The failure of composites is initiated by imperfections on microscale. The interface between fiber and matrix is a key parameter concerning failure initiation. In order to get an improved understanding of local failure processes a fracture mechanical analysis of interfacial failure in a composite ply under transverse stresses is performed. The mixed mode energy release rate is calculated. In addition the failure of interfaces under cyclic loading is studied on a single fiber model. The quasistatic debonding process is compared with the interfacial failure under fatigue loading. It is shown that the tan delta can be used as an indicator for the damage propagation.