The presentation gives an overview of BAM's activities on processing influences and application properties of MPEAs in the form of joined and machined high and medium entropy alloys (CoCrFeMnNi and CoCrNi). In the case of welding, the focus is on defect-free welded joints with sufficient mechanical properties. In the case of machining, the focus is on the possible influence on the surface quality of the materials through adequate milling parameters. In addition, the hydrogen absorption and diffusion properties as well as the electrochemical corrosion behavior are fundamentally examined.
Future structural components made of the novel high-entropy (HEA) or medium-entropy alloys (MEA) components can be potentially exposed to hydrogen containing environments like high-temperature water in pressurized nuclear reactors or aerospace structures. Further applications are vessels wall materials for cryogenic or high-pressure hydrogen storage. So far, the susceptibility of HEA/MEAs to hydrogen assisted cracking (if any) and the hydrogen diffusion is not investigated in detail yet and can limit or extend possible applications of HEA/MEA as structural materials. In our work, we focused on the hydrogen absorption, diffusion, and distribution in a HEA (Co20Cr20Fe20Mn20Ni20, the original Cantor-alloy) and a MEA (Co33.3Cr33.3Ni33.3). Conventional cathodic hydrogen charging was carried out for the hydrogen ingress in the materials. Thermal desorption analysis (TDA) via carrier gas hot extraction with coupled mass spectrometry revealed complex hydrogen trapping in both alloy types up to 300 °C. The absorbed total hydrogen concentrations were ≥ 70 ppm for the HEA and approximately 40 ppm for the MEA-type. Although both materials have different chemical composition, the TDA spectra were comparable. In addition, it was shown that the consideration of the sample geometry is an important influence on the sample temperature. It decreases the effective applied heating rate, which must be anticipated for each hydrogen peak after deconvolution of the spectra. This increases the activation energy and shifts the peak to lower temperatures. As a result, microstructure effects can be separated from experimental boundary conditions like the concentration gradient due to the charging process and later thermal activation.
Martensitic 9 %-Cr steels like P91 and P92 show susceptibility to delayed hydrogen assisted cracking depending on their microstructure. In that connection, effective hydrogen diffusion coefficients are used to assess the possible time-delay. The small number of available diffusion coefficients varies already at room temperature by several orders of magnitude (mostly regarded as result of present microstructure). Especially P91 weld metal diffusion coefficients are rare so far. For that reason, electrochemical permeation experiments had been conducted using P92 base metal and P91 weld metal (in as-welded and heat-treated condition) with different thicknesses. The diffusion coefficients are calculated by two methods (time-lag and inflection point method) were performed. The results show that, despite of microstructural effects, the sample thickness must be considered as it influences the calculated diffusion coefficients. Finally, the comparison of calculated and measured hydrogen concentrations (determined by carrier gas hot extraction) enables the identification of realistic diffusion coefficients.