Admixtures are important constituents to enhance the performance of concrete. They allow for more efficient use of binders which can mitigate negative environmental impacts from producing cement-based materials. Commonly used rheology modifying agents like polycarboxylate ethers or cellulose ethers are synthetic or semi-synthetic, respectively. This requires additional energy consumption for their production and global supply chains particularly for many developing regions, which will be large consumers of concrete in the future. However, many locally available bio-based polysaccharides could be effectively used instead. These polymers are often overlooked by engineers and scientists due to their limited distribution and inherent complexity, yet they represent an underleveraged source of precursors for admixtures. This study investigates the action mechanisms of some bio-based rheology modifying agents, i.e., acacia gum and miscanthus gum, and provides a comparison to a conventionally modified starch. The results show that the mechanism of action of these polymers is closely related to the composition of the mixture, mixing regime, and the composition of the aqueous phase. Depending on the agent, either plasticizing or stabilizing effects on rheology can be revealed.
In this paper, we demonstrate the value of 1H NMR
relaxometry for studying the hydration of clinker-reduced, more
climate-friendly cementitious binders. The results were obtained
on typical CEM I cements and samples containing two different
reactive agricultural ashes as well as non-reactive biochars as
supplementary cementitious materials. The findings prove that
time-resolved NMR measurements provide valuable additional
information when combined with classical heat flow calorimetry.
Dredging sediment refers to materials removed from the bottom of a water body during dredging operations. Mainly the dreading mud contains clay, silt, sand, water, and alkalis. This work incorporated dredging mud into the calcium sulfoaluminate cement at replacement levels of 0%, 10%, 30%, and 50% by weight. Pastes were evaluated after 1d, 28d, and 90d- hydration through mechanical strengths and the reaction rate by isothermal conduction calorimetry. XRD and MIP characterized the reaction products. The findings showed that small replacements (10% and 30%) increased early strength with higher ettringite formation in the system at 1d of curing. However, the evolution of mechanical strength was lower than the reference (0% replacement) over time. The results showed that in low replacement dosages, the dredging mud act as a nucleation site for the hydration of calcium sulfoaluminate phases.
This study investigated the effect of incorporating three types of nanosilica (NS), two powders, and one colloidal suspension on the hydration, strength, and microstructure of calcium sulfoaluminate (CSA) cement pastes prepared with and without a superplasticizer (SP). X-ray diffraction, Fourier transform infrared spectroscopy, scanning electron microscopy (SEM), and compressive strength tests were performed after 2, 5, and 28 days of hydration. The results showed that both NS powders delayed cement hydration at an early age, which was attributed to particle agglomeration (confirmed by dynamic light scattering). Whereas well-dispersed colloidal NS did not significantly affect the hydration of CSA at the investigated ages. SP incorporation improved the dispersion of CSA cement particles, resulting in a 10% increase in the degree of hydration of ye’elimite at 28 days for the system without NS. Conversely, when the SP was incorporated in NS-containing mixtures, it hindered cement hydration of the systems with powdered NS, but did not significantly affect the cement hydration of the system containing colloidal NS. The SEM images suggested that the SP changed the ettringite morphology, thereby negatively affecting the mechanical strength of the CSA pastes.
Binary systems composed of Portland cement (PC) and calcium sulfoaluminate (CSA) cement have stood out for applications requiring high early strengths. Nevertheless, the application of these systems may be limited due to their properties in the fresh state, which requires a better understanding of the rheological behavior of these materials. Thus, this study evaluated the incorporation of different polycarboxylate-based superplasticizer (SP) contents (0.15, 0.20, and 0.25 wt%) on PC and PC-CSA binary cement pastes. Rotational rheometry, isothermal calorimetry, X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), and nitrogen adsorption and desorption tests to assess the pore size distribution of cement pastes were conducted. While the SP incorporation reduced the dynamic yield stress of PC pastes, it progressively increased the yield stress of PC-CSA systems. The increase in SP content increased the main heat flow peak of PC-CSA pastes, although it did not significantly affect the cumulative heat after 160 h of hydration. FTIR and XRD confirm higher ettringite contents in the binary systems and indicate the presence of carboaluminates phases after 7 d of hydration in both PC and PC-CSA and hemicarboaluminate in PC-CSA pastes. The CSA incorporation reduced the cumulative pore volume by up to 32% compared to PC pastes, while the SP content evaluated did not significantly affect the porosity of PC-CSA pastes.
For the construction of hot water storage tanks, ultra high performance concrete proofed to be a suitable building material to ensure water tightness. Common storage tanks build with concrete are designed to endure temperatures up to 90 °C. To increase the energy efficiency however, modern tanks need to withstand temperatures above 100 °C. With increasing temperature and correlating water vapor pressures, the cement must meet new requirements. Thermodynamic modelling is a promising tool for predicting the phase stabilities of minerals in the cement within these temperature and pressure ranges (T/P). Thus, mixture designs can be investigated and optimized with regard to the expected mineral phases in selected T/P-ranges. Additionally, predictions of the long-term material behavior can be derived from thermodynamic data and subsequently the experimental effort can be reduced notably. On the other hand, validation of predictions is needed. The base for the thermodynamic model is a thermodynamic equilibrium and thus, the experimental data for validation should approach the presumed conditions of the equilibrium. This study investigates variable experimental conditions for the hydration of Portland cement at 100 °C to reach a sufficiently progressed development of the phase composition. In case of Portland cement, the highest degree of hydration achievable within a reasonable time span is the most significant parameter. Therefore, Portland cement pastes with w/c ratios from 0.4 to 0.6 and dwell times up to three weeks were examined with powder X-ray diffraction to identify mineral phase changes. At 100 °C and high humidity, Portland cement paste shows the expected mineral phases like portlandite, katoite, and remaining clinker phases. The cement pastes with high water content and long dwell time seem to have the highest degree of hydration, even though the AFm phases stabilize with increasing w/c ratio. A dwell time of two weeks and a w/c ratio of 0.5 was found to provide the mineral composition with the highest degree of hydration including the major phase transitions.
The adaption of the set-up for gas permeability measurements for ultra-high performance concrete
(2022)
In the framework of this project, a steam pressure vessel was to be developed from ultra-high perfor-mance concrete (UHPC) to withstand process temperatures of 200 °C and the respective steam pressure of 15,5 bar. To guarantee the long-term water vapour tightness of the system, the permeability of two UHPC mixtures were tested after long-term cyclic autoclaving. As UPHC shows a high density and therefore low permeability, measurements after the RILEM-Recommendation (TC 116-PCD) reached their detection limit. Therefore, the measurement set-up was adapted to measure the permeability of highly dense UHPC more reliably and quickly. This adaption includes measurements in a higher pres-sure range, the change of sample size thickness and the usage of Ar as a medium compared with the RILEM Recommendation. Additionally, the system was equipped with two pressure sensors and Ar-flowmeters to guarantee a continuous record of the experimental parameters. The new system was tested and evaluated by comparing measurements with the RILEM recommended system. Preliminary results show that the adapted system is capable to provide efficient and reliable results of concrete with low permeability.
Tricalcium aluminate (C3A) is found with less than 10% wt. of the total composition; however, during hydration, C3A plays an important role in the early hydration of cement in the presence of gypsum as a set retarder.
The aim of this investigation is to assess the suitability of optical spectroscopy and a dye-based optical probe to monitor early hydration of C3A in the presence of gypsum and hemihydrate. Optical evaluation was performed using steady-state fluorescence and diffuses reflectance spectroscopy (UV-VisDR). Phase characterization during hydration was done with in-situ X-ray diffraction. UV-VisDR with a cyanine dye probe was used to monitor the formation of metastable phases and was employed together with fluorescence spectroscopy, to follow the Aggregation and disaggregation of the dye during hydration. In conclusion, for the first time, a cyanine dye was identified as a feasible and stable probe to monitor C3A hydration changes in the presence of calcium sulfate.
Nonclassical crystallization typically occurs via the attachment of individual nanoparticles. Intuitively, materials synthesized via this route should exhibit pronounced surface roughness and porosity as a hallmark of the formation process via particle accretion. Here, we demonstrate that nonclassical mineralization of calcium carbonate allows synthesis of ultra-smooth and dense surfaces with unprece-dented root-mean-square roughness of 0.285 nm, simply by con-trolling the hydration state of the nanosized building blocks using Mg doping. High fidelity coating of corrugated substrates can even be achieved. Nonclassical crystallization can thus lead to space-filling inorganic solid-state materials transgressing the implicit porosity commonly expected for particle-driven self-organization processes.
Building materials consist of cement, water and chemical admixtures, which adjust cement paste properties. They can act beyond their aimed functions causing changes in hydration course. The mechanisms are still under investigation. We investigate cement hydration in levitated droplets using an ultrasonic levitator. Hydrate phase formation is followed in situ by synchrotron XRD. The data allows detailed conclusions about the mechanisms of the admixture action in the ongoing hydration reactions.
Chemical admixtures like superplasticisers or stabilising agents are of ever increasing importance for modern concrete technology. They liberate the workability of concrete from its dependency on water content, and thus, open the gate towards innovative and future oriented concrete technologies such as selfcompacting concrete. Meanwhile admixtures have become common practice in concrete technology, but the understanding of these highly complex polymers in the entire concrete system lags far behind their application. Due to its complex time-dependent, multi-phase and multi-scale behaviour, flowable concrete systems are highly complicated and cannot be described comprehensively by simple models. It is therefore extremely challenging to identify the relevant parameters that predominantly control flow phenomena on different size scales, since these may occur on any scale between the nano scale (e.g. superplasticizer adsorption) and macro scale (e.g. grading of the aggregates). The present study discusses fundamental mechanisms at the interface between particle or hydrate surfaces and the fluid phase at a very early stage of concrete formation, and links these effects to macroscopic flow phenomena. Methods are discussed that appear promising interdisciplinary tools for enhancement of the understanding of the relevant interactions that are responsible for the macroscopic flow of flowable concrete.