An effective method for evaluating the fatigue strength of thick unidirectional composite laminates of wing spar caps has been presented here. A typical width-tapered bending specimen has been developed for a four-point loading set up. Static and fatigue loading was performed at a load ratio R = -1. The complex stress state has been investigated numerically by finite element analysis. Finally, the concept is proven experimentally on specimens made of pultruded fibre rods.
The fatigue behavior of the continuously tapered width by water Jet cutting has been compared to discrete tapering via rod-drop. The new method enables a screening of material fatigue behavior caused by normal and shear loading.
Composite pressure vessels for transporting dangerous goods and for hydrogen and natural gas vehicles consist of a load-bearing composite and a gas-tight, metallic or polymeric barrier layer (liner). To investigate the aging behavior of such composite pressure vessels, BAM carried out the interdisciplinary project COD-AGE. The aim of the project was the development of methods and models for the description and determination of the aging behavior of carbon fiber composites using the example of pressure vessels in order to better predict aging and safe working life. One focus of this project was the provision of suitable NDT methods. These included both test-related tests and the possible development of test equipment for later practical use.
In the lecture, test results of the age-related eddy current test on composite pressure vessels are presented.
In aging tests, pressure vessels made of an approximately 4 mm thick aluminum liner and approx. 8 mm thick CFRP layer were examined. Typical application of such pressure vessels are respiratory protective devices of the fire department. The pressure vessels were tested using conventional eddy current technology from the outer and inner side as well as with high-frequency eddy current technology. Both damage to the metallic liner and structures of the CFRP could be detected. A particular mechanical challenge was the inspection of the inside of the liners, since a cylindrical surface with an inside diameter of 150 mm has to be tested with an access of only 15 mm diameter.
Impact damages and delaminations in fibre-reinforced composites (FRC) might not be visible at the surface, but could have an influence on the resistance and on the long-term behaviour of the component. Therefore, and especially for safety relevant structures, non-destructive methods are required for the assessment of such damages.
Active thermography methods are suitable to characterize damages after loading using different kind of excitation techniques and various configurations of infrared (IR) camera and heating sources. Here, flash lamps, impulse excitation with infrared radiator and lock-in technique with halogen lamps or widened laser beams are suited. In addition, non-optical sources like sonotrodes (requiring direct contact to the structure) or induction generators (only suited for carbon fibre reinforced polymer (CFRP) structures) could be applied as well. For the investigation of the evolution of the damage during the impact, passive thermography can be applied in-situ. Elastic and plastic deformations alter the temperature of the structure and thus the temperature on the surface.
In this contribution, at first the general principles of quantitative defect characterisation in FRC using active thermography with flash, impulse and lock-in excitation are described. Optical and thermal properties of the FRC material and its anisotropy are considered. Results of phase differences obtained at flat bottom holes with flash and lock-in thermography are compared for qualifying both methods for quantitative defect characterization. Secondly, the damage evolution of CFRP and GFRP structures under impact load and static tensile loading is described. The spatial and temporal evolution of the surface temperature enables us to distinguish matrix cracks or fibre-matrix separation from delaminations between the layers. Afterwards, all results for loading defects, obtained by passive and active thermography, are compared with each other. Fig. 1 and 2 show the difference of passive and flash thermography obtained at impact and tensile loaded CFRP plates, respectively. As one purpose of these investigations is the development of standards within national (DIN) and European (CEN) standardisation bodies, new draft and final standards are presented and further needs are discussed at the end of the presentation.
Quantification of impact damages in CFRP and GFRP structures with thermography and ultrasonics
(2018)
The extent of damage caused by impacts in fibre reinforced composites depends on the energy of the impacts, on the velocity and the shape of the impacting body, on the material and structure of the composite and on the geometry of the structure. Here, mainly the thickness of the component is essential. The non-destructive evaluation of these damages can be carried out using both ultrasound and active thermography methods. A comparison of the detection sensitivity of these methods for the different damages is carried out in this paper depending on the fibre composite material used (CFRP and GFRP), the thickness of the material and the impact energy. The NDT methods used after the damage are supplemented by thermographic measurements with high temporal resolution, which were already recorded during the impact.
For assuring the safety and reliability of components and constructions in energy applications made of fiber reinforced polymers (e. g. blades of wind turbines and tidal power plants, engine chassis, flexible oil and gas pipelines) innovative non-destructive testing methods are required. Within the EMRP project VITCEA complementary methods (shearography, microwave, ultrasonics and thermography) are further developed and validated. Together with partners from the industry, test specimens were constructed and selected on-site containing different artificial and natural defect artefacts. As base materials, carbon and glass fibers in different orientations and layering embedded in different matrix materials (epoxy, polyamide) were considered.
In this contribution, the validation of different techniques of active thermography like flash, step heating and lock-in thermography to these testing problems is presented. Experimental data are compared to analytical and numerical models. Among others shows that although flash and lock-in thermography have the same detectability of flat bottom holes in the phase images, the detectability of delaminations is different. In another example, it is demonstrated that for GFRP, the transmissivity of the material has to be considered for the quantitative data analysis.
Defects in FRP structures may be introduced during the processing and fabrication of composite components and can initiate or grow in-service. In the context of this JRP, the term ‚defect‘ refers to imperfections introduced during manufacture/processing and/or secondary machining operations, as well as damage sustained during a component‘s service life. One of the challenges facing accurate and repeatable defect detection in FRP composites is the multitude of defect types that exist, each with characteristics that present different challenges to the NDE practitioner. In order for a particular NDE technique to achieve broad acceptance by industry, it is desirable for the technique to be able to detect a range of defect types with a high level of confidence. Project VITCEA (Validated Inspection Techniques for Composites in Energy Applications) is developing and validating traceable procedures for novel NDE techniques with contrasting detection capabilities, which will underpin the increased use of FRP composites for improved efficiency and reliability in energy related applications e.g. wind and marine turbine blades, nacelles, oil and gas flexible risers.
Da kohlenstofffaserverstärkte Kunststoffe (CFK) in anspruchsvollen sicherheitsrelevanten Einsatzgebieten wie im Automobilbau und in der Luftfahrt eingesetzt werden, besteht ein zunehmender Bedarf an zerstörungsfreien Prüfmethoden. Ziel ist die Gewährleistung der Sicherheit und Zuverlässigkeit der eingesetzten Bauteile. Aktive Thermografieverfahren ermöglichen die effiziente Prüfung großer Flächen mit hoher Auflösung in wenigen Arbeitsschritten. Ein wichtiges Teilgebiet der Prüfungen ist die Ortung und Charakterisierung von Delaminationen, die sowohl bereits in der Fertigung als auch während der Nutzung eines Bauteils auftreten können, und dessen strukturelle Integrität schwächen.
In diesem Beitrag werden CFK-Strukturen mit künstlichen und natürlichen Delaminationen mit Hilfe unterschiedlich zeitlich modulierter Strahlungsquellen experimentell untersucht. Verwendet werden dabei Anregungen mit Blitzlampen und mit frequenzmodulierten Halogenlampen. Mittels Filterfunktionen im Zeit- und Frequenzbereich wird das Kontrast-zu-Rausch-Verhältnis (CNR) der detektierten Fehlstellen optimiert. Verglichen werden anschließend die Nachweisempfindlichkeit, das CNR und die Ortsauflösung der zu charakterisierenden Delaminationen für die unterschiedlichen Anregungs- und Auswertungstechniken. Ergänzt werden die Experimente durch numerische Simulationen des dreidimensionalen Wärmetransportes.
Flash thermography is a fast and reliable non-destructive testing method for the investigation of defects in carbon fiber reinforced polymer (CFRP) materials. In this paper numerical simulations of transient thermography data are presented, calculated for a quasi-isotropic flat bottom hole sample. They are compared to experimental data. These simulations are one important step towards the quantitative reconstruction of a flaw by assessing thermographic data. The applied numerical model is based on the finite-element method, extended by a semi-analytical treatment of the boundary of the sample, which is heated by the flash light. A crucial part for a reliable numerical model is the prior determination of the material parameters of the specimen as well as of the experimental parameters of the set-up. The material parameters in plane and in depth diffusivity are measured using laser line excitation. In addition, the absorption and heat transfer process of the first layers is investigated using an IR microscopic lens. The performance of the two distinct components of CFRP during heating – epoxy resin and carbon fibers – is examined. Finally, the material parameters are optimized by variation and comparison of the simulation results to the experimental data. The optimized parameters are compared to the measured ones and further methods to ensure precise material parameter measurements are discussed.
Similar to the success story of digital photography a major upheaval has been observed in digital industrial radiology. This paper is split into 3 parts:
Part 1: Film Replacement and Backscatter Imaging: Computed radiography with phosphor imaging plates substitutes film applications. Digital Detector Arrays enable an extraordinary increase of contrast sensitivity in comparison to film radiography. The increased sensitivity of digital detectors enables the efficient usage for dimensional measurements and functionality tests substituting manual maintenance. The digital measurement of wall thickness and corrosion status is state of the art in petrochemical industry. Photon counting and energy discriminating detectors are applied up to 300 Kv provide increased thickness dynamic and material discrimination by synchronously acquisition of images of the high and low energy part of the spectrum. X-ray back scatter techniques have been applied in safety and security relevant applications with single sided access of source and detector. First inspections of CFRP in aerospace industry were successfully conducted with newly designed back scatter cameras. Numeric modeling is used to design X-Ray optics and inspection scenarios as well as conducting RT training.
Part 2: Computed tomography (CT)
Part 3: Micro Radiography and Micro CT.
Faser-Kunststoff Verbunde und insbesondere Kohlenstofffaserverstärkte Kunststoffe werden bereits im Bereich der hohen (HCF) und sehr hohen Lastspielzahlen (VHCF) eingesetzt. Während statische Festigkeiten für diese Materialien bereits gut vorhersagbar sind, gibt es noch keine verlässliche Methode Schwingfestigkeiten zu bestimmen.
Vergangene Studien an Faser-Kunststoff Verbunden an der BAM zeigten, dass bei Schwingbelastung Mikrorisse und Zwischenfaserrisse bereits weit vor dem finalen Versagen auftreten. Diese Schäden erhöhen die innere Oberfläche des Materials. Die Änderung der inneren Oberfläche kann mittels der Röntgenrefraktion bestimmt werden.
Damit konnte im Rahmen der aktuellen Arbeit eine Lastgrenze ermittelt werden, bei der im untersuchten Lastwechselbereich keine Mikrorisse auftreten. Unter den gegebenen Material- und Versuchsparametern kann damit von einer ermittelten Dauerfestigkeitsgrenze gesprochen werden.
Nondestructive investigation of the VHCF-endurance on cyclically loaded CFRP by X-Ray-Refractography
(2016)
Carbon fiber-reinforced-plastics (CFRP) are already used under high-cycle- (HCF) and very-high-cycle-fatigue (VHCF) at relatively low loads not only in aerospace industry, but also in other growing markets like especially wind energy and increasingly also automotive industry. While the static strength of CFRP is satisfyingly predictable by means of layerwise-strenght-analysis and material data from single layers, it is more and more uncertain to predict residual strength or lifetime as the design lifetime increases. Previous studies showed that local minor cracks and inter-fiber-fracture (IFF) originate long before total failure of single layers. Reliable fatigue estimation for fiber-reinforced-plastics is not available at present. Subsequently safety-related primary structures made out of FRP are over dimensioned.
It is possible to detect the change of inner surface in a specimen by means of X-Ray-Refractography. This includes voids, intact fiber-matrix-interfaces as well as defective ones, cracks and all interfaces in plane with the X-Ray-beam. As the crack-density (including IFF) increases, the inner surface of the material correspondingly increases.
The borderline where even at high cycles no early cracks were detected was identified for selected laminates out of woven and non-crimped fabric with epoxy-matrix.
When no micro-cracks were detected up to 106 cycles, the specimens also lasted in the VHCF-regime. Furthermore for the epoxy resin LY556 in combination with carbon fiber it was distinguished that at a load minor to 50% IFF-load level, no micro cracks were detected and consequently the VHCF-endurance reached.
The integration of the set-up small-sized testing machine into the X-Ray buildup in order to achieve in-situ non-destructive detection of the crack initiation while loading the specimens (CFRP and GFRP- woven fabric and non-crimped-fabric) at the same time will increase the performance of the studies.
In earlier investigations at BAM it was shown, that the matrix has a strong influence on the micro-crack formation and finally on the total lifetime. In order to determine the influence of the matrix properties on the boarderline to infinite life, research is done on laminates while replacing the epoxy-based matrix with an equivalent one with different fracture mechanical properties.
With the evolution of early cracks and IFF monitored as well as the influence of the matrix on the crack propagation investigated we are working on an appropriate model to improve lifetime prediction in CFRP. This work is done within the priority program “infinite life” (SPP 1466) funded by Deutsche Forschungsgemeinschaft (DFG).
Nondestructive investigation of the VHCF-endurance on cyclically loaded CFRP by X-Ray-Refractography
(2016)
Carbon fiber-reinforced-plastics (CFRP) are already used under high-cycle- (HCF) and very-high-cycle-fatigue (VHCF) at relatively low loads not only in aerospace industry, but also in other growing markets like especially wind energy and increasingly also automotive industry. While the static strength of CFRP is satisfyingly predictable by means of layerwise-strenght-analysis and material data from single layers, it is more and more uncertain to predict residual strength or lifetime as the design lifetime increases. Previous studies showed that local minor cracks and inter-fiber-fracture (IFF) originate long before total failure of single layers. Reliable fatigue estimation for fiber-reinforced-plastics is not available at present. Subsequently safety-related primary structures made out of FRP are over dimensioned.
It is possible to detect the change of inner surface in a specimen by means of X-Ray-Refractography. This includes voids, intact fiber-matrix-interfaces as well as defective ones, cracks and all interfaces in plane with the X-Ray-beam. As the crack-density (including IFF) increases, the inner surface of the material correspondingly increases.
The borderline where even at high cycles no early cracks were detected was identified for selected laminates out of woven and non-crimped fabric with epoxy-matrix.
When no micro-cracks were detected up to 106 cycles, the specimens also lasted in the VHCF-regime. Furthermore for the epoxy resin LY556 in combination with carbon fiber it was distinguished that at a load minor to 50% IFF-load level, no micro cracks were detected and consequently the VHCF-endurance reached.
The integration of the set-up small-sized testing machine into the X-Ray buildup in order to achieve in-situ non-destructive detection of the crack initiation while loading the specimens (CFRP and GFRP- woven fabric and non-crimped-fabric) at the same time will increase the performance of the studies.
In earlier investigations at BAM it was shown, that the matrix has a strong influence on the micro-crack formation and finally on the total lifetime. In order to determine the influence of the matrix properties on the boarderline to infinite life, research is done on laminates while replacing the epoxy-based matrix with an equivalent one with different fracture mechanical properties.
With the evolution of early cracks and IFF monitored as well as the influence of the matrix on the crack propagation investigated we are working on an appropriate model to improve lifetime prediction in CFRP. This work is done within the priority program “infinite life” (SPP 1466) funded by Deutsche Forschungsgemeinschaft (DFG).
Carbon Fibre Reinforced Plastics (CFRP) are more and more used in modern civil aircrafts. These days the whole fuselage is made of this material (B787; A350). Due to strict certification standards the normal in-service loading gives a low stress level compared to the static and even the fatigue strength of the material. Hence CFRP are assumed to have an infinite life. To evaluate this assumption, fatigue tests on CFRP-specimens were performed up to 108 load cycles and the first inter-fibre failure was evaluated non-destructively by accompanying X-ray-refraction topography.
A tensile testing machine was integrated in a small angle X-ray scattering (SAXS) setup. X-ray refraction topography was performed while the CFRP-samples were tensile loaded. This non-destructive technique enables the detection of micro-cracking and inter-fibre failure especially for CFRP. For Glass Fibre Reinforced Plastic (GFRP) X-ray refraction and in-situ loading has already been successfully used. The increase of inner surfaces due to inter fibre failure was measured as a function of the stress state. Fatigue tests were performed at and below the limit of inter-fibre failure strength.
State of the art is to assume the failure of the samples under cyclic loading as the fatigue life. Accompanying non-destructive X-ray refraction measurements reflects the damage state and enables to trace its evolution even if the total failure of the specimens does not occur. This investigation technique is of high interest to give the engineer a design value of infinite life which is practically often reached due to knock down factors of certification standards. Finally the infinite life was found for cyclic fatigue loaded CFRP-samples even under high inter fibre transverse and shear loading investigated up to 108 load cycles.
The increased use of fibre-reinforced plastic (FRP) composites for improved efficiency and reliability in energy related applications e.g. wind and marine turbine blades, nacelles, oil and gas flexible risers, also increases the demand for innovative non-destructive testing technologies. Thus, in order to achieve increased acceptance of suited and optimized non-destructive testing (NDT) methods in industry, the European Metrology Research Programme (EMRP) project ENG57 Validated Inspection Techniques for Composites in Energy Applications (VITCEA) deals with the development and validation of innovative NDT technologies. In this contribution, results concerning thermographic investigations at test specimens during tensile loading and active thermography testing after tensile loading are presented. Additionally, the determination of the optical properties (relative transmittance and directional spectral emissivity) of CFRP and GFRP test specimens is described.
The increased use of fibre-reinforced plastic (FRP) composites for improved efficiency and reliability in energy related applications e.g. wind and marine turbine blades, nacelles, oil and gas flexible risers, also increases the demand for innovative non-destructive testing technologies. Thus, in order to achieve increased acceptance of suited and optimized non-destructive testing (NDT) methods in industry, the European Metrology Research Programme (EMRP) project ENG57 Validated Inspection Techniques for Composites in Energy Applications (VITCEA) deals with the development and validation of innovative NDT technologies. In this contribution, results concerning thermographic investigations at test specimens during tensile loading and active thermography testing after tensile loading are presented. Additionally, the determination of the optical properties (relative transmittance and directional spectral emissivity) of CFRP and GFRP test specimens is described.
Carbon Fibre Reinforced Plastics (CFRP) are more and more used in modern civil aircrafts. These days the whole fuselage is made of this material (B787; A350). Due to strict certification standards the normal in-service loading gives a low stress level compared to the static and even the fatigue strength of the material. Hence CFRP are assumed to have an infinite life. To evaluate this assumption, fatigue tests on CFRP-specimens were performed up to 108 load cycles and the first inter-fibre failure was evaluated non-destructively by accompanying Xray-refraction topography. A tensile testing machine was integrated in a small angle X-ray scattering (SAXS) setup. X-ray refraction topography was performed while the CFRP samples were tensile loaded. This non-destructive technique enables the detection of micro-cracking and inter-fibre failure especially for CFRP. For Glass Fibre Reinforced Plastic (GFRP) X-ray refraction and in-situ loading has already been successfully used. The increase of inner surfaces due to inter fibre failure was measured as a function of the stress state. Fatigue tests were performed at and below the limit of inter-fibre failure strength. State of the art is to assume the failure of the samples under cyclic loading as the fatigue life. Accompanying non-destructive X-ray refraction measurements reflects the damage state and enables to trace its evolution even if the total failure of the specimens does not occur. This investigation technique is of high interest to give the engineer a design value of infinite life which is practically often reached due to knock down factors of certification standards. Finally the infinite life was found for cyclic fatigue loaded CFRP-samples even under high inter fibre transverse and shear loading investigated up to 108 load cycles.
Amongst various other NDT methods, within the EMRP-project
‘VITCEA’ active thermography is validated for testing of CFRP and
GFRP structures constructed for energy application. In this
contribution, the optical and thermal properties of CFRP and GFRP
reference defect artefact (RDA) and natural defects artefact (NDA)
test specimens are characterized. Different excitation techniques
and techniques for data analysis are compared for optimizing the
number of detected defects.
Amongst various other NDT methods, within the EMRP-project ‘VITCEA’ active thermography is validated for testing of CFRP and GFRP structures constructed for energy application. In this contribution, the optical and thermal properties of CFRP and GFRP reference defect artefact (RDA) and natural defects artefact (NDA) test specimens are characterized. Different excitation techniques and techniques for data analysis are compared for optimizing the number of detected defects.
Since a few years the direct detection of X-ray photons into electrical signals is possible by usage of highly absorbing photo conducting materials (e.g. CdTe) as detection layer of an underlying CMOS semiconductor X-ray detector. Even NDT energies up to 400 keV are possible today, as well. The image sharpness and absorption efficiency is improved by the replacement of the unsharp scintillation layer (as used at indirect detecting detectors) by a photo conducting layer of much higher thickness. If the read-out speed is high enough (ca. 50 – 100 ns dead time) single X-ray photons can be counted and their energy measured. Read-out noise and dark image correction can be avoided. By setting energy thresholds selected energy ranges of the X-ray spectrum can be detected or suppressed. This allows material discrimination by dual-energy techniques or the reduction of image contributions of scattered radiation, which results in an enhanced contrast sensitivity. To use these advantages in an effective way, a special calibration procedure has to be developed, which considers also time dependent processes in the detection layer. This contribution presents some of these new properties of direct detecting digital detector arrays (DDAs) and shows first results on testing fiber reinforced composites as well as first approaches to dual energy imaging.