Today an expanding application of high-strength steels in modern welded constructions can be observed. The economical use of these steel grades largely depends on the strength and reliability of the weldments. Therefore the special microstructure and mechanical properties of these grades have to be taken into account by keener working ranges regarding the welding parameters. However, performance and safety of welded components are strongly affected by the stresses occurring during and after welding fabrication locally in the weld seam and globally in the whole component, especially if the shrinkage and distortion due to welding are restrained. Some extensive studies describe the optimization of the welding stresses and the metallurgical effects regarding an adapted welding heat control. In particular lower working temperatures revealed to be effective to significantly reduce the local and global welding induced residual stresses of the completed weld. However, decreased interpass temperatures cause concurrently higher stresses during welding fabrication. This work shows some strategies to reduce these in-process stresses. With help of multi-axial welding stress analyses in component-related weld tests using a special 2-MN-testing facility differences in stress build-up are described in detail for root welds, filler layers and subsequent cooling to ambient temperature.
In an increasing number of modern steel applications high-strength steel grades are demanded to meet specifications regarding a high load bearing capacity and a low operating weight. Lightweight design rules enhance the safety requirements, especially for welded joints. Besides a higher cracking risk for HSLA steel welds, the formation of tensile residual stresses might lead to fracture due to overloading or premature failure if not adequately considered. In codes and standards, therefore, residual stress on the amount of the yield strength are expected, disregarding the circumstance that generally the residual stresses are much lower in HSLA steel welds. Oftentimes this leads to an underestimation of the proof strength in high-strength welded components and economical disadvantages using HSLA steels. In this study, a stress-strain analysis was conducted at component related structures from S960QL using digital image correlation while preheating welding and cooling adjacent to the weld seam. X-ray diffraction analysis of the local residual stresses in the weld seam showed a good comparability with the global analyses. The comparison of two different seam geometries revealed significantly lower multi-axial stresses if a narrower weld groove is used.
Optimization of welding loads with narrow groove and application of modified spray arc process
(2017)
Current efforts for lightweight design result in a growing application of high-strength fine-grained structural steel in modern constructions, e.g. mobile cranes, with yield strength from 960 MPa. The design of welded structures and welding processes becomes more challenging with increasing material strength and elastic ratios. High residual stresses are able to diminish lifetime, load capacity and component safety and should be avoided. Recent analyses have shown strong influences of heat control and restraint of the weld due to arising reaction stresses, superimposing with local residual welding stresses. Modern inverter technologies allowed the development of numerous modified spray arc processes driven by power source manufacturers, which provide virtually similar features and several benefits, enabling welding of narrower seams with reduced weld volumes and total heat inputs. This research focuses on welding loads due to modified weld seams. The global reaction forces and moments and their superposition with local residual stresses in welded components due to external shrinkage restraints were investigated using a special testing facility and XRD. The restraint intensity, weld seam geometry and welding process were varied for statistical evaluations of resulting welding loads. When welding under restraint, a reduction of the weld seam volume causes significantly lower reaction stress levels.
Today an expanding application of high-strength steels in modern welded constructions can be observed. The economical use of these steel grades largely depends on the strength and reliability of the weldments. Therefore the special microstructure and mechanical properties of these grades have to be taken into account by keener working ranges regarding the welding parameters. However, performance and safety of welded components are strongly affected by the stresses occurring during and after welding fabrication locally in the weld seam and globally in the whole component, especially if the shrinkage and distortion due to welding are restrained. Some extensive studies describe the optimization of the welding stresses and the metallurgical effects regarding an adapted welding heat control. In particular lower working temperatures revealed to be effective to significantly reduce the local and global welding induced residual stresses of the completed weld. However, decreased interpass temperatures cause concurrently higher stresses during welding fabrication. This work shows some strategies to reduce these in-process stresses. With help of multi-axial welding stress analyses in component-related weld tests using a special 2-MN-testing facility differences in stress build-up are described in detail for root welds, filler layers and subsequent cooling to ambient temperature.
In an increasing number of modern steel applications high-strength steel grades are demanded to meet specifications regarding a high load bearing capacity and a low operating weight. Lightweight design rules enhance the safety requirements, especially for welded joints. Besides a higher cracking risk for HSLA steel welds, the formation of tensile residual stresses might lead to fracture due to overloading or premature failure if not adequately considered. In codes and standards, therefore, residual stress on the amount of the yield strength are expected, disregarding the circumstance that generally the residual stresses are much lower in HSLA steel welds. Oftentimes this leads to an underestimation of the proof strength in high-strength welded components and economical disadvantages using HSLA steels. In this study, a stress-strain analysis was conducted at component related structures from S960QL using digital image correlation while preheating welding and cooling adjacent to the weld seam. X-ray diffraction analysis of the local residual stresses in the weld seam showed a good comparability with the global analyses. The comparison of two different seam geometries revealed significantly lower multi-axial stresses if a narrower weld groove is used.
In order to satisfy the growing requirements towards lightweight design and resource efficiency in modern steel constructions, e.g. mobile cranes and bridges, high-strength steels with typical yield strength ≥ 690 MPa are coming into use to an increasing extent. However, these steels require special treatment in welding. The susceptibility for degradation of the mechanical properties in presence of hydrogen increases significantly with increasing yield strength. In case of missing knowledge about how and which amount of hydrogen is uptaken during welding, hydrogen assisted cracking (HAC) can be a negative consequence. Moreover, modern weld technology like the modified spray arc process enables welding of narrower weld seams. In this context, a reduced number of weld beads, volume and total heat input are technical and economic benefits. This work presents the influence of welding parameters on the diffusible hydrogen content in both singlepass and multi-layer welds. Different hydrogen concentrations were detected by varied contact tube distance, wire feed speed, arc length as well as varied arc type (transitional arc and modified spray arc). The results show, that all welding parameters have significant influence on the diffusible hydrogen concentration in the single-pass welds. By increasing the number of weld beads in case of multi-layer welding, the hydrogen concentration have been substantially reduced. Whereby, differences in hydrogen concentrations between both arc types are present.
Present trends to lightweight design lead to an expanding relevance of high-strength fine-grained structural steels especially in mobile crane constructions. With growing material strength, the challenge for welding fabrication increases, since high loading capacities and safety requirements have to be accomplished. The utilisation of the high strength potential often requires complex constructions associated with high restraint conditions while welding. Increased residual stresses may occur due to superimposing reaction and restraint stresses, which have to be quantified and evaluated to ensure the safety and integrity of high-strength steel constructions. Particularly, the scope of residual stresses has to be taken into account for different effects in the HAZ, notches, weld and base metal. Commonly, conservative assumptions of residual stresses lead to distinct underestimations of the load bearing capacity particularly for welded high-strength steel constructions. This study concludes results of recent works of the researchers regarding the complex interaction among heat control, material and restraint intensity on the residual stress state in welded components. These analyses are extended by further experiments. Based on the obtained major effects, an approach for a welding residual stress assessment regarding component design according to prevailing standards for crane construction, an important application for high-strength steels, is presented.