Niobium-titanium carbide cermets with nickel binder have been prepared by colloidal processing in water without a milling step by using Poly-diallyl-dimethyl-ammonium chloride (Poly-DADMAC) as a dispersant. Homogeneous microstructures with relative densities larger than 99% of the theoretical density have been achieved by gas pressure sintering in argon atmosphere. However, mechanical properties like hardness and strength were slightly decreased due to precipitation of free carbon.
The current study reports on the influence of the Addition of 5–15 vol% VC or/and Mo2C carbide on the microstructure and mechanical properties of nickel bonded NbC cermets, which are compared to cobalt bonded NbC cermets. The NbC, Ni and secondary carbides powder mixtures were liquid phase sintered for 1 h at 1420 °C in vacuum. The fully densified cermets are composed of a cubic NbC grains matrix and an evenly distributed fcc Ni binder. NbC grain growth was significantly inhibited and a homogeneous NbC grain size distribution was obtained in the cermets with VC/Mo2C additions. The mechanical properties of the NbC-Ni matrix cermets are strongly dependent on the carbide and Ni binder content and are directly compared to their NbC-Co equivalents.
The liquid phase sintered NbC-12 vol% Ni cermet had a modest Vickers hardness (HV30) of 1077 ± 22 kg/mm2 and an indentation toughness of 9.1 ± 0.5 MPa·m1/2. With the addition of 10–15 vol% VC, the hardness increased to 1359 ± 15 kg/mm2, whereas the toughness increased to 11.3 ± 0.1 MPa·m1/2. Addition of 5 and 10 vol% Mo2C into a NbC-12 vol% Ni mixtures generated the same values in HV30 and KIC when compared to VC additions. A maximum flexural strength of 1899 ± 77 MPa was obtained in the cermet with 20 vol% Ni binder and 4 vol% VC+4 vol% Mo2C addition, exhibiting a high fracture toughness of 15.0 ± 0.5 MPa·m1/2, but associated with a loss in hardness due to the high Ni content. The dry sliding wear behaviour was established at room temperature and 400 °C from 0.1 to 10 m/s.
The differences between the binary phase diagrams W-C and Nb-C illuminate several parameters for tailoring the properties of NbC. In the region of homogeneity of NbCx, with Nb4C3 and Nb6C5 other Niobium carbide phases occur. Properties, like micro-hardness, hot hardness, sliding wear, elastic modules and toughness can be tailored by the C/Nb Ratio, secondary carbides and the type of binder. Supporting results from different grades with varying C/Nb ratio or binder types will be illuminated. Thus, the NbC system offers to producers a wider parameter window, than WC.