Artificial bone replacement by individual customized three-dimensional resorbable bioactive glass has not yet been widely established in the clinical use. This is mainly due to the antagonism of sintering ability and suitable bioactivity. Competitive crystallization often prevents the generation of dense sintered bodies, especially for additive manufactured 3D structures. Previous studies of the fluoride-containing glass F3 have shown its potential to combine both sintering ability and suitable bioactivity. Furthermore, the occurring sintering blockade by surface crystallization of Na2CaSi2O6 was tunable by glass particle size.
In this study the glasses F3, F3-Cu with 1 mol% CuO added at the expense of CaO and the well-known 13-93 were chosen to determine the influence of surface crystallization on 3D printed sinter bodies. For this purpose, grain size fractions in range of smaller 32 µm to 315 µm in fraction size of 6-20 µm were sieved from jaw crushed glass frit as well as glass cubes were cut from casted blocks for all glasses. Sintering behavior of both pressed and printed powder compacts was observed via heating microscopy. Crystallization was determined by DTA and crystallization progress was monitored on fractured sinter bodies and polished cubes via electron and laser scanning microscopy as well as with diffractometry.
Depending on grain size the formation of crystalline support framework along former grain boundaries shows the capability to stabilize fully densified sinter bodies before softening. Beside of this, the generation of complex hierarchic porosity was possible as well.
Chemically modified bioactive glasses based on ICIE16 were prepared with the melt-quenching method using water as a quenching medium. The sinterability of these bioactive glasses was investigated and is discussed in this article. The sintering experiments were conducted with different sintering temperatures, sintering times and heating rates. Those parameters are crucial for dense glass with an amorphous structure. The particle size (d50) of the starting glass powder was determined at 88 μm and kept constant. The pre-pressed glass pellets were cold-isostatically pressed at 300 MPa to a green density of around 63 %. Density development, phase identification, shrinkage behavior and the microstructure were investigated to determine the sinterability of the developed glasses. The glass powders were sintered at different temperatures inside the processing window while crystallization was monitored. The results have shown that the sinterability of the developed glasses strongly dependsonthe proposed chemical additions. The highest density reached was 96 %, which belongs to BP1 glass with sintering conditions of 20 K/min heating rate for 60 min at 750 °C.