In concrete pavements, damages occurred which are related to an Alkali-Silica-Reaction (ASR). Although the background for such an ASR has been studied extensively, special conditions in pavements increase this reaction significantly. These are especially the superposition of microstructural degradation caused by cyclic loading with an external alkali supply. Previous investigations of ASR focused mainly on the material itself (aggregates, cements, assessment of the concrete) while these special circumstances have not been considered. Concrete pavements are subjected to cyclic loadings by traffic and climate changes.
Within cooperative research projects the different interdependent influencing factors for a damaging ASR in concrete pavements are studied by experiments as well as by numeric modelling. On the micro-level the ASR-related processes within the aggregate, such as gel-formation or ion-transport, are investigated. On the meso-level, the project focuses on the characterization of degradation effects in the concrete microstructure due to cyclic loading. Further, special attention is paid to the transport behavior of fluids in such pre-damaged concrete structures with and without the effect of overrunning tires as well as the impact on the ASR itself. Finally, on the macro-level the risk of an ASR-damage is assessed.
Ultrashort laser pulses with durations in the fs- to ps-range were used for large area surface processing of steel aimed at mimicking the morphology and extraordinary wetting behaviour of bark bugs (Aradidae) found in nature. The processing was performed by scanning the laser beam across the surface of initially polished flat sample surfaces. A systematic variation of the laser processing parameters (peak fluence, scan velocity, line overlap) allowed the identification of different regimes associated with characteristic surface morphologies (laser-induced periodic surface structures (LIPSS), grooves, spikes, etc.). Additionally, we show that different laser processing strategies, varying laser wavelength, pulse duration and repetition rates, allowed to achieve a range of morphologies that resemble different structures found in bark bugs. For identifying the ideal combination of parameters for mimicking bug-like structures, the surfaces were inspected by optical and scanning electron microscopy.
Complementary to the morphology study, the wetting behaviour of the surface structures for water and oil was examined intensively in terms of philic/-phobic nature and fluid transport. With these results in hand, tribological tests were carried out investigating the wear resistance of the laser-induced nano- and microstructures. Our results demonstrate a route towards reproducing complex structures inspired by nature and their functional response in technologically relevant materials.
Nature provides countless examples of surface structures featuring extraordinary properties such as directional fluid transport. In order to mimic the morphology and outstanding wetting behaviour of bark bugs, ultrashort laser pulses with durations in the fs- to ps-range were employed for large area surface processing of steel. By scanning the laser beam across the surface of initially polished flat sample surfaces and systematically varying the laser processing parameters (peak fluence, scan velocity, line overlap), different regimes associated with characteristic surface morphologies (laser-induced periodic surface structures (LIPSS), grooves, spikes, etc.) could be identified. Additionally, different laser processing strategies were applied, varying laser wavelength, pulse duration and repetition rates, which allowed to achieve a range of morphologies that resemble different structures found on bark bugs. For identifying the ideal combination of parameters for mimicking such bug-like structures, the surfaces were inspected by means of optical and scanning electron microscopy.
Complementary to the morphology study, the wetting behaviour of the surface structures for water and oil was examined intensively in terms of fluid transport and philic/-phobic nature. Additionally, with these results in hand, tribological tests investigating the wear resistance of the laser-induced nano- and microstructures were carried out. Our results demonstrate that the functionality of surface structures found in nature could be transferred to technologically relevant materials, such as steel, providing a huge potential for industrial applications for instance in friction and wear reduction.
Inorganic materials, such as steel, were functionalized by ultrashort laser pulse irradiation (fs- to ps-range) to modify the surface’s wetting behavior. The laser processing was performed by scanning the laser beam across the surface of initially polished flat sample material. A systematic experimental study of the laser processing parameters (peak fluence, scan velocity, line overlap) allowed the identification of different regimes associated with characteristic surface morphologies (laser-induced periodic surface structures, grooves, spikes, etc.). Analyses of the surface using optical as well as scanning electron microscopy revealed morphologies providing the optimum similarity to the natural skin of lizards. For mimicking skin structures of moisture-harvesting lizards towards an optimization of the surface wetting behavior, additionally a two-step laser processing strategy was established for realizing hierarchical microstructures. In this approach, micrometer-scaled capillaries (step 1) were superimposed by a laser-generated regular array of small dimples (step 2). Optical focus variation imaging measurements finally disclosed the three dimensional topography of the laser processed surfaces derived from lizard skin structures. The functionality of these surfaces was analyzed in view of wetting properties.
The wetting behavior of material surfaces can be controlled by surface structures. We functionalized case-hardened alloyed carbon steel to modify the wetting behavior using ultrashort laser pulses (fs- to ps-range). The laser processing was performed by scanning the laser beam across the surface of initially polished flat sample material. An experimental study of the laser processing parameters (peak fluence, scan velocity, line overlap) rendered an assignment of different regimes associated with characteristic surface morphologies (laser-induced periodic surface structures, grooves, micro cones, etc.) possible. Analyzing the surface using optical as well as scanning electron microscopy allowed the identification of morphologies providing the optimum similarity to the natural skin of non-moisture havesting lizards. For mimicking skin structures of moisture-harvesting lizards, additionally a two-step laser processing strategy was established for realizing hierarchical microstructures. In this approach, micrometer-scaled capillaries (step 1) were superimposed by a laser-generated regular array of small dimples (step 2). Optical focus variation imaging measurements finally revealed the three dimensional topography of the laser processed surfaces derived from lizard skin structures. The functionality of these surfaces was analyzed in view of wetting and directional fluid transport properties. The results suggest possible applications of the laser-structured surfaces.