The susceptibility of concrete structures due to alkali–silica reaction (ASR) can be assessed by means of ASR concrete prism testing at 60 °C, according to RILEM AAR 4.1. There, expansion of concrete prisms indicates alkali-reactivity of the examined concrete mix. This work applies in situ expansion measurement to accelerated concrete prism testing. Automated measuring facilitates both storage without the usually necessary interruptions for manual measurement and acquisition of quasi-continuousexpansion data. A comparative experimental programme showed that conventional testing resulted in stronger expansion and leaching of alkalis than automated testing. Experimental simulation of interruptions, typically associated with manual measurements in conventional testing, could prove the influence of these cooling–heating cycles. Two phenomenological approaches, frequently used for describing reaction kinetics of ASR by linking it to expansion results from ASR-testing, were validated with continuous expansion data of three types of aggregate. Experimental expansion depicted s-shaped curves similar to them of the modelling approaches. However, strong swelling recorded in the beginning of the test was not covered by the model curves. Auxiliary measurement of acoustic emissions and ultrasonic velocity helped characterising mechanisms such as hydration and cracking, which also influence prism expansion. The proposed modification of the measurement procedure provides an extended basis to analyse expansion mechanisms. Regarding data for validation of ASR-expansion models, continuous expansion results are preferable to conventional test results.
The accelerated concrete prism test (ACPT-60 °C) facilitates testing of alkali-silica reactivity of aggregates within five months. Manual measurement is usually conducted to determine expansion of test specimen every 28 days. This conventional procedure gives only limited insight to expansion behaviour of ASR-affected prisms. Due to the large time intervals, expansion exceeding the critical value of 0.3 mm/m is likely to be noticed late. Continuous recording resolves this problem and delivers beneficial information on the shape of the expansion curve.
Displacement transducers integrated into a special testing equipment developed at BAM put continuous measurement into practice. Additionally, ultrasonic velocity and acoustic emissions are measured in-situ and provide deeper insights into hydration and crack formation processes during the test.
Aiming for an automated testing method close to the German guideline, the following technical and methodical challenges arise. Changing of the vertical orientation of the prisms with every manual measurement as standardised cannot be implemented. Furthermore, preliminary results already proved true that cooling and heating cycles, as necessarily associated with each manual measurement, can evoke additional expansion. Therefore, interrupted and continuously measured expansions reveal systematic differences, indicating the necessity to adjust the threshold expansion value for automated testing.
Results presented in the paper: Different types of reactive aggregate have been tested applying continuous and manual expansion measurement to the concrete specimens. Development of continuously measured ultrasonic velocity and acoustic emissions of the aggregates tested diverge significantly while the expansion curves vary in shape and maximum strain. Prisms produced from a slowly reacting aggregate do not exhibit noticeable crack formation. It shows that comprehensive measuring helps describing and distinguishing ASR-damage mechanisms.
Models of ASR-induced expansion, available in the open literature, so far are validated with discontinuous data hardly tracing the modelled curve. Continuous measurement improves validation and further model development.