The martensitic steels X30CrMoN15-1 and 100Cr6 did not show any hydrogen enhanced wear in sliding friction tests against alumina balls in hydrogen gas environment. However, depending on the purity of the environment, unexpected high wear occurred at the alumina ball. The results of a tests series with a broad variation of test parameters are presented.
Sliding wear of martensitic steels in hydrogen – X30CrMoN15-1 and 100Cr6 – the role of water traces
(2016)
Initially the primary objective of the project has been the investigation of the influence of gaseous hydrogen on the wear of martensitic steels under heavy tribological stress. As a counter body an Al2O3 ball has been used because the material is inert and hard so that a low amount of wear was expected. If only the gas pressure is responsible for the absorption of hydrogen from the gas to pure α-iron it would require 15·105 MPa (~15 Mbar) to press 1 ppm into the material.
In the test series the Al2O3 balls showed in N2 and H2 atmosphere a higher wear compared to aerial experiments which showed a smaller wear track and a severer wear for the disc. Because of scattering and thereof following investigations it was shown that hydrogen has no noticeable influence but water traces in the gas are manipulating the outcome of the tests distinctly.