The novel heat treatment concept of “Quenching and Partitioning” (Q&P) enables producing low alloyed martensitic steels with high strength and formability. Therefore austenite, retaining from a quenching temperature between Mf and Ms, is stabilised by carbon diffusion. This stabilised austenite transforms in martensite (TRIP effect) under mechanical loading. Current investigations on the Q&P heat treatment of martensitic stainless steels reveal a further enhancement of mechanical properties due to higher amounts of austenite. Thus a tensile strength of 1.800 MPa and a maximum elongation of 20 % are possible, while mechanical properties under compression are much higher due to a distinct SD effect.
The presentation aims to gain a further understanding of the Q&P heat treatment and the resulting mechanical properties for the steel X46Cr13, especially the mechanical behaviour under dynamic mechanical loading condition. Results of drop work and Split Hopkinson Pressure Bar test confirms the findings of quasi static compression test. Furthermore, Charpy impact tests show higher impact toughness compared to the common heat treatment of quenching and tempering (Q&T). Complementary investigations indicate a higher corrosion resistance of Q&P compared to Q&T.
A further improvement of the excellent properties of UHPC can be realized with thermal Treatment. Like for normal concrete, it accelerates the hardening and prevents shrinkage after the treatment. Additionally, an increase in strength can be achieved. Aim of this study was the optimisation of the thermal Treatment conditions of UHPC for very different Treatment methods; heat Treatment at 90 °C for unprotected and sealed samples, hot water bath at 90 °C and hydrothermal Treatment at 185 °C/1.1 MPa. The pre-storage time and the dwell time were systematically varied for each method to gain a higher strength. The compressive strength depends on the manner of Treatment at which higher water accessibility leads to higher strengths. The Phase composition changes considerably with different Treatment tempereatures. Finally, it can activate unhydrated binder components forming additional C-S-H, leading to higher strength.
Potential of martensitic stainless steel X5CrNiCuNb 16-4 as pipe steel in corrosive CCS environment
(2017)
Pipe steels suitable for carbon capture and storage technology (CCS) require resistance against the corrosive environment of a potential CCS-site (heat, pressure, salinity of the aquifer, CO2-partial pressure). X5CrNiCuNb16-4 has been proven to be sufficient resistant in corrosive environments, but shows rather unusual corrosion behaviour in CCS environment. Therefore differently heat treated coupons of 1.4542 were kept at T=60 °C and ambient pressure as well as p=100 bar for 700 h - 8000 h in an a) water saturated supercritical CO2 and b) CO2-saturated synthetic aquifer environment similar to on-shore CCS-sites in the Northern German Basin. Additionally fatigue tests were performed via push-pull tests with a series of 30 specimens was tested at stress amplitudes between 150 MPa and 500 MPa (sinusoidal dynamic test loads, R=-1; resonant frequency ~ 30 Hz). Best corrosion resistance in the liquid phase is achieved via normalizing prior to exposure and hardening+tempering at 670 °C leads to lowest corrosion rates in the supercritical phase. With no regard to atmosphere discontinuously ellipsoidal surface corrosion regions appear after exposure of 4000 h and more. The endurance limit of X5CrNiCuNb16-4 measured in air is reduced by more than 50% when exposed to CCS environment (maximum number of cycles (10 x 106) at a stress amplitude of 150 MPa) The scatter range TN = 1:34 is disproportionately large contributing to an overall unusual corrosion behaviour.
The quenching and partitioning (Q+P) heat treatment enables a higher deformability of high strength martensitic steels. Therefore, it is necessary to have some metastable austenite in the microstructure, which transforms in martensite during plastic deformation (TRIP-effect). This condition is guaranteed by the quenching and the additional partitioning treatment. Due to local carbon diffusion retained austenite is stabilized and a partial reversion of austenite from martensite occurs. The Q+P heat treatment was investigated for the martensitic stainless steel 1.4034 (X46Cr13) concerning the influence of partitioning time. In line with these efforts metallographic, XRD- and EBSD-measurements were performed to characterize the microstructural evolution. The mechanical experiments included mechanical testing with different strain rates. The reversion of austenite by the partitioning treatment could be detected with EBSD- and XRD-measurements. Further-more the results of the mechanical testing showed improved values of strength and de-formability because of the Q+P heat treatment.
Ti-6Al-4V bridges were additively fabricated by selective laser melting (SLM) under different scanning speed conditions, to compare the effect of process energy density on the residual stress state. Subsurface lattice strain characterization was conducted by means of synchrotron diffraction in energy dispersive mode. High tensile strain gradients were found at the frontal surface for samples in an as-built condition. The geometry of the samples promotes increasing strains towards the pillar of the bridges. We observed that the higher the laser energy density during fabrication, the lower the lattice strains. A relief of lattice strains takes place after heat treatment.
The novel heat treatment concept, “quenching and partitioning” (Q&P) has been developed for high strength steels with enhanced formability. This heat treatment involves quenching of austenite to a temperature between martensite start and finish, to receive a several amount of retained austenite. During the subsequent annealing treatment, the so called partitioning, the retained austenite is stabilized due to carbon diffusion, which results in enhanced formability and strength regarding strain induced austenite to martensite transformation. In this study a Q&P heat treatment was applied to a Fe-0.45C-0.65Mn-0.34Si-13.95Cr stainless martensite. Thereby the initial quench end temperature and the partitioning time were varied to characterize their influence on microstructural evolution. The microstructural changes were analysed by dilatometer measurements, X-ray diffraction and scanning electron microscopy, including electron backscatter diffraction. Compression testing was made to examine the mechanical behaviour. It was found that an increasing partitioning time up to 30 min leads to an enhanced formability without loss in strength due to a higher amount of stabilized retained and reversed austenite as well as precipitation hardening.
The novel heat treatment concept, “quenching and partitioning” (Q&P) has been devel-oped for high strength steels with enhanced formability. This heat treatment involves quenching of austenite to a temperature between martensite start and finish, to receive a several amount of retained austenite. During the subsequent annealing treatment, the so called partitioning, the retained austenite is stabilized due to carbon diffusion, which results in enhanced formability and strength regarding strain induced austenite to mar-tensite transformation. In this study a Q&P heat treatment was applied to a Fe-0.45C-0.65Mn-0.34Si-13.95Cr stainless martensite. Thereby the initial quench end temperature and the partitioning time were varied to characterize their influence on microstructural evolution. The microstructural changes were analysed by dilatometer measurements, X-ray diffraction and scanning electron microscopy, including electron back-scatter diffrac-tion. Compression testing was made to examine the mechanical behaviour. It was found that an increasing partitioning time up to 30 min leads to an enhanced formability with-out loss in strength due to a higher amount of stabilized retained and reversed austenite as well as precipitation hardening.