The corrosion behavior of galvanized steels and zinc components under atmospheric exposure depends mostly on the corrosion product‐based cover layer formation under the prevailing conditions. The use of agar‐based gel electrolytes makes it possible to use electrochemical methods to obtain a characteristic value from these cover layers that describe their current and future protective capacity. It is shown here that different states of galvanized steel can be distinguished very well under laboratory conditions and that this method is also suitable for use under practical conditions. Based on the characteristic values and assuming future time of wetness, it is very easy to draw up a forecast for the future corrosion rate, which provides plausible values.
Determination of the corrosion product layer resistance on zinc samples by using gel electrolytes
(2022)
Crash barriers, railings, lamp posts, waste glass containers - these are just a few of the many examples of galvanized surfaces. They withstand wind and weather for decades, which is possible thanks to a protective layer made of corrosion products. When designing the atmospheric durability of galvanized components, a linear corrosion loss is assumed. In the past 30 years, however, the surrounding atmosphere has changed a lot. Due to the restriction of sulfur exhaust air, acid rain completely disappeared in Europe and Germany, which has a direct influence on the type and protective effect of the corrosion products. Under the influence of current atmospheric conditions, zinc layers are significantly more resistant and no longer show any linear corrosion loss. The established test methods cannot correctly map this change in neither short-term nor long-term tests and thus provide incorrect results. In order to solve this problem, a new measurement method was developed at BAM that can assess the protective effect of the formed surface layers in a minimally invasive manner without damaging the sample and in short test times. For this new method, gel electrolytes are used and the so-called corrosion product layer resistance RL, which is made up of various surface resistances, is measured electrochemically. As a single measurement, the surface layer resistance can provide information about the existing corrosion protection, while time-dependent measurements assess the stability of the layer. Thus, it is possible again to evaluate the corrosion protection layer. Furthermore, this method can also be used for field measurements on real components.
Although zinc and zinc coatings have been widely used for corrosion protection for decades new zinc coatings are constantly being developed. Characterizing the corrosion protectiveness of these new coatings, however, should not be underestimated. While exposure tests are time intensive, cyclic tests can only be used for a very limited field of application. Thus, electrochemical measurements provide both an efficient and an effective alternative. Conventional aqueous bulk electrolytes influence the surface layers of a tested zinc coating and are therefore not reliable. Gel electrolytes, however, have evolved over the last few years, are minimally invasive and provide reliable results.
This work describes experiments with gel electrolytes made of agar. Unlike previous work, it proposes a composition of gel electrolyte for minimally invasive description of the protective power of naturally formed oxide layers on zinc and zinc coatings. Therefore, as a first part, the gel electrolyte made of agar is verified as a method for zinc and zinc-coated samples. Afterwards, this paper introduces the corrosion product layer resistance RL as a promising parameter to evaluate the protective power of zinc coatings. Results are verified with EIS and FTIR measurements. An example on a representative zinc coating demonstrates the practical application.