A comparison between the results obtained from a Computational Fluid Dynamic (CFD) simulation and from the application of an empirical formula for determining the temperature distribution inside a tunnel in case of fire is presented. The temperature is measured and calculated at different distances from the location of the fire and at different time intervals. The fire considered varies with time following a time-heat release rate curve which has a parabolic growing phase, a constant period and a linear decay. The comparison reveals differences in the results. The temperatures calculated with the empirical formula resulted higher than the temperatures obtained by means of the CFD simulation. A list of possible reasons for this limited correspondence is also presented and commented. A proposal for further studies to better define the limitations of both the procedures and to define the influence of each parameter involved is finally presented.
Unilateral thermal exposure of concrete building components induces moisture transport processes that have a significant influence on the spalling behaviour of dense high-strength concrete (HSC). These transport processes are based on evaporation and condensation mechanisms of liquid and gaseous water in the pores as well as the chemically bound water within the concrete. The low permeability of HSC and the formation of a saturated zone within building components (also known as a moisture clog) leads to high water-vapour pressures, which contributes to explosive spalling. The formation of these pressures has already been verified by means of pore-pressure measurement techniques. In addition, the redistribution of the moisture within concrete specimens subject to unilateral thermal exposure has been demonstrated on fractured surfaces. Investigations by means of the nuclear magnetic resonance (NMR) relaxometry technique and neutron radiography have shown one-dimensional changes in moisture distribution during thermal exposure.
However, none of these methods has been able to depict the moisture distribution in three dimensions (3D), so the link between pore size, concrete micro-structure and moisture content is missing. The research project presented in this paper aims to fill this gap by developing a new multi-level test methodology to characterise non-destructively the temporal course of spatial moisture distribution during unilateral thermal exposure. The procedure used during this programme included the collection of X-ray 3D-computed tomography (CT) measurements using a miniaturised specimen subjected to in-situ thermal exposure and the comparison of those CT results with the results of one-dimensional NMR-relaxometry before and after the heating process.
In the first step, a mobile heating device was developed, built and tested. To simulate a unilaterally-heated construction component, a cylindrical specimen made of HSC (Ø = 40 mm, L = 100 mm) was cast into an impermeable glass ceramic shell. The ceramic shell ensured a one-dimensional moisture flux and limited the thermal expansion of the concrete. An additional high-temperature wool (HTW) insulating shell ensured a one-dimensional heat flux. The heating device, which operated using infrared radiation (IR), allowed the unilateral heating of the specimens up to 300 °C using variable heating regimes.
In the second step, the mobile heating device was integrated into the CT-scanner, which enabled the collection of measurements before, during and after heating. By subtraction of successive 3D-CT images, X-ray attenuation differences could be resolved three-dimensionally in the specimen and interpreted as changes in the moisture content.
Initial results show that this test methodology can monitor the 3D changes of moisture content inside the specimen during thermal exposure. It enables the researcher to visualise areas with moisture accumulation as well as dehydrated areas inside the specimen. Comparative one-dimensional NMR-relaxometry measurements confirm the results of the CT image analysis.
Unilateral thermal exposure of concrete building components induces moisture transport processes that have a significant influence on the spalling behaviour of dense high-strength concrete (HSC). These transport processes are based on evaporation and condensation mechanisms of liquid and gaseous water in the pores as well as the chemically bound water within the concrete. The low permeability of HSC and the formation of a saturated zone within building components (also known as a moisture clog) leads to high water-vapour pressures, which contributes to explosive spalling. The formation of these pressures has already been verified by means of pore-pressure measurement techniques. In addition, the redistribution of the moisture within concrete specimens subject to unilateral thermal exposure has been demonstrated on fractured surfaces. Investigations by means of the nuclear magnetic resonance (NMR) relaxometry technique and neutron radiography have shown one-dimensional changes in moisture distribution during thermal exposure.
However, none of these methods has been able to depict the moisture distribution in three dimensions (3D), so the link between pore size, concrete micro-structure and moisture content is missing. The research project presented in this paper aims to fill this gap by developing a new multi-level test methodology to characterise non-destructively the temporal course of spatial moisture distribution during unilateral thermal exposure. The procedure used during this programme included the collection of X-ray 3D-computed tomography (CT) measurements using a miniaturised specimen subjected to in-situ thermal exposure and the comparison of those CT results with the results of one-dimensional NMR-relaxometry before and after the heating process.
In the first step, a mobile heating device was developed, built and tested. To simulate a unilaterally-heated construction component, a cylindrical specimen made of HSC (Ø = 40 mm, L = 100 mm) was cast into an impermeable glass ceramic shell. The ceramic shell ensured a one-dimensional moisture flux and limited the thermal expansion of the concrete. An additional high-temperature wool (HTW) insulating shell ensured a one-dimensional heat flux. The heating device, which operated using infrared radiation (IR), allowed the unilateral heating of the specimens up to 300 °C using variable heating regimes.
In the second step, the mobile heating device was integrated into the CT-scanner, which enabled the collection of measurements before, during and after heating. By subtraction of successive 3D-CT images, X-ray attenuation differences could be resolved three-dimensionally in the specimen and interpreted as changes in the moisture content.
Initial results show that this test methodology can monitor the 3D changes of moisture content inside the specimen during thermal exposure. It enables the researcher to visualise areas with moisture accumulation as well as dehydrated areas inside the specimen. Comparative one-dimensional NMR-relaxometry measurements confirm the results of the CT image analysis.
In order to study damage in concrete exposed to fire, a series of continuous X-ray computed tomography (CT) measurements were performed on a concrete sample heated, in-situ, on one side. The water migration relative to time and 3D space and, in particular, the dynamic condensation and vaporization of water droplets in the pores was quantified. This approach shows significant potential for further investigation of fire-related concrete damage.
Although concrete itself is not a combustible material, concrete mixtures with high density, such has high-performance concretes (HPCs), are susceptible to significant damage during fires due to explosive spalling. Past research has shown that the inclusion of polymer fibers in high density concrete can significantly mitigate fire damage due to the contribution of the fibers to increased permeability levels at high temperature. This allows vapor pressures caused by the evaporation of internal water during fire to escape from the material without causing significant spalling. Recent microscopic investigations have also shown that the addition of polypropylene (PP) fibers to high-density HPC with a high amount of fine-aggregate has a considerable influence on the nature and character of crack formation due to autogenous shrinkage. Initial cracks, which originate from the fiber beds, undergo further expansion and propagation when concrete is subjected to thermal exposure in excess of 170 °C. It is thus of interest to determine whether the resulting cracks join the adjacent fiber beds and therefore contribute to a significant increase in the permeability of the concrete, which is directly correlated to lower pore pressures and reduced spalling during fire.
In this study, X-ray Computed Tomography (CT) was applied to provide a clear demonstration of the interaction between polymer fibers and cracking during thermal exposure. For this purpose, two concrete samples containing different polymer fiber types were subjected to incremental application of a defined thermal exposure. CT images were acquired before and after each thermal exposure and powerful image processing tools were used to segment the various material components, such as polymer fibers, cracks, aggregates and cement matrix, in each image. This enabled a detailed analysis of crack formation and propagation as well as the visualization and quantification of polymer fiber characteristics within the concrete. This paper will provide a description of the distribution and orientation characteristics of the polymer fibers within each sample obtained through the CT-based analysis. Using these results, the impact of fiber distribution and orientation characteristics on actual cracking geometries have been measured and visualized. This paper will also provide recommendations for further optimization of the selected materials and propose improved methods for future CT-based analysis techniques.
A probabilistic finite elements analysis (FEA) of a tunnel lining subject to fire is presented. The probability distributions of the parameters related to the thermal analysis was considered in order to study the variability of the results and to carry out a reliability analysis. This assessment considered as random variables the thermo-mechanical properties of the concrete, the maximum heat release rate (HRR), the duration of the period of maximum HRR, the convective coefficient, the emissivity at the surface exposed to the fire, the air velocity within the tunnel, and the initial fire radius. The temperature-time curve was described by a correlation. An experimental design based on a Latin Hypercube Sampling algorithm was performed to define the input parameters to each analysis case. The definition of a limit state function based on the punctual strain status has permitted to carry out a reliability analysis.
Probabilistic thermo-Mechanical analysis of a concrete tunnel lining subject to fire The probability distributions of the parameters related to the thermal analysis was considered in order to study the variability of the results and to carry out a reliability analysis. This assessment considered as random variables the thermo-mechanical properties of the concrete, the maximum heat release rate (HRR), the duration of the period of maximum HRR, the convective coefficient, the emissivity at the surface exposed to the fire, the air velocity within the tunnel, and the initial fire radius. The temperature-time curve was described by a correlation. An experimental design based on a Latin Hypercube Sampling algorithm was performed to define the input parameters to each analysis case. The definition of a limit state function based on the punctual strain status has permitted to carry out a reliability analysis.
A probabilistic approach for finite element analysis (FEA) for tunnel linings exposed to the nominal fire is presented. The probabilistic FEA accounted for the uncertainties distributions tied to the conductivity and specific heat as well as of the compressive strength, tensile strength, Young’s modulus, and ultimate strain in compression. To get an understanding on the influence of different probability density functions on the distribution of maximum displacements of the tunnel lining, a sensitivity analysis was performed. Four sets of FEAs were carried out with different probability distributions of the conductivity, the specific heat, and the compressive strength of the concrete, respectively. An experimental design based on a Latin Hypercube Sampling algorithm was performed to define the input parameters which describe each analysis case. A reliability analysis was executed considering a limit state function based on the temperature-dependent ultimate strain. The results show that, depending on the distribution adopted, the standard deviation of the maximum displacements can vary up to 47,4% of the minimum standard deviation. The large standard deviation is associated with the possibility of a greater displacement and, hence, to a structure more vulnerable to fire.
The results are based on data1. Figure 3 displays temperatures of the tank wall and of the gas phase over testing time. It can be seen that a complete coating strongly delayed the heating of tank wall and gas phase, whereas the partly coated tanks only had a minor influence on temperature development. There was no significant difference between a half coated and a thirdly coated tank measurable. Figure 4 shows the internal pressure of tanks over testing time. Only the fully coated tank enabled a low pressure over 90 min testing time. Hence, a complete coating is necessary to guarantee the fire safety of hazmat tanks and a partly coating is not sufficient.
Die Entwicklung von leistungsfähigen Fließmitteln in den letzten Jahrzehnten ermöglicht die Herstellung von Beton mit sehr geringem w/z-Wert, bei gleichzeitig guter Verarbeitbar-keit. Die Reduzierung des w/z-Wertes geht dabei mit einer Erhöhung der Festigkeit und einer Verdichtung der Gefü-gestruktur einher. Aufgrund der hohen Druckfestigkeit finden diese Hochleistungsbetone vermehrten Einsatz im Hoch-, Brücken-, und Tunnelbau. Unter Brandbeanspruchung neigen diese Hochleistungsbetone allerdings zu explosionsartigen Abplatzungen. Diese werden nach derzeitigem Stand auf thermomechanische und thermohydraulische Prozesse zurückgeführt. Letztere beruhen auf der Generierung hoher Wasserdampfdrücke in einseitig brandbeanspruchten Beton-bauteilen, die zum einen auf die geringe Permeabilität des Hochleistungsbetons und zum anderen auf die Bildung einer wassergesättigten Zone, der sogenannten „moisture clog“ zurückzuführen sind. Dabei spielen Verdampfungs- und Kondensationsvorgänge sowie der vorhandene Temperatur-gradient eine wichtige Rolle. Die Interaktion des Feuchtetra-nsportes mit den Gefügeveränderungen während der thermi-schen Beanspruchung soll im Rahmen weiterer Versuche eingehend untersucht werden.
Zur Analyse des Feuchtetransports während der thermischen Beanspruchung wurden miniaturisierte Prüfkörper aus Hoch-leistungsbeton hergestellt, die mit Hilfe eines elektrischen Heizelements einseitig erwärmt wurden. Zur Sicherstellung eines eindimensionalen Wärme- und Feuchtetransportes ist der Betonprüfkörper mit einer speziellen Glaskeramik und einer Hochtemperaturwolle ummantelt. Simultan zur Erwär-mung werden eine Reihe röntgentomographischer Aufnah-men durchgeführt. Durch Differenzbildung aufeinanderfol-gender Aufnahmen können Dichteveränderungen lokal und zeitlich aufgelöst werden. Diese lassen Rückschlüsse auf Än-derungen der Feuchteverteilung im Prüfkörper während der Erwärmung zu. Parallel dazu werden Untersuchungen mittels NMR-Relaxometrie (nuclear magnetic resonance) vor und nach der thermischen Beanspruchung durchgeführt. Diese Prüfmethodologie ermöglicht es erstmals, die Veränderungen der Feuchteverteilung infolge thermischer Beanspruchung im Hochleistungsbeton von den Gelporen bis hin zu vorhande-nen Verdichtungsporen abzubilden. So zeigen erste Ergebnis-se, dass die gewählten Untersuchungsmethoden Veränderun-gen der Feuchteverteilung im Prüfkörper räumlich und zeitlich auflösen können.