Chromia forming high alloyed ferritic-austenitic steels are being used as boiler tube materials in biomass and coal-biomass co-fired power plants. Despite thermodynamic and kinetic boundary conditions, microstructural features such as grain orientation, grain sizes or surface deformation contribute to the oxidation resistance and formation of protective chromium-rich oxide layers. This study elucidates the impact of microstructure such as the grain size and number of carbide precipitates on high temperature oxidation at 650°C in 0.5% SO2 atmosphere. Cold-rolled Fe-16Cr-0.2C material was heat-treated to obtain two additional microstructures. After exposure to hot and reactive gases for 10 h < t < 1000 h layer thicknesses and microstructure of oxide scales are observed by scanning electron microscopy and Energy-dispersive X-ray spectroscopy. The two heat treated alloys showed reasonable oxidation resistance after 1000 h of exposure. The oxidation rate was substantially higher for the alloy with a duplex matrix after heat treatment compared to the fine-grained material.
The fundamental impact of sulfur and water on corrosion rates and potential failure of the exposed material is well known. However, the access to the related corrosion mechanism causing material degradation is often a problem to solve. This study investigates the effect of SO2 and water vapor in the initial stages of corrosion of an Fe9Cr0.5Mn model alloy at 650 °C in situ. The analysis was carried out under laboratory conditions using energy-dispersive X-ray diffraction (EDXRD).
Ferritic alloys containing Cr form Cr5S6 precipitates along grain boundaries in hot SO2 environment. Grain boundary precipitates may influence the steel’s mechanical behavior. Cr5S6 precipitates were reconstructed three-dimensionally using FIB tomography analysis to determine the volume, number, and penetration depth. The volume growth of Cr5S6 precipitates increased only for the initial aging time of 3 h but became constant after 6 h. The number of precipitates increased linearly.
Ferritic steels with Cr-contents up to 13 wt. % are used as heat exchanger or boiler tube materials in combustion based power plants. These materials are subject to aggressive corrosion caused by the reaction of the steel with highly corrosive gases under high temperatures up to 650°C. The early stages of corrosion and sulfidation especially and the influence of the Cr-content in the alloy are thereby not understood but of fundamental interest.
Our work shows corrosion mechanisms and presents corrosion models for Fe and different Fe-Cr-alloys under pure SO2 und SO2+O2 atmospheres for different time scales. Modell alloys of high purity are used to focus on the reaction of the intended elements: Fe, Cr, S, and O. Long-time experiments (≥12h) took place in tube furnaces and short-time experiments (≥5min) in a special designed light furnace. Heating and cooling took place under inert atmosphere. The reactive gases were added not until the experimental temperature was reached. Samples were analyzed using high resolution synchrotron X-ray diffraction using a micro focus setup and electron microscopy including FIB.
Many earlier studies on corrosion and sulfidation on iron based alloys show a higher corrosion rate and material loss when sulfur was present in the atmosphere. In contrast, later studies propose an inhibiting effect of sulfur containing atmospheres. On the one side, most likely due to the formation of a protective layer of Mx(SO4)y -phases at the scale-gas interface. On the other side, a very recent study proposes the theory that MxSy-phases limit the further diffusion of elements. Up to now, no Mx(SO4)y –phases were detected in our samples, but sulfide phases nucleated within the oxide phases. For pure Fe our samples show FeS at the scale-metal interface working as a diffusion barrier for Fe-Cations from the base material in to the oxide scale. The above lying spalled off oxide-sulfide scale shows a wide area of small voids and accumulations of FeS-Crystals at the bottom. Under the main oxide scale a second generation of oxide-sulfide scale starts to form. For the Fe-Cr-alloys the inner oxide scale only shows FeS- and CrS-phases surrounded by hollow space. The here presented study will explain and discuss a new growth model for the shown phenomenon.