To understand the influence of water and alkalis on aluminosilicate glasses, three polymerized glasses with varying ratios of Na/K were synthesized [(22. 5-x)Na2O-xK2O-22.5 Al2O3-55 SiO2 with x = 0, 7.5, and 11.25]. Subsequently, these glasses were hydrated (up to 8 wt% H2O) in an internally heated gas pressure vessel. The density of hydrous glasses linearly decreased with water content above 1 wt%, consistent with the partial molar volume of H2O of 12 cm3/mol. Near-infrared spectroscopy revealed that hydroxyl groups are the dominant species at water content of <4 wt%, and molecular water becomes dominating at water content of >5 wt%. The fraction of OH is particularly high in the pure Na-bearing glass compared to the mixed alkali glasses. 27Al magic angle spinning-NMR spectroscopy shows that aluminum is exclusively fourfold coordinated with some variations in the local geometry. It appears that the local structure around Al becomes more ordered with increasing K/Na ratio. The incorporation of H2O reinforces this effect. The differential thermal analysis of hydrous glasses shows a significant mass loss in the range of glass transition already during the first upscan, implying the high mobility of water in the glasses. This observation can be explained by the open structure of the aluminosilicate network and by the low dissociation enthalpy of H2O in the glasses (≈ 8 kJ/mol). The effect of the dissolved H2O on the glass transition temperature is less pronounced than for other aluminosilicate glasses, probably because of the large fraction of Al in the glasses.
To understand the impact of dissolved water on structure and properties, four boron-rich glasses of molar compositions 15-x Na2O x CaO 15 SiO2 70 B2O3 (with x=0, 7.5, 10) and 10 Na2O 15 SiO2 75 B2O3 were prepared and subsequently hydrated (up to 8 wt% H2O). Density measurements show a non-linear trend upon hydration implying large structural changes in particular at water contents<2 wt%. Near-infrared spectroscopy shows hydroxyl groups are the dominant species in all glasses upon the entire range of water content. Molecular H2O is detectable only at total water contents>2 wt%. 11B MAS NMR spectra show that the abundance of BO4 species is mainly controlled by ratio of (Na2O+CaO)/B2O3 while incorporation of water plays a minor role.
Compared to borate glasses, the efficiency of formation of BO4 tetrahedra is favored by crosslinking of the network by SiO4-units. The glass transition temperatures, determined by differential thermal analysis, decreases continuously with water content due to breakage of B-O-B bonds by hydrolysis. However, compared to Silicates and aluminosilicates, the effect of dissolved water is less pronounced which can be explained by weaker B-O-B bonds in comparison to Si-O-Si bonds.
Pharmaceutical cocrystals are homogenous crystalline structures made up of two or more components in a definite stoichiometric ratio, where at least one of the components in the crystal lattice is an active pharmaceutical ingredient (API).1 Pharmaceutical cocrystals have opened the opportunity for engineering solid-state forms designed to have tailored properties to enhance drug product bioavailability and stability, as well a enhance processability of the solid material inputs in drug product manufacture. In this work the cocrystallization of bexarotene, an approved API by the U.S. Food and Drug Administration that belongs to Biopharmaceutics Classification System Class II (low solubility–high permeability), with pyridine carboxamide isomers (picolinamide, nicotinamide and isonicotinamide) was successfully undertaken. The synthesis was achieved by liquid assisted grinding (LAG) and the solids obtained were characterized by differential scanning calorimetry (DSC), infrared spectroscopy (FTIR-ATR), powder X-ray diffraction (XRPD), single crystal X-ray diffraction (SXD), and polarized light thermomicroscopy (PLTM). For bexarotene: picolinamide and bexarotene:isonicotinamide, 1:1 cocrystals were obtained directly from milling. SXD data of bexarotene:isonicotinamide cocrystal reveal acid∙∙∙aromatic nitrogen supramolecular heterosynthon and that the homosynthon amide∙∙∙amide in isonicotinamide is preserved. The bexarotene:nicotinamide mixtures prepared by ball milling give rise to simple binary solid–liquid phase diagram with an eutectic point, well described by the Schröder-van Laar equation. Melt crystallization of the 1:1 mixture gives rise to a cocrystal for which a complex phase behaviour is observed.
The adsorption behavior of Platinum nanoparticles was studied for the as-received catalyst (under inert gas), under hydrogen and CO atmosphere using our newly designed in-situ cell. X-ray Absorption Spectroscopy (XAS) and Diffuse Reflectance Infrared Fourier Transform Spectroscopy (DRIFTS) experiments were performed simultaneously with high data quality. Structural information and the type of adsorbate could be revealed via Extended X-ray Absorption Fine Structure (EXAFS) analysis, Δμ X-ray Absorption Near Edge Structure analysis (Δμ XANES) and in-situ DRIFTS. The as-received catalyst showed sub-surface oxygen and O(n-fold). Under CO atmosphere only CO(atop) was found. Reversible adsorbate induced changes of the Pt nanoparticle structure were derived from changes in the Pt-Pt coordination number and the corresponding bond distance. Under reducing conditions (H2, CO) a significant increase in both values occurred. Temperature dependent desorption of CO revealed a gradual shift from Pt-CO to Pt-O. Reoxidation was clearly assigned to strong metal support interaction from the SiO2 support.