The X-ray intensities of the K-, L- and M-lines of copper, zirconium and tungsten have been measured with an energy-dispersive X-ray spectrometer of known efficiency as function of photon energy. X-ray production efficiencies were determined from the measured intensities for Kα- and L-series of Cu and Zr and for the L- and M-series of W. These data were compared to calculated X-ray production efficiencies based on the widely used matrix correction models of Pouchou and Pichoir (XPP) and Bastin (PROZA96).
Our results indicate that a replacement of the stopping power in the PROZA96 algorithm by expressions of Joy and Jablonski has only a minor influence on the calculated X-ray production efficiencies. In contrast, the modifications of the ionization cross-section show a stronger effect. We replaced the ionization cross-sections for K lines of the PROZA96 algorithm with different models.
The results for L- and M-Lines are different. For the L-lines of Cu the original XPP and PROZA96 models show the best agreement while using the Bote cross-sections result in an overestimation. For the Zr-L and W-L1, -L2, -L3 X-ray production efficiencies, the Bote cross-sections lead to a significant improvement compared to all other models. The original XPP model represents the best agreement for the M5 efficiencies but underestimates the M4 efficiencies.
There is no superior model or modification because the parameter sets in the models need to be aligned to each other. However, using the ionization cross-sections of Bote, which are based on quantum mechanical calculations, show promising results in many cases.
Since geothermal wells are a feasible energy source to replace fossil fuel supply, many technologies have been developed to take advantage of geothermal energy. Nevertheless, service conditions in geothermal facilities are in many cases extreme in terms of corrosion due to the chemical composition of hydrothermal fluids and temperatures. Therefore, materials selection based on preliminary material qualification is essential to guarantee a secure and reliable operation of the facilities. During operation of a geothermal research facility in Groß Schönebeck copper and lead effects have been found downhole. Occurring mechanisms and measures to prevent precipitation or scaling needed to be investigated as well as potential influences of such precipitates on corrosion resistance of metallic materials used for equipment.
This contribution deals with the evaluation of the corrosion behavior of carbon steel and corrosion resistant alloys in copper and/or lead containing artificial geothermal water, simulating the conditions in the Northern German Basin.
The behavior of these materials in an artificial geothermal water obtained by electrochemical measurements and exposure tests are presented. While carbon steel exhibits precipitation and deposition, higher alloyed material shows different response to such species and a higher resistance in saline geothermal water.
Basing on these results the suitability of the investigated corrosion resistant alloy is given for use in such conditions, whereas carbon steel creates difficulties due to its susceptibility to Cu- and Pb-precipitation.
Significant Cu-deposition and precipitation only occurred in combination with carbon steel. High-alloyed materials prevent the disturbing Cu-agglomeration. Pb-deposition and precipitation only occurred in combination with carbon steel. No negative Pb-effect could be observed in combination with high-alloyed steels. High alloyed corrosion resistant alloys are suitable and shall be chosen for future design of the piping system, either in massive or in cladded form, to prevent unwanted interactions with brine components.
Efforts towards digitalization in the material science and technology community have enhanced in the last years. In 2019 the German digitalization initiative platform „MaterialDigital“1 (MD) has been started. Numerous projects concerning digitalization, including the copper related project „KupferDigital“ (copper digital) have been initiated under the umbrella of MD. The initiative strives to
address numerous issues concerning data access, exchange, security, provenance and sovereignty. Heterogeneous data origin, storage and evaluation often result in problems concerning comparability and reproducibility of scientific and technological results. In many cases material data are recorded, but the methods of testing are insufficiently described, or such information is not communicated along with the raw data. The material data can also have numerous different formats such as paper printouts, pdfs, excel sheets or csv-files. Hence, gathering and integrating material data from different sources is challenging for potential users like materials scientists and engineers, especially if there are contradictory data where the reasons for contradictions is not clear due their vague description. In order to address these problems, data should comply to the so called „FAIR“ principle which calls for data to be findable, accessible, interoperable, and reusable (FAIR)2 and hence be accessible via so-called decentralized but interconnected data spaces. By using knowledge representation withontologies, data can be enriched with meaning and the methods of the testing procedures can be accurately provided. In this presentation we want to introduce our approach to such knowledge representation based on a high-throughput alloy development process for Cu-based alloys³ along with characterization techniques such as hardness testing and microstructural characterization (e.g. EBSD – Electron Backscattered Diffraction).
A large amount of publicly available data is reproduced every day in the field of materials science, while these kind of material data can have different formats and types like paper-type publications, standards, datasheets or isolated datasets in repositories. However, gathering a specific library from such extensive and diverse material data is always challenging for the materials scientists and engineers, since the time-related limitations are not allowed to fully access the large publicly available databases; search across these disparate databases, manage the large volumes of heterogeneous datasets, and integrate data from multiple sources. To address these challenges and make data findable, accessible, interoperable, and reusable (FAIR), an efficient data management system is necessary to build comprehensive, documented, and connected data spaces in the future. A formal standardized knowledge representation through an ontology can address such problems and make data more available and interoperable between related domains. Ontology can also rich machine processable semantic descriptions that increases the performance of scientific searches. In this regard, the Platform MaterialDigital (PMD) is currently working on developing a high-level ontology for the materials and material related processes. For example, in one of the PMD projects of “KupferDigital”, we will try to develop a data ecosystem for digital materials research based on ontology-based digital representations of copper and copper alloys. As a case study, this paper describes the methodology for ontology development of Brinell hardness, based on PMD core ontology. The methodology we describe includes the following steps; gathering the required domain terminology from different resources like standards (DIN EN ISO 6506-1) and test reports, representing the performance of a standard-conformant hardness test and the treatment of the recorded values up to a “reportable” hardness value for a material, designing the process chain according to the semantic technologies, and developing a domain-level ontology of Brinell hardness based on PMD ontology semantic formalization. Apart the mentioned methodology, some interesting tools and methods were introduced and ontology design challenges and possible solutions for modelling materials and processes were discussed. Furthermore, a dataset from the Brinell hardness measurement of cast copper samples is prepared for testing the query process.
Significant Cu-deposition and ‑precipitation only occurred in combination with carbon steel. High-alloyed materials prevent the disturbing Cu-agglomeration. Pb-deposition and ‑precipitation only occurred in combination with carbon steel. No negative Pb-effect could be observed in combination with high-alloyed steels. High alloyed corrosion resistant alloys are suitable and shall be chosen for future design of the piping system, either in massive or in cladded form, if formation of crevices with non-metallic materials can be excluded!
Influence of Precipitating Brine Components on Materials Selection for Geothermal Applications
(2021)
Since geothermal wells are a feasible energy source to replace fossil fuel supply, many technologies have been developed to take advantage of geothermal energy. Nevertheless, service conditions in geothermal facilities are in many cases extreme in terms of corrosion due to the chemical composition of hydrothermal fluids and temperatures. Therefore, materials selection based on preliminary material qualification is essential to guarantee a secure and reliable operation of the facilities. During operation of a geothermal research facility in Groß Schönebeck copper and lead effects have been found downhole. Occurring mechanisms and measures to prevent precipitation or scaling needed to be investigated as well as potential influences of such precipitates on corrosion resistance of metallic materials used for equipment.
This contribution deals with the evaluation of the corrosion behavior of carbon steel and corrosion resistant alloys in copper and/or lead containing artificial geothermal water, simulating the conditions in the Northern German Basin.
The behavior of these materials in an artificial geothermal water obtained by electrochemical measurements and exposure tests are presented. While carbon steel exhibits precipitation and deposition, higher alloyed material shows different response to such species and a higher resistance in saline geothermal water.
Basing on these results the suitability of the investigated corrosion resistant alloy is given for use in such conditions, whereas carbon steel creates difficulties due to its susceptibility to Cu- and Pb-precipitation.
Influence of Precipitating Brine Components on Materials Selection for Geothermal Applications
(2021)
By exposure and electrochemical tests in the laboratory the Cu- and Pb-effect on corrosion behavior and performance of carbon steel and a corrosion resistant alloy could be assessed. Critical material specific properties were determined by static exposure and electrochemical tests in artificial geothermal water with high salinity and low pH, containing Cu/Pb.
It could be shown that significant Cu- resp. Pb-deposition and precipitation only occurred in combination with carbon steel. Corrosion resistant alloys (e. g. Cr- and Ni-dominated stainless steels) prevent the disturbing Cu-agglomeration resp. Pb-deposition. Therefore, they are suitable to be chosen for future design of geothermal piping system, either in massive or in cladded form. Regarding corrosion, formation of crevices with non-metallic materials shall be avoided.
So, in addition to its already known limited corrosion resistance, carbon steel shall not be used when copper or lead species are content of the geothermal brine. Otherwise precipitation and/or deposition of metallic copper resp. lead must be expected, increasing the susceptibility of clogging the piping system.
From the interactions and pitting corrosion point of view, corrosion resistant alloys (preferably Ni-rich) seem to be most favorable when selecting materials for applications in such geothermal brines.
Geothermal brines often contain high amounts of lead and copper ions that can precipitate as native Cu and Pb as consequence of galvanic corrosion when brines react with carbon steel materials. This contribution evaluates which materials could overcome the problem of galvanic corrosion at geothermal environment.
The behavior of these materials in water containing high chloride concentration (> 100 g/L NaCl) as well as various amounts of dissolved bCl2 and/or CuCl2 was characterized by electrochemical and exposure measurements.
Both methods reveal carbon steel suffers corrosion susceptibility, accompanied by Cu◦ and/or Pb◦ precipitation on the surface. Electrochemical measurements on stainless steels result in significant difference in corrosion and repassivation potentials (Ecorr = -189 mV, Erep = 70 mV), indicating a good corrosion resistance.
Since geothermal wells are a feasible energy source to replace fossil fuel supply, many technologies have been developed to take advantage of geothermal energy. Nevertheless, service conditions in geothermal facilities are in many cases extreme in terms of corrosion due to the chemical composition of hydrothermal fluids and temperatures. Therefore, materials selection based on preliminary material qualification is essential to guarantee a secure and reliable operation of the facilities. During operation of a geothermal research facility in Groß Schönebeck copper and lead effects have been found downhole. Occurring mechanisms and measures to prevent precipitation or scaling needed to be investigated as well as potential influences of such precipitates on corrosion resistance of metallic materials used for equipment.
This contribution deals with the evaluation of the corrosion behavior of carbon steel and corrosion resistant alloys in copper and/or lead containing artificial geothermal water, simulating the conditions in the Northern German Basin.
The behavior of these materials in an artificial geothermal water obtained by electrochemical measurements and exposure tests are presented. While carbon steel exhibits precipitation and deposition, higher alloyed material shows different response to such species and a higher resistance in saline geothermal water.
Basing on these results the suitability of the investigated corrosion resistant alloy is given for use in such conditions, whereas carbon steel creates difficulties due to its susceptibility to Cu- and Pb-precipitation.
By exposure and electrochemical tests in the laboratory the Cu-effect on corrosion behavior of carbon steel, high-alloyed steels and Ti-alloy can be assessed.
Critical materials specific properties were determined by static exposure and electrochemical tests in an artificial geothermal water with high salinity and low pH, containing Cu. Conclusions were drawn using characteristic potential values.
It could be shown that significant Cu-deposition and -precipitation only occurred in combination with carbon steel. High-alloyed materials (S31603, S31653, S31700, S31703, S31803 and N08904) prevent the disturbing Cu-agglomeration. Therefore, they are suitable to be chosen for future design of the piping system, either in massive or in cladded form, if formation of crevices with non-metallic materials can be excluded.
From the interactions and pitting corrosion point of view, R50400 seems to be most favorable.
The elemental dissolution of Cu-Zn alloys was investigated as a function of Zn content ranging from 0 to 45 wt%. Atomic emission spectroelectrochemistry (AESEC) was utilized to directly monitor Cu2+ and Zn2+ release and oxide growth as function of time during potentiodynamic experiments. It was determined that Cu dissolution undergoes a simultaneous mechanism of Cu2O formation and Cu2+ release. The addition of Zn in Cu-Zn alloy does not measurably change the dissolution mechanism of Cu2+ and the rate of aqueous Cu2+ was only dependent on the potential. Zn dissolution was however blocked by the formation of a Cu(0) film which shifted the Zn dissolution in the anodic direction.
The elemental dissolution of Cu-Zn alloys was investigated as a function of Zn content ranging from 0 to 45 wt%. Atomic emission spectroelectrochemistry (AESEC) was utilized to directly monitor Cu2+ and Zn2+ release, oxide growth, and the enrichment of Cu metal as function of time during potentiodynamic experiments. It was determined that Cu dissolution undergoes a simultaneous mechanism of Cu2O formation and Cu2+ release. The addition of Zn in Cu-Zn alloy does not measurably change the dissolution mechanism of Cu2+ and the rate of aqueous Cu2+ was only dependent on the potential. Zn dissolution was however blocked by the formation of a Cu(0) film which shifted the Zn dissolution in the anodic direction.
Finally, this book fulfills its intension of facilitating the materials selection regarding current technical and normative aspects for all users, recyclers, test personnel and byers of Cu-materials in all kinds of applications. The well-structured data provide a reliable help for making decisions when applying or using Cu-alloys within the daily business. It shall not be missed in their book-shelfs.
The book „Electropolishing“ by M. Buhlert is dealing with the electrolytic brightening, smoothing and deburring of technical materials like steel, copper, brass, aluminum, titanium and magnesium. The book content covers the basics and the main influencing parameters of the electropolishing process and provides detailed and application orientated procedure information for technical relevant materials.
After a brief introduction into the topic of electrolytic polishing in the first chapter, the author gives a detailed description of the basic electrochemical reaction mechanisms in the second chapter. The reader will also be informed about the physical and chemical parameters, which control the electrochemical removal process. Additionally, the author reports about the advantages and disadvantages of electropolishing.
The third chapter provides a detailed insight into the influencing manufacturing parameters affecting the results of the electropolishing process. Distinct aspects of the manufacturing e.g. workpiece preparation, electrolyte composition, polishing time, electrolyte temperature and alloy compositions will be discussed in detail by the author.
In the fourth and fifth chapter, the author gives useful hints and information about the parameter variation and the suitable handling of hull cells for the optimization of the removal process, followed by a particular overview about material specific electrolyte mixtures for common-used technical metals and alloys, like steel, aluminum, brass, magnesium, copper and titanium.
The sixth chapter of the book provides many selected manufacturing results and investigations on electropolishing of different metals and alloys, which allows the reader the opportunity to develop a systematic understanding of the topic and to adopt the knowledge on the optimization of his own electropolishing process.
Finally, the book concludes with a brief chapter about some remarks with respect to the work safety and environmental efforts.
In summary, this book contains a very detailed and clear arranged overview about the electropolishing method for the surface optimization process. For this reason, it is a suitable and useful lecture for people, which want to take an in depth look into the topic in order to start using this method or are interested in optimize their existing electropolishing processes.
Circumventing boundary effects while characterizing epoxy/copper interphases using nanoindentation
(2017)
Characterization of the size and mechanical properties of interphases is essential when designing multicomponent materials. When nanoindentation is used to investigate the size and mechanical properties of an interphase, a common challenge is that the indenter or the stress zone formed around it are often restricted by the reinforcement, making it difficult to distinguish the mechanical property variations caused by the interphase itself from those caused by the boundary effect. In this work, a testing system was developed that allows determining the indent affected zone and accounting for it in the interphase measurements of an epoxy/Cu system. Using finite element analysis, we confirmed the validity of the proposed system. Nanoindentation was used to investigate the Interphase between copper and two different epoxy systems; amine-cured and anhydride-cured. Nanoindentation results showed that a copper layer that is only 10 nm thick still exhibits a constriction effect on the indentations in its vicinity. The amine-cured epoxy did not show any sign of interphase existence using the introduced method. However,
a soft interphase with a thickness of ~1.7 μm was measured on theanhydride-cured epoxy. Furthermore, we show that the proposed system can be used to determine the interphase thickness as well as its relative mechanical properties regardless of the indentation depth.
This system can be further used for investigating other polymer/metal interphases to better understand the factors influencing them, thus helping engineer the interphase size and properties to enhance composite performance.
Copper is one of the most important components in brake pads and its amount can reach up to 14%. In spite of a number of positive features copper usage in brake pad formulations has recently become the subject of considerable discussions, primarily due to concerns about potential risks related to environmental impacts of copper particles. So, for developing new pad formulations with possible replacements of copper content, it is very important to understand the functionality of copper additions to brake friction materials. In the paper theoretical investigation of the role of copper as a pad ingredient was carried out on the basis of modelling by the method of movable cellular automata (MCA). Our previous studies show that copper as a constituent of the tribofilm formed during braking provides smooth sliding by forming a granular layer of mechanically mixed materials from the friction layers. In the present study the concentration of copper particles in a Fe3O4-matrix was varied systematically in the range 5.5-28 vol. % and compared to mixtures with the same amount of graphite nanoparticles. The sliding simulations were performed while assuming material properties at 500°C in order to assess the beneficial role of copper during severe braking conditions corresponding to fading cycles during dynamometer testing.
For inspection of thick-walled (50mm) copper canisters for final disposal of spent nuclear fuel in Sweden, ultrasonic inspection using phased array technique (PAUT) is applied. Because thick-walled copper is not commonly used as a structural material, previous experience on Phased Array Ultrasonic Testing for this type of application is limited. The paper presents the progress in understanding the amplitudes and attenuation changes acting on the Phased Array Ultrasonic Testing inspection of copper canisters. Previous studies showed the existence of a low pass filtering effect and a heterogeneous grain size distribution along the depth, thus affecting both the detectability of defects and their "Probability of Detection" determination. Consequently, the difference between the first and second back wall echoes were not sufficient to determine the local attenuation (within the inspection range), which affects the signal response for each individual defect. Experimental evaluation of structural attenuation was carried out onto step-wedge samples cut from full-size, extruded and pierced&drawn, copper canisters. Effective attenuation values has been implemented in numerical simulations to achieve a Multi Parameter Probability of Detection and to formulate a Model Assisted Probability of Detection through a Monte-Carlo extraction model.
The canister for the permanent storage of spent nuclear fuel used by SKB in Sweden consists of a cast iron insert surrounded by a five centimetre thick shell of copper. It is a safety critical component and in order to secure long-term structural integrity non-destructive methods are used to inspect 100% of the volume of each canister, before it is disposed of in the repository. One of the critical components that requires inspection is a sealing weld, joining the copper tube and the lid. The friction stir weld is inspected using an ultrasonic phased array system. The area of the weld is inspected with several inspection channels with different angles and varying coverage. To make sure that no defects that might occur in the weld are overseen, the reliability of the inspection must be quantified. The reliability of NDT is usually quantified with the probability of detection curves. The influence of the parameters that might influence the POD of the flaws in the weld is investigated analysing the experimental results, as well as with a help of a numerical simulation of the inspection.
The canister for the permanent storage of spent nuclear fuel used by SKB in Sweden consists of a cast iron insert surrounded by a five centimetre thick shell of copper. It is a safety critical component and in order to secure long-term structural integrity non-destructive methods are used to inspect 100% of the volume of each canister, before it is disposed of in the repository. One of the critical components that requires inspection is a sealing weld, joining the copper tube and the lid. The friction stir weld is inspected using an ultrasonic phased array system. The area of the weld is inspected with several inspection channels with different angles and varying coverage. To make sure that no defects that might occur in the weld are overseen, the reliability of the inspection must be quantified. The reliability of NDT is usually quantified with the probability of detection curves. The influence of the parameters that might influence the POD of the flaws in the weld is investigated analysing the experimental results, as well as with a help of a numerical simulation of the inspection.