The longitudinal and transverse strength of three unidirectional thermoplastic prepreg systems: carbon fiber/polypropylene (CF/PP), polyamide 6 (CF/PA6), and polyphenylene sulfide (CF/PPS) are studied and analytical formulas are proposed for the estimation of matrix and fiber/matrix interface properties from composites properties. Since the matrices are semi-crystalline thermoplastics, the influence of cooling rate on the strength is statistically evaluated. While the 0° tensile strength is found to be independent of the cooling rate, the 90° tensile strength is strongly influenced by the matrix type and cooling rate. The matrix modulus increases as the cooling rate is decreased; the degree of crystallinity also increases. The matrix residual stress, interfacial shear strength, and mode II interlaminar fracture toughness are also found to depend on the cooling rate, with the trends different for different matrices.
Three high-strength Nb-,.Ti- and Ti+ V-bearing S690QL steels were welded to investigate and compare the effects of microalloy addition on heat-affected zone (HAZ) toughness. Charpy V notch impact tests from three microalloyed welds under different cooling rates have been performed. Fractographic examination shows that several factors, including large-sized grain, upper bainite or hard second phase, interact to determine brittle fracture and impaired toughness in Nb-bearing weld with high heat input. In contrast to this reduced toughness, Ti-bearing welds exhibits satisfied toughness regardless of at fast or slow cooling. This is attributed to its limited austenite grain and refines favorable intragranular acicular ferrite structure. Moreover, in the case of such refined structure as matrix, TiN particles are found to be irrelevant to the facture process. The crystallographic results also confirm that high-angle boundaries between fine ferrites plates provide effective barriers for crack propagation and contribute to improved toughness.
Three high strength Nb-, Ti- and Ti+V- bearing S690QL steels were welded to investigate and compare the effects of microalloy addition on HAZ toughness. Charpy V notch impact tests from three microalloyed welds under different cooling rates have been performed. Fractographic examination shows that several factors including large-sized grain, upper bainite or hard second phase, interact to determine the brittle fracture mode and impaired toughness of Nb bearing weld at high heat input. In contrast to this reduced toughness, Ti bearing welds exhibits satisfied toughness regardless of at a fast or slow cooling rate as a result of limited austenite grain and refined favourable intragranular acicular ferrite structure. Moreover, in the case of such refined structure as matrix, TiN particles are found to be irrelevant to the fracture process and crystallographic misorientation results also confirms that high angle boundaries between fine ferrites plates provide much effective barrier for crack propagation and contribute to improved toughness.
Effect of cooling rate on microstructure and properties of microalloyed HSLA steel weld metals
(2015)
Two high strength Nb/Ti microalloyed S690QL steels were welded with identical filler material, varying welding parameters to obtain three cooling rates: slow, medium and fast cooling. As cooling rate increased, the predominantly acicular ferrite in Nb weld metal (WM) is substituted by bainite, with a consequence of obvious hardness increase, but in Ti WM, no great variation of acicular ferrite at all cooling rates contributed to little increment of hardness. The transition between bainite and acicular ferrite has been analysed from the point view of inclusions characteristics, chemical composition and cooling rate. Excellent Charpy toughness at 233 K was obtained with acicular ferrite as predominantly microstructure. Even with bainite weld of high hardness, the toughness was nearly enough to fulfill the minimal requirements. WM for Ti steel showed to be markedly less sensitive to the variations of cooling rate than that for Nb steel.
As consequence for increasing threats by IEDs (Improvised Explosive Devices) on vehicles, the blast resistance of the welded frames and bodies becomes increasingly important. Considering vehicle welds subjected to blasting, the real configurations of the joints in the structure and the position of the blast loads have to be considered. The present contribution thus focuses on a weld joint at the explosion endangered wheel well of a tactical truck. The high-strength steel welds were subsequently impacted by explosion loads within the upper range from those experienced in practical military operation to cause not only deformation, but also to investigate the ultimate fracture behaviour of the high-strength weld. The interaction between cooling time t8/5 and displacement, crack path as well as fracture surface was analysed. The analyses of the fracture surfaces revealed ductile overload failure and also the size of the dimples was influenced by the cooling time t8/5. As a prominent feature, these investigations showed that the crack path of such high-strength steel welds under blasting is less influenced by the final hardness level in the respective weld microstructures but much more affected by the hardness gradient at the fusion line and inside the Heat Affected Zone (HAZ).