Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Dokumenttyp
- Vortrag (6) (entfernen)
Sprache
- Englisch (6) (entfernen)
Referierte Publikation
- nein (6)
Schlagworte
- Corrosion resistance (6)
- Heat treatment (5)
- Stainless steel (5)
- Corrosion (4)
- Corrosion testing (3)
- EPR (3)
- KorroPad (2)
- Martensitic stainless steels (2)
- Pitting corrosion (2)
- ThermoCalc (2)
- Atmospheric corrosion (1)
- Martensite (1)
- Nitrogen (1)
- Quenching and partitioning (1)
- REM (1)
- Stainless steels (1)
- Surface treatment (1)
Organisationseinheit der BAM
Eingeladener Vortrag
- nein (6)
Nickel-free, nitrogen alloyed austenitic stainless-steels, with about 19 wt.-% Mn and 0,8 wt. % N, are an interesting alternative to classic CrNi austenitic stainless steels due to their superior mechanical properties (Rm > 900 MPa, A5 > 50 %, Av > 350 J) in the solution annealed condition. The formation of chromium-rich nitrides during suboptimal heat treatment, processing or application leads to an inhomogeneous distribution of alloying elements in the microstructure, which reduces the corrosion resistance. Consequently, an accurate knowledge of the sensitization behavior is indispensable for the use of nickel-free, high-nitrogen austenitic stainless steels. The relationship between artificial aging, phase formation and corrosion resistance was investigated on the alloys X8CrMnN18-19 (1.3815) and X8CrMnMoN18-19-2 (1.4456), both alloyed with 0,8 wt.-% Nitrogen, in the present work. The microstructural evolution was studied by LM and SEM while the corrosion resistance was characterized with the electrochemical potentiodynamic reactivation (EPR) and the KorroPad indicator-test. Both alloys showed increased corrosion susceptibility within critical aging parameters. Finally, a sensitization diagram was described successfully for both alloys showing the positive effect of molybdenum.
The copper alloyed stainless steel 1.4542 (X5CrNiCuNb16-4) is used in different areas due to its good mechanical properties and corrosion resistance. Strength and corrosion resistance can be adjusted by the heat treatment, which is of importance for the application of this alloy. The mechanical properties (strength and hardness) are attributed to the dispersive precipitation of the copper rich ε–Phase. The additional precipitation of chromium carbides can reduce the corrosion resistance. Different ageing states were produced to investigate the precipitation behaviour with various methods. Furthermore, the influence of cold-rolling on the precipitation behaviour was studied in comparison to a solution annealed state without deformation. The microstructure was studied by SEM and the variations of hardness and magnetic proportion were characterised. The electrochemical potentiodynamic reactivation (EPR) was used to determine the corrosion resistance and detect chromium depletion in all heat-treated states. The results show that a work hardening accelerates the precipitation rate, while ageing at 600 °C reduces the corrosion resistance due to chromium depletion.
The corrosion resistance of stainless-steels grades is of high importance for the technical safety in different environmental conditions. Processing and surface finish influences the corrosion resistance of ferritic stainless steels, which may be considered for some application in marine environment. Three ferritic stainless steel alloys (X2CrNi12, X2CrTiNb18 and X2CrMoTi18-2) were exposed in four different surface finishes (rolled, dry grinding, glass beaded and electro polished) for five years in marine environment to obtain reliable information about the corrosion resistance. All samples were assessed after 22 and 60 months according to DIN EN ISO 10289 in validation degrees from 1 to 10. Complementary investigation using accelerated chamber test (salt spray test followed by four weeks storage at 30 °C / 80 % relative humidity) and short-term electrochemical methods (electrochemical potentiodynamic reactivation, pitting potentials and the KorroPad method) were conducted to compare their results. The presentation gives an overview on all methods and the generated results, which show benefits and restrictions of long-term, accelerated and short-term corrosion tests.
The double loop electrochemical potentiodynamic reactivation (EPR) method is a standardised procedure for detecting and quantifying sensitisation on austenitic, ferritic and ferritic-austenitic stainless-steel grades. This sensitisation is caused by microstructural alternations, as the formation of chromium carbides, nitrides or sigma-phases, which generate local chromium depleted zones nearby. The latter strongly influence the corrosion resistance and the electrochemical response of a stainless steel during electrochemical potentiodynamic reactivation, providing important information on the degree of chromium depletion. In case of martensitic stainless steels, which are used for cutlery and surgical instruments, the heat treatment has a strong impact on the microstructure, the material properties and especially on the corrosion resistance. To study this interaction, the EPR method was modified for the application on martensitic stainless steels with about 13 wt.-% chromium. Different H2SO4 concentrations and EPR-parameters were tested and compared on two standard martensitic stainless-steel grades (AISI 420 A / X20Cr13 and AISI 420 C / X46Cr13) to define applicable parameters. Afterwards, these parameters were used to study the effect of austenitisation time and cooling rate on the corrosion resistance of both martensitic stainless steels. The response of both alloys was different due to the different carbon levels, which will be explained by microstructural investigations in detail. All results allow postulating a process window, in which chromium depletion is suppressed and an optimised corrosion resistance is guaranteed. Based on this research, the modified EPR-test is now used to control the heat treatment and its impact on the corrosion resistance of martensitic stainless steels in the cutlery industry. The EPR-test is thus an interesting alternative for manufacturers, processors, users and researchers to the time-consuming exposition test normally used to characterise the corrosion resistance of martensitic stainless steels.
The novel heat treatment concept of “Quenching and Partitioning” (Q&P) enables producing low alloyed martensitic steels with high strength and formability. Therefore austenite, retaining from a quenching temperature between Mf and Ms, is stabilised by carbon diffusion. This stabilised austenite transforms in martensite (TRIP effect) under mechanical loading. Current investigations on the Q&P heat treatment of martensitic stainless steels reveal a further enhancement of mechanical properties due to higher amounts of austenite. Thus a tensile strength of 1.800 MPa and a maximum elongation of 20 % are possible, while mechanical properties under compression are much higher due to a distinct SD effect.
The presentation aims to gain a further understanding of the Q&P heat treatment and the resulting mechanical properties for the steel X46Cr13, especially the mechanical behaviour under dynamic mechanical loading condition. Results of drop work and Split Hopkinson Pressure Bar test confirms the findings of quasi static compression test. Furthermore, Charpy impact tests show higher impact toughness compared to the common heat treatment of quenching and tempering (Q&T). Complementary investigations indicate a higher corrosion resistance of Q&P compared to Q&T.
The corrosion resistance of martensitic stainless steels (MSS) depends strongly on the chemical composition and the applied heat treatment. Both determine the distribution of the alloying elements in the microstructure and the resulting material properties. The addition of nitrogen is known to be beneficial for the pitting corrosion resistance of stainless steels. In case of MSS this effect is not only connected to nitro-gen itself because nitrogen can be used to substitute carbon which also influences the result of the heat treatment process. This paper shows the effect of nitrogen on the corrosion resistance in relation to the hardening process of MSS. Therefore the effects of austenitization temperature and cooling rate on microstructure, hardness and corrosion resistance were studied on the MSS X30CrMoN15 1 and X50CrMoV15. The effect of different cooling rates was studied using the jominy end quench test. The changes in corrosion resistance were detected with electrochemical potentiodynamic reactivation (EPR) and by the determination of critical pitting potentials. Besides this experimental approach thermodynamic calculations with the software thermocalc will be presented and used for the interpretation of the effect of nitrogen on the corrosion resistance of MSS.