- 7.6 Korrosion und Korrosionsschutz (8) (entfernen)
The corrosivity of atmospheres in Europe has changed significantly in recent decades. For the Federal Republic of Germany, no current values for the corrosion rate based on 1‐year atmospheric exposure of standard specimens can be found in the scientific literature after 2000. This paper presents results from a field exposure study in the Berlin metropolitan area and Helgoland in 2016. Based on standard specimens, values for the corrosion rate and the corresponding atmospheric corrosivity category are determined for open exposure and indirect weathering in a ventilated enclosure as sheltering after 1 year of exposure. The results prove that determined corrosivity categories are material‐specific. Sheltered exposure is a typical atmospheric situation for many building components. It allows statements on the effect of the concentration of airborne substances on the corrosivity beyond the normative requirements.
Although zinc and zinc coatings have been widely used for corrosion protection for decades new zinc coatings are constantly being developed. Characterizing the corrosion protectiveness of these new coatings, however, should not be underestimated. While exposure tests are time intensive, cyclic tests can only be used for a very limited field of application. Thus, electrochemical measurements provide both an efficient and an effective alternative. Conventional aqueous bulk electrolytes influence the surface layers of a tested zinc coating and are therefore not reliable. Gel electrolytes, however, have evolved over the last few years, are minimally invasive and provide reliable results.
This work describes experiments with gel electrolytes made of agar. Unlike previous work, it proposes a composition of gel electrolyte for minimally invasive description of the protective power of naturally formed oxide layers on zinc and zinc coatings. Therefore, as a first part, the gel electrolyte made of agar is verified as a method for zinc and zinc-coated samples. Afterwards, this paper introduces the corrosion product layer resistance RL as a promising parameter to evaluate the protective power of zinc coatings. Results are verified with EIS and FTIR measurements. An example on a representative zinc coating demonstrates the practical application.
The corrosion resistance of aluminium surfaces is closely linked to the surfacecstate after a grinding process. For years, iron‐containing abrasive materials were suspected to lead to increased corrosion susceptibility after processing of aluminium surfaces. To prove a possible correlation between the iron content of an abrasive and the corrosion behaviour of aluminium components, scientific investigations and experimentally practical corrosion tests are necessary.
For the current investigation, specimens of a technical Al‐Si alloy from the same batch were used. The test specimens were mechanically ground with various resin‐bonded model abrasives containing different iron contents. The performed corrosion tests did not reveal a negative influence of the different iron‐containing abrasives on the corrosion behaviour of the Al–Si alloy.
However, the most sensitive measuring method (electrochemical noise)
showed differences in the surface activity depending on the type of abrasive.
Samples of the austenitic stainless steel grade X5CrNi18‐10 (1.4301, AISI 304) were ground industrially with various grinding parameters to study their influence on corrosion resistance. The ability of the mechanically ground surfaces to form a stable passive layer was evaluated by KorroPad test and a modified electrochemical potentiodynamic reactivation test based on a single loop (EPR‐SL). Furthermore, the surfaces were characterized by surface analytical methods. The main influence was determined regarding abrasive belt type. Surfaces mechanically ground with granulate abrasive belts constantly had a lower corrosion resistance than surfaces ground with single‐coated grain. The granulate abrasive belts generated more sensitized surface areas and left formations of welded sample material on the mechanically ground surfaces. A post‐treatment with a nonwoven abrasive proved to be an effective finishing process by which the surface defects and sensitized material got removed and the surfaces regained the expected corrosion resistance.
The present work describes the combination of electrochemical investigations by using a gel‐type electrolyte with Fourier‐transformed infrared spectroscopy to investigate partially extremely thin corrosion product films on titanium‐zinc. The gel pad method enables the determination of corrosion relevant parameters such as the potential and the linear polarization resistance without altering the corrosion product layers, which are extremely prone to re‐dissolution when freshly formed. Complementary infrared spectroscopy enables the determination of main compounds of even very thin surface layers of few tenth of nanometers with a certain lateral resolution. It was found that zinc forms mostly zinc carboxy‐hydroxides such as hydrozincite, under various exposure conditions. The protective properties of these hydrozincite layers depend on the structure of the corrosion product film rather than on its thickness. In mid‐term exposure tests, shallow corrosion pits were found even in the absence of corrosive agents such as chloride.
Forschungsprojekt zum Korrosionsverhalten von Edelstählen - BAM und VSM mit neuen Erkenntnissen
(2019)
Wie kann man verhindern, dass Edelstahl korrodiert? Und welchen Einfluss haben Kornarten und Körnungen von Schleifmitteln auf das Korrosionsverhalten? Diesen Fragen ist die Bundesanstalt für Materialforschung und -prüfung (BAM) mit Unterstützung der VSM AG zwei Jahre lang auf den Grund gegangen. Heute wurden im VSM Technical Center am Hauptsitz von VSM in Hannover die Ergebnisse vorgestellt. Die zentralen Erkenntnisse: Kornarten und Zusätze im Schleifmittel haben keinen Einfluss auf die Korrosion. Aber: Je feiner die Oberfläche geschliffen ist, desto besser ist der Korrosionsschutz. Dabei ist das Einhalten der Schleiffolge besonders wichtig.
Bei der Planung und Gestaltung von Konstruktionen spielt der Korrosionsschutz und eine korrosionsschutzgerechte Bauweise eine zentrale Rolle. In einigen Fällen jedoch kann es durch bestimmte Randbedingungen und Eigenschaftsanforderungen an Komponenten und Bauteilen zur Ausbildung von galvanischer Korrosion durch Korrosionselemente kommen. Eine sehr häufig auftretende Form der galvanischen Korrosion ist die Bimetallkorrosion, bei der das Korrosionselement durch die Kombination verschiedener metallener Werkstoffe gebildet wird. Unter bestimmten Einsatzbe¬dingun¬gen kann ein solches Korrosionselement zu einem signifikant erhöhten Korrosionsabtrag führen und damit die technische Sicherheit gefährden. Trotz dem Vorhandensein solcher Korrosionselemente (z.B. Mischbauweise bei Konstruktionen) lässt sich das Risiko für galvanische Korrosion durch entsprechende Planung und konstruktive Gestaltung aber auch minimieren. Die Grundlagen der galvanischen Korrosion und Einflussgrößen vor allem auf die Bimetallkorrosion werden dargestellt und deren praktische Bedeutung anhand von Beispielen verdeutlicht.
Nine different stainless steel alloys were exposed for 5 years under marine environment and their corrosion behaviour was compared and assessed. The investigation of four different surface finishes for all alloys tested further enabled to consider industry-specific features of the surface finish for the material comparison. The results of the exposure tests yield conclusions regarding the influence of alloy composition, surface finish and exposure duration under marine environment. The three duplex stainless steels revealed excellent corrosion resistance even in case of crevices during the 5 years of exposure under the given exposure conditions. Also the molybdenum-alloyed ferritic steel 1.4521 showed good corrosion resistance comparable to the classical austenitic materials 1.4301 and 1.4404.