Ingenieurwissenschaften und zugeordnete Tätigkeiten
Filtern
Dokumenttyp
- Zeitschriftenartikel (54) (entfernen)
Schlagworte
- Corrosion (21)
- KorroPad (13)
- Nichtrostender Stahl (12)
- Korrosionsschnelltest (11)
- Passivschicht (11)
- Korrosion (8)
- Carbon steel (5)
- Corrosion testing (4)
- Impurities (4)
- Stainless steel (4)
- EPR (3)
- Geothermie (3)
- Pitting corrosion (3)
- Al2O3 (2)
- Alloy 31 (2)
- Aluminium (2)
- Anlagensicherheit (2)
- Austenitic stainless steel (2)
- CCUS (2)
- Carbon dioxide (2)
- Coating (2)
- Condensate (2)
- Copper (2)
- Corrosion rate (2)
- Corrosion resistance (2)
- Gel electrolytes (2)
- Geothermal energy (2)
- Grinding (2)
- Heat treatment (2)
- Legierungen (2)
- Qualitätssicherung (2)
- Steel (2)
- Zinc coatings (2)
- Abrasive belt (1)
- Additive manufacturing (1)
- Agar (1)
- Ageing treatment (1)
- Aktiv-Passiv-Element (1)
- Al-Composite (1)
- Al/SiO2 composite (1)
- Alkali-activated materials (1)
- Aquifer fluid (1)
- Atmospheric corrosion (1)
- Atmospheric exposure (1)
- Atmosphärische Korrosion (1)
- Behmite (1)
- Belüftungselement (1)
- Bimetallkorrosion (1)
- Binary zinc alloys (1)
- Brass (1)
- CCS (1)
- CCUS, supercritical/dense phase CO2, carbon steels, martensitic steel, superaustenite steel, droplet corrosion (1)
- CO2 pipeline transport (1)
- CO2 quality (1)
- Carbon capture (1)
- Carbon capture storage (1)
- Carbon capture, utilization and storage technology (1)
- Casing (1)
- Cement (1)
- Contact angle (1)
- Corrosion costs (1)
- Corrosion protection (1)
- Corrosivity category (1)
- Crevice corrosion (1)
- Critical chloride content (1)
- Critical pitting temperature (1)
- Dealloying (1)
- Disinfectants (1)
- Drinking water (1)
- Electrochemical characterisation (1)
- Electrochemical deposition (1)
- Electrochemical methods (1)
- Electrochemical potentiodynamic reactivation (1)
- Electrochemical potentiokinetic reactivation (1)
- Elektrochemie (1)
- Energy systems (1)
- Environmental Chemistry (1)
- Explosion (1)
- FT-IR (1)
- Flue gas desulphurisation facilities (1)
- Free weathering (1)
- Gel-type electrolytes (1)
- Gelartige Elektolyte (1)
- Geothermal (1)
- Green-Death solution (1)
- Growth defects (1)
- Gutachten (1)
- High‐nitrogen steel (1)
- ISO 9223 (1)
- In-situ ED-XRD (1)
- Iron–chromium–nickel alloy (1)
- Konzentrationselement (1)
- Korrosionsprüfung (1)
- Korrosionsschutz (1)
- Korund (1)
- Kupferazid (1)
- Lead (1)
- Lean duplex (1)
- Lochkorrosion (1)
- Magnesium (1)
- Marine atmosphere (1)
- Martensitic stainless steel (1)
- Martensitic steel (1)
- Martensitic steels (1)
- Mass loss (1)
- Material properties (1)
- Materials (1)
- Materials Chemistry (1)
- Materialuntersuchung (1)
- Mechanical Engineering (1)
- Mechanical properties (1)
- Mechanical strength (1)
- Mechanics of Materials (1)
- Metals and Alloys (1)
- Oxyfuel (1)
- PVD hard coating (1)
- Passive film (1)
- Passivity (1)
- Physical vapour deposition (PVD) (1)
- Pinholes (1)
- Pipeline network (1)
- Pitting (1)
- Polarisation (1)
- Polyaniline (1)
- Preventive strategies (1)
- Protection (1)
- Recommendations (1)
- Schadensanalyse (1)
- Schleifen (1)
- Semiconductive layer (1)
- Sensitisation (1)
- SiO2 Nanoparticle (1)
- Silica (1)
- Stainless steels (1)
- Steel corrosion (1)
- Steel-concrete interface (1)
- Surface (1)
- Surfaces, Coatings and Films (1)
- Survey (1)
- Tafel Plot (1)
- Ternary zinc alloys (1)
- TiMgN (1)
- Titanium nitride (1)
- Umlaufkühler (1)
- Utilization, and storage (CCUS) technology (1)
- Wetting (1)
- Whole-chain CCS scenario (1)
- X-ray photoelectron spectroscopy (1)
- Zinkdeckschichten (1)
- Znc (1)
- magnesium (1)
Organisationseinheit der BAM
- 7.6 Korrosion und Korrosionsschutz (54) (entfernen)
The copper alloyed stainless steel 1.4542 (X5CrNiCuNb16-4) is used in different areas due to its good mechanical properties and corrosion resistance. Strength and corrosion resistance can be adjusted by the heat treatment, which is of importance for the application of this alloy. The mechanical properties (strength and hardness) are attributed to the dispersive precipitation of the copper rich ε–Phase. The additional precipitation of chromium carbides can reduce the corrosion resistance. Different ageing states were produced to investigate the precipitation behaviour with various methods. Furthermore, the influence of cold-rolling on the precipitation behaviour was studied in comparison to a solution annealed state without deformation. The microstructure was studied by SEM and the variations of hardness and magnetic proportion were characterised. The electrochemical potentiodynamic reactivation
(EPR) was used to determine the corrosion resistance and detect chromium depletion in all heattreated states. The results show that a work hardening accelerates the precipitation rate, while ageing at 600 °C reduces the corrosion resistance due to chromium depletion.
Aging of passive film formed on UNS N08031 was investigated as a function of passivation time in Green-Death solution at 40°C. The specimen surface was in a stable passive state in the solution.
The passive current density increased with an increase in the passivation potential. Electrochemical Impedance Spectroscopy and Mott–Schottky (M–S) analyses revealed that a more defective n-type
semiconductive passive film formed as the potential increased while the film became stable as the defects in the film decreased at potential lower than 1.0 VSSE. The increase of the applied potential and the polarisation time are likely reasons for the change in passive film stability.
Nickel‐free high‐nitrogen‐alloyed stainless steels like the P2000 (X13CrMnMoN18‐14‐3) were developed to enhance the strength and corrosion resistance of austenitic stainless steels like 304 and 316 while keeping the typical high ductility. The mechanical and corrosive properties of P2000 were investigated and compared with 304 and 316 to highlight the application opportunities of this new alloy. The microstructure of the solution‐annealed condition was characterised by electron backscatter diffraction and the mechanical properties were studied by uniaxial tensile tests, Charpy impact tests and hardness measurements. The passivation behaviour was analysed using the electrochemical potentiodynamic reactivation, whereas the pitting corrosion resistance was compared by pitting potentials and pitting temperatures. However, secondary thermal influences or suboptimal heat treatment can impair the corrosion resistance due to the precipitation of secondary phases and the resulting sensitisation. Thermodynamic calculations and artificial ageing treatment in the range of 500–900°C for up to 100 h were used to determine critical time–temperature parameters for sensitisation. The microstructure of the various aged states was evaluated by scanning electron microscopy and compared with the degrading corrosion resistance characterised by the KorroPad method.
Chloride contents at the steel–mortar interface that initiate steel corrosion were determined for carbon steel in alkali‐activated fly ash mortar for three different exposure conditions: exposure to 1 M NaCl solution; leaching in deionized water and then exposure to 1 M NaCl solution; and leaching in deionized water, aging in air at 20°C and natural CO2 concentration, and then exposure to 1 M NaCl solution. For comparison, a Portland cement mortar, exposed to 1 M NaCl solution, was studied. The median values of the corrosion‐initiating chloride contents (average over the full length of the rebar) in the alkali‐activated fly ash mortar varied between 0.35 and 1.05 wt% Cl with respect to binder, consistently lower than what was obtained for the Portland cement mortar, but with no clear trend regarding the exposure conditions. For most of the alkali‐activated fly ash mortar specimens, preferential corrosion at the connection between the working electrode and the external measurement setup was observed, while preferential corrosion did not occur for the Portland cement mortar. Scanning electron microscopy and auxiliary experiments in synthetic solutions indicated that this behavior was caused by inhomogeneities at the steel–mortar interface in the alkali‐activated mortar, likely due to its peculiar rheological properties in the fresh state.
Interfacial properties related to wettability and corrosion in CO2 transport pipelines are experimentally determined by the sessile and the pendant drop methods. The contact angle of a water drop in a compressed CO2 atmosphere is analyzed on an X70 pipeline carbon steel and compared to that on a martensitic steel S41500 to elucidate the effect of corrosion process on active wetting behaviour. The measurements are performed with liquid CO2 at 278 K and pressures ranging from 5 to 20 MPa. The results show that the contact angle (CA) increases with pressure from 132 ° to 143 ° for S41500 and from 117 ° to 137 ° for X70 and decreases with drop age by 20 ° to 24 ° regardless of the pressure and of the fact that corrosion only occurs on X70, which is confirmed by scanning electron microscopy, element mapping and energy dispersive x-ray spectrometry (EDS) analysis. At higher pressure, the contact angles on both materials converge. Further, related properties like density and interfacial tension were determined. CO2 - saturated water has a higher density than pure water: At 5 MPa saturated water reaches a density of 1017 kg⋅m^(-3) and at 20 MPa 1026 kg⋅m^(-3) compared to pure water with a density of 1002 kg⋅m^(-3) and 1009 kg⋅m^(-3), respectively. In this pressure range the IFT drops from 33 mN⋅m^(-1)at 5 MPa to 23 mN⋅m^(-1) at 20 MPa.
Geothermal energy is an interesting alternative to polluting fossil energy sources. Therefore, in Belgium, two wells have been drilled for a deep geothermal power plant. However, the environment to which the installations are exposed is challenging. The geothermal brine has 165 g/l total dissolved solids (of which 90% are sodium and chlorine) and the production temperature can be up to 130 °C. To assess their suitability to be used in a geothermal power plant, the corrosivity of the artificial brine to three common construction materials was investigated with exposure and electrochemical tests. The metals under consideration are a low-alloyed carbon steel (S235JR), an austenitic stainless steel (UNS S31603) and a duplex stainless steel (UNS S31803). The carbon steel, that was found to corrode uniformly, could be considered as a constructional material if a sufficient wall thickness is chosen. The austenitic stainless steel and the duplex stainless steel demonstrate very low uniform
corrosion rates. They are however susceptible to pitting and crevice corrosion. To guarantee safe operation of the geothermal power plant, the susceptibility of the alloys to stress corrosion cracking should be tested and in situ experiments should be performed.
A global transition towards more sustainable, affordable and reliable energy systems is being stimulated by the Paris Agreement and the United Nation's 2030 Agenda for Sustainable Development. This poses a challenge for the corrosion industry, as building climate‐resilient energy systems and infrastructures brings with it a long‐term direction, so as a result the long‐term behaviour of structural materials (mainly metals and alloys) becomes a major prospect. With this in mind “Corrosion Challenges Towards a Sustainable Society” presents a series of cases showing the importance of corrosion protection of metals and alloys in the development of energy production to further understand the science of corrosion, and bring the need for research and the consequences of corrosion into public and political focus. This includes emphasis on the limitation of greenhouse gas emissions, on the lifetime of infrastructures, implants, cultural heritage artefacts, and a variety of other topics.
The composites combining aluminum and silica nanoparticles with the addition of tetramethylammonium hydroxide (Al-SiO2(T)) and butanol (Al-SiO2(B)) as mixing media have been successfully fabricated. Corrosion behavior of Al-SiO2 composites before and after exposure in 1M NaCl solution was examined using potentiodynamic polarization (Tafel curve analysis). The study was also equipped with scanning electron microscopy (SEM), energy dispersive X-ray (EDX), and X-ray diffraction (XRD) investigations. Before exposure, Al-SiO2(T) exhibited the best corrosion resistance. Performance improvement was indicated by Al-SiO2(B) up to 10 times better than Al-SiO2(T) after exposure. The increased SiO2 content did not significantly enhance the corrosion resistance of the composites. The Al-SiO2 composites with 5% SiO2 content showed very high corrosion resistance (as the optimum composition). Furthermore, pitting corrosion was observed in the Al-SiO2 composites, indicated by the formation of corrosion products at grain boundaries. The product was affected by the presence of SiO2 in the Al matrix and the NaCl environment at 90 °C (approach to synthetic geothermal media: Na+, Cl, H+, OH-). Our study revealed the presence of γ-Al2O3, γ-Al(OH)3, and Al(OH)2Cl as the dominant corrosion products.
Hard coated steel components are used in a wide application range, mostly for protective, wear resistant and decorative purposes. Despite of these coatings being regarded as relatively dense, there is always a high risk of localized corrosion when a coated low alloyed steel component encounters a surrounding high humidity atmosphere or even an aqueous medium. An approach to enhance the corrosion properties is the addition of magnesium to physical vapor deposited hard coatings, like TiN. It has been found that there is a remarkable increase in corrosion resistance in dependence of magnesium content of the TiMgN coating and its surface properties. In this work the authors will explain the underlying corrosion protection mechanisms by means of electrochemical and analytical studies. The positive impact of magnesium in the coating relates on its preferred dissolution vs. steel. This causes the potential to shift to more negative direction with respect to the steel substrate and additionally leads to a temporarily passivation of the steel due to alkalization of the surrounding electrolyte by formation of magnesium hydroxide.
Hard and wear resistant coatings deposited by PVD techniques have been characterized for decades for their capabilities to protect steel substrates from corrosion. In the present work the effect of Mg incorporated into TiN coatings is described in terms of the corrosion behavior as well as the mechanical and structural properties.
TiN and TiMgN films with Mg contents between 10 and 35 at.% were deposited onto mirror polished 100Cr6 (1.3505) steel samples with 2.5 and 5 μm thickness by using DC magnetron sputtering. The corrosion protection capabilities of the coatings were characterized by neutral salt spray (NSS) test, considering the amounts and sizes of growth defects inherent in each coated sample as determined by a recently developed optical scan method (Large Area High Resolution mapping). The defect data were statistically analyzed for improved interpretation of NSS test results. Chosen growth defects were additionally analyzed by focused ion beam technique. Furthermore the coating composition and morphology, the hardness and the tribological behavior were characterized.
Polished steel samples coated with 2.5 μm TiMgN containing about 35 at.% Mg were in the plane free of corrosion after 24 h in a NSS test. TiMgN with 10 or 20 at.% Mg only provided a slightly improved corrosion protection in relation to pure TiN coatings, which was limited to certain types of growth defects. The highest Mg containing coatings exhibited a decreased hardness down to 1200 or 1800 HV depending on type of deposition (HV 1200: Ti- and Mg-target with rotating substrate holder, 1800: Mg-plugged Ti-target with static substrate holder), but also showed a strongly improved wear resistance against Al2O3 related to pure TiN. By analyzing the NSS test results it was found that the corrosion behavior of the coated samples did not only depend strongly on the Mg content, but also on the sample individual defect concentrations. Therefore this subject is extensively discussed.