The layer-wise slurry deposition (LSD) is an innovative process for the deposition of powder layers with a high packing density for Additive Manufacturing (AM). A slurry with small organic content is repetitively spread as thin layers on top of each other by means of a doctor blade. During the deposition, the ceramic particles settle to form thin layers with a high packing density (55-60%). Each layer is then dried, resulting in the stacking of a dry powder bed with high powder packing. When coupled with a printing head or with a laser source, the LSD enables novel AM technologies inspired to the 3D printing or selective laser sintering, but taking advantage of having a highly dense powder bed.
The LSD -3D printing, in particular, offers the potential of producing large (> 100 mm) and high quality ceramic parts, with microstructure and properties similar to traditional processing.
This presentation will give an overview of the milestones in the development of this technology, with focus on the latest results applied both to silicate and to technical ceramics.
Up to now, there exists a lack of methods for the additive manufacturing of voluminous ceramic parts with properties comparable to those of conventionally manufactured ones. A high density after sintering is needed to reach the superior properties of ceramic materials. We have developed a new additive manufacturing method, Laser-Induced Slip casting (LIS), to generate ceramic green bodies with high particle packing density and with virtually no restriction in the particle size of the feedstock, especially in terms of small particles. This is achieved by laser-induced local drying of slurries, with the process resembling many features of the well-established stereolithography, but without the excessive use of polymeric material. Thus, unlike the stereolithography process, the resulting green bodies can be processed like traditionally produced ceramic parts. This method allows large and dense additive-manufactured parts to be obtained from conventional water-based ceramic slurries. As an example, we will demonstrate the application of this novel technique with Si3N4.
The combination of tomographic, microstructural data with other experimental techniques and with modeling is paramount, if we want to extract the maximum amount of information on material and component properties. In particular, quantitative image analysis, statistical approaches, direct discretization of tomographic reconstructions represent concrete possibilities to extend the power of the tomographic 3D representation to insights into the material and component performance. This logic thread equally holds for industrial and academic research, and valorizes expensive experiments such as those carried out at synchrotron sources, which cannot be daily repeated.
I will show a few examples of possible use of X-ray tomographic data for quantitative assessment of damage evolution and microstructural properties, as well as for non-destructive testing. Examples of micro-structured inhomogeneous materials will be given, such as Composites, Ceramics, Concrete, and Additively manufactured parts. I will also show how X-ray refraction computed tomography (CT) can be highly complementary to classic absorption CT, being sensitive to internal interfaces.
Additionally, I will present a new technique in our portfolio, Neutron Diffraction, which is extremely well suited to the study of internal stresses, both residual and under external load.
Applications of X-ray refraction to non-destructive characterization of ceramics and composites
(2017)
X-ray refraction is analogous to visible light deflection by matter, with two main differences: 1- convex objects cause divergence (i.e., the refraction index n is smaller than 1), and 2- deflection angles are very small, from a few seconds to a few minutes of arc (i.e., n is near to 1). Trivially but importantly, deflection of X-rays is also sensitive to the orientation of the object boundaries. These features make X-ray refraction techniques extremely suitable to a) detect defects such as pores and microcracks, and quantify their densities in bulk (light) materials, and b) evaluate porosity and particle properties such as orientation, size, and spatial distribution (by mapping). While X-ray refraction techniques cannot in general image single defects, their detectability is simply limited by the wavelength of the radiation.
We will thereby show the application of X-ray refraction 2D mapping (topography) and tomography to different sorts of problems in ceramic science and technology: 1) Sintering of SiC green bodies; 2) Porosity analysis in diesel particulate filter silicates; 3) fiber de-bonding in metal and polymer matrix composites; 4) micro-cracking of glass-precursor -eucryptite. We will see that the use of X-ray refraction analysis yields quantitative results, also directly usable in available models.
Spray drying based granulation processes aim for flowable granules neither containing voids nor hard shells thus leading to a homogenous microstructure in the green and sinter bodies without strength reducing large pores. The increase of the specific surface area due to the utilization of finer powders as raw materials makes the production of granules of demanded quality more sophisticated. Innovations regarding additives as well as process engineering are therefore required.
While conventional spray granulation processes of ceramic materials are based on rotational, one stream or two stream nozzles for nebulization, the investigations in the ZIM project concentrate on the applicability of an ultra sound atomizer unit. A spray dryer comprised of the aforementioned ultra sound atomization unit implemented in a commercial spray dryer (Niro, Denmark) was used as test system. Potential advantages of the ultra sound nebulization are investigated for model systems of alumina, zirconia and a ZTA composite while focusing on solids content, yield, pressability and granule properties (size, size distribution, flowability, shape and microstructure) as well as the final sinter body properties (density, microstructure and flexural strength).
First ultra sound spray drying experiments yielded granules with excellent processability. Spray drying of identical slurries, as before tested and optimized for a two stream nozzle atomization process, resulted in a more suitable size distribution for dry pressing (less particles below 20 µm) and a higher yield. Furthermore, sinter bodies produced of ultra sound granules seem to have less large pores and a more homogenous microstructure
Advanced spray drying process by controlled slurry destabilization and ultrasonic atomization
(2017)
Spray drying of ceramic slurries aims for soft and free-flowing granules with homogenous microstructure suitable for uniaxial and isostatic pressing. A stable and continuous spray drying process of slurries with maximized solids content is a further development target, since a reduction of the energy intensive drying procedure is desirable.
First part of the investigation focuses on the development of an appropriate zirconia slurry for spray drying with optimized organic additive contents (dispersant + binder + pressing and lubricating agents). Characterization and improvement of slurries are based on zeta potential measurements and investigations of the sedimentation behavior in an optical centrifuge. Therefor the slurries were spray dried with a conventional spray dryer with a two stream nozzle run in fountain mode. The controlled destabilization of the slurries was introduced, since the unwanted formation of hard granules with donut-like shape could be circumvented. Spray drying of such modified slurries resulted in soft granules without voids and finally leaded to sintered bodies with improved microstructure, density and bending strength.
Expectedly, the destabilization process causes a significant increase in viscosity of the ceramic slurry. Hence, an alternative spraying concept utilizing an ultrasonic nozzle was tested. Indeed, the ultrasonic nozzle seems able to atomize slurries with viscosities beyond the capability of the regular two stream nozzles due to the slurry’s shear thinning behavior. In second part of the investigation the integration of the ultrasonic nozzle in a commercial spray dryer is shown and first results of the spraying tests are discussed. Continuous spraying processes of highly viscous alumina, zirconia and ZTA slurries were realized over an extended production period.