Eingeladener Vortrag
- nein (5)
The detection and characterization of surface breaking cracks in steel prior to damage is a technologically as well as economically important task especially for safety-relevant structures. Detection of small cracks already during the steel production process might significantly reduce the risk of failure and reduce production costs due to an obsolete post-processing.
However, the hostile environmental conditions (high temperature specimens) together with very strict requirements in current steel production (production speeds, in-line testing and evaluation) are challenging and render many well-established NDE techniques hardly applicable.
We present an approach to use laser thermographic testing as a fast, remote and contactless NDE method, that addresses these challenges and might ultimately allow for online crack detection.
The basic idea of laser thermographic testing, introduced by Kubiak in 1968, is the monitoring of the heat flow as induced by local heating. Disturbances within the heat flow generated by the presence of surface cracks can then be analyzed by image processing algorithms, as we have shown in previous work.
The aim of the presented work is to advance laser thermographic testing to be applicable to the specific conditions of steel production environments. This purpose was met by the development of a laboratory setup that allows us to simulate production conditions, as rolling speed, specimen temperature, laser heating power and study their influence on crack detection performance. This parametric study enabled us to develop and improve data processing and crack detection algorithms with the final goal of providing optimized in-line crack detection. The studies were accompanied by comprehensive FEM simulations to intensify the understanding of the contrast formation as well as the crucial parameters influencing the performance of the method.
Laser-induced periodic surface structures (LIPSS) can be generated by irradiation of almost any material with linearly polarized laser beams, particularly when using ultrashort laser pulses.
Within this work, different types of steel were irradiated at optimized conditions for the processing of large surface areas. For these nanostructured surfaces, the coefficient of friction (COF) using different lubricants was determined and the corresponding wear tracks were characterized by scanning electron microscopy (SEM). Our experiments provide a qualification of the tribologicalperformance of the fs-LIPSS on different steel surfaces, which are relevant for technical applications.
Ultrashort laser pulses with durations in the fs- to ps-range were used for large area surface processing of steel aimed at mimicking the morphology and extraordinary wetting behaviour of bark bugs (Aradidae) found in nature. The processing was performed by scanning the laser beam across the surface of initially polished flat sample surfaces. A systematic variation of the laser processing parameters (peak fluence, scan velocity, line overlap) allowed the identification of different regimes associated with characteristic surface morphologies (laser-induced periodic surface structures (LIPSS), grooves, spikes, etc.). Additionally, we show that different laser processing strategies, varying laser wavelength, pulse duration and repetition rates, allowed to achieve a range of morphologies that resemble different structures found in bark bugs. For identifying the ideal combination of parameters for mimicking bug-like structures, the surfaces were inspected by optical and scanning electron microscopy.
Complementary to the morphology study, the wetting behaviour of the surface structures for water and oil was examined intensively in terms of philic/-phobic nature and fluid transport. With these results in hand, tribological tests were carried out investigating the wear resistance of the laser-induced nano- and microstructures. Our results demonstrate a route towards reproducing complex structures inspired by nature and their functional response in technologically relevant materials.
Nature provides countless examples of surface structures featuring extraordinary properties such as directional fluid transport. In order to mimic the morphology and outstanding wetting behaviour of bark bugs, ultrashort laser pulses with durations in the fs- to ps-range were employed for large area surface processing of steel. By scanning the laser beam across the surface of initially polished flat sample surfaces and systematically varying the laser processing parameters (peak fluence, scan velocity, line overlap), different regimes associated with characteristic surface morphologies (laser-induced periodic surface structures (LIPSS), grooves, spikes, etc.) could be identified. Additionally, different laser processing strategies were applied, varying laser wavelength, pulse duration and repetition rates, which allowed to achieve a range of morphologies that resemble different structures found on bark bugs. For identifying the ideal combination of parameters for mimicking such bug-like structures, the surfaces were inspected by means of optical and scanning electron microscopy.
Complementary to the morphology study, the wetting behaviour of the surface structures for water and oil was examined intensively in terms of fluid transport and philic/-phobic nature. Additionally, with these results in hand, tribological tests investigating the wear resistance of the laser-induced nano- and microstructures were carried out. Our results demonstrate that the functionality of surface structures found in nature could be transferred to technologically relevant materials, such as steel, providing a huge potential for industrial applications for instance in friction and wear reduction.
X5CrNiCuNb16-4 has been proven to be sufficient resistant in corrosive environments, but shows rather unusual corrosion behaviour in CCS environment. Therefore a series of 30 specimens was tested at stress amplitudes between 150 MPa and 500 MPa (sinusoidal dynamic test loads, R=-1; resonant frequency ∼ 30 Hz). Due to the rather heterogeneous fine machined surfaces (Rz=4) the specimens are comparable with prefabricated parts. X5CrNiCuNb16-4 reached the maximum number of cycles (10 x 106) at a stress amplitude of 150 MPa and lies 60% below the stress amplitude measured in air. The scatter range TN = 1:34 is disproportionately large. Although the fracture surface exhibited the typical striations and corroded surface areas no significant differences were found. The hardness was found to be homogeneous in all specimens tested at 335 HV10. Non-metallic inclusions were found within the microstructure, but no correlation could be found between the inclusions and early rupture. Still specimens that showed inclusions at the fracture surface and its cross section endured lower number of cycles. Additionally Aluminium was analysed in specimens with low number of cycles and may be cause for early rupture during corrosion fatigue tests. These findings reveal a very high sensitivity on a homogeneous microstructure upon the corrosion and corrosion fatigue behaviour of X5CrNiCuNb16-4 and needs to be taken into account when regarding this steel as pipe steel during injection of CO2 into saline aquifers.
Unusual Corrosion Behavior of 1.4542 Exposed a Laboratory Saline Aquifer Water CCS-Environment
(2017)
Differently heat treated coupons of 1.4542 were kept at T=60 °C and ambient pressure as well as p=100 bar for 700 h - 8000 h in an a) water saturated supercritical CO2 and b) CO2-saturated synthetic aquifer environment similar to on-shore CCS-sites in the Northern German Basin. Surface corrosion layers are homogeneous but unusually discontinuously ellipsoidal. After 8000 h at 100 bar maximum corrosion rate in the liquid phase is approximately 0.014 mm/year, with normalizing providing best corrosion resistance and approximately 0.003 mm/year in the supercritical phase where hardening+tempering at 670 °C leads to lowest corrosion rates.
The frictional response of molybdenum bis(C11-14 branched and linear alkyl) carbamodithioate oxo thioxo complex (Mo-dttc) versus bismuth dimethyldithiocarbamate (Bi-dtc) and bismuth dodecylbenzene Sulfonate (Bi-ddbsa) slip-rolling under mixed/boundary lubrication (T=120°C, n=10 millions of cycles, P0max=2.25 GPa) in PAO-based formulation against three different steel alloys were compared.
Biofilm formation poses high risks in multiple industrial and medical settings. However, the robust nature of biofilms makes them also attractive for industrial applications where cell biocatalysts are increasingly in use. Since tailoring material properties that affect bacterial growth or its inhibition is gaining attention, here we focus on the effects of femtosecond laser produced nanostructures on bacterial adhesion. Large area periodic surface structures were generated on steel surfaces using 30-fs laser pulses at 790 nm wavelength. Two types of steel exhibiting a different corrosion resistance were used, i.e., a plain structural steel (corrodible) and a stainless steel (resistant to corrosion). Homogeneous fields of laser-induced periodic surface structures (LIPSS) were realized utilizing laser fluences close to the ablation threshold while scanning the sample under the focused laser beam in a multi-pulse regime. The nanostructures were characterized with optical and scanning electron microscopy. For each type of steel, more than ten identical samples were laser-processed. Subsequently, the samples were subjected to microbial adhesion tests. Bacteria of different shape and adhesion behavior (Escherichia coli and Staphylococcus aureus) were exposed to laser structures and to polished reference surfaces. Our results indicate that E. coli preferentially avoids adhesion to the LIPSS-covered areas, whereas S. aureus favors these areas for colonization.
Inorganic materials, such as steel, were functionalized by ultrashort laser pulse irradiation (fs- to ps-range) to modify the surface’s wetting behavior. The laser processing was performed by scanning the laser beam across the surface of initially polished flat sample material. A systematic experimental study of the laser processing parameters (peak fluence, scan velocity, line overlap) allowed the identification of different regimes associated with characteristic surface morphologies (laser-induced periodic surface structures, grooves, spikes, etc.). Analyses of the surface using optical as well as scanning electron microscopy revealed morphologies providing the optimum similarity to the natural skin of lizards. For mimicking skin structures of moisture-harvesting lizards towards an optimization of the surface wetting behavior, additionally a two-step laser processing strategy was established for realizing hierarchical microstructures. In this approach, micrometer-scaled capillaries (step 1) were superimposed by a laser-generated regular array of small dimples (step 2). Optical focus variation imaging measurements finally disclosed the three dimensional topography of the laser processed surfaces derived from lizard skin structures. The functionality of these surfaces was analyzed in view of wetting properties.
The wetting behavior of material surfaces can be controlled by surface structures. We functionalized case-hardened alloyed carbon steel to modify the wetting behavior using ultrashort laser pulses (fs- to ps-range). The laser processing was performed by scanning the laser beam across the surface of initially polished flat sample material. An experimental study of the laser processing parameters (peak fluence, scan velocity, line overlap) rendered an assignment of different regimes associated with characteristic surface morphologies (laser-induced periodic surface structures, grooves, micro cones, etc.) possible. Analyzing the surface using optical as well as scanning electron microscopy allowed the identification of morphologies providing the optimum similarity to the natural skin of non-moisture havesting lizards. For mimicking skin structures of moisture-harvesting lizards, additionally a two-step laser processing strategy was established for realizing hierarchical microstructures. In this approach, micrometer-scaled capillaries (step 1) were superimposed by a laser-generated regular array of small dimples (step 2). Optical focus variation imaging measurements finally revealed the three dimensional topography of the laser processed surfaces derived from lizard skin structures. The functionality of these surfaces was analyzed in view of wetting and directional fluid transport properties. The results suggest possible applications of the laser-structured surfaces.
Ferritic steels with chromium contents up to 13 wt% are used as materials for power plant components as boiler materials (< 2 wt% Cr) and super heater tubes (> 9 wt% Cr). These materials are subject to aggressive corrosion caused by hot gases such as CO2, H2O, O2 and SO2. Especially SO2 causes fatal corrosion even as a minor component. To examine sulfurous corrosion mechanisms, experiments with pure SO2 were conducted. A proper analysis of the material changes requires phase identification and quantification with a high lateral resolution within the corrosion scale.