A few layer/multilayer graphene (MLG) with a specific surface area of BET ≥ 250 m2/g is proposed as an efficient multifunctional nanofiller for rubbers. The preparation method, i.e., ultrasonically-assisted solution or latex premixing of master batches followed by conventional two-roll milling, strongly influences the dispersion in the elastomeric matrix and is fundamental for the final properties. When homogenously dispersed, single stacks of only approximately 10 graphene sheets, with an aspect ratio of ca. 35, work at low loadings, enabling the replacement of large amounts of carbon black (CB), an increase in efficiency, and a reduction in filler load. The appropriate preparation yielded nanocomposites in which just 3 phr are sufficient to significantly improve the rheological, curing, gas barrier properties, electrical and thermal conductivity, as well as mechanical properties of different rubbers, as shown for chlorine-Isobutylene-Isoprene rubber (CIIR), nitrile-butadiene rubber (NBR), natural rubber (NR), and styrene-butadiene rubber (SBR).[1-5] 3 phr of MLG tripled the Young’s modulus of CIIR, an effect equivalent to 20 phr of CB. The stronger interactions between MLG and NR or SBR also resulted in a reduction in the elongation at break by 20% and 50%, respectively, while the same parameter was hardly changed for CIIR/MLG and NBR/MLG. CIIR/MLG and NBR/MLG were stiffer but just as defomable than CIIR and NBR. The strong reinforcing effect of 3 phr MLG was confirmed by the increase of greater than 10 Shore A in hardness. MLG reduces gas permeability, increases thermal and electrical conductivities, and retards flammability. We investigated MLG also as a synergist for reducing the aluminium trihydrate loading in flame retardant hydrogenated acrylonitrile-butadiene (HNBR), polybutadiene chloroprene (BR/CR), and chlorosulfonated polyethylene rubber(CSM).[6-8] The higher the nanofiller concentration is, the greater the improvement in the properties. For instance, the permeability decreased by 30% at 3 phr of MLG, 50% at 5 phr and 60% at 10 phr, respectively. Moreover, the MLG nanocomposites improve stability of mechanical properties against the effects of weathering. In key experiments an increase in UV-absorption and a pronounced radical scavenging were proved as stabilizing mechanisms. In a nutshell, MLG is an efficient multifunctional nanofiller ready to be used for innovative rubber development.
Die Forderung, dass der Flammschutz von Kunststoffen nicht nur zum bei der Herstellung der jeweiligen Produkte, sondern auch über die gesamte Einsatzdauer im geforderten Maß wirksam ist, stellt eine große Aufgabe dar. Ferner ist die Anforderung für viele Produkte in der Praxis neu, da bisher vor allem der Einfluss der Flammschutzmittel auf die Stabilität der Polymerwerkstoffe, nicht aber die Stabilität des Flammschutzes untersucht wurde. Das Langzeitverhalten halogenfreier Systeme ist bis heute wenig untersucht, insbesondere weil Phosphor- und Stickstoff-basierte Systeme die oxidative Beständigkeit von Polymeren weniger zu beeinflussen scheinen als halogenhaltige FSM. Die Frage, wie zuverlässig der Flammschutz wirkt, wenn Kunststoffe einige Jahre im Innen- und Außenbereich im Einsatz sind und dabei wechselnden Beanspruchungen ausgesetzt waren, wurde bislang nur vereinzelt untersucht. Mögliche Auswirkungen von Witterungseinflüssen auf flammgeschützte Polymerwerkstoffe sind, dass die Flammschutzmittel selbst abbauen, ausgewaschen werden, oder auch durch Wechselwirkung mit den eingesetzten Additiven oder mit den Alterungsprodukten der Polymermatrix in ihrer Wirkung nachlassen. Hier bestand großer Forschungsbedarf, um an den Punkt zu gelangen, die Beständigkeit der Flammschutzeigenschaften eines Produktes über seine gesamte Lebensdauer zuverlässig garantieren zu können. Diese Fragestellung greift das durchgeführte Forschungsvorhaben auf.
Ziel war die Untersuchung der Langzeitstabilität der Flammschutzwirkung von halogenfrei flammgeschützten Polymerwerkstoffen unter diversen Witterungseinflüssen. Dazu wurden die Schädigungsmechanismen der Polymerwerkstoffe und der Flammschutzmittel sowie die auftretenden Wechselwirkungen analysiert, um ein Verständnis für die ablaufenden Prozesse zu entwickeln und Empfehlung für die Reduzierung der Alterung zu erarbeiten. Gegenstand der Untersuchungen waren anwendungsrelevante Flammschutz-Konzepte, die miteinander verglichen wurden. Die Erarbeitung von Struktur-Eigenschafts-Beziehungen ermöglichte die Beschreibung der Empfindlichkeiten und den Vergleich zwischen den Systemen. Darauf basierend wurden für die FSM spezifische Leitlinien für die Optimierung der Langzeitstabilität des Flammschutzes erstellt.
A rigid aromatic phosphorus-containing hyperbranched flame retardant structure is synthesized from 10-(2,5 dihydroxyphenyl)-10H-9-oxa-
10-phosphaphenanthrene-10-oxide (DOPO-HQ), tris(4-hydroxyphenyl)phosphine oxide (THPPO), and 1,4-terephthaloyl chloride (TPC). The resulting poly-(DOPO-HQ/THPPO-terephthalate) (PDTT) is implemented as a flame retardant into an epoxy resin (EP) at a 10 wt% loading. The effects on EP are compared with those of the monomer DOPO-HQ and triphenylphosphine oxide (OPPh3) as low molar mass flame retardants. The glass transition temperature, thermal decomposition, flammability (reaction to small flame), and burning behavior of the thermosets are investigated using differential scanning calorimetry, thermogravimetric analysis, pyrolysis combustion flow calorimetry, UL 94-burning chamber testing, and cone calorimeter measurements.
Although P-contents are low at only 0.6 wt%, the study aims not at attaining V-0, but at presenting a proof of principle: Epoxy resinswith PDTT show promising fire performance, exhibiting a 25% reduction in total heat evolved (THE), a 30% reduction in peak heat release rate (PHRR) due to flame inhibition (21% reduction in effective heat of combustion (EHC)), and an increase in Tg at the same time. This study indicates that rigid aromatic hyperbranched polymeric structures offer a promising route toward multifunctional flame retardancy.
Recycling of crosslinked fiber-reinforced polymers is difficult. Moreover, as they are often based on flammable resins, additional additives are needed. So-called “vitrimers” open the possibility of Recycling and reprocessing and repairing with dynamically crosslinked chemistries. To date, vitrimer-based composites still need flame retardant additives, such as organophosphates. An additive-free vitrimer composite has not been reported. Herein, we synthesized an intrinsic flame-retardant vitrimer, relying on vinylogous polyurethanes containing covalently installed phosphonates as flame-retardant units and prepared glassfiber-reinforced composites. We studied recycling and flame retardant properties and compared the data to phosphorus-free vitrimers and conventional epoxy resins (with and without additive flame retardant).
Our phosphonate-based vitrimer proved in first tests, a flame retardant effect comparable to commercial flame retardant resins. The bending strength and bending modulus for the phosphorus-vitrimer glass fiber composites were comparable to glass fiber composites with permanently cross-linked epoxies. In summary, we were able to prove that the covalent installation of phosphonates into vitrimers allows the preparation of recyclable and intrinsic flame retardant composites that do not need flame retardant additives. We believe this concept can be expanded to other polymer networks and additives to generate recyclable and sustainable high-performance materials.
Scientific publications addressing the durability of the flame retardance of cables during their long-term application are rare and our understanding lacks. Three commercial flame retardants, aluminum hydroxide, aluminum diethyl phosphinate (AlPi-Et), and intumescent flame retardant based on ammonium polyphosphate, applied in ethylene-vinyl acetate copolymer (EVA) model cables, are investigated. Different artificial aging scenarios were applied: accelerated weathering (UV-irradiation/temperature/rain phases), humidity exposure (elevated temperature/humidity), and salt spray exposure. The deterioration of cables’ surface and flame retardancy were monitored through imaging, color measurements, attenuated total reflectance Fourier transform infrared spectroscopy, and cone calorimeter investigations. Significant degradation of the materials’ surface occurred. The flame retardant EVA cables are most sensitive to humidity exposure; the cable with AlPi-Et is the most sensitive to the artificial aging scenarios. Nevertheless, substantial flame retardance persisted after being subjected for 2000 h, which indicates that the equivalent influence of natural exposure is limited for several years, but less so for long-term use.
First phosphorus AB2 monomer for flame-retardant hyperbranched polyphosphoesters: AB2vs. A2 + B3
(2019)
Branched polymers are an important class of polymers with a high number of terminal groups, lower viscosity compared to their linear analogs and higher miscibility, which makes them especially interesting for flame retardant applications, where the flame retardants (FR) are blended with another polymer matrix. Hyperbranched polyphosphoesters (hbPPEs) are gaining more and more interest in the field of flame retardancy, as low molar mass FRs often have the disadvantage of blooming out or leaching, which is not desired in consumer products. Here, we present the first phosphorus-based AB2 monomer for the synthesis of hbPPEs and assess its flame-retardant performance in an epoxy resin compared to a hbPPE synthesized by an A2 + B3 approach. The hbPPE synthesized from an AB2 monomer exhibited a slightly higher performance compared to a similar hbPPE, which was prepared by A2 + B3 polyaddition, probably due to its higher phosphorus content.
Nowadays, various polymeric materials are used in E&E applications with sufficient flame retardance by adding rather different flame retardants. It doesn’t matter whether cables are used outdoor or are installed indoor as building products, the weathering exposures such as UV radiation, humidity and variation in temperature occur and influence the flame-retardant property. Recently, the lifetime of the flame retardance itself becomes an increasingly important factor. In this work, several devices were used to perform accelerated artificial ageing simulating different environment exposures.
The comprehensive and global understanding of the durability of flame retardance in dependence on the weathering or ageing conditions is still a matter of discussion. Therefore, the weathering resistance of various halogen-free fire-retarded polymers was investigated in this work. Polymeric systems with different kinds of fire retardants were chosen, including various fire retardant mechanisms. Ethylene Vinyl Acetate (EVA) blends with high amounts of inorganic flame retardant such as aluminum hydroxide (ATH), boehmite and synergists, which mainly dilutes the polymer resin work as heat sink and cooling agent, and enhance residue formation was examined. Thermoplastic Polyurethane (TPU) was modified with melamine cyanurate (MC), which mainly acts by changed melt flow and dripping behavior as well as fuel dilution. Additionally, aluminum diethylphosphinate and boehmite are induced as assistant flame retardant. Furthermore, glass fiber reinforced Polyamide 66 (PA) was investigated containing different kinds of aluminum diethylphosphinate based flame retardant mixtures, which acts by flame inhibition and additional char formation.
The degradation of the surface was analyzed after the different weathering conditions. Most of the specimens exhibited an intensive material degradation at the top surface accompanied by a distinct discoloration, e.g. getting darker or showing yellowing. The weathering of the EVA samples lead to numerous cracks (already) after 4000 h. The corresponding changes in the chemical structure was investigated by ATR FT-IR for all materials.
The flammability was investigated by cone calorimeter, UL-94 burning chamber, and oxygen index (LOI) using plate and bar specimens. The flame retardance of most of the materials studied degrades only slightly or were rather stable for the investigated exposure times. Interestingly, also some opposite results were found. EVA modified by different inorganic flame retardants such as ATH achieved higher LOI after exposing in the humidity chamber and the accelerated oxidation under water in the autoclaves. It is suggested that the particle size of ATH and boehmite plays an important role, when these flame retardants agglomerate at the surface during accelerated weathering.
Both materials, EVA and TPU, were also investigated as cable jackets. While EVA modified with inorganic flame retardants exhibits low-smoke and non-dripping fire behavior, TPU flame-retarded with MC yields cables with pronounced melt-dripping. Cone calorimeter tests were carried out using cable rafts of the size of 100 mm * 100 mm as well as our self-made cable module test, which simulates the vertical full-scale test of a bundle of cables at the bench-scale. Both methods were used to investigate the weathering resistance of the flame retardance in cables. The results of the cable module test for the flame-retarded EVA cables were only slightly affected even when a long time hydrothermal ageing was carried out. This is because of inorganic residue which just delays the fire growth but does not extinguish. However, for the flame-retarded TPU cable jackets, the cable module test exhibited an accelerated fire spread and a melt-dripping behavior which was promoted by weathering exposure.
The impact of polyaniline in phosphorus flame retardant ethylene-propylene-diene-rubber (EPDM)
(2019)
Usually elastomers are loaded with high amounts of flame retardants to fulfill fire safety requirements. In this study the potential char precursor polyaniline (PANI) and the established fire retardant pentaerythritol (PER) were implemented in ethylene-propylene-diene monomer rubber (EPDM). PANI and PER were used in low loadings (7 phr) and combined with two phosphorous flame retardants, Ammonium polyphosphate (APP) and a piperazine-pyrophosphate/phosphoric acid compound (FP), to boost their performance. A comprehensive study is presented, explaining the impact of PANI on curing and mechanical properties, including compensation for the plasticizer-like effect of APP in EPDM, and improved flame retardancy. In the cone calorimeter test, the combination of EPDM/FP/PANI reduced the effective heat of combustion by 20%. All nine EPDM rubber compounds were investigated with the LOI and UL 94 tests, cone calorimeter, FMVSS 302 and glow wire testing to quantify fire performance. The PANI containing EPDM rubbers, EPDM/APP/PANI and EPDM/FP/PANI outperformed the corresponding PER containing, EPDM/APP/PER and EPDM/FP/PER rubbers in various tests. Moreover, the study investigated the impact of PANI and PER on the mode of action of the phosphorus species and showed that the addition of PANI increased the amount of phosphorus in the condensed phase. To receive a broader understanding of the flame retardant mode of action of PANI in combination with APP and FP, calculations were carried out to estimate the impact of PANI on the protective layer effect.