High-strength steels are increasingly applied in modern steel constructions to meet today’s lightweight requirements. Welding of these steels demands a profound knowledge of the interactions between the welding process, cooling conditions, heat input and the resulting metallurgical occurrences in the weld and its vicinity. Additionally, welding stresses may be detrimental for the safety and performance of high-strength steel component welds during fabrication and service, especially due to the high yield ratio. For a development of strategies to adjust welding heat control, all these effects should be considered, to reach a complete exploitation of the high-strength steel potential. In recent researches at BAM, multilayer GMAW experiments were performed with high-strength steels, in which cooling conditions and resulting microstructure were analysed for varied heat control parameters. The application of a unique 3d-operating testing facility and X-ray diffraction measurements allowed the analysis of local stresses in the weld while welding and cooling under component relevant shrinkage restraints. As a result, correlations between material behaviour, welding and cooling condition and the arising multi-axial stresses and forces were found. Based on this study, statements for the development of adapted heat control concepts were derived, which are presented by means of specific analysis examples.
High-strength steels are increasingly applied in modern steel constructions to meet today’s lightweight requirements. Welding of these steels demands a profound knowledge of the interactions between the welding process, cooling conditions, heat input and the resulting metallurgical occurrences in the weld and its vicinity. Additionally, welding stresses may be detrimental for the safety and performance of high-strength steel component welds during fabrication and service, especially due to the high yield ratio. For a development of strategies to adjust welding heat control, all these effects should be considered, to reach a complete exploitation of the high-strength steel potential. In recent researches at BAM, multilayer GMAW experiments were performed with high-strength steels, in which cooling conditions and resulting microstructure were analysed for varied heat control parameters. The application of a unique 3d-operating testing facility and X-ray diffraction measurements allowed the analysis of local stresses in the weld while welding and cooling under component relevant shrinkage restraints. As a result, correlations between material behaviour, welding and cooling condition and the arising multi-axial stresses and forces were found. Based on this study, statements for the development of adapted heat control concepts were derived, which are presented by means of specific analysis examples.
Today an expanding application of high-strength steels in modern welded constructions can be observed. The economical use of these steel grades largely depends on the strength and reliability of the weldments. Therefore the special microstructure and mechanical properties of these grades have to be taken into account by keener working ranges regarding the welding parameters. However, performance and safety of welded components are strongly affected by the stresses occurring during and after welding fabrication locally in the weld seam and globally in the whole component, especially if the shrinkage and distortion due to welding are restrained. Some extensive studies describe the optimization of the welding stresses and the metallurgical effects regarding an adapted welding heat control. In particular lower working temperatures revealed to be effective to significantly reduce the local and global welding induced residual stresses of the completed weld. However, decreased interpass temperatures cause concurrently higher stresses during welding fabrication. This work shows some strategies to reduce these in-process stresses. With help of multi-axial welding stress analyses in component-related weld tests using a special 2-MN-testing facility differences in stress build-up are described in detail for root welds, filler layers and subsequent cooling to ambient temperature.
In an increasing number of modern steel applications high-strength steel grades are demanded to meet specifications regarding a high load bearing capacity and a low operating weight. Lightweight design rules enhance the safety requirements, especially for welded joints. Besides a higher cracking risk for HSLA steel welds, the formation of tensile residual stresses might lead to fracture due to overloading or premature failure if not adequately considered. In codes and standards, therefore, residual stress on the amount of the yield strength are expected, disregarding the circumstance that generally the residual stresses are much lower in HSLA steel welds. Oftentimes this leads to an underestimation of the proof strength in high-strength welded components and economical disadvantages using HSLA steels. In this study, a stress-strain analysis was conducted at component related structures from S960QL using digital image correlation while preheating welding and cooling adjacent to the weld seam. X-ray diffraction analysis of the local residual stresses in the weld seam showed a good comparability with the global analyses. The comparison of two different seam geometries revealed significantly lower multi-axial stresses if a narrower weld groove is used.
Today an expanding application of high-strength steels in modern welded constructions can be observed. The economical use of these steel grades largely depends on the strength and reliability of the weldments. Therefore the special microstructure and mechanical properties of these grades have to be taken into account by keener working ranges regarding the welding parameters. However, performance and safety of welded components are strongly affected by the stresses occurring during and after welding fabrication locally in the weld seam and globally in the whole component, especially if the shrinkage and distortion due to welding are restrained. Some extensive studies describe the optimization of the welding stresses and the metallurgical effects regarding an adapted welding heat control. In particular lower working temperatures revealed to be effective to significantly reduce the local and global welding induced residual stresses of the completed weld. However, decreased interpass temperatures cause concurrently higher stresses during welding fabrication. This work shows some strategies to reduce these in-process stresses. With help of multi-axial welding stress analyses in component-related weld tests using a special 2-MN-testing facility differences in stress build-up are described in detail for root welds, filler layers and subsequent cooling to ambient temperature.
In an increasing number of modern steel applications high-strength steel grades are demanded to meet specifications regarding a high load bearing capacity and a low operating weight. Lightweight design rules enhance the safety requirements, especially for welded joints. Besides a higher cracking risk for HSLA steel welds, the formation of tensile residual stresses might lead to fracture due to overloading or premature failure if not adequately considered. In codes and standards, therefore, residual stress on the amount of the yield strength are expected, disregarding the circumstance that generally the residual stresses are much lower in HSLA steel welds. Oftentimes this leads to an underestimation of the proof strength in high-strength welded components and economical disadvantages using HSLA steels. In this study, a stress-strain analysis was conducted at component related structures from S960QL using digital image correlation while preheating welding and cooling adjacent to the weld seam. X-ray diffraction analysis of the local residual stresses in the weld seam showed a good comparability with the global analyses. The comparison of two different seam geometries revealed significantly lower multi-axial stresses if a narrower weld groove is used.