The quenching and partitioning (Q&P) heat treatment enables a higher deformability of high strength martensitic steels. The Q&P heat treatment was applied on the martensitic stainless steel 1.4034 (X46Cr13) to study the influence of partitioning time. Therefore, extensive characterizations of the mechanical properties, focussing on the materials behaviour under different mechanical load scenarios, were performed. A comprehensive analysis of the microstructural evolution was per-formed for different heat treatment and mechanical loading states. A complete solution of chromium carbides was detected to be a first requirement for successful Q&P heat treatment. The comparison of common quenching and tempering with the Q&P heat treatment verifies the extensively enhanced materials strength whereat the formability is still acceptable. The microstructural reason was detected to be an increasing aus-tenite fraction due to austenite reversion at subgrain boundaries of martensite besides the stabilising of retained austenite. Further a distinctive strength differential effect was observed.
Numerical Sensitivity Analysis of TRIP-Parameter K on Weld Residual Stresses and Weld Distortion
(2016)
A combined experimental numerical approach is applied for a sensitivity analysis of the transformation induced plasticity (TRIP)-parameter K on welding residual stresses and welding distortion for the welding of the low-alloyed high-strength S960QOL with the high-alloyed hig-strength filler material CN13-4-IG. A thermo-mechanical FE model of a real GMA welding process was experimentally validated against termperature field, X-Ray stress measurments and optical distortion measurement. Within the sensititvity analysis K was varied and the influence on the calculated welding residual stresses and welding distortion is evaluated by performing corresponding FEA. The correct order of K magnitude is necessary in order to reproduce the residual stresses qualitatively and quantitatively. For the sufficient reproducing of the welding distortion the transformation induced plasticity can be neglected.