Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Dokumenttyp
- Zeitschriftenartikel (54) (entfernen)
Schlagworte
- Corrosion (21)
- KorroPad (13)
- Nichtrostender Stahl (12)
- Korrosionsschnelltest (11)
- Passivschicht (11)
- Korrosion (8)
- Carbon steel (5)
- Corrosion testing (4)
- Impurities (4)
- Stainless steel (4)
- EPR (3)
- Geothermie (3)
- Pitting corrosion (3)
- Al2O3 (2)
- Alloy 31 (2)
- Aluminium (2)
- Anlagensicherheit (2)
- Austenitic stainless steel (2)
- CCUS (2)
- Carbon dioxide (2)
- Coating (2)
- Condensate (2)
- Copper (2)
- Corrosion rate (2)
- Corrosion resistance (2)
- Gel electrolytes (2)
- Geothermal energy (2)
- Grinding (2)
- Heat treatment (2)
- Legierungen (2)
- Qualitätssicherung (2)
- Steel (2)
- Zinc coatings (2)
- Abrasive belt (1)
- Additive manufacturing (1)
- Agar (1)
- Ageing treatment (1)
- Aktiv-Passiv-Element (1)
- Al-Composite (1)
- Al/SiO2 composite (1)
- Alkali-activated materials (1)
- Aquifer fluid (1)
- Atmospheric corrosion (1)
- Atmospheric exposure (1)
- Atmosphärische Korrosion (1)
- Behmite (1)
- Belüftungselement (1)
- Bimetallkorrosion (1)
- Binary zinc alloys (1)
- Brass (1)
- CCS (1)
- CCUS, supercritical/dense phase CO2, carbon steels, martensitic steel, superaustenite steel, droplet corrosion (1)
- CO2 pipeline transport (1)
- CO2 quality (1)
- Carbon capture (1)
- Carbon capture storage (1)
- Carbon capture, utilization and storage technology (1)
- Casing (1)
- Cement (1)
- Contact angle (1)
- Corrosion costs (1)
- Corrosion protection (1)
- Corrosivity category (1)
- Crevice corrosion (1)
- Critical chloride content (1)
- Critical pitting temperature (1)
- Dealloying (1)
- Disinfectants (1)
- Drinking water (1)
- Electrochemical characterisation (1)
- Electrochemical deposition (1)
- Electrochemical methods (1)
- Electrochemical potentiodynamic reactivation (1)
- Electrochemical potentiokinetic reactivation (1)
- Elektrochemie (1)
- Energy systems (1)
- Environmental Chemistry (1)
- Explosion (1)
- FT-IR (1)
- Flue gas desulphurisation facilities (1)
- Free weathering (1)
- Gel-type electrolytes (1)
- Gelartige Elektolyte (1)
- Geothermal (1)
- Green-Death solution (1)
- Growth defects (1)
- Gutachten (1)
- High‐nitrogen steel (1)
- ISO 9223 (1)
- In-situ ED-XRD (1)
- Iron–chromium–nickel alloy (1)
- Konzentrationselement (1)
- Korrosionsprüfung (1)
- Korrosionsschutz (1)
- Korund (1)
- Kupferazid (1)
- Lead (1)
- Lean duplex (1)
- Lochkorrosion (1)
- Magnesium (1)
- Marine atmosphere (1)
- Martensitic stainless steel (1)
- Martensitic steel (1)
- Martensitic steels (1)
- Mass loss (1)
- Material properties (1)
- Materials (1)
- Materials Chemistry (1)
- Materialuntersuchung (1)
- Mechanical Engineering (1)
- Mechanical properties (1)
- Mechanical strength (1)
- Mechanics of Materials (1)
- Metals and Alloys (1)
- Oxyfuel (1)
- PVD hard coating (1)
- Passive film (1)
- Passivity (1)
- Physical vapour deposition (PVD) (1)
- Pinholes (1)
- Pipeline network (1)
- Pitting (1)
- Polarisation (1)
- Polyaniline (1)
- Preventive strategies (1)
- Protection (1)
- Recommendations (1)
- Schadensanalyse (1)
- Schleifen (1)
- Semiconductive layer (1)
- Sensitisation (1)
- SiO2 Nanoparticle (1)
- Silica (1)
- Stainless steels (1)
- Steel corrosion (1)
- Steel-concrete interface (1)
- Surface (1)
- Surfaces, Coatings and Films (1)
- Survey (1)
- Tafel Plot (1)
- Ternary zinc alloys (1)
- TiMgN (1)
- Titanium nitride (1)
- Umlaufkühler (1)
- Utilization, and storage (CCUS) technology (1)
- Wetting (1)
- Whole-chain CCS scenario (1)
- X-ray photoelectron spectroscopy (1)
- Zinkdeckschichten (1)
- Znc (1)
- magnesium (1)
Organisationseinheit der BAM
- 7.6 Korrosion und Korrosionsschutz (54) (entfernen)
The corrosion behavior of galvanized steels and zinc components under atmospheric exposure depends mostly on the corrosion product‐based cover layer formation under the prevailing conditions. The use of agar‐based gel electrolytes makes it possible to use electrochemical methods to obtain a characteristic value from these cover layers that describe their current and future protective capacity. It is shown here that different states of galvanized steel can be distinguished very well under laboratory conditions and that this method is also suitable for use under practical conditions. Based on the characteristic values and assuming future time of wetness, it is very easy to draw up a forecast for the future corrosion rate, which provides plausible values.
Durch Auslagerungs- und elektrochemische Tests im Labor kann das Korrosionsverhalten verschiedener metallener Werkstoffe beurteilt werden. Aus den Versuchsergebnissen, die in verschiedenen synthetischen Geothermalwässern im Labor erzielt wurden, lassen sich die folgenden Schlussfolgerungen ziehen:
• Die Anfälligkeit für Spaltkorrosion wurde als wichtigster Aspekt für die Werkstoffqualifizierung ermittelt.
• Der niedriglegierte Stahl 25CrMo4 zeigte bei niedrigem Salzgehalt in MB-Geothermalwasser eine gleichmäßige Korrosion unterhalb der akzeptierten Schwelle von 0,3 mm/Jahr. Daher kann er als geeignet für geothermische Bedingungen mit niedrigem Salzgehalt angesehen werden, wie sie für MB getestet wurden. Es besteht keine Notwendigkeit, auf höherlegierte (teurere) Werkstoffe auszuweichen. Ein niedrigerer pH-Wert (wie bei LHD) führt zu Korrosionsraten oberhalb der akzeptablen Grenzwerte, so dass die niedriglegierten Werkstoffe nicht für Flüssigkeiten mit niedrigem pH-Wert geeignet sind.
• Stark salzhaltige Geothermalwässer erfordern höherlegierte Werkstoffe, da die Korrosionsrate von niedriglegiertem Stahl zu hoch ist.
• Der Duplexstahl X2CrNiMo22-5-3 und der Superduplexstahl X2CrNiMoCuWN25-7-4 wurden aufgrund ihrer kritischen Anfälligkeit für örtliche Korrosion in Form von Loch- und Spaltkorrosion unter Betriebsbedingungen nicht als geeignet für geothermische Anwendungen in Geothermalwässern mit einer mit NDB und ORG vergleichbaren Zusammensetzung angesehen.
• Der superaustenitische Stahl X1CrNiMoCu32-28-7 eignet sich für ORG und salzarme Wässer. In NDB-Geothermalwasser wurde er bei 100 °C als geeignet angesehen. Jedoch schränkt seine Anfälligkeit für Spaltkorrosion seine Anwendbarkeit ein. Neben seiner guten Korrosionsbeständigkeit ist sein Repassivierungsverhalten für seine begrenzte Anwendbarkeit in Geothermalwässern mit niedrigem pH-Wert verantwortlich.
• Die Nickelbasislegierung NiCr23Mo16Al wurde als geeignet erachtet und stellt eine sichere Option für den Einsatz in geothermischen Anlagen dar, selbst wenn mit stark salzhaltigem Geothermalwasser gearbeitet wird.
Durch Auslagerungs- und elektrochemische Tests im Labor kann das Korrosionsverhalten verschiedener metallener Werkstoffe beurteilt werden. Aus den Versuchsergebnissen, die in verschiedenen synthetischen Geothermalwässern im Labor erzielt wurden, lassen sich die folgenden Schlussfolgerungen ziehen:
• Die Anfälligkeit für Spaltkorrosion wurde als wichtigster Aspekt für die Werkstoffqualifizierung ermittelt.
• Der niedriglegierte Stahl 25CrMo4 zeigte bei niedrigem Salzgehalt in MB-Geothermalwasser eine gleichmäßige Korrosion unterhalb der akzeptierten Schwelle von 0,3 mm/Jahr. Daher kann er als geeignet für geothermische Bedingungen mit niedrigem Salzgehalt angesehen werden, wie sie für MB getestet wurden. Es besteht keine Notwendigkeit, auf höherlegierte (teurere) Werkstoffe auszuweichen. Ein niedrigerer pH-Wert (wie bei LHD) führt zu Korrosionsraten oberhalb der akzeptablen Grenzwerte, so dass die niedriglegierten Werkstoffe nicht für Flüssigkeiten mit niedrigem pH-Wert geeignet sind.
• Stark salzhaltige Geothermalwässer erfordern höherlegierte Werkstoffe, da die Korrosionsrate von niedriglegiertem Stahl zu hoch ist.
• Der Duplexstahl X2CrNiMo22-5-3 und der Superduplexstahl X2CrNiMoCuWN25-7-4 wurden aufgrund ihrer kritischen Anfälligkeit für örtliche Korrosion in Form von Loch- und Spaltkorrosion unter Betriebsbedingungen nicht als geeignet für geothermische Anwendungen in Geothermalwässern mit einer mit NDB und ORG vergleichbaren Zusammensetzung angesehen.
• Der superaustenitische Stahl X1CrNiMoCu32-28-7 eignet sich für ORG und salzarme Wässer. In NDB-Geothermalwasser wurde er bei 100 °C als geeignet angesehen. Jedoch schränkt seine Anfälligkeit für Spaltkorrosion seine Anwendbarkeit ein. Neben seiner guten Korrosionsbeständigkeit ist sein Repassivierungsverhalten für seine begrenzte Anwendbarkeit in Geothermalwässern mit niedrigem pH-Wert verantwortlich.
• Die Nickelbasislegierung NiCr23Mo16Al wurde als geeignet erachtet und stellt eine sichere Option für den Einsatz in geothermischen Anlagen dar, selbst wenn mit stark salzhaltigem Geothermalwasser gearbeitet wird.
The corrosivity of atmospheres in Europe has changed significantly in recent decades. For the Federal Republic of Germany, no current values for the corrosion rate based on 1‐year atmospheric exposure of standard specimens can be found in the scientific literature after 2000. This paper presents results from a field exposure study in the Berlin metropolitan area and Helgoland in 2016. Based on standard specimens, values for the corrosion rate and the corresponding atmospheric corrosivity category are determined for open exposure and indirect weathering in a ventilated enclosure as sheltering after 1 year of exposure. The results prove that determined corrosivity categories are material‐specific. Sheltered exposure is a typical atmospheric situation for many building components. It allows statements on the effect of the concentration of airborne substances on the corrosivity beyond the normative requirements.
Novel agar-based test electrolytes are used to perform electrochemical corrosion investigations on ZnFe and ZnNi binary as well as ZnFeMo ternary zinc coatings. The objectives of the electrochemical investigations include the characterization of the corrosion behavior, the description of the protective effect of the coatings as well as the investigation of the layer formation and degradation under artificial aging. ZnFe and ZnFeMo coatings are applied with varying iron content as well as an additional passivation layer, respectively, to study the effect on corrosion resistance. The results show that the protective effect of the coatings is not negatively influenced by different iron contents or the addition of molybdenum. Additional passivation of the ZnFe-containing coatings by means of a passivating agent leads to a significant improvement in the protective effect. Artificial aging leads to slight degradation of the additional passivation layer whereas coatings without post-treatment enhance their protective effect by the formation of corrosion product layers.
Ein Umlaufkühler ist im Betrieb explodiert. Splitter des zerborstenen Gehäuses aus Kunststoff wurden mit dem Kühlwasser in die Umgebung geschleudert, am Betriebsort entstand Personenschaden. Bei Funktionsprüfungen am beschädigten Gerät traten unerwartet - aber reproduzierbar - Knalleffekte bei Berührung der Außenoberfläche der Kupfer-Kühlschlange auf. Ein möglicher Mechanismus konnte im Labor durch Synthese von Kupferazid auf Kupferproben und Auslösung vergleichbarer Knalleffekte nachgestellt werden. Damit ist die Plausibilität des beschriebenen Schadensereignisses mit diesem oder einem ähnlich reagierenden Stoff belegt. Ein eindeutiger Nachweis darüber, dass bei dem aufgetretenen Schadensfall dieselbe chemische Reaktion stattgefunden hat, war nicht möglich, da die Belag-Überreste aus dem explodierten Kühlgerät für eine Analyse nicht mehr in ausreichender Menge verfügbar gewesen sind.
To set up recommendations on how to define “reasonable minimum composition thresholds” for CO2 streams to access CO2 pipeline networks, we investigated potential impacts of CO2 streams with different and temporally variable compositions and mass flow rates along the CCS chain. All investigations were based on a generic “CCS cluster scenario” in which CO2 streams captured from a spatial cluster of eleven emitters (seven fossil-fired power plants, two cement plants, one refinery and one steel mill) are collected in a regional pipeline network. The resulting CO2 stream (19.78 Mio t impure CO2 per year) is transported in a trunk line (onshore and offshore) and injected into five generic replicate storage structures (Buntsandstein saline aquifers) offshore. Experimental investigations and modeling of selected impacts revealed beneficial as well as adverse impacts of different impurities and their combinations. Overall, no fundamental technical obstacles for transporting, injecting and storing CO2 streams of the considered variable compositions and mass flow rates were observed. We recommend to define minimum composition thresholds for each specific CCS project through limiting
i) the overall CO2 content,
ii) maximum contents of relevant impurities or elements,
iii) acceptable variability of concentrations of critical impurities, and defining impurity combinations to be avoided.
A global transition towards more sustainable, affordable and reliable energy systems is being stimulated by the Paris Agreement and the United Nation's 2030 Agenda for Sustainable Development. This poses a challenge for the corrosion industry, as building climate‐resilient energy systems and infrastructures brings with it a long‐term direction, so as a result the long‐term behaviour of structural materials (mainly metals and alloys) becomes a major prospect. With this in mind “Corrosion Challenges Towards a Sustainable Society” presents a series of cases showing the importance of corrosion protection of metals and alloys in the development of energy production to further understand the science of corrosion, and bring the need for research and the consequences of corrosion into public and political focus. This includes emphasis on the limitation of greenhouse gas emissions, on the lifetime of infrastructures, implants, cultural heritage artefacts, and a variety of other topics.
The suitability of an Al2O3 coating for corrosion protection on X20Cr13 was evaluated in various artificial geothermal brines, focusing on the influence of different pH (4, 6 and 8) and their chemical compositions on the coating properties. All experiments were performed in the laboratory using autoclaves at 150 ◦C and 1 MPa in deaerated condition for 1 and 7 days. Results showed that the pH of geothermal waters is the most detrimental factor in the transformation of ɣ-Al2O3 and its protective abilities. Delaminations were found in the Coating exposed to geothermal brines with pH 4. FTIR spectra indicated a transformation of ɣ-Al2O3 to boehmite AlOOH after exposure to pH 4 and 6, and bayerite Al(OH)3 was formed after exposure to pH 8. Different Crystal structures of the hydrated Al2O3 also contribute to the stability of the coatings, observed by the SEM- EDX of the surface and cross-section of coatings. This study indicated that ɣ-Al2O3 sol-gel coating presents a promising aspect of corrosion protection in geothermal environment with a neutral pH.
Nickel‐free high‐nitrogen‐alloyed stainless steels like the P2000 (X13CrMnMoN18‐14‐3) were developed to enhance the strength and corrosion resistance of austenitic stainless steels like 304 and 316 while keeping the typical high ductility. The mechanical and corrosive properties of P2000 were investigated and compared with 304 and 316 to highlight the application opportunities of this new alloy. The microstructure of the solution‐annealed condition was characterised by electron backscatter diffraction and the mechanical properties were studied by uniaxial tensile tests, Charpy impact tests and hardness measurements. The passivation behaviour was analysed using the electrochemical potentiodynamic reactivation, whereas the pitting corrosion resistance was compared by pitting potentials and pitting temperatures. However, secondary thermal influences or suboptimal heat treatment can impair the corrosion resistance due to the precipitation of secondary phases and the resulting sensitisation. Thermodynamic calculations and artificial ageing treatment in the range of 500–900°C for up to 100 h were used to determine critical time–temperature parameters for sensitisation. The microstructure of the various aged states was evaluated by scanning electron microscopy and compared with the degrading corrosion resistance characterised by the KorroPad method.
Although zinc and zinc coatings have been widely used for corrosion protection for decades new zinc coatings are constantly being developed. Characterizing the corrosion protectiveness of these new coatings, however, should not be underestimated. While exposure tests are time intensive, cyclic tests can only be used for a very limited field of application. Thus, electrochemical measurements provide both an efficient and an effective alternative. Conventional aqueous bulk electrolytes influence the surface layers of a tested zinc coating and are therefore not reliable. Gel electrolytes, however, have evolved over the last few years, are minimally invasive and provide reliable results.
This work describes experiments with gel electrolytes made of agar. Unlike previous work, it proposes a composition of gel electrolyte for minimally invasive description of the protective power of naturally formed oxide layers on zinc and zinc coatings. Therefore, as a first part, the gel electrolyte made of agar is verified as a method for zinc and zinc-coated samples. Afterwards, this paper introduces the corrosion product layer resistance RL as a promising parameter to evaluate the protective power of zinc coatings. Results are verified with EIS and FTIR measurements. An example on a representative zinc coating demonstrates the practical application.
Geothermal brines often contain high amounts of lead and copper ions that can precipitate as native Cu and Pb as consequence of galvanic corrosion when brines react with carbon steel materials. This contribution evaluates which materials could overcome the problem of galvanic corrosion at geothermal environment.
The behavior of these materials in water containing high chloride concentration (> 100 g/L NaCl) as well as various amounts of dissolved bCl2 and/or CuCl2 was characterized by electrochemical and exposure measurements.
Both methods reveal carbon steel suffers corrosion susceptibility, accompanied by Cu◦ and/or Pb◦ precipitation on the surface. Electrochemical measurements on stainless steels result in significant difference in corrosion and repassivation potentials (Ecorr = -189 mV, Erep = 70 mV), indicating a good corrosion resistance.
Al2O3 has been widely used as a coating in industrial applications due to its excellent chemical and thermal resistance. Considering high temperatures and aggressive mediums exist in geothermal systems, Al2O3 can be a potential coating candidate to protect steels in geothermal applications. In this study, γ-Al2O3 was used as a coating on martensitic steels by applying AlOOH sol followed by a heat treatment at 600 °C. To evaluate the coating application process, one-, two-, and three-layer coatings were tested in the artificial North German Basin (NGB), containing 166 g/L Cl−, at 150 °C and 1 MPa for 168 h. To reveal the stability of the Al2O3 coating in NGB solution, three-layer coatings were used in exposure tests for 24, 168, 672, and 1296 h, followed by surface and cross-section characterization. SEM images show that the Al2O3 coating was stable up to 1296 h of exposure, where the outer layer mostly transformed into boehmite AlOOH with needle-like crystals dominating the surface. Closer analysis of cross-sections showed that the interface between each layer was affected in long-term exposure tests, which caused local delamination after 168 h of exposure. In separate experiments, electrochemical impedance spectroscopy (EIS) was performed at 150 °C to evaluate the changes of coatings within the first 24 h. Results showed that the most significant decrease in the impedance is within 6 h, which can be associated with the electrolyte penetration through the coating, followed by the formation of AlOOH. Here, results of both short-term EIS measurements (up to 24 h) and long-term exposure tests (up to 1296 h) are discussed.
For reliability and safety issues of injection wells, corrosion resistance of materials used needs to be determined. Herein, representative low-cost materials, including carbon steel X70/1.8977 and low alloyed steel 1.7225, were embedded in mortar to mimic the realistic casing-mortar interface. Two types of cement were investigated: (1) Dyckerhoff Variodur commercial Portland cement, representing a highly acidic resistant cement and (2) Wollastonite, which can react with CO2 and become stable under a CO2 stream due to the carbonation process. Exposure tests were performed under 10 MPa and at 333 K in artificial aquifer fluid for up to 20 weeks, revealing crevice corrosion and uniform corrosion instead of expected pitting corrosion. To clarify the role of cement, simulated pore water was made by dispersing cement powder in aquifer fluid and used as a solution to expose steels. Surface analysis, accompanied by element mapping on exposed specimens and their crosssections, was carried out to trace the chloride intrusion and corrosion process that followed.
Indonesien gilt aufgrund seiner vielen Vulkane als einer der Hotspots für Geothermie. Doch Salz und Hitze setzen den Geothermie‐Anlagen zu und gefährden ihre Sicherheit und Wirtschaftlichkeit. Ein Team an der BAM hat günstigen, lokal verfügbaren Baustahl jetzt so beschichtet, dass ein nachhaltiger und sicherer Betrieb der Geothermie‐Kraftwerke möglich ist ‐ auch unter Extrembedingungen.
Das BAM‐Team will das Beschichtungssystem nun den Anwendern in Indonesien zur Verfügung stellen, damit es unter Realbedingungen in einem Geothermie‐Kraftwerk getestet werden kann. Der Schutz vor Korrosion ist mitentscheidend, weil sie die Lebensdauer dieser Kraftwerke bestimmt. Unsere Arbeit könnte die Effizienz der Energieproduktion mit Geothermie wesentlich verbessern.
The corrosion resistance of aluminium surfaces is closely linked to the surfacecstate after a grinding process. For years, iron‐containing abrasive materials were suspected to lead to increased corrosion susceptibility after processing of aluminium surfaces. To prove a possible correlation between the iron content of an abrasive and the corrosion behaviour of aluminium components, scientific investigations and experimentally practical corrosion tests are necessary.
For the current investigation, specimens of a technical Al‐Si alloy from the same batch were used. The test specimens were mechanically ground with various resin‐bonded model abrasives containing different iron contents. The performed corrosion tests did not reveal a negative influence of the different iron‐containing abrasives on the corrosion behaviour of the Al–Si alloy.
However, the most sensitive measuring method (electrochemical noise)
showed differences in the surface activity depending on the type of abrasive.
Susceptibility of 304 Stainless Steel to Crevice Corrosion in Electrochemically Active Fluids
(2020)
The susceptibility of Type 304 stainless steel (SS) to crevice corrosion upon contacting with electrochemically active fluids was investigated using exposure tests and stepwise potentiostatic polarization. Crevice materials made of 304 SS and polyether ether ketone (PEEK) were focused on in this study. The combined influence of oxidant and chloride concentration on crevice corrosion was examined in detail in the two types of crevice combinations (304 SS-to-PEEK and 304 SS-to-304 SS). The 304 SS specimens were strongly susceptible to crevice corrosion when coupled with 304 SS. Even at a low concentration of 5 mg/L free chlorine and 150 mg/L chloride, which is below nominal dilutions in beverage industries, the examined specimens underwent crevice corrosion in both crevices. The effect of water composition on crevice corrosion was also studied, indicating high susceptibility of 304 SS to crevice corrosion in low pH (pH ≤ 5) solutions. The corroded surface morphology was analyzed using scanning electron microscope, energy dispersive x-ray, and confocal.
Chloride contents at the steel–mortar interface that initiate steel corrosion were determined for carbon steel in alkali‐activated fly ash mortar for three different exposure conditions: exposure to 1 M NaCl solution; leaching in deionized water and then exposure to 1 M NaCl solution; and leaching in deionized water, aging in air at 20°C and natural CO2 concentration, and then exposure to 1 M NaCl solution. For comparison, a Portland cement mortar, exposed to 1 M NaCl solution, was studied. The median values of the corrosion‐initiating chloride contents (average over the full length of the rebar) in the alkali‐activated fly ash mortar varied between 0.35 and 1.05 wt% Cl with respect to binder, consistently lower than what was obtained for the Portland cement mortar, but with no clear trend regarding the exposure conditions. For most of the alkali‐activated fly ash mortar specimens, preferential corrosion at the connection between the working electrode and the external measurement setup was observed, while preferential corrosion did not occur for the Portland cement mortar. Scanning electron microscopy and auxiliary experiments in synthetic solutions indicated that this behavior was caused by inhomogeneities at the steel–mortar interface in the alkali‐activated mortar, likely due to its peculiar rheological properties in the fresh state.
Often 3D‐printing and additive manufacturing are mentioned as the 3rd industrial revolution. In this conjunction this book provides a brief overview on additively manufactured metal pieces.
This book fulfills its intension to serve as an educational guide, providing a holistic picture encompassing science, technology and applications for the real‐life use of Metal Additive Manufacturing.
Early Stage of Corrosion Formation on Pipeline Steel X70 Under Oxyfuel Atmosphere at Low Temperature
(2020)
The early stage of corrosion formation on X70 pipeline steel under oxyfuel atmosphere was investigated by applying a simulated gas mixture (CO2 containing 6700 ppmv O2, 100 ppmv NO2, 70 ppmv SO2 and 50 ppmv H2O) for 15 h at 278 K and ambient pressure. Short-term tests (6 h) revealed that the corrosion starts as local spots related to grinding marks progressing by time and moisture until a closed layer was formed. Acid droplets (pH 1.5), generated in the gas atmosphere, containing a mixture of H2SO4 and HNO3, were identified as corrosion starters. After 15 h of exposure, corrosion products were mainly X-ray amorphous and only partially crystalline. In-situ energy-dispersive X-ray diffraction (EDXRD) results showed that the crystalline fractions consist primarily of water-bearing iron sulfates. Applying Raman spectroscopy, water-bearing iron nitrates were detected as subordinated phases. Supplementary long-term tests exhibited a significant increase in the crystalline fraction and formation of additional water-bearing iron sulfates. All phases of the corrosion layer were intergrown in a nanocrystalline network. In addition, numerous globular structures have been detected above the corrosion layer, which were identified as hydrated iron sulphate and hematite. As a type of corrosion, shallow pit formation was identified, and the corrosion rate was about 0.1 mma−1. In addition to in-situ EDXRD, SEM/EDS, TEM, Raman spectroscopy and interferometry were used to chemically and microstructurally analyze the corrosion products.