Several studies have shown that the electron beam (e-beam) can be used to create nanomaterials from microparticles in situ in a TEM. However, attempts to produce gold nanoparticles (NPs) on silicon oxide substrate remained to be accomplished. Here, we show that the production of gold NPs is possible by using the e-beam in a SEM, under a set of parameters. To understand the physical mechanisms leading to the gold NPs, the mechanisms of e-beam induced charging as well as e-beam induced heating of the MPs were discussed. Several hints point to heating as the driving mechanism.
Several studies have shown that the electron beam (e-beam) can be used to create nanomaterials from microparticles in situ in a TEM. However, attempts to produce gold nanoparticles (NPs) on silicon oxide substrate remained to be accomplished. Here, we show that the production of gold NPs is possible by using the e-beam in a SEM, under a set of parameters. The NPs produced present a size gradient along the radial direction. A parameter study shows that the microparticles may: 1) flicker away without producing NPs, 2) fragment to form NPs and/or 3) react with the silicon oxide substrate, depending on the applied current. A hypothesis regarding the driving physical phenomena that lead the microparticles to fragment into NPs is discussed. Fabrication of gold NPs in the SEM provides a more cost-effective option as compared to the established method in the TEM.
1. Introduction
A normally unwanted process that can arise when converging an electron beam onto, e.g. microparticles, has been called "damage induced by electric field" (DIEF) [1]. By DIEF, the convergent electron beam (CEB) imparts a high amount of energy to the microparticle locally and strongly interacts with its atoms. At a specific current density J, which can be controlled by the convergence angle α, the irradiated material begins to transform. The phenomenon of expelling nanomaterial from microparticles under the influence of a convergent electron beam (CB) in a transmission electron microscope (TEM) has been largely studied [2]. Several types of nanoparticles (NPs) have been observed for different metallic materials and metal oxides after specific CB protocols (P) in the TEM. Thus, DIEF can be used as a promising synthesis method controlled changes of micrometric material to create new nanometric material compositions and morphologies.
While these reactions have been observed in situ at the high acceleration voltages associated with TEM, it remains unclear whether the SEM can also be used to fabricate NPs via DIEF. In contrast to TEM there is no possibility to statically convert the electron beam to a range of α to reach the needed J as in TEM. Instead, the scanning parameters and the magnification can be manipulated so as to find an integrated J. Considering that the scanning electron microscope (SEM) is easier to use, more accessible and cheaper than a TEM, here we explore the possibility to transfer the concepts of DIEF known to operate in the TEM for in situ NP generation SEM.
2. Objectives
The main goal is to determine whether DIEF can be translated to the SEM perform to controlled in situ fabrication of nanoparticles from microparticles, using gold microparticles on amorphous SiO substrate as precursors. We determine what experimental parameters must be taken into account to create SEM-based CBPs for NP creation in the SEM with these materials.
3. Materials & methods
Gold microparticles with diameter of around 1 to 3 µm were deposited on electron transparent amorphous SiO/SiO2 substrate. Using a convergent electron beam protocol (CBP) in a scanning electron microscope (SEM) at an acceleration voltage of 30 kV, the gold microparticles were irradiated until a production of NPs takes place as shown in figure 1. The beam current varied between 16 and 23 nA.
4. Results
Depending on the CBP parameters, either only Au NPs or a mixture of Au and Si NPs are produced. The particle size ranges from a few nm up to 100 nm, and it depends on the distance of the NP to the initial position of the microparticle. Further beam parameters such as the dwell time, the effective irradiated volume and particle size determine whether NPs are produced or if the microparticles only are expelled from the substrate without reacting.
5. Conclusion
The SEM can be used as an instrument for synthesizing nanomaterials via DIEF. Different CBP protocols can be applied for obtaining either gold nanoparticles or silicon + gold nanoparticles
Since the TEM has the capacity to observe the atomic structure of materials, in-situ TEM synthesis methods are uniquely suited to advance our fundamental understanding of the bottom-up dynamics that drive the formation of nanostructures. E-beam induced fragmentation (potentially identified as a manifestation of Coulomb explosion) and electron stimulated desorption (ESD) are phenomena that have received attention because they trigger chemical and physical reactions that can lead to the production of various nanostructures. Here we report a simple TEM protocol implemented on WO2.9 microparticles supported on thin amorphous carbon substrates. The method produces various nanostructures such as WC nanoparticles, WC supported films and others. Nevertheless, we focus on the gradual graphitization and gasification of the C substrate as it interacts with the material expelled from the WO2.9 microparticles. The progressive gasification transforms the substrate from amorphous C down to hybrid graphitic nanoribbons incorporating W nanoparticles. We think these observations open interesting possibilities for the synthesis of 2D nanomaterials in the TEM.