Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Erscheinungsjahr
- 2021 (2) (entfernen)
Dokumenttyp
- Beitrag zu einem Tagungsband (2) (entfernen)
Sprache
- Englisch (2)
Referierte Publikation
- nein (2)
Schlagworte
- Archaeological provenance (1)
- Biocorrosion (1)
- Dead Sea Scrolls (1)
- Environmental condition (1)
- Flow Model (1)
- Fragmented manuscripts (1)
- Hi-Tension (1)
- Korrosion (1)
- MIC (1)
- Microbiologically influenced corrosion (1)
- Modelling (1)
- Text analysis (1)
- X-ray based techniques (1)
Organisationseinheit der BAM
- 4 Material und Umwelt (2) (entfernen)
The first manuscripts from the Qumran caves were found in 1947. Within the following 10 years, clandestine and legal excavations revealed some 900 highly fragmented manuscripts from the late Second Temple period. This collection is generally known as Scrolls of the Judea Desert or Dead Sea Scrolls (DSS). For many years after their discovery, text analysis and fragmeents attribution were the main concern of the scholars dealing with the scrolls. The uncertain archaeological provenance of the larger part of the collection added an additional difficulty to the formidable task of sorting some 19000 fragments. After 60 years of scholar research the question of origin, archaeological provenance and correct attribution of the fragmenst are still hotly debated. To dtermine a possible contribution to the debate from the point of view of writing materials, we used otpical and electron microscopy, various X-ray based techniques as well as vibratiional sprectroscopy. We validated our approach with SY - based studies using the advantages of the synchroton radiation source with respect to the benchtop devices. Our laboratory studies showed that often production and storage locality could be distinguished thenks to the specific residues ("fingerprint") they left on the material. Moreover, we have diescovered that diferrent parchment production processses coexisted in the antiquity, and the resulting writing materials can readily be distinguished.
MFC was used to study the corrosiveness of iron-utilizing methanogen, Methanobacterium IM1 under flow conditions. Comparing against electrical SRM, Desulfovibrio ferrophilus IS5, results showed under standard mesophilic conditions, average corrosion rates of Methanobacterium IM1 was double that of SRM. The highest corrosion rate of Methanobacterium IM1 reached up to 0.60 mm/yr under neutral conditions, and severe pitting was observed on the iron surface. Furthermore, the corrosion products of Methanobacterium IM1 were characterized with TOF-SIM, FIB-SEM and EDX, and preliminary results revealed FeCO3 is not the only corrosion product of Mi-MIC, as previously reported. Under low pH conditions, the maximum corrosion rate of Methanobacterium IM1 reached 1.57 mm/yr, which resulted in severed deformity of the iron specimen. Additional comparisons using different types of incubation material were conducted to standardize MFC MIC testing.