Composition and microstructure stability of cement compound under cyclic hydrothermal condition
(2020)
There have been many researches focused on the performance improvement of ultra-high performance concrete (UHPC) by autoclaving treatment. The goal of autoclaving is to increase the pozzolanic reaction, and to densify the cement stone and the transition zone which originates from the incorporation of supplementary cementitious materials (SCMs), such as silica fume, fly ash and blast furnace slag. Due to the superior properties, UHPC can also be utilized under high mechanical load and aggressive condition, for example, the fabrication of water tanks for thermal storage which is of great significance for saving energy and reducing CO2 emission. It is known that mineral stability of the hydration products of an inorganic binder is highly related to the temperature and pressure of the environment. A certain stable composition at room temperature, however, may undergo a phase transformation at high temperature and the performance decrease under this severe condition will generally be more severe. In this way, the rationale behind this deterioration under long-term hydrothermal condition involving many cycles and long duration has to be clarified, and then appropriate optimizing methods will be performed in order to obtain a kind of construction with high durability under aggressive environment. For this purpose, different types and amounts of SCMs are introduced into the standard mixture of UHPC and the phase compositions after autoclaving at 200 °C and 15.5 bar are determined by combined X-ray diffraction and scanning electron microscope. Mercury intrusion porosimeter is used to characterise the microstructure of the samples. In order to establish the relationship between microstructure and macroscopic properties, compressive and flexural strength are also investigated.
Composition and microstructure stability of cement compound under cyclic hydrothermal condition
(2020)
There have been many researches focused on the performance improvement of ultra-high performance concrete (UHPC) by autoclaving treatment. The goal of autoclaving is to increase the pozzolanic reaction, and to densify the cement stone and the transition zone which originates from the incorporation of supplementary cementitious materials (SCMs), such as silica fume, fly ash and blast furnace slag. Due to the superior properties, UHPC can also be utilized under high mechanical load and aggressive condition, for example, the fabrication of water tanks for thermal storage which is of great significance for saving energy and reducing CO2 emission. It is known that mineral stability of the hydration products of an inorganic binder is highly related to the temperature and pressure of the environment. A certain stable composition at room temperature, however, may undergo a phase transformation at high temperature and the performance decrease under this severe condition will generally be more severe. In this way, the rationale behind this deterioration under long-term hydrothermal condition involving many cycles and long duration has to be clarified, and then appropriate optimizing methods will be performed in order to obtain a kind of construction with high durability under aggressive environment. For this purpose, different types and amounts of SCMs are introduced into the standard mixture of UHPC and the phase compositions after autoclaving at 200 °C and 15.5 bar are determined by combined X-ray diffraction and scanning electron microscope. Mercury intrusion porosimeter is used to characterise the microstructure of the samples. In order to establish the relationship between microstructure and macroscopic properties, compressive and flexural strength are also investigated.
A research project of reconstructing historical gold mosaics deals with reconstructing weatherproof gold and silver mosaics according to historical models.
The gold mosaics examinded originate mainly from germany from 1880 to 1920 and are composed of three parts. They consist of a matching support glass, the gold or silver layer and a cover glass. By examining the morphology and layer thicknesses with the ESEM, and using chemical analysis with the EDX, the relationship of glass composition and damage patterns was established. The glass analysis provided quantitative composition data and made it possible to determine its chemical stability. It supplied the basis for calculating glass characteristics and was referred to when casting suitable historical mosaic glass. The analysis of the qualitative composition of the gold and silver layers also served as a model for reconstruction. After testing selected reconstructed gold mosaics in the climate chamber, the ESEM was used for capturing leaching and other process data and the glass composition was optimized accordingly. Over 100 predominantly historical gold mosaics were analyzed and the results entered into a database which can now be consulted for comparative investigations to determine both origin and date.
Using channeling-enhanced energy-dispersive X-ray spectroscopy (EDX), we demonstrate polarity sensitive orientation determination of a non-centrosymmetric crystal in the scanning electron microscope. The authors observe a characteristic asymmetry in the channeling-enhanced, angle-dependent EDX data of a GaAs sample, which is in good agreement to simulations using the dynamical theory of diffraction for the incident electron beam. This allows us to assign the orientation of the GaAs crystal according to the non-centrosymmetric point group. The method shown here overcomes the limitation of a reduced point-group sensitivity of electron backscatter diffraction Patterns and electron channeling patterns for crystalline phases that contain atoms of approximately equal electron scattering cross sections.