Effect of different sulphur-based crosslink networks on the nitrile rubber resistance to biodiesel
(2017)
Biodiesel possesses some comparable physical properties to petroleum diesel in addition to its improved environmental benefits. Nonetheless, both fuels differ greatly with respect to their chemical compositions.
Therefore, the compatibility of the materials, which are commonly employed in contact with diesel, must also be assured for biodiesel. This paper assessed the influence of sulphur-based curing systems on the resistance of nitrile rubber to soybean biodiesel. Formulations were prepared using highacrylonitrile-content nitrile rubber by employing a two-level experimental design. The amounts of two different accelerators and sulphur were varied to achieve different types of vulcanisation systems.
Thermal analyses, mechanical tests and microscopy analyses were conducted to evaluate the behaviour of the material after contact with biodiesel. The results showed that the choice of the accelerator played an important role on the resistance of the rubber to the biofuel, and crosslink density was not a key factor with respect to the resistance.
Due to the increasing demand for utilization and improvement of energy efficient materials, especially concerning requirements in lightweight construction and design, polyolefin materials are used extensively and in an increasingly broad range of applications.
Although loaded with stresses under yield stress, preformed voids, inhomogeneities or notches can possibly lead to damage and unexpected failure induced by liquid media in polyolefin materials. For PE-HD, slow crack growth (SCG) as well as environmental stress cracking (ESC) are relevant mechanisms of damage. SCG appears without influence of a surrounding medium or in “inert” media whereas ESC occurs in “active” media, which have decisive influence on damage mechanism and time to failure. To characterize the intrinsic resistance of the material against those damage mechanisms, the Full-Notch Creep Test (FNCT) is widely used and of paramount importance particularly for the assessment of pipe and blow molding types of PE-HD.
In this study, the FNCT – usually applied as a standardized testing method (ISO 16770) using a few universal model liquid media – is extended by investigations of selected relevant PE-HD materials with a variety of properties also in real media. Mainly topical fuels, customary in the market such as diesel and biodiesel are examined. Especially the influence of temperature, and the ESC behavior of PE-HD in media that are sorbed to a significant extent, are addressed. The underlying diffusion-controlled sorption process was assessed before comparing non-saturated specimens with samples previously saturated with sorbing media.
The investigations were performed using a novel FNCT-device with 12 individual sub-stations, each equipped with individual electronic stress and temperature control and continuous online monitoring of the specimen elongation.
In addition to acquired results concerning time to failure and elongation behavior, imaging techniques, such as light microscopy (LM), laser scanning microscopy (LSM) and X-ray computed tomography (CT scan) were utilized to obtain data concerning crack propagation and media migration. Fracture surface analysis (LM, LSM) and quasi in-situ imaging (CT scan) via measurement in different load stages are considered explicitly. Correlations of elongation behavior and data derived from imaging analysis such as fracture plane roughness and height of areas of ductile deformation were obtained.
Due to the increasing demand for utilization and improvement of energy efficient materials, especially concerning requirements in lightweight construction and design, polyolefin materials are used extensively and in an increasingly broad range of applications.
Although loaded with stresses under yield stress, preformed voids, inhomogeneities or notches can possibly lead to damage and unexpected failure induced by liquid media in polyolefin materials. For PE-HD, slow crack growth (SCG) as well as environmental stress cracking (ESC) are relevant damage mechanisms. SCG appears without influence of a surrounding medium or in “inert” media whereas ESC occurs in “active” media, which have decisive influence on damage mechanism and time to failure. To characterize the inherent resistance of the material against those damage mechanisms, the Full-Notch Creep Test (FNCT) is widely used. Therefore, the FNCT is of paramount importance particularly for the assessment of pipe and blow molding types of PE-HD – especially in the field of polymer development and improvement for high-performance applications.
In this study, the FNCT – usually applied as a standardized testing method (ISO 16770) using a few universal model liquid media – is extended by investigation of selected relevant PE-HD materials with a variety of properties also in real media. Mainly topical fuels, customary in the market such as diesel and biodiesel are examined. Especially the influence of temperature, and the ESC behavior of PE-HD in media that are sorbed to a significant extent, are addressed.
The investigations were performed using a novel FNCT-device with 12 individual sub-stations, each equipped with individual electronic stress and temperature control and continuous online monitoring of the specimen elongation.
Additional to acquired results concerning time to failure and elongation behavior, imaging techniques, such as light microscopy (LM), laser scanning microscopy (LSM) and X-ray computed tomography (CT scan) were utilized to obtain data concerning crack propagation and media migration. Correlations of elongation behavior and data derived from imaging analysis were obtained.
Changes in fuel composition and the introduction of alternative fuels often create problems of corrosion and degradation in materials. The objective of this research was to determine the corrosion behaviour of commercial metallic tank materials (unalloyed steels, austenitic CrNi- and CrNiMo-steels, aluminium and its alloys) in fuels and heating oil with admixtures of biogenic sources, such as gasoline with addition of ethanol (E10, E85), pure biodiesel and heating oil with 10 % biodiesel (B10).
Metallic tank materials were evaluated as resistant in a liquid if the annual corrosion rate due to uniform corrosion did not exceed 0.1 mm/year, and localized corrosion effects in the form of pitting corrosion, stress corrosion cracking and crevice corrosion did not occur.
The corrosion rates of the tank materials after exposure to E10, E85, non-aged and two-year aged pure biodiesel, and non-aged and one-year aged heating oil B10 for four weeks at 50 °C, according to DIN 50905/4, were well below the limit of 0.1 mm/year. For the unalloyed steels, the formation of rust was observed independently of the biofuels amount of ageing. U-bend specimens made of unalloyed steel were not damaged in form of stress corrosion cracking in all test fuels at this test temperature.
Changes in fuel composition and the introduction of alternative fuels often create problems of corrosion and degradation in materials. The objective of this research was to determine the corrosion behaviour of commercial metallic tank materials (unalloyed steels, austenitic CrNi- and CrNiMo-steels, aluminium and its alloys) in fuels and heating oil with admixtures of biogenic sources, such as gasoline with addition of ethanol (E10, E85), pure biodiesel and heating oil with 10 % biodiesel (B10).
Metallic tank materials were evaluated as resistant in a liquid if the annual corrosion rate due to uniform corrosion did not exceed 0.1 mm/year, and localized corrosion effects in the form of pitting corrosion, stress corrosion cracking and crevice corrosion did not occur.
The corrosion rates of the tank materials after exposure to E10, E85, non-aged and two-year aged pure biodiesel, and non-aged and one-year aged heating oil B10 for four weeks at 50 °C, according to DIN 50905/4, were well below the limit of 0.1 mm/year. For the unalloyed steels, the formation of rust was observed independently of the biofuels amount of ageing. U-bend specimens made of unalloyed steel were not damaged in form of stress corrosion cracking in all test fuels at this test temperature.
Präsentation des Themenfeldprojekt MIC innerhalb des Themenfeld Material, mit Schwerpunkt auf dem aktuellem Status.Präsentiert würden die neusten Ergebnisse bei der Entwicklung von optischen Nanosensoren sowie der mikrobiologische Zerstörung/Abbau von Kraftstoffen und Tanksystemen. Vorstellung eines neuen Themenbereichs: Der Mikrobiell beeinflussten Korrosion durch methanogene Archaea.
The full-notch creep test (FNCT) is widely used to characterize the slow crack growth (SCG) behavior of polyolefin materials in “inert” media as well as effects of environmental stress cracking (ESC) in which the medium has decisive influence on damage mechanism and time to failure. The test is of greatest importance for pipe and blow molding types of polyethylene, high density (PE-HD). Usually the full-notch creep test is applied as a standardized testing method (ISO 16770) using a few universal liquid media, such as solutions of Arkopal N 100. In our study, selected relevant polyethylene, high density materials are investigated also in real media – practical formulations as well as representative pure chemicals – and influences of temperature and geometry of specimen and notch are explicitly addressed. Furthermore, the investigations comprise also the environmental stress cracking behavior of polyethylene, high density in media that are sorbed to a significant extent – examples are diesel and biodiesel – based on comparison with samples previously saturated with those media. Thus, also the underlying diffusion controlled sorption process has to be assessed before. The investigations were performed using a full-notch creep testing device with 12 individual sub-stations, each equipped with individual electronic stress and temperature control and continuous online monitoring of the specimen elongation.
Sustainable energy and clean engine fuels receive more and more attention. Petrodiesel could be substituted by biofuels such as biodiesel produced from renewable resources. Biodiesel is derived by transesterification of oils with alcohols for example vegetable oils, animal fats or food waste. Its chemical composition of unsaturated fatty methyl acids causes biodiesels susceptibility to oxidation. Especially, the polymer-biodiesel performance under long-term conditions has been considered only in few researches.
Our study addresses a long-term storage scenario of a polymeric fuel tank containing biodiesel or diesel.