-heated building component.
A preliminary test methodology and the first experimental results were presented at the 5th International Workshop on Concrete Spalling in Borås, Sweden (2017). The contribution for the upcoming workshop presents an improved version of this test methodology and new results for a high-performance concrete (HPC) mixture exposed to temperatures up to 500 °C. Regarding the CT measurements, a higher time-resolution of 15 min was achieved and a quantification of the moisture changes was implemented. Due to an increase in signal quality of the NMR measurements, a pore-size specific moisture distribution can now be resolved. This allows to conclude about the moisture reconfiguration between small gel pores and larger interhydrate pores. Additionally, the NMR measurement are no longer limited to first 2.5 cm below the heated surface but a one-dimensional moisture distribution can now be estimated over the whole 10 cm long specimen.
The presented results demonstrate that the combination of X-ray CT and NMR measurements enables to image and quantify the thermally-induced moisture transport and reconfiguration from small gel pores up to macro pores. This provides important insights into the thermohydraulic damage mechanism and leads to a better understanding of spalling avoidance strategies, like the addition of polypropylene fibres.
Thermally-induced moisture transport in high-performance concrete studied by X-ray-CT and 1H-NMR
(2019)
The thermohydraulic damage mechanism is one of the primary causes for explosive spalling of highperformance concrete. This paper presents the spatially- and temporally-resolved analysis of the thermally-induced moisture transport and reconfiguration processes by means of X-ray-CT and 1HNMR.
Thermal testing results for a high-performance concrete, which is sensitive to explosive spalling and which was prepared with and without added polypropylene fibres, are presented in this paper. These results indicate that the addition of fibres leads to a faster and deeper migration of the drying front and, thus, to a lower likelihood of vapour-pressure induced explosive spalling.
Explosive spalling is caused by, among others, the thermohydraulic spalling mechanism. During this process, vaporization, dehydration, moisture-transport and condensation processes interact. As a result, a drying and dehydration zone as well as a saturated zone, known as a moisture clog, are observed inside the unilaterally-heated concrete. The presented research is focused on the experimental investigation of the underlying thermohydraulic processes.
To investigate these, a test methodology based on X-ray computed tomography (CT) and nuclear magnetic resonance (NMR) was developed. Thereby, the X-ray CT scans are carried out simultaneously during the application of a defined unilateral-heating regime on a specially-constructed specimen. This miniaturized specimen, equipped with a double-layer casing, reproduces the condition within a planar, unilaterally-heated building component.
A preliminary test methodology and the first experimental results were presented at the 5th International Workshop on Concrete Spalling in Borås, Sweden (2017). The contribution for the upcoming workshop presents an improved version of this test methodology and new results for a high-performance concrete (HPC) mixture exposed to temperatures up to 500 °C. Regarding the CT measurements, a higher time-resolution of 15 min was achieved and a quantification of the moisture changes was implemented. Due to an increase in signal quality of the NMR measurements, a pore-size specific moisture distribution can now be resolved. This allows to conclude about the moisture reconfiguration between small gel pores and larger interhydrate pores. Additionally, the NMR measurement are no longer limited to first 2.5 cm below the heated surface but a one-dimensional moisture distribution can now be estimated over the whole 10 cm long specimen.
The presented results demonstrate that the combination of X-ray CT and NMR measurements enables to image and quantify the thermally-induced moisture transport and reconfiguration from small gel pores up to macro pores. This provides important insights into the thermohydraulic damage mechanism and leads to a better understanding of spalling avoidance strategies, like the addition of polypropylene fibres.
Beton, der heutzutage meist verwendete Baustoff, weist neben gutem Festigkeits- und Dauerhaftig-keitsverhalten ebenfalls erhöhte Brandschutzeigenschaften auf. Jedoch zeigen zahlreiche Schadensfälle, dass vor allem gefügedichte Betone im Brandfall zu explosionsartigen Abplatzungen neigen. Diese führen zum Freilegen der vorhandenen Stahlbewehrung und zur Verminderung des tragfähigen Bauteilquer-schnitts. Das wiederum kann im schlimmsten Fall eine Gefährdung der Standsicherheit eines Bauwerks zur Folge haben.
Nach derzeitigem Stand werden die explosionsartigen Abplatzungen auf thermomechanische und thermohydraulische Prozesse zurückgeführt. Letztere beruhen auf der Generierung hoher Wasserdampfdrücke in einseitig brandbeanspruchten Betonbauteilen, die zum einen auf die geringe Permeabilität des hochfesten Betons und zum anderen auf die Bildung einer wassergesättigten Zone, der sogenannten „moisture clog“ zurückzuführen sind. Die experimentelle Analyse der dabei ablaufenden Feuchtetransport- und Feuchteumlagerungsmechanismen ist Gegenstand des Vortrags.
Dazu wurde an der BAM im Rahmen eines MI-Typ 2 Projektes (FB 7.1, 7.3, 8.5) ein Versuchsstand aufgebaut, der die dreidimensionale, simultane Analyse und Quantifizierung des Feuchtetransports an einsei-tig erwärmten, miniaturisierten Prüfkörpern aus gefügedichtem Beton mittels Röntgencomputertomographie erstmals ermöglicht. Zusätzlich wird die eindimensionale Feuchteverteilung im Prüfkörper mittels Nuclear Magnetic Resonance (NMR) Technik vor und nach einseitiger Erwärmung untersucht. Mithilfe dieser Prüfmethodologie ist es möglich, die Ausbildung einer Trocknungs- bzw. Dehydrationszone sowie einer tiefergelegenen Feuchteakkumulationszone zeitlich aufgelöst abzubilden. Darüber hinaus können die Einflüsse einer Polypropylenfaserzugabe auf den thermisch induzierten Feuchtetransport quantifiziert werden.
Die Kenntnis von Materialeigenschaften spielt bei der Entwicklung oder Optimierung von
Betonen und Bauweisen für den Straßenbau sowie der Qualitätskontrolle und -sicherung eine bedeutende Rolle. Gleichermaßen bilden physikalische Materialkennwerte die Grundlage für die rechnerische Dimensionierung und die Restsubstanzbewertung von Betonfahrbahndecken.
Einen relevanten Kennwert bei der Untersuchung thermisch induzierter Spannungsund Verformungszustände stellt der thermische Ausdehnungskoeffizient von Beton dar.
Dieser beeinflusst beispielsweise maßgeblich das Längsdehnungsverhalten des Deckensystems sowie das Ausmaß von Plattenkrümmungen und Fugenbewegungen. Im Zuge der systematischen Weiterentwicklung der rechnerischen Dimensionierung aber auch im Zusammenhang mit der gezielten Verbesserung der Gebrauchseigenschaften von Fahrbahndecken gilt es zu hinterfragen, ob lastunabhängige Formänderungseigenschaften, wie z. B. der thermische Ausdehnungskoeffizient der verwendeten Betone, aktuell ausreichend Beachtung finden, ob allgemeine Literaturwerte für die heutigen Fahrbandeckenbetone stets Gültigkeit besitzen und ob deren Implementierung in moderne Rechenmodelle zu validen Ergebnissen führt. Für eine empirische Herangehensweise ist die Verfügbarkeit adäquater Prüfverfahren von entscheidender Bedeutung. In Deutschland existiert aktuell jedoch kein standardisiertes oder genormtes Verfahren für die prüftechnische Bestimmung des thermischen Ausdehnungskoeffizienten von Beton. Daher wurden unter Beachtung straßenbauspezifischer Gesichtspunkte zwei Prüfansätze entwickelt, die in diesem Beitrag vorgestellt und hinsichtlich möglicher Messunsicherheiten und Messungenauigkeiten diskutiert werden.
Außerdem erfolgt die Darstellung ausgewählter Ergebnisse aus Analysen an Bestandsbetonen aus dem BAB-Netz. Im Ergebnis sollen die Untersuchungen einen Beitrag zur Schaffung der prüftechnischen Voraussetzungen für eine abgesicherte Quantifzierung der thermischen Dehnung von Fahrbahndeckenbetonen leisten.
Polyether and -ester urethanes (PU) were exposed to artificial weathering at 40 °C and artificial UV radiation in a weathering chamber. In 3 parallel exposures, humidity was varied between dry, humid, and wet conditions. Material alteration was investigated by various analytical techniques like size exclusion chromatography
(SEC), liquid chromatography-infrared spectroscopy (LC-FTIR), thermal-desorption gas chromatography-mass spectrometry (TD-GC-MS), fluorescence mapping and dynamic mechanical analysis (DMA). Our results show that depending on the weathering conditions, different degradation effects can be observed. By means of SEC an initial strong decrease of the molar masses and a broadening of the mass distributions was found. After a material dependent time span this was followed by a plateau where molar mass changes were less significant. A minor moisture-dependent degradation effect was only found for polyester PU. Fluorescence measurements on two materials revealed an increase in the luminescence intensity upon weathering process reaching a saturation level after about 500 h. The changes in the optical properties observed after different exposure conditions and times were very similar. The TD-GC-MS data showed the fate of the stabilizers and antioxidant in the course of weathering. LC-FTIR measurements revealed a change in peak intensities and the ratio of urethane and carbonyl bands.
In the 21st century, adequate habitat and functioning infrastructure are critical for global societal and economic stability. In addition, growing urbanisation and environmental pollution cause challenges to societies.
With increasing velocity, humanity faces that the current way of living is not sustainable. Thus, habitat,infrastructure, urbanisation, environment and sustainability are definitively among the most striking challenges of the 21st century.
By consulting, planning, building, maintaining, exploiting and processing of global resources, civil engineers contribute significantly to the existence of these challenges. This is a high responsibility, but due to the heavy involvement, together with adjacent disciplines such as architecture, geosciences, chemistry,
physics, environmental sciences and economics, civil engineers also hold the key to mitigate these challenges and provide a brighter global future.
Solutions towards greener, more sustainable and economically viable materials do exist, and there is ongoing research on how greener technologies can contribute to better livelihood and economic growth, but their level of implementation is limited, a major reason for which is that these approaches require more fundamental understanding rather than standard application.
While today, engineers can choose from a wide range of rheology modifying admixtures, in some parts of the world, these are difficult to access, due to their complex processing. However, alternatives can be bio-based polymers such as polysaccharides from various sources. These are easily accessible all over the world, do not demand for complicated processing, and typically they are more sustainable than many established materials, which are crude oil-based.
The paper presents the effects of acacia gum, cassava starch and the gum of triumfetta pendrata A. Rich on the rheological performance of cementitious systems. It is shown that acacia gum can be as efficient as polycarboxylate based superplasticisers, cassava starch can reduce the yield stress slightly with little effect on the plastic viscosity, and the gum of triumfetta pendrata A. Rich increases the thixotropy of cement pastes with plasticizing polymers significantly.
Polyethylen hoher Dichte (PE-HD) wird als Werkstoff für Rohre und Behälter für den Transport und zur Lagerung von Gefahrgütern verwendet. Für die Beurteilung und technische Freigabe dieser Materialien ist insbesondere das Verständnis des Schädigungsmechanismus des langsamen, umgebungsbedingten Spannungsrisses (engl.: „environmental stress cracking“, ESC) essentiell. ESC tritt bei relativ geringen auf einen Werkstoff einwirkenden mechanischen Spannungen auf. An lokalen Fehlstellen (z.B. Defekte, Inhomogenitäten, Kerben) beginnend wächst ein Riss langsam durch das Material und führt nach gewisser Zeit zu einem charakteristischen, pseudo-spröden Bruch. Dabei wird das Risswachstum durch äußere Medieneinwirkung zusätzlich entscheidend beeinflusst. Dieses langsame Risswachstum wird als Hauptursache für das plötzliche und unerwartete Versagen von Polymerwerkstoffen angesehen.
Eine etablierte Prüfmethode zur Bewertung des Materialverhaltens gegenüber dieses Schädigungsmechanismus ist der Full-Notch Creep Test (FNCT), der für PE-HD Behältermaterialien üblicherweise unter Verwendung von wässrigen Netzmittellösungen (Arkopal N 100) durchgeführt wird. Die aus dem FNCT erhaltene Standzeit dient dabei als Bewertungskriterium für verschiedene PE-HD-Werkstoffe. In einer Studie wurden neben einer typischen Arkopal-N-100-Netzmittellösung praktisch relevante, organische Flüssigkeiten wie Biodiesel und Diesel als Testmedien verwendet, um deren Einfluss auf das ESC-Verhalten von PE-HD-Behältermaterialien zu charakterisieren. Neben der klassischen Standzeit-Auswertung erfolgte eine erweiterte Bruchflächenanalyse mittels Licht- (LM), Laserscanning- (LSM) und Rasterelektronenmikroskopie (REM). Insbesondere die LSM erlaubt eine schnelle und einfache Unterscheidung pseudo-spröder und duktiler Bruchbilder, die zur Beurteilung der Repräsentativität des FNCT für das dem Spannungsriss zugrundeliegenden langsamen Risswachstum von Bedeutung ist.
During their lifetime, polymer components subjected to mechanical loads and environmental influences show a loss of their mechanical properties required for their specific applications. In this respect, the craze-crack damage mechanism slow crack growth (SCG) is relevant for PE-HD components used in high-performance applications such as pipes and containers for the storage and transport of dangerous goods. SCG is considered to be the major failure mechanism in polyolefins and it typically occurs suddenly and unexpectedly. Due to the fields of application, SCG is a safety relevant issue. To test for the resistance of PE-HD pipe and container materials against SCG, the full-notch creep test (FNCT) is widely applied in Europe. In this study, SCG phenomena in PE-HD are investigated in detail based on an improved FNCT, especially including the consideration of the influence of environmental liquids effecting the damage mechanism. Using an enhanced fracture surface and a crack propagation analysis with imaging techniques such as light microscopy (LM), laser scanning microscopy (LSM), X-ray computed tomography (CT-scan) and scanning electron microscopy (SEM), detailed data concerning SCG are obtained.
The combined application of FNCT and such imaging techniques is explicitly advantageous and recommended to gain important information on damage occurring to PE-HD induced by mechanical stress and the influence of environmental liquids, which is essential within the Fourth Industry Revolution.
The full-notch creep test (FNCT) is a common method to evaluate the environmental stress cracking (ESC) behavior of high-density polyethylene (PE-HD) container materials . The test procedure as specified in ISO 16770 provides a comparative measure of the resistance against ESC using the time to failure of specimens mechanically loaded in a well-defined liquid environment. Since the craze-crack damage mechanism underlying the ESC process is associated with brittle failure, the occurrence of globally brittle fracture surfaces is a prerequisite to consider an FNCT measurement as representative for ESC . Therefore, an optical evaluation of FNCT fracture surfaces concerning their brittleness is essential. Due to the experimental setup, an inevitable increase of the true mechanical stress and the associated appearance of small ductile parts on fracture surfaces is induced in any case. Hence, an FNCT experiment is considered as 'valid', if the corresponding fracture surface is predominantly brittle . Based on laser scanning microscopy (LSM) height data of FNCT fracture surfaces , a universal and easy-to-use phenomenological criterion was developed to assess the validity of distinct FNCT experiments. This criterion is supposed to facilitate a quick evaluation of FNCT results in practical routine testing.
Depending on the CO2 generating and the capture process as well as on consecutive purification steps applied, CO2 streams from different emitters may differ in their composition. When CO2 streams with different compositions are fed into a larger pipeline network, there are several aspects that must be considered: i) chemical reactions, such as acid formation, may occur within the joint CO2 stream; ii) there may be a variation of mass flow rate and CO2 stream composition within the pipeline network if the feed-in behavior of different CO2 sources changes with time. Potential impacts of changing CO2 stream compositions and mass flow rates in CCS cluster systems were investigated in the collaborative project "CLUSTER" (see also www.bgr.bund.de/CLUSTER). In this presentation, we focus on the experimental investigations of formation and condensation of strong acids and their impacts on the corrosion of pipeline steels. When SO2, NO2, O2 and H2O are present simultaneously in CO2 streams chemical cross-reactions may occur leading to the formation of strong acids such as sulfuric and nitric acid. To prevent this acid formation the concentration of at least one of these four impurities must be kept very low (e.g., Rütters et al., 2016). At temperatures below the acid dew point temperature, acids will condense, e.g., on pipeline steel surfaces. In turn, these acid condensates may trigger steel corrosion. To better understand the process of acid formation and condensation and its implications for steel corrosion, exposure tests were performed on pipeline steel X70 in dense CO2 with varying SO2, NO2 and O2 concentration under high pressure and at 278 K in an observable autoclave, in which water was added as droplets or as vapor. Further, electrochemical tests were carried out with X70 specimens immersed in 500 mL CO2-saturated synthetic condensate solution or in droplets of the same solution on the specimen’s surface. Depending on impurity concentrations in the CO2 streams, condensates consisting of different relative amounts of nitric and sulfuric acid were formed. In condensates containing both nitric and sulfuric acid, corrosion rates were higher than the sum of those of the individual acids. In addition, corrosion products and forms depended on the condensate composition. Investigations of water droplets on steel surfaces in impurity-containing dense-phase CO2 revealed the diffusion of SO2 and NO2, followed by cross-reactions forming corresponding acids. An increase in droplet size (from 1 to 5 µl) lead to higher corrosion rates. However, in comparison to measurements in bulk solution, corrosion reactions in droplets resulted in thick, high-resistance corrosion products and observed droplet corrosion rates were significantly lower. In addition, the possibility of acid droplet formation and growth in impure liquid CO2 is influenced by the wetting behavior of the acid droplet on the steel surface. Thus, the contact angle between a water droplet and the surface steel specimens in a CO2 atmosphere was investigated in a high pressure view cell following the sessile drop method. The contact angle wasand found to be larger at higher CO2 pressures (studied from 5 to 20 MPa) and at higher temperatures (e.g. 278 K to 333 K). Further, measured contact angles were larger on rough than on smooth metal surfaces. In addition, acid formation reduced the contact angle, i.e. lead to better wetting, thereby stimulating condensation that was followed by a corrosion process. These detailed insights on the complex interplay of acid formation, condensation, wetting behavior and corrosion allow a better assessment of material suitability for pipeline transportation of impure CO2 streams
Ergebnisse aus dem AiF Forschungsvorhaben IGF 18823 N/1 "Optimierung von Korundschleifprozessen"
Ein Referenzwerkstoff mit einem definierten Oberflächenzustand wurde zunächst umfassend mittels elektrochemischer Korrosionsuntersuchungen, KorroPad-Untersuchungen und oberflächenanalytischer Verfahren charakterisiert. Anhand definierter Schleifversuche an diesem Referenzzustand wurden anschließend verschiedene Schleifparameter variiert, deren Auswirkungen auf die Korrosionsbeständigkeit mit den gleichen Methoden beurteilt wurden. Somit war es möglich, den Einfluss einzelner Schleifparameter auf das Korrosionsverhalten aufzuzeigen.
Samples of the austenitic stainless steel grade X5CrNi18‐10 (1.4301, AISI 304) were ground industrially with various grinding parameters to study their influence on corrosion resistance. The ability of the mechanically ground surfaces to form a stable passive layer was evaluated by KorroPad test and a modified electrochemical potentiodynamic reactivation test based on a single loop (EPR‐SL). Furthermore, the surfaces were characterized by surface analytical methods. The main influence was determined regarding abrasive belt type. Surfaces mechanically ground with granulate abrasive belts constantly had a lower corrosion resistance than surfaces ground with single‐coated grain. The granulate abrasive belts generated more sensitized surface areas and left formations of welded sample material on the mechanically ground surfaces. A post‐treatment with a nonwoven abrasive proved to be an effective finishing process by which the surface defects and sensitized material got removed and the surfaces regained the expected corrosion resistance.
Durch eine breite Beteiligung von Schleifmittelherstellern, -anwendern und wissenschaftlichen Einrichtungen im projektbegleitenden Ausschuss (PA) konnte der vielschichtige Themenkomplex „Schleifen“ im Kontext zu den Projektzielen umfassend untersucht werden. Es wurden praxisrelevante Parameterfelder definiert, die eine erfolgreiche Aufklärung der Projektfragestellung ermöglichten.
Im Zuge der Untersuchungen wurde ein signifikanter Einfluss beim Einsatz von Granulatschleifbändern auf das Korrosionsverhalten geschliffener Oberflächen festgestellt. Damit zeigten geschliffene Oberflächen regelmäßig eine schlechtere Korrosionsbeständigkeit als Oberflächen, die mit sonst gleichen Parametern mit einlagig gestreuten Bändern bearbeitet wurden.
Die durch einige Untersuchungsergebnisse aus vorangegangenen AiF-Vorhaben ursprünglich verfolgte These, dass Unterschiede in der Korrosionsbeständigkeit auf die Kornart der Schleifmittel Korund bzw. SiC zurückzuführen ist, konnte nur bedingt bestätigt werden. Bei den systematischen Untersuchungen innerhalb dieses Projektes erwies sich der Einfluss der Kornart im Vergleich zum Einfluss des Schleifbandtyps (Granulat bzw. einlagig gestreutes Korn) als weniger relevant.
Durch weiterführende Untersuchungen konnten auf Oberflächen, die mit Granulatschleifbändern bearbeitet wurden, große Materialaufplattungen aus Eigenmaterial festgestellt werden. Das Eigenmaterial wird dabei im Schleifprozess zunächst abgetragen und aufgrund der Topografie des Schleifbandes zeitweise auf den Bändern festgehalten. Später lösen sich diese Materialanhäufungen vom Band ab und können prozessbedingt durch Wärme- und Krafteinwirkung auf den bearbeiteten Oberflächen aufgeplattet werden. Durch REM und KorroPad Untersuchungen ließen sich Bereiche mit solchen Eigenmaterialaufplattungen eindeutig als wesentliche Ausgangspunkte für Korrosionsprozesse identifizieren. Das aufgeplattete Material ist stark verformt, thermisch beeinflusst und bildet eine Spaltgeometrie zur Bauteiloberfläche aus. Diese Veränderungen führen zur Störung der Passivschichtausbildung in diesen Bereichen und verursachen damit eine erhöhte Korrosionsanfälligkeit der Oberflächen.
Durch gezielte Nachbearbeitungsprozesse ist es möglich, die Eigenmaterialaufplattungen von den Oberflächen zu entfernen. Im Rahmen des Vorhabens wurde dazu eine Nachbearbeitung mittels Schleifvlies geprüft, die zu einer Entfernung der Eigenmaterialaufplattungen und damit zu einer Wiederherstellung der erwarteten Korrosionsbeständigkeit führte. Wird der Endschliff von Oberflächen mit einlagig gestreutem Korn ausgeführt, sind ebenfalls keine korrosionsrelevanten Materialaufplattungen zu erwarten.
Die in einem vorhergehenden AiF Vorhaben IGF 17136 N/1 entwickelte Methode der KorroPad-Prüfung konnte auch hier erfolgreich für die Untersuchung der Auswirkung unterschiedlicher Prozessparameter auf die Korrosionsbeständigkeit der Oberflächen eingesetzt werden. Zudem erwies sich das EPR-SL-Verfahren als ein weiterer Ansatz, um die Passivschichtstabilität verschieden geschliffener Oberflächen vergleichend untersuchen zu können.
Mit den nun vorliegenden Erkenntnissen können kmU künftig durch Anpassungen und Optimierung von Schleifprozessen eine gute Korrosionsbeständigkeit der bearbeiteten Oberflächen sicherstellen. Die Optimierung der Prozessparameter und -schritte kann durch den Einsatz der KorroPad-Prüfung Inhouse erfolgen und somit die laufende Fertigung im Rahmen der Qualitätsprüfung überwacht und dokumentiert werden.
In Europe biodiesel gained from rapeseeds are considered as an alternative to common fossil fuels due to its environmental performance and its independence from import of raw materials. Biodiesel is also suitable to serve as blending component to heating oil. In that case, it must be considered that changes of fuel composition might cause material degradation.
The objective of this research was to investigate the resistance of metallic materials exposed to heating oil, heating oil blend B20 with 20 % biodiesel and pure biodiesel. Furthermore, the resistance of metals to eight-year aged B10 and six-year aged pure biodiesel was evaluated. Ageing of biodiesel forms acids and water which might propagate metal corrosion. The investigated metals (aluminium, unalloyed steel, austenitic CrNi-steel, copper, die cast zinc and brass) are commonly used for components in middle distillate facilities.
According to DIN 50905-4 the immersed metals were exposed in a climate chamber at 50°C for 4 weeks. The metallic materials were evaluated as resistant if the annual corrosion rate due to uniform corrosion remained under 0.1 mm/year and no localized corrosion in the form of pitting occurred.
The corrosion rates of the exposed materials stayed far below the limit of 0.1 mm/year for all tested fuels. An exception was die cast zinc ZP0410 in eight-year aged B10; a corrosion rate up to 0.3 mm/year due to uniform corrosion was measured. In no case localized corrosion occurred. Copper and brass caused discolouration of biodiesel from yellow to green.
In conclusion, the tested metallic materials were resistant in heating oil, heating oil blend B20 and pure biodiesel at 50 °C. Even the metals exposed to six-year aged biodiesel and eight-year aged B10 showed no uniform or localized corrosion; except for zinc, which was not resistant in eight-year aged B10.
Aus Rapsöl gewonnener Biodiesel ist eine umweltfreundliche Alternative zu fossilen Energiequellen. In der Europäischen Union, in der 80 % der ölhaltigen Brennstoffe importiert werden müssen, besteht zudem ein Interesse, die Abhängigkeit von exter-nen Ölversorgern zu reduzieren.
Bei jeder Veränderung der Zusammensetzung eines Brennstoffs muss auch die Ma-terialverträglichkeit gewährleistet bleiben. Es stellt sich die Frage, ob Elastomere im Vergleich zu reinem Heizöl auch in Heizöl mit 20 % Biodiesel (B20) beständig sind.
Die Polarität des Biodiesels erhöht die Quellung und fördert die Permeation und Ex-traktion. Sowohl Quellung als auch Extraktion bedingen Änderungen der physikali-schen Eigenschaften der Elastomere. Extraktion verändert die chemische des Heiz-öls. Diese chemischen Veränderungen können auch den Abbau (Hydrolyse und Oxi-dation) der Polymere durch das Herauslösen von Additiven und Stabilisatoren be-schleunigen.
Ziel dieser Arbeit war die Bestimmung der Beständigkeit der Elastomere ACM (Poly-acrylatkautschuk), HNBR (Hydrierter Acrylnitrilbutadienkautschuk), FKM (Fluorkaut-schuk) und PUR (Polyurethan) in Heizöl und im Heizölgemisch B20.
Prüfkörper der Elastomere wurden für 42 Tage (Härteprüfung) und 84 Tage (Zugprü-fung) bei 40 °C ausgelagert. Anschließend wurde die Änderung der Masse, Shore Härte A, Zugfestigkeit, und Reißdehnung bezogen auf die Werte vor der Aus-lagerung bestimmt. Die weniger zur Quellung neigenden Elastomere FKM und HNBR wurden zusätzlich bei 70 °C ausgelagert.
Um die Elastomere im verpressten Zustand zu testen, wurde der Druckverformungs-rest nach DIN ISO 815 bestimmt. Hierzu wurden zylindrische Prüfkörper aus ACM, HNBR und FKM verpresst und in Heizöl und Heizöl mit 20 % FAME für 3, 7, 14, 28, 56 und 90 Tage bei 40 °C ausgelagert. Anschließend wurde über die Dickenmes-sung der Druckverformungsrest ermittelt. Zum Vergleich wurden Prüfkörper verpresst und ohne Medium bei 40 °C ausgelagert.
In den internationalen Normen wurde kein Grenzwert für die Veränderung der Zugei-genschaften und der Härte für eine positive Bewertung der Beständigkeit festgelegt. Deshalb wurde in der BAM ein Grenzwert von 15 % für die Beständigkeitsbewertung herangezogen.
Bei 40 °C lag die Änderung der Zugeigenschaften und der Shore Härte von ACM, HNBR und FKM in Heizöl und in B20 unter 15 %. Folglich sind ACM, HNBR und FKM bei 40 °C in Heizöl und in B20 beständig. PUR ist bei 40 °C in Heizöl beständig, je-doch nicht für eine Verwendung in B20 geeignet, da sich die Zugfestigkeit und Reiß-dehnung um 50 % vermindert haben.
Bei 70 °C ist FKM in Heizöl und B20 beständig, wohingegen HNBR an seine Einsatz-grenzen gelangt und unbeständig ist, in B20 haben sich die Zugfestigkeit um 40 % und die Reißdehnung um 50 % reduziert.
Für Bauteile (Komponenten) von Versorgungsanlagen für flüssige Brenn- und Kraftstoffe muss die Beständigkeit der metallenen Werkstoffe und Polymere nachgewiesen werden. Im Anwendungsfall von Heizöl mit 20 % biogenen Anteilen in Form von Rapsölfettsäuremethylester (FAME, Biodiesel) ist es für eine konservative Beurteilung des Korrosionssystems Werkstoff/Medium/Umgebung wichtig, die Alterungseffekte des Mediums einzubeziehen.
Entwicklung eines Prüfverfahrens für die Untersuchung der Beständigkeit von metallenen Werkstoffen und Polymeren in Heizöl und Heizöl-FAME-Blends, das für eine Vorauswahl der Werkstoffe und zum Nachweis der Beständigkeit im Hinblick auf die bauaufsichtlichen Zulassungsverfahren geeignet ist.
Water migration in one-side heated concrete: 4D in-situ CT monitoring of the moisture-clog-effect
(2019)
Explosive spalling due to fire exposure in concrete structures can lead severe damage and, in the worst case, to premature component failure. For this reason, an in situ investigation of water Migration in concrete due to surface heating was undertaken.
During these experiments, a miniaturized concrete specimen within a confining and insulating double-hull was subjected to surface heating during simultaneous X-ray computed tomography (CT) scanning. Through the use of subtraction-based Image analysis techniques, it was possible to observe and quantify not only drying within areas of the concrete matrix close to the heated surface, but also the migration of moisture to both pore and matrix regions deeper within the specimen. It was also discovered that the correction of CT images for specimen deformation using DVC and variable detector performance using calibrated image filters significantly improved the quality of the results. This clearly demonstrates the potential of X-ray CT for evaluation of other rapid-density-change phenomena in concrete and other building materials.
A central challenge to ensure the sustainable production and use of nanotechnologies is to understand and effectively control the risks along the industrial innovation value chain. Knowledge about nanotechnology processes and nanosafety issues (hazards, fate, risk...) is growing rapidly but the effective use of this knowledge for risk management by market actors is lagging behind.
EC4SafeNano (European Centre for Risk Management and Safe Innovation in Nanomaterials and Nanotechnologies) promotes a harmonized vision of expertise in risk assessment and management for the public and private sectors to enable the safe development and commercialization of nanotechnology.
EC4SafeNano is operated together by major European risk institutes with the support of numerous associated partners, gathering all stakeholders involved in Nanomaterials and Nanotechnologies (regulators, industry, society, research, service providers...).
In a case study the surface chemical transformations upon 2 different ageing procedures (long-term UV irradiation or swimming pool water) of a representative set of titanium dioxide nanoparticles has been investigated. The materials have been analyzed by various analytical techniques. Each method addresses different aspects of the complex endpoint surface chemistry. The multi technique approach allows evaluation of the capabilities and limitations of the applied methods regarding their suitability to address the endpoint surface chemistry and their sensitivity to identify even small surface chemical transformations.
Results:
- To obtain a comprehensive picture, it is insufficient to concentrate on a single analysis technique.
- By using time-of-flight secondary ion mass spectrometry (ToF-SIMS) in combination with principal component analysis (PCA) it was possible to identify even subtle changes in the surface chemistry of the investigated materials.
- A general trend that was observed for the UV-aged samples is the decrease of organic material on the nanomaterial surface.
This project has received funding from the European Union’s Horizon 2020 research and innovation programme under grant agreement No 723623.
The elemental dissolution of Cu-Zn alloys was investigated as a function of Zn content ranging from 0 to 45 wt%. Atomic emission spectroelectrochemistry (AESEC) was utilized to directly monitor Cu2+ and Zn2+ release and oxide growth as function of time during potentiodynamic experiments. It was determined that Cu dissolution undergoes a simultaneous mechanism of Cu2O formation and Cu2+ release. The addition of Zn in Cu-Zn alloy does not measurably change the dissolution mechanism of Cu2+ and the rate of aqueous Cu2+ was only dependent on the potential. Zn dissolution was however blocked by the formation of a Cu(0) film which shifted the Zn dissolution in the anodic direction.